Wire-in-Wire TiO₂/C Nanofibers Free-Standing Anodes for Li-Ion and K-Ion Batteries with Long Cycling Stability and High Capacity.

ABSTRACT: Wearable and portable mobile phones play a critical role in the market, and one of the key technologies is the flexible electrode with high specific capacity and excellent mechanical flexibility. Herein, a wire-in-wire TiO₂/C nanofibers (TiO₂ ww/CN) film is synthesized via electrospinning with selenium as a structural inducer. The interconnected carbon network and unique wire-in-wire nanostructure cannot only improve electronic conductivity and induce effective charge transports, but also bring a superior mechanic flexibility. Ultimately, TiO₂ ww/CN film shows outstanding electrochemical performance as free-standing electrodes in Li/K ion batteries. It shows a discharge capacity as high as 303 mAh g^-1 at 5 A g^-1 after 6000 cycles in Li half-cells, and the unique structure is well-reserved after long-term cycling. Moreover, even TiO₂ has a large diffusion barrier of K⁺, TiO₂ ww/CN film demonstrates excellent performance (259 mAh g^-1 at 0.05 A g^-1 after 1000 cycles) in K half-cells owing to extraordinary pseudocapacitive contribution. The Li/K full cells consisted of TiO₂ ww/CN film anode and LiFePO₄/Perylene-3,4,9,10-tetracarboxylic dianhydride cathode possess outstanding cycling stability and demonstrate practical application from lighting at least 19 LEDs. It is, therefore, expected that this material will find broad applications in portable and wearable Li/K-ion batteries.

SUBMITTER: Su D

PROVIDER: S-EPMC8035377 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Carbon nanoparticle-entrapped macroporous Mn3O4 microsphere anodes with improved cycling stability for Li-ion batteries.

Project description:Manganese oxide (Mn3O4) has garnered substantial attention as a low-cost, environment-friendly anode material. It undergoes a conversion reaction involving the formation of Li2O and metallic Mn to provide high-energy Li-ion batteries. However, its low electrical conductivity and significant volume change reduce its capacity during the initial lithiation/delithiation, hindering its practical application. To improve the cycle performance, we propose a new composite structure wherein we entrap carbon nanoparticles in macroporous Mn3O4 microspheres with a unique maze-like porous interior. We fabricate the Mn3O4/C composites using a scalable two-step process involving the thermal decomposition of MnCO3 in water vapor and mixing in a carbon-dispersed solution. The fabricated Mn3O4/C composites with varying carbon contents exhibit a high maximum discharge capacity retention of 86% after 50 cycles, compared to the 18% given by bare Mn3O4. The entrapped carbon nanoparticles improve the cycle performance both electrochemically and physically. The microstructure of the composite particles and the fabrication process developed in this study will help improve the performance of other conversion-type anode materials that suffer from cycle degradation, including inexpensive transition metal oxides and sulfides.

| S-EPMC9283411 | biostudies-literature

An investigation of Li2TiO3-coke composite anode material for Li-ion batteries.

Project description:Anode material Li2TiO3-coke was prepared and tested for lithium-ion batteries. The as-prepared material exhibits excellent cycling stability and outstanding rate performance. Charge/discharge capacities of 266 mA h g-1 at 0.100 A g-1 and 200 mA h g-1 at 1.000 A g-1 are reached for Li2TiO3-coke. A cycling life-time test shows that Li2TiO3-coke gives a specific capacity of 264 mA h g-1 at 0.300 A g-1 and a capacity retention of 92% after 1000 cycles of charge/discharge.

| S-EPMC9064618 | biostudies-literature

Free-standing Fe2O3 nanomembranes enabling ultra-long cycling life and high rate capability for Li-ion batteries.

Project description:With Fe2O3 as a proof-of-concept, free-standing nanomembrane structure is demonstrated to be highly advantageous to improve the performance of Li-ion batteries. The Fe2O3 nanomembrane electrodes exhibit ultra-long cycling life at high current rates with satisfactory capacity (808 mAh g(-1) after 1000 cycles at 2 C and 530 mAh g(-1) after 3000 cycles at 6 C) as well as repeatable high rate capability up to 50 C. The excellent performance benefits particularly from the unique structural advantages of the nanomembranes. The mechanical feature can buffer the strain of lithiation/delithiation to postpone the pulverization. The two-dimensional transport pathways in between the nanomembranes can promote the pseudo-capacitive type storage. The parallel-laid nanomembranes, which are coated by polymeric gel-like film and SEI layer with the electrolyte in between layers, electrochemically behave like numerous "mini-capacitors" to provide the pseudo-capacitance thus maintain the capacity at high rate.

| S-EPMC4264016 | biostudies-literature

High-performance spinel-rich Li1.5MnTiO4+δ ultralong nanofibers as cathode materials for Li-ion batteries.

Project description:Recently, composite materials based on Li-Mn-Ti-O system were developed to target low cost and environmentally benign cathodes for Li-ion batteries. The spinel-layered Li1.5MnTiO4+δ bulk particles showed excellent cycle stability but poor rate performance. To address this drawback, ultralong nanofibers of a Li1.5MnTiO4+δ spinel-layered heterostructure were synthesized by electrospinning. Uniform nanofibers with diameters of about 80 nm were formed of tiny octahedral particles wrapped together into 30 μm long fibers. The Li1.5MnTiO4+δ nanofibers exhibited an improved rate capability compared to both Li1.5MnTiO4+δ nanoparticles and bulk particles. The uniform one-dimensional nanostructure of the composite cathode exhibited enhanced capacities of 235 and 170 mAh g-1 at C/5 and 1 C rates, respectively. Its unique structure provided a large effective contact area for Li+ diffusion, and low charge transfer resistance. Moreover, the layered phase contributed to its capacity in over 3 V region, which increased specific energy (726 Wh kg-1) compared to the bulk particles (534 Wh kg-1).

| S-EPMC5374536 | biostudies-literature

Exploring the potential of MB2 MBene family as promising anodes for Li-ion batteries.

Project description:In recent years, finding high-performance energy storage materials has become a major challenge for Li-ion batteries. B-based two-dimensional materials have become the focus of attention because of their abundant reserves and non-toxic characteristics. A series of two-dimensional transition metal borides (MBenes) are reported and their electrochemical properties as anode materials for Li-ion batteries are investigated by density functional theory (DFT) calculations. The surface of MB2 possesses medium adsorption strength and diffusion energy barrier for Li atoms, which are conducive to the insertion and extraction of Li-ions during the charge/discharge process of Li-ion batteries. Herein, we explore the potential of MB2 (M = Sc, Y, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Cu and Zn) as the anode material for LIBs. Excitingly, the Li atom can be stably adsorbed on the surface of MB2 (M = Sc, Ti, V, Nb, Mo, W) monolayers, and the theoretical capacity of the MB2 monolayer is high (521.77-1610.20 mA h g-1). The average open circuit voltage range is within 0.10-1.00 V (vs. Li/Li+). The relationship between the p-band center of the B atom and the adsorption energy of Li on the surface of MB2 is also investigated. Furthermore, it is found that the charge transfer of Li atom and metallic center in the most stable position is strongly related to the corresponding value of diffusion energy barrier. These results confirm that MB2 monolayers are promising 2D anode materials for Li-ion batteries, demonstrating the application prospects of B-based 2D materials.

| S-EPMC10999910 | biostudies-literature

Electrospinning preparation of oxygen-deficient nano TiO2-x/carbon fibre membrane as a self-standing high performance anode for Li-ion batteries.

Project description:Improving the specific capacity and electronic conductivity of TiO2 can boost its practical application as a promising anode material for lithium ion batteries. In this work, a three-dimensional networking oxygen-deficient nano TiO2-x/carbon fibre membrane was achieved by combining the electrospinning process with a hot-press sintering method and directly used as a self-standing anode. With the synergistic effects of three-dimensional conductive networks, surface oxygen deficiency, high specific surface area and high porosity, binder-free and self-standing structure, etc., the nano TiO2-x/carbon fibre membrane electrode displays a high electrochemical reaction kinetics and a high specific capacity. The reversible capacity could be jointly generated from porous carbon, full-lithiation of TiO2 and interfacial lithium storage. At a current density of 100 mA g-1, the reversible discharge capacity can reach 464 mA h g-1. Even at 500 mA g-1, the discharge capacity still remains at 312 mA h g-1. Compared with pure carbon fibre and TiO2 powder, the TiO2-x/C fibre membrane electrode also exhibits an excellent cycle performance with a discharge capacity of 209 mA h g-1 after 700 cycles at the current density of 300 mA g-1, and the coulombic efficiency always remains at approximately 100%.

| S-EPMC5541555 | biostudies-literature

TiO2 Hollow Spheres With Flower-Like SnO2 Shell as Anodes for Lithium-Ion Batteries.

Project description:SnO2 is a promising anode material for lithium-ion batteries due to its high theoretical specific capacity and low operation voltage. However, its poor cycling performance hinders its commercial application. In order to improve the cycling stability of SnO2 electrodes, novel flower-like SnO2/TiO2 hollow spheres were prepared by facile hydrothermal method using carbon spheres as templates. Their flower-like shell and mesoporous structure highlighted a large specific surface area and excellent ion migration performance. Their TiO2 hollow sphere matrix and 2D SnO2 nano-flakes ensured good cycle stability. The electrochemical measurements indicated that novel flower-like SnO2/TiO2 hollow spheres delivered a high specific capacity, low irreversible capacity loss and superior rate performance. After 1,000 cycles at current densities of 200 mA g-1, the capacity of the flower-like SnO2/TiO2 hollow spheres was still maintained at 720 mAh g-1. Their rate capacity reached 486 mAh g-1 when the current densities gradually increase to 2,000 mA g-1.

| S-EPMC8692286 | biostudies-literature

Bio-Derived, Binderless, Hierarchically Porous Carbon Anodes for Li-ion Batteries.

Project description:Here we explore the electrochemical performance of pyrolyzed skins from the species A. bisporus, also known as the Portobello mushroom, as free-standing, binder-free, and current collector-free Li-ion battery anodes. At temperatures above 900 °C, the biomass-derived carbon nanoribbon-like architectures undergo unique processes to become hierarchically porous. During heat-treatment, the oxygen and heteroatom-rich organics and potassium compounds naturally present in the mushroom skins play a mutual role in creating inner void spaces throughout the resulting carbon nanoribbons, which is a process analogous to KOH-activation of carbon materials seen in literature. The pores formed in the pyrolytic carbon nanoribbons range in size from sub-nanometer to tens of nanometers, making the nanoribbons micro, meso, and macroporous. Detailed studies were conducted on the carbon nanoribbons using SEM and TEM to study morphology, as well as XRD and EDS to study composition. The self-supporting nanoribbon anodes demonstrate significant capacity increase as they undergo additional charge/discharge cycles. After a pyrolysis temperature of 1100 °C, the pristine anodes achieve over 260 mAh/g after 700 cycles and a Coulombic efficiency of 101.1%, without the use of harmful solvents or chemical activation agents.

| S-EPMC4586494 | biostudies-other

Fabrication of Li4Ti5O12-TiO2 Nanosheets with Structural Defects as High-Rate and Long-Life Anodes for Lithium-Ion Batteries.

Project description:Development of high-power lithium-ion batteries with high safety and durability has become a key challenge for practical applications of large-scale energy storage devices. Accordingly, we report here on a promising strategy to synthesize a high-rate and long-life Li4Ti5O12-TiO2 anode material. The novel material exhibits remarkable rate capability and long-term cycle stability. The specific capacities at 20 and 30?C (1?C?=?175?mA?g-1) reach 170.3 and 168.2?mA?h g-1, respectively. Moreover, a capacity of up to 161.3?mA?h g-1 is retained after 1000 cycles at 20?C, and the capacity retention ratio reaches up to 94.2%. The extraordinary rate performance of the Li4Ti5O12-TiO2 composite is attributed to the existence of oxygen vacancies and grain boundaries, significantly enhancing electrical conductivity and lithium insertion/extraction kinetics. Meanwhile, the pseudocapacitive effect is induced owing to the presence of abundant interfaces in the composite, which is beneficial to enhancing specific capacity and rate capability. Additionally, the ultrahigh capacity at low rates, greater than the theoretical value of spinel Li4Ti5O12, may be correlated to the lithium vacancies in 8a sites, increasing the extra docking sites of lithium ions.

| S-EPMC5462757 | biostudies-literature

ALD Al2O3-Coated TiO2 Nanotube Layers as Anodes for Lithium-Ion Batteries.

Project description:The utilization of the anodic TiO2 nanotube layers, with uniform Al2O3 coatings of different thicknesses (prepared by atomic layer deposition, ALD), as the new electrode material for lithium-ion batteries (LIBs), is reported herein. Electrodes with very thin Al2O3 coatings (∼1 nm) show a superior electrochemical performance for use in LIBs compared to that of the uncoated TiO2 nanotube layers. A more than 2 times higher areal capacity is received on these coated TiO2 nanotube layers (∼75 vs 200 μAh/cm2) as well as higher rate capability and coulombic efficiency of the charging and discharging reactions. Reasons for this can be attributed to an increased mechanical stability of the TiO2 nanotube layers upon Al2O3 coating, as well as to an enhanced diffusion of the Li+ ions within the coated nanotube layers. In contrast, thicker ALD Al2O3 coatings result in a blocking of the electrode surface and therefore an areal capacity decrease.

| S-EPMC5494640 | biostudies-literature