Substantially Improved Na-Ion Storage Capability by Nanostructured Organic-Inorganic Polyaniline-TiO2 Composite Electrodes.

ABSTRACT: Developing sodium (Na)-ion batteries is highly appealing because they offer the potential to be made from raw materials, which hold the promise to be less expensive, less toxic, and at the same time more abundant compared to state-of-the-art lithium (Li)-ion batteries. In this work, the Na-ion storage capability of nanostructured organic-inorganic polyaniline (PANI) titanium dioxide (TiO2) composite electrodes is studied. Self-organized, carbon-coated, and oxygen-deficient anatase TiO2-x -C nanotubes (NTs) are fabricated by a facile one-step anodic oxidation process followed by annealing at high temperatures in an argon-acetylene mixture. Subsequent electropolymerization of a thin film of PANI results in the fabrication of highly conductive and well-ordered, nanostructured organic-inorganic polyaniline-TiO2 composite electrodes. As a result, the PANI-coated TiO2-x -C NT composite electrodes exhibit higher Na storage capacities, significantly better capacity retention, advanced rate capability, and better Coulombic efficiencies compared to PANI-coated Ti metal and uncoated TiO2-x -C NTs for all current rates (C-rates) investigated.

SUBMITTER: Werner D

PROVIDER: S-EPMC7189615 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Substantially Improved Na-Ion Storage Capability by Nanostructured Organic-Inorganic Polyaniline-TiO<sub>2</sub> Composite Electrodes.

Werner Daniel D Griesser Christoph C Stock David D Griesser Ulrich J UJ Kunze-Liebhäuser Julia J Portenkirchner Engelbert E

ACS applied energy materials 20200312 4

Developing sodium (Na)-ion batteries is highly appealing because they offer the potential to be made from raw materials, which hold the promise to be less expensive, less toxic, and at the same time more abundant compared to state-of-the-art lithium (Li)-ion batteries. In this work, the Na-ion storage capability of nanostructured organic-inorganic polyaniline (PANI) titanium dioxide (TiO<sub>2</sub>) composite electrodes is studied. Self-organized, carbon-coated, and oxygen-deficient anatase TiO ...[more]

PMID: 32363329

Similar Datasets

Project description:Tunable porous composite materials to control metal and metal oxide functionalization, conductivity, pore structure, electrolyte mass transport, mechanical strength, specific surface area, and magneto-responsiveness are critical for a broad range of energy storage, catalysis, and sensing applications. Biotemplated transition metal composite aerogels present a materials approach to address this need. To demonstrate a solution-based synthesis method to develop cobalt and cobalt oxide aerogels for high surface area multifunctional energy storage electrodes, carboxymethyl cellulose nanofibers (CNF) and alginate biopolymers were mixed to form hydrogels to serve as biotemplates for cobalt nanoparticle formation via the chemical reduction of cobalt salt solutions. The CNF-alginate mixture forms a physically entangled, interpenetrating hydrogel, combining the properties of both biopolymers for monolith shape and pore size control and abundant carboxyl groups that bind metal ions to facilitate biotemplating. The CNF-alginate hydrogels were equilibrated in CaCl2 and CoCl2 salt solutions for hydrogel ionic crosslinking and the prepositioning of transition metal ions, respectively. The salt equilibrated hydrogels were chemically reduced with NaBH4, rinsed, solvent exchanged in ethanol, and supercritically dried with CO2 to form aerogels with a specific surface area of 228 m2/g. The resulting aerogels were pyrolyzed in N2 gas and thermally annealed in air to form Co and Co3O4 porous composite electrodes, respectively. The multifunctional composite aerogel's mechanical, magnetic, and electrochemical functionality was characterized. The coercivity and specific magnetic saturation of the pyrolyzed aerogels were 312 Oe and 114 emu/gCo, respectively. The elastic moduli of the supercritically dried, pyrolyzed, and thermally oxidized aerogels were 0.58, 1.1, and 14.3 MPa, respectively. The electrochemical testing of the pyrolyzed and thermally oxidized aerogels in 1 M KOH resulted in specific capacitances of 650 F/g and 349 F/g, respectively. The rapidly synthesized, low-cost, hydrogel-based synthesis for tunable transition metal multifunctional composite aerogels is envisioned for a wide range of porous metal electrodes to address energy storage, catalysis, and sensing applications.

Dataset Information

Substantially Improved Na-Ion Storage Capability by Nanostructured Organic-Inorganic Polyaniline-TiO2 Composite Electrodes.

Publications

Substantially Improved Na-Ion Storage Capability by Nanostructured Organic-Inorganic Polyaniline-TiO<sub>2</sub> Composite Electrodes.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets