Controlled Synthesis of Poly(pentafluorostyrene-ran-methyl methacrylate) Copolymers by Nitroxide Mediated Polymerization and Their Use as Dielectric Layers in Organic Thin-film Transistors.

ABSTRACT: A library of statistically random pentafluorostyrene (PFS) and methyl methacrylate (MMA) copolymers with narrow molecular weight distributions was produced, using nitroxide mediated polymerization (NMP) to study the effect of polymer composition on the performance of bottom-gate top-contact organic thin-film transistors, when utilized as the dielectric medium. Contact angle measurements confirmed the ability to tune the surface properties of copolymer thin films through variation of its PFS/MMA composition, while impedance spectroscopy determined the effect of this variation on dielectric properties. Bottom-gate, top-contact copper phthalocyanine (CuPc) based organic thin-film transistors were fabricated using the random copolymers as a dielectric layer. We found that increasing the PFS content led to increased field-effect mobility, until a point after which the CuPc no longer adhered to the polymer dielectric.

SUBMITTER: Peltekoff AJ

PROVIDER: S-EPMC7361672 | biostudies-literature | 2020 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Controlled Synthesis of Poly(pentafluorostyrene-ran-methyl methacrylate) Copolymers by Nitroxide Mediated Polymerization and Their Use as Dielectric Layers in Organic Thin-film Transistors.

Peltekoff Alexander J AJ Tousignant Mathieu N MN Hiller Victoria E VE Melville Owen A OA Lessard Benoît H BH

Polymers 20200529 6

A library of statistically random pentafluorostyrene (PFS) and methyl methacrylate (MMA) copolymers with narrow molecular weight distributions was produced, using nitroxide mediated polymerization (NMP) to study the effect of polymer composition on the performance of bottom-gate top-contact organic thin-film transistors, when utilized as the dielectric medium. Contact angle measurements confirmed the ability to tune the surface properties of copolymer thin films through variation of its PFS/MMA ...[more]

PMID: 32485806

Similar Datasets

Project description:The key impact and significance of a multilayer polymer-based dielectric system on the remarkable photoresponse properties of zinc phthalocyanine (ZnPc)-based photosensitive organic field-effect transistors (PS-OFETs) have been systematically analyzed at various incident optical powers. A combination of inorganic aluminum oxide (Al2O3) and organic nonpolar poly(methyl methacrylate) (PMMA) is used as the bilayer dielectric configuration, whereas in the trilayer dielectric system, a bilayer polymer dielectric, consisting of PMMA, as the low-k dielectric polymer, on top of poly(vinyl alcohol) (PVA), the high-k polar dielectric, has been fabricated along with Al2O3 as the third layer. Before fabricating the OFETs, a systematic optimization of the nature of growth of the ZnPc molecules, deposited on PMMA-coated glass substrates at different substrate temperatures (T s) was performed and examined by atomic-force microscopy, field-emission scanning electron microscopy, X-ray diffraction, and Raman analysis. At 90 °C, the fabricated PS-OFETs with the Al2O3/PVA/PMMA trilayer dielectric configuration showed the best p-channel behavior, with an enhanced and remarkable photoresponsivity of R ∼ 9689.39 A W-1 compared to that of the Al2O3/PMMA bilayer dielectric system (R ∼ 2679.40 A W-1) due to the polarization of the dipoles inside the polar PVA dielectric, which increases the charge transport through the channel. The charge carrier mobility of the device also improved by one order (μh ∼ 1.3 × 10-2 cm2 V-1 s-1) compared to that of the bilayer dielectric configuration (μh ∼ 3.5 × 10-3 cm2 V-1 s-1). The observed specific detectivity (D*) and NEP values of the bilayer dielectric system were 6.01 × 1013 Jones and 2.655 × 10-17 W Hz-1/2, whereas for the trilayer dielectric system, the observed D* and NEP values were 5.13 × 1014 Jones and 1.043 × 10-17 W Hz-1/2, respectively. Additionally, the operating voltage of each of the fabricated devices was also very low (-10 V) due to the influence of the inorganic high-k Al2O3 dielectric layer. The electrical stability of all of the fabricated devices was also investigated by bias stress analysis under both light and dark conditions in vacuum. To the best of our knowledge, the photoresponsivity (R) reported here with an Al2O3/PVA/PMMA trilayer dielectric configuration is the highest reported value for thin film-based PS-OFETs, at a remarkably low operating voltage of -10 V, on low-cost glass substrates without indium tin oxide or/and Si/SiO2.

Dataset Information

Controlled Synthesis of Poly(pentafluorostyrene-ran-methyl methacrylate) Copolymers by Nitroxide Mediated Polymerization and Their Use as Dielectric Layers in Organic Thin-film Transistors.

Publications

Controlled Synthesis of Poly(pentafluorostyrene-ran-methyl methacrylate) Copolymers by Nitroxide Mediated Polymerization and Their Use as Dielectric Layers in Organic Thin-film Transistors.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets