Digital Image Correlation of Tensile Properties for Monel 400/SS 316L Dissimilar Metal Welding Joints.

ABSTRACT: Dissimilar metal weld joints of Monel 400 and Stainless Steel 316L stainless steel were carried out using Gas Tungsten Arc Welding (GTAW). Conventional annealing and cryogenic treatment were performed on the welded joints. Weld joints of this combination of materials have enormous potential applications in power industry and the available related literature is limited. In the present study, the tensile properties of heat treated (HT), cryotreated (CT), and untreated (UT) specimens were studied. The engineering stress and strain were determined experimentally as per Standard Test Methods for Tension Testing of Metallic Materials (ASTM E8). The strain distribution was evaluated at different zones of weld joint was evaluated using Digital Image Correlation (DIC). Significant difference was noticed between the zones. Weld zone of all samples had less local stress and strain and SS 316L heat affected zone (HAZ) zone had more local stress and strain when compared to other zones. The local strain distribution along distance from weld center line and local stress-strain curves of different zones are also predicted. Scanning Electron Microscopy was used to analyze the fracture behavior of welded samples for HT, CT, and UT specimens.

SUBMITTER: Mani C

PROVIDER: S-EPMC8005209 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

An Evaluation of Global and Local Tensile Properties of Friction-Stir Welded DP980 Dual-Phase Steel Joints Using a Digital Image Correlation Method.

Project description:The effect of the microstructure heterogeneity on the tensile plastic deformation characteristic of friction-stir-welded (FSW) dual-phase (DP) steel was investigated for the potential applications on the lightweight design of vehicles. Friction-stir-welded specimens with a butt joint configuration were prepared, and quasi-static tensile tests were conducted, to evaluate the tensile properties of DP980 dual-phase steels. The friction-stir welding led to the formation of martensite and a significant hardness rise in the stir zone (SZ), but the presence of a soft zone in the heat-affected zone (HAZ) was caused by tempering of the pre-existing martensite. Owing to the appearance of severe soft zone, DP980 FSW joint showed almost 93% joint efficiency with the view-point of ultimate tensile strength and relatively low ductility than the base metal (BM). The local tensile deformation characteristic of the FSW joints was also examined using the digital image correlation (DIC) methodology by mapping the global and local strain distribution, and was subsequently analyzed by mechanics calculation. It is found that the tensile deformation of the FSW joints is highly heterogeneous, leading to a significant decrease in global ductility. The HAZ of the joints is the weakest region where the strain localizes early, and this localization extends until fracture with a strain near 30%, while the strain in the SZ and BM is only 1% and 4%, respectively. Local constitutive properties in different heterogeneous regions through the friction-stir-welded joint was also briefly evaluated by assuming iso-stress conditions. The local stress-strain curves of individual weld zones provide a clear indication of the heterogeneity of the local mechanical properties.

| S-EPMC5458860 | biostudies-other

A welding phenomenon of dissimilar nanoparticles in dispersion.

Project description:The oriented attachment of small nanoparticles (NPs) is recognized as an important mechanism involved in the growth of inorganic nanocrystals. However, non-oriented attachment of dissimilar NPs has been rarely observed in dispersion. This communication reports a welding phenomenon occurred directly between as-synthesized dispersions of single-component Au and chalcogenide NPs, which leads to the formation of asymmetric Au-chalcogenide hybrid NPs (HNPs). The welding of dissimilar NPs in dispersion is mainly driven by the ligand desorption-induced conformal contact between NPs and the diffusion of Au into chalcogenide NPs. The welding process can occur between NPs with distinct shapes or different capping agents or in different solvent media. A two-step assembly-welding mechanism is proposed for this process, based on our in situ electron spin resonance measurements and ab initio molecular dynamics simulation. The understanding of NP welding in dispersion may lead to the development of unconventional synthetic tools for the fabrication of hybrid nanostructures with diverse applications.

| S-EPMC6333817 | biostudies-literature

Project description:In this study, the friction-stir welding (FSW) technique was successfully applied for joining of AA2519 to AA5181 alloy. Microstructure and mechanical properties of dissimilar FSW joints were investigated by optical microscopy, microhardness, and tensile testing. The deformation behaviour of the welded joints was elucidated via the digital image correlation technique. After welding, the ultimate tensile strength of joints was ~300 MPa and ductility was ~16%. The microhardness values observed at the stir zone were higher than those in the base material AA5182. The produced welds demonstrate nearly 100% (based on AA5182) joint efficiency.

| S-EPMC9786200 | biostudies-literature

Tailoring of Dissimilar Friction Stir Lap Welding of Aluminum and Titanium.

Project description:An approach was proposed to optimize dissimilar friction stir lap welding of aluminum and titanium alloys. The basic concept of the new technique included (i) the plunging of the welding tool solely into the aluminum part (i.e., no direct contact with the titanium side) and (ii) the welding at a relatively high-heat input condition. It was shown that sound welds could be readily produced using an ordinary cost-effective tool, with no tool abrasion and no dispersion of harmful titanium fragments within the aluminum side. Moreover, the intermetallic layer was found to be as narrow as ~0.1 µm, thus giving rise to excellent bond strength between aluminum and titanium. On the other hand, several important shortcomings were also revealed. First of all, the high-heat input condition provided significant microstructural changes in the aluminum part, thereby resulting in essential material softening. Furthermore, the new approach was not feasible in the case of highly alloyed aluminum alloys due to the relatively low rate of self-diffusion in these materials. An essential issue was also a comparatively narrow processing window.

| S-EPMC9738075 | biostudies-literature

A study to characterize the mechanical properties and material constitution of adult descending thoracic aorta based on uniaxial tensile test and digital image correlation.

Project description:The mechanical properties and material constitution of the aorta are important in forensic science and clinical medicine. Existing studies on the material constitution of the aorta do not satisfy the practical requirements of forensic and clinical medicine, as the reported failure stress and failure strain values for human aortic materials have a high dispersion. In this study, descending thoracic aortas were obtained from 50 cadavers (dead within 24 h) free of thoracic aortic disease, aged from 27 to 86 years old, which were divided into six age groups. The descending thoracic aorta was divided into proximal and distal segments. A customized 4-mm cutter was used to punch a circumferential and an axial dog-bone-shaped specimen from each segment; the aortic ostia and calcification were avoided. Instron 8,874 and digital image correlation were used to perform a uniaxial tensile test on each sample. Four samples from each descending thoracic aorta produced ideal stress-strain curves. All parameter-fitting regressions from the selected mathematical model converged, and the best-fit parameters of each sample were obtained. The elastic modulus of collagen fiber, failure stress, and the strain showed a decreasing trend with age, while the elastic modulus of elastic fiber showed an increasing trend with age. The elastic modulus of collagen fiber, failure stress, and strain of circumferential tensile were all greater than those for axial tensile. There was no statistical difference in model parameters and physiological moduli between the proximal and distal segments. The failure stress and strain in the proximal circumferential, distal circumferential, and distal axial tensile were all greater for the male group than for the female group. Finally, the Fung-type hyperelastic constitutive equations were fitted for the different segments in different age groups.

| S-EPMC10306407 | biostudies-literature

Attenuation of the in vitro neurotoxicity of 316L SS by graphene oxide surface coating.

Project description:A persistent theme in biomaterials research comprises of surface engineering and modification of bare metallic substrates for improved cellular response and biocompatibility. Graphene Oxide (GO), a derivative of graphene, has outstanding chemical and mechanical properties; its large surface to volume ratio, ease of surface modification and processing make GO an attractive coating material. GO-coatings have been extensively studied as biosensors. Further owing to its surface nano-architecture, GO-coated surfaces promote cell adhesion and growth, making it suitable for tissue engineering applications. The need to improve the long-term durability and therapeutic effectiveness of commercially available bare 316L stainless steel (SS) surfaces led us to adopt a polymer-free approach which is cost-effective and scalable. GO was immobilized on to 316L SS utilizing amide linkage, to generate a strongly adherent uniform coating with surface roughness. GO-coated 316L SS surfaces showed increased hydrophilicity and biocompatibility with SHSY-5Y neuronal cells, which proliferated well and showed decreased reactive oxygen species (ROS) expression. In contrast, cells did not adhere to bare uncoated 316L SS meshes nor maintain viability when cultured in the vicinity of bare meshes. Therefore the combination of the improved surface properties and biocompatibility implies that GO-coating can be utilized to overcome pertinent limitations of bare metallic 316L SS implant surfaces, especially SS neural electrodes. Also, the procedure for making GO-based protective coatings can be applied to numerous other implants where the development of such protective films is necessary.

| S-EPMC5312756 | biostudies-literature

Flat hardness distribution in AA6061 joints by linear friction welding.

Project description:It is known that one of the main concerns associated with the conventional welding of precipitation-strengthened Al alloys is the formation of softening regions, resulting in the deterioration of mechanical properties. In this study, we show that linear friction welding (LFW) can completely suppress softening regions in precipitation-strengthened AA6061-T6 alloy by introducing a large shear strain and by controlling the interfacial temperature. We found that the LFW process resulted in an extremely low interfacial temperature; it decreased as the applied pressure increased from 50 to 240 MPa. This approach can essentially suppress both softening and hardening regions, leading to uniform hardness distribution in Al joints. The high-pressure LFW process demonstrated here can thus provide an innovated guidance to obtain high-performance Al alloy joints and be extended to other precipitation-strengthened Al alloys, which undergo high-temperature softening.

| S-EPMC8175386 | biostudies-literature

Full-Field Indentation Damage Measurement Using Digital Image Correlation.

Project description:A novel approach based on full-field indentation measurements to characterize and quantify the effect of contact in thin plates is presented. The proposed method has been employed to evaluate the indentation damage generated in the presence of bending deformation, resulting from the contact between a thin plate and a rigid sphere. For this purpose, the 3D Digital Image Correlation (3D-DIC) technique has been adopted to quantify the out of plane displacements at the back face of the plate. Tests were conducted using aluminum thin plates and a rigid bearing sphere to evaluate the influence of the thickness and the material behavior during contact. Information provided by the 3D-DIC technique has been employed to perform an indirect measurement of the contact area during the loading and unloading path of the test. A symmetrical distribution in the contact damage region due to the symmetry of the indenter was always observed. In the case of aluminum plates, the presence of a high level of plasticity caused shearing deformation as the load increased. Results show the full-field contact damage area for different plates' thicknesses at different loads. The contact damage region was bigger when the thickness of the specimen increased, and therefore, bending deformation was reduced. With the proposed approach, the elastic recovery at the contact location was quantified during the unloading, as well as the remaining permanent indentation damage after releasing the load. Results show the information obtained by full-field measurements at the contact location during the test, which implies a substantial improvement compared with pointwise techniques.

| S-EPMC5551817 | biostudies-other

TIG welding of Ti6Al4V alloy: Microstructure, fractography, tensile and microhardness data.

Project description:Titanium alloy is widely used in many industries due to its unique weight to strength ratio and high corrosion resistance. A suitable method of joining Titanium and its alloys is using Tungsten Inert Gas (TIG) welding. A significant advantage of TIG welding over other fusion welding is its ability to use non-consumable electrodes. This research was carried out on Ti6Al4V alloy of 2-3 mm thickness using TIG welding. Current and gas flow rates were varied, with Argon used as the inert gas for the welding. The data and images presented in this article account for the mechanical (tensile and microhardness), fractography, and microstructural properties of the welded samples. This article will foster simulation of heat input and flux and mechanical properties of TIG-welded Ti6Al4V alloy.

| S-EPMC8367793 | biostudies-literature

Experimental image dataset for validation of the noise-induced bias that affects Digital Image Correlation.

Project description:The present article shares with the scientific community several image sets used for experimentally validating the noise-induced bias on different Digital Image Correlation (DIC) formulations, as reported in Baldi et al. [1]. These sets are provided with a description of the experimental setup used for image acquisition. The basic idea is to acquire a series of images obtained by rigidly translating the target, where incremental displacement is of the order of a small fraction of a pixel. This condition requires a high-precision control of the target position through the tests. Moreover, the noise content of each image set is modulated using a statistical approach that uncouples the intensity field from the standard deviation. Lastly, the images are acquired with different exposure conditions to analyze the gray tone gradient effect on noise-induced bias.

| S-EPMC9046951 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data