Relationship between the morphological, mechanical and permeability properties of porous bone scaffolds and the underlying microstructure.

ABSTRACT: Bone scaffolds are widely used as one of the main bone substitute materials. However, many bone scaffold microstructure topologies exist and it is still unclear which topology to use when designing scaffold for a specific application. The aim of the present study was to reveal the mechanism of the microstructure-driven performance of bone scaffold and thus to provide guideline on scaffold design. Finite element (FE) models of five TPMS (Diamond, Gyroid, Schwarz P, Fischer-Koch S and F-RD) and three traditional (Cube, FD-Cube and Octa) scaffolds were generated. The effective compressive and shear moduli of scaffolds were calculated from the mechanical analysis using the FE unit cell models with the periodic boundary condition. The scaffold permeability was calculated from the computational fluid dynamics (CFD) analysis using the 4×4×4 FE models. It is revealed that the surface-to-volume ratio of the Fischer-Koch S-based scaffold is the highest among the scaffolds investigated. The mechanical analysis revealed that the bending deformation dominated structures (e.g., the Diamond, the Gyroid, the Schwarz P) have higher effective shear moduli. The stretching deformation dominated structures (e.g., the Schwarz P, the Cube) have higher effective compressive moduli. For all the scaffolds, when the same amount of change in scaffold porosity is made, the corresponding change in the scaffold relative shear modulus is larger than that in the relative compressive modulus. The CFD analysis revealed that the structures with the simple and straight pores (e.g., Cube) have higher permeability than the structures with the complex pores (e.g., Fischer-Koch S). The main contribution of the present study is that the relationship between scaffold properties and the underlying microstructure is systematically investigated and thus some guidelines on the design of bone scaffolds are provided, for example, in the scenario where a high surface-to-volume ratio is required, it is suggested to use the Fischer-Koch S based scaffold.

SUBMITTER: Lu Y

PROVIDER: S-EPMC7462274 | biostudies-literature | 2020

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Relationship between the morphological, mechanical and permeability properties of porous bone scaffolds and the underlying microstructure.

Lu Yongtao Y Cheng LiangLiang L Yang Zhuoyue Z Li Junyan J Zhu Hanxing H

PloS one 20200901 9

Bone scaffolds are widely used as one of the main bone substitute materials. However, many bone scaffold microstructure topologies exist and it is still unclear which topology to use when designing scaffold for a specific application. The aim of the present study was to reveal the mechanism of the microstructure-driven performance of bone scaffold and thus to provide guideline on scaffold design. Finite element (FE) models of five TPMS (Diamond, Gyroid, Schwarz P, Fischer-Koch S and F-RD) and th ...[more]

PMID: 32870933

Similar Datasets

Project description:A composite comprising Ti and NaCl powders was sintered similar to a three-dimensional (3D)-printed patient-customized artificial bone scaffold. Additionally, a proper microstructure of the mimetic scaffold and the optimum processing parameters for its development were analyzed. The mechanical properties of the metal-based porous-structured framework used as an artificial bone scaffold were an optimum replacement for the human bone. Thus, it was confirmed that patient-customized scaffolds could be manufactured via 3D printing. The 3D-printed mimetic specimens were fabricated by a powder-sintering method using Ti for the metal parts, NaCl as the pore former, and polylactic acid as the biodegradable binder. Scanning electron microscopy (SEM) images showed that pores were formed homogeneously, while X-ray computed tomography confirmed that open pores were generated. The porosity and pore size distribution were measured using a mercury porosimeter, while the flexural strength and flexural elastic modulus were calculated using the three-point bending test. Based on these measurements, a pore-former content of 15 vol % optimized the density and flexural strength to 2.52 g cm-2 and 283 MPa, respectively, similar to those of the actual iliac bone. According to the 3D-printing production method, a selective laser-sintering process was applied for the fabrication of the mimetic specimen, and it was determined that the microstructure and properties similar to those of previous metal specimens could be achieved in the as-prepared specimen. Additionally, a decellularized extracellular matrix (dECM) was used to coat the surfaces and interiors of the specimens for evaluating their biocompatibilities. SEM image analysis indicated that the adipose-derived stem cells grew evenly inside the pores of the coated specimens, as compared with the bulky Ti specimens without the dECM coating. The doubling time at 65% was measured at 72, 75, and 83 h for specimens with pore-former contents of 5, 10, and 15 vol %, respectively. The doubling time without the pore former was 116 h. As compared with the specimens without the pore former (73 h), 15% of the dECM-coated specimens showed a doubling time of 64%, measured at 47 h.

Dataset Information

Relationship between the morphological, mechanical and permeability properties of porous bone scaffolds and the underlying microstructure.

Publications

Relationship between the morphological, mechanical and permeability properties of porous bone scaffolds and the underlying microstructure.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets