Dataset Information

Adsorption Performance for Reactive Blue 221 Dye of ?-Chitosan/Polyamine Functionalized Graphene Oxide Hybrid Adsorbent with High Acid-Alkali Resistance Stability in Different Acid-Alkaline Environments.

ABSTRACT: A hybrid material obtained by blending ?-chitosan (CS) with triethylenetetramine-functionalized graphene oxide (TFGO) (CSGO), was used as an adsorbent for a reactive dye (C.I. Reactive Blue 221 Dye, RB221), and the adsorption and removal performances of unmodified CS and mix-modified CSGO were investigated and compared systematically at different pH values (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, and 12). The adsorption capacities of CS and CSGO were 45.5 and 56.1 mg/g, respectively, at a pH of 2 and 5.4 and 37.2 mg/g, respectively, at a pH of 12. This indicates that TFGO was successfully introduced into CSGO, enabling ?-? interactions and electrostatic attraction with the dye molecules. Additionally, benzene ring-shaped GO exhibited a high surface chemical stability, which was conducive to maintaining the stability of the acid and alkali resistance of the CSGO adsorbent. The RB221 adsorption performance of CS and CSGO at acidic condition (pH 3) and alkaline condition (pH 12) and different temperatures was investigated by calculating the adsorption kinetics and isotherms of adsorbents. Overall, the adsorption efficiency of CSGO was superior to that of CS; thus, CSGO is promising for the treatment of dye effluents in a wide pH range.

SUBMITTER: Chiu CW

PROVIDER: S-EPMC7221750 | biostudies-literature | 2020 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Adsorption Performance for Reactive Blue 221 Dye of β-Chitosan/Polyamine Functionalized Graphene Oxide Hybrid Adsorbent with High Acid-Alkali Resistance Stability in Different Acid-Alkaline Environments.

Chiu Chih-Wei CW Wu Ming-Tsung MT Lin Chih-Lung CL Li Jia-Wun JW Huang Chen-Yang CY Soong Yu-Chian YC Lee Jimmy Chi-Min JC Lee Sanchez William Anderson WA Lin Hsuan-Yu HY

Nanomaterials (Basel, Switzerland) 20200414 4

A hybrid material obtained by blending β-chitosan (CS) with triethylenetetramine-functionalized graphene oxide (TFGO) (CSGO), was used as an adsorbent for a reactive dye (C.I. Reactive Blue 221 Dye, RB221), and the adsorption and removal performances of unmodified CS and mix-modified CSGO were investigated and compared systematically at different pH values (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, and 12). The adsorption capacities of CS and CSGO were 45.5 and 56.1 mg/g, respectively, at a pH of 2 and 5. ...[more]

PMID: 32295277

Similar Datasets

Project description:With increasing awareness of reduction of energy and CO2 footprint, more waste is considered recyclable for generating value-added products. Here we reported the negatively-valued iron mud, a waste from groundwater treatment plant, was successfully converted into magnetic adsorbent. Comparing with the conventional calcination method under the high temperature and pressure, the synthesis of the magnetic particles (MPs) by Fe2+/Fe3+ coprecipitation was conducted at environment-friendly condition using ascorbic acid (H2A) as reduction reagent and nitric acid (or acid wastewater) as leaching solution. The MPs with major component of Fe3O4 were synthesized at the molar ratio (called ratio subsequently) of H2A to Fe3+ of iron mud ≥ 0.1; while amorphous ferrihydrite phase was formed at the ratio ≤ 0.05, which were confirmed by vibrating sample magnetometer (VSM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). With the ratio increased, the crystalline size and the crystallization degree of MPs increased, and thus the Brunauer-Emmett-Teller (BET) surface and the cation-exchange capacity (CEC) decreased. MPs-3 prepared with H2A to Fe3+ ratio of 0.1 demonstrated the highest methylene blue (MB) adsorption of 87.3 mg/g and good magnetic response. The adsorption of MB onto MPs agreed well with the non-linear Langmuir isotherm model and the pseudo-second-order model. Pilot-scale experiment showed that 99% of MB was removed by adding 10 g/L of MPs-3. After five adsorption-desorption cycles, MPs-3 still showed 62% removal efficiency for MB adsorption. When nitric acid was replaced by acid wastewater from a propylene plant, the synthesized MPs-3w showed 3.7 emu/g of saturation magnetization (Ms) and 56.7 mg/g of MB adsorption capacity, 2.8 times of the widely used commercial adsorbent of granular active carbon (GAC). The major mechanism of MPs adsorption for MB was electrostatic attraction and cation exchange. This study synthesized a magnetic adsorbent from the negatively-valued iron mud waste by using an environment-friendly coprecipitation method, which had a potential for treatment of dye wastewater.

Dataset Information

Adsorption Performance for Reactive Blue 221 Dye of ?-Chitosan/Polyamine Functionalized Graphene Oxide Hybrid Adsorbent with High Acid-Alkali Resistance Stability in Different Acid-Alkaline Environments.

Publications

Adsorption Performance for Reactive Blue 221 Dye of β-Chitosan/Polyamine Functionalized Graphene Oxide Hybrid Adsorbent with High Acid-Alkali Resistance Stability in Different Acid-Alkaline Environments.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets