Magnetic, electrical and mechanical properties of Fe₄₀Mn₄₀Co₁₀Cr₁₀ high entropy alloy.

ABSTRACT: A prototypical, single-phase, and non-equiatomic high entropy alloy Fe₄₀Mn₄₀Co₁₀Cr₁₀ has been mechanically deformed at room and cryogenic temperatures. Plastic deformation was accommodated via crystallographic slip at room temperature while transformation induced plasticity (TRIP) has been observed in samples deformed at 77 K. The stress-induced martensitic transformation occurred from face-centered cubic (FCC) to hexagonal close-packed (HCP) structures. A detailed electron backscatter diffraction analysis was utilized to detect phase change and evaluate the evolution of the HCP phase volume fraction as a function of plastic strain. Physical properties of undeformed and deformed samples were measured to elucidate the effect of deformation-induced phase transitions on the magnetic and electrical properties of Fe₄₀Mn₄₀Co₁₀Cr₁₀ alloy. Relatively small magnetic moments along with non-saturating magnetic field dependencies suggest that the ground state in the considered material is ferrimagnetic ordering with coexisting antiferromagnetic phase. The temperature evolution of the coercive fields has been revealed for all samples. The magnitudes of the coercive fields place the considered system into the semi-hard magnetic alloys category. The temperature dependence of the zero-field cooled (ZFC) and field cooled (FC) magnetization was measured for all samples in the low field regime and the origin of irreversibility in ZFC/FC curves was discussed. Besides, the temperature dependence of the resistivity in all samples was measured and the possible conduction mechanisms were discussed.

SUBMITTER: Egilmez M

PROVIDER: S-EPMC8044135 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Microstructure and Mechanical Properties of High-Entropy Alloy Co20Cr26Fe20Mn20Ni14 Processed by High-Pressure Torsion at 77?K and 300?K.

Project description:In this work, the mechanical characteristics of high-entropy alloy Co20Cr26Fe20Mn20Ni14 with low-stacking fault energy processed by cryogenic and room temperature high-pressure torsion (HPT) were studied. X-ray diffraction, scanning electron microscopy (SEM), and transmission electron microscopy (TEM) analyses were performed to identify the phase and microstructure variation and the mechanical properties characterized by Vickers hardness measurements and tensile testing. Cryogenic HPT was found to result in a lower mechanical strength of alloy Co20Cr26Fe20Mn20Ni14 than room temperature HPT. Microstructure analysis by SEM and TEM was conducted to shed light on the microstructural changes in the alloy Co20Cr26Fe20Mn20Ni14 caused by HPT processing. Electron microscopy data provided evidence of a deformation-induced phase transformation in the alloy processed by cryogenic HPT. Unusual softening phenomena induced by cryogenic HPT were characterized by analyzing the dislocation density as determined from X-Ray diffraction peak broadening.

| S-EPMC6056509 | biostudies-literature

Data on the microstructure and deformation of Fe50Mn25Cr15Co10Nx (x=0∼1.6) supporting the modifications of partial-dislocation-induced defects (PDIDs) and strength/ductility enhancement in metastable high entropy alloys.

Project description:The data presented in this article are related to a research paper on the modification of deformed nanostructure and mechanical performance of metastable high entropy alloys (HEAs) [1]. Fe50Mn25Cr15Co10 alloys with and without nitrogen were synthesized in a vacuum induction furnace using pure metals of 99.99% purity and FeCrN2 as nitrogen source. The nitrogen content was determined by Leco O/N-836 determinator for nitrogen-doped alloys. Transmission electron microscopy (TEM) were carried at 200 kV equipped with energy dispersive spectroscopy (EDS). Tensile testing was performed at room temperature. The strain rate jump tests were conducted by changing the strain rate between 10-3 and 10-2 s-1 to measure the strain rate sensitivity. The nanostructural evolutions by deformation including extended stacking faults (ESFs), ε-martensite and twins were examined using EBSD and TEM for the annealed samples and those strained to different strain levels. The role of partial dislocations on the formation of various PDIDs were analysed and the energies stored as deformed nanostructure (ESDN) after the PDID band formation were used to predict the evolution of various nanostructure with strain. The data and approach would provide a useful insight into the nanostructural evolution in metastable high entropy alloys.

| S-EPMC7807141 | biostudies-literature

Optimizing mechanical properties of Fe26.7Co26.7Ni26.7Si8.9B11 high entropy alloy by inducing hypoeutectic to quasi-duplex microstructural transition.

Project description:High-entropy alloys (HEAs) have inspired considerable interest due to their attractive physical and mechanical properties. In this work, the microstructural evolution induced by different heat treatments on rapidly solidified hypoeutectic precursors of a Fe26.7Co26.7Ni26.7Si8.9B11 HEA is investigated and correlated with the corresponding mechanical properties. The microstructures of the rapidly solidified precursors are composed of primary fcc solid solution dendrites embedded in a eutectic matrix. When the samples are annealed at different temperatures after furnace cooling or quenching, respectively, the eutectic structure gradually decomposes into fcc, tetragonal (Fe,Co)2B, and hexagonal Ni31Si12 crystals with increasing annealing temperature, leading to a gradual increase of the content of the fcc crystals and both their aggregation and coarsening. Then the dominant structural framework gradually transforms from eutectic structures to fcc dendrites and ultimately the (Fe,Co)2B crystals become isolated as dominant reinforcement particles distributed in the interdendritic regions. This gradual microstructural transition from hypoeutectic to quasi-duplex structures leads to the change of the dominant deformation mechanism from crack-controlled to dislocation-dominated deformation, which allows to control both ductility and strength in a wide range. Hence, this study provides some guideline for how to tune the microstructure and mechanical properties of HEAs.

| S-EPMC6344508 | biostudies-literature

Small-scale mechanical behavior of a eutectic high entropy alloy.

Project description:Eutectic high entropy alloys, with lamellar arrangement of solid solution phases, represent a new paradigm for simultaneously achieving high strength and ductility, thereby circumventing this well-known trade-off in conventional alloys. However, dynamic strengthening mechanisms and phase-boundary interactions during external loading remain unclear for these eutectic systems. In this study, small-scale mechanical behavior was evaluated for AlCoCrFeNi2.1 eutectic high entropy alloy, consisting of a lamellar arrangement of L12 and B2 solid-solution phases. The ultimate tensile strength was 1165 MPa with ductility of ~18% and ultimate compressive strength was 1863 MPa with a total compressive fracture strain of ~34%. Dual mode fracture was observed with ductile failure for L12 phase and brittle mode for B2 phase. Phase-specific mechanical tests using nano-indentation and micro-pillar compression showed higher hardness and strength and larger strain rate sensitivity for B2 compared with L12. Micro-pillars on B2 phase deformed by plastic barreling while L12 micro-pillars showed high density of slip steps due to activation of more slip systems and homogenous plastic flow. Mixed micro-pillars containing both the phases exhibited dual yielding behavior while the interface between L12 and B2 was well preserved without any sign of separation or cracking. Phase-specific friction analysis revealed higher coefficient of friction for B2 compared to L12. These results will pave the way for fundamental understanding of phase-specific contribution to bulk mechanical response of concentrated alloys and help in designing structural materials with high fracture toughness.

| S-EPMC7021732 | biostudies-literature

Two-Dimensional Transition Metal Boride TMB12 (TM = V, Cr, Mn, and Fe) Monolayers: Robust Antiferromagnetic Semiconductors with Large Magnetic Anisotropy.

Project description:Currently, two-dimensional (2D) materials with intrinsic antiferromagnetism have stimulated research interest due to their insensitivity to external magnetic fields and absence of stray fields. Here, we predict a family of stable transition metal (TM) borides, TMB12 (TM = V, Cr, Mn, Fe) monolayers, by combining TM atoms and B12 icosahedra based on first-principles calculations. Our results show that the four TMB12 monolayers have stable antiferromagnetic (AFM) ground states with large magnetic anisotropic energy. Among them, three TMB12 (TM=V, Cr, Mn) monolayers display an in-plane easy magnetization axis, while the FeB12 monolayer has an out-of-plane easy magnetization axis. Among them, the CrB12 and the FeB12 monolayers are AFM semiconductors with band gaps of 0.13 eV and 0.35 eV, respectively. In particular, the AFM FeB12 monolayer is a spin-polarized AFM material with a Néel temperature of 125 K. Moreover, the electronic and magnetic properties of the CrB12 and the FeB12 monolayers can be modulated by imposing external biaxial strains. Our findings show that the TMB12 monolayers are candidates for designing 2D AFM materials, with potential applications in electronic devices.

| S-EPMC10745289 | biostudies-literature

Half metallicity in Cr substituted Fe2TiSn.

Project description:Band structure tailoring has been a great avenue to achieve the half-metallic electronic ground state in materials. Applying this approach to the full Heusler alloy Fe2TiSn, Cr is introduced systematically at Ti site that conforms to the chemical formula [Formula: see text]Sn. Compositions so obtained have been investigated for its electronic, magnetic, and electrical transport properties with an aim to observe the half-metallic ferromagnetic ground state, anticipated theoretically for Fe2CrSn. Our experimental study using synchrotron X-ray diffraction reveals that only compositions with [Formula: see text] 0.25 yield phase pure L2[Formula: see text] cubic structures. The non-magnetic ground state of Fe2TiSn gets dramatically affected upon inclusion of Cr giving rise to a localized magnetic moment in the background of Ruderman-Kittel-Kasuya-Yosida (RKKY) correlations. The ferromagnetic interactions begin to dominate for x = 0.25 composition. Results of its resistivity and magnetoresistance (MR) measurement point towards a half-metallic ground state. The calculation of exchange coupling parameter, [Formula: see text], and orbital projected density of states that indicate a change in hybridization between 3d and 5p orbital, support the observations made from the study of local crystal structure made using the extended X-ray absorption fine structure spectroscopy. Our findings here highlight an interesting prospect of finding half-metallicity via band structure tailoring for wide application in spintronics devices.

| S-EPMC7803981 | biostudies-literature

Mechanical Enhancement of Core-Shell Microlattices through High-Entropy Alloy Coating.

Project description:Mechanical metamaterials such as microlattices are an emerging kind of new materials that utilize the combination of structural enhancement effect by geometrical modification and the intrinsic properties of its material constituents. Prior studies have reported the mechanical properties of ceramic or metal-coated composite lattices. However, the scalable synthesis and characterization of high-entropy alloy (HEA) as thin film coating for such cellular materials have not been studied previously. In this work, stereolithography was combined with Radio Frequency (RF) magnetron sputtering to conformally deposit a thin layer (~800?nm) of CrMnFeCoNi HEA film onto a polymer template to produce HEA-coated three-dimensional (3D) core-shell microlattice structures for the first time. The presented polymer/HEA hybrid microlattice exhibits high specific compressive strength (~0.018?MPa kg-1 m3) at a density well below 1000?kg m-3, significantly enhanced stiffness (>5 times), and superior elastic recoverability compared to its polymer counterpart due to its composite nature. The findings imply that this highly scalable and effective route to synthesizing HEA-coated microlattices have the potential to produce novel metamaterials with desirable properties to cater specialized engineering applications.

| S-EPMC5882655 | biostudies-literature

Robust manipulation of magnetism in LaAO3/BaTiO3 (A = Fe, Mn and Cr) superstructures by ferroelectric polarization.

Project description:Robust control of magnetism is both fundamentally and practically meaningful and highly desirable, although it remains a big challenge. In this work, perovskite oxide superstructures LaFeO3/BaTiO3 (LFO/BTO), LaMnO3/BaTiO3 (LMO/BTO) and LaCrO3/BaTiO3 (LCO/BTO) (001) are designed to facilitate tuning of magnetism by the electric field from ferroelectric polarization, and are systemically investigated via first-principles calculations. The results show that the magnetic ordering, conductivity and exchange interactions can be controlled simultaneously or individually by the reorientation of the ferroelectric polarization of BTO in these designed superstructures. Self-consistent calculations within the generalized gradient approximation plus on-site Coulomb correction did not produce distinct rotations of oxygen octahedra, but there were obvious changes in bond length between oxygen and the cations. These changes cause tilting of the oxygen octahedra and lead to spin, orbital and bond reconstruction at the interface, which is the structural basis responsible for the manipulation. With the G-type antiferromagnetic (G-AFM) ordering unchanged for both ±P cases, a metal-insulator transition can be observed in the LFO/BTO superstructure, which is controlled by the LFO thin film. The LMO/BTO system has A-type antiferromagnetic (A-AFM) ordering with metallic behavior in the +P case, while it shifts to a half-metallic ferromagnetic ordering when the direction of the polarization is switched. LCO/BTO exhibits C-type antiferromagnetic (C-AFM) and G-AFM orders in the +P and -P cases, respectively. The three purpose-designed superstructures with robust intrinsic magnetoelectric coupling are a particularly interesting model system that can provide guidance for the development of this field for future applications.

| S-EPMC6400182 | biostudies-literature

Au19M (M=Cr, Mn, and Fe) as magnetic copies of the golden pyramid.

Project description:An investigation on structure, stability, and magnetic properties of singly doped Au19M (M=Cr, Mn, and Fe) clusters is carried out by means of density functional theory calculations. The studied clusters prefer forming magnetic versions of the unique tetrahedral Au20. Stable sextet Au19Cr is identified as the least reactive species and can be qualified as a magnetic superatom. Analysis on cluster electronic structures shows that the competition between localized and delocalized electronic states governs the stability and magnetic properties of Au19M clusters.

| S-EPMC5700080 | biostudies-other

Design for Fe-high Mn alloy with an improved combination of strength and ductility.

Project description:Recently, Fe-Mn twinning-induced plasticity steels with an austenite phase have been the course of great interest due to their excellent combination of tensile strength and ductility, which carbon steels have never been able to attain. Nevertheless, twinning-induced plasticity steels also exhibit a trade-off between strength and ductility, a longstanding dilemma for physical metallurgists, when fabricated based on the two alloy design parameters of stacking fault energy and grain size. Therefore, we investigated the tensile properties of three Fe-Mn austenitic steels with similar stacking fault energy and grain size, but different carbon concentrations. Surprisingly, when carbon concentration increased, both strength and ductility significantly improved. This indicates that the addition of carbon resulted in a proportionality between strength and ductility, instead of a trade-off between those characteristics. This new design parameter, C concentration, should be considered as a design parameter to endow Fe-Mn twinning-induced plasticity steel with a better combination of strength and ductility.

| S-EPMC5472627 | biostudies-literature