An Investigation on the Thermally Induced Compatibilization of SBR and α-Methylstyrene/Styrene Resin.

ABSTRACT: The miscibility between two polymers such as rubbers and performance resins is crucial to achieve given targeted properties in terms of tire performances. To this aim, α-methylstyrene/styrene resin (poly(αMSt-co-St)) are used to modify the viscoelastic behavior of rubbers and to fulfill the requirements of the final applications. The initial aim of this work was to understand the influence of poly(αMSt-co-St) resins blended at different concentrations in a commercial styrene-butadiene rubber (SBR). Interestingly, while studying the viscoelastic properties of SBR blends with poly(αMSt-co-St), crosslinking of the rubber was observed under conditions where it was not expected to happen. Surprisingly, after the crosslinking reactions, the poly(αMSt-co-St) resin was irreversibly miscible with SBR at concentrations far above its immiscibility threshold. A detailed investigation involving characterization technics including solid state nuclear magnetic resonance led to the conclusion that poly(αMSt-co-St) is depolymerizing under heating and can graft onto the chains of SBR. It results in an irreversible compatibilization mechanism between the rubber and the resin.

SUBMITTER: Wolf A

PROVIDER: S-EPMC8069804 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Thermal Stability and Flammability of Styrene-Butadiene Rubber-Based (SBR) Ceramifiable Composites.

Project description:Ceramifiable styrene-butadiene (SBR)-based composites containing low-softening-point-temperature glassy frit promoting ceramification, precipitated silica, one of four thermally stable refractory fillers (halloysite, calcined kaolin, mica or wollastonite) and a sulfur-based curing system were prepared. Kinetics of vulcanization and basic mechanical properties were analyzed and added as Supplementary Materials. Combustibility of the composites was measured by means of cone calorimetry. Their thermal properties were analyzed by means of thermogravimetry and specific heat capacity determination. Activation energy of thermal decomposition was calculated using the Flynn-Wall-Ozawa method. Finally, compression strength of the composites after ceramification was measured and their micromorphology was studied by scanning electron microscopy. The addition of a ceramification-facilitating system resulted in the lowering of combustibility and significant improvement of the thermal stability of the composites. Moreover, the compression strength of the mineral structure formed after ceramification is considerably high. The most promising refractory fillers for SBR-based ceramifiable composites are mica and halloysite.

| S-EPMC5456863 | biostudies-other

Compatibilization Behavior of Double Spherical TETA-SiO2@PDVB Janus Particles Anchored at the Phase Interface of Acrylic Resin/Epoxy Resin (AR/EP) Polymer Blends.

Project description:The inorganic particles used as a compatibilizer play a role in crack termination and heat resistance. However, the poor compatibility of inorganic particles and polymer hinders their application. Herein, the double spherical SiO2@PDVB Janus particles (JPs) were modified with triethylenetetramine (TETA), and the obtained anisotropic TETA-SiO2@PDVB JPs were used as the compatibilizer of acrylic resin/epoxy resin (AR/EP) composites. The modification and the compatibilization of TETA-SiO2@PDVB JPs were studied by scanning electron microscopy, X-ray photoelectron spectroscopy, differential scanning calorimetry, and dynamic mechanical analyzer, impact test, tensile test, and so forth. Results show that amino groups grafted onto the SiO2 lobe can react with epoxy groups of EP, which results in the TETA-SiO2 lobe being embedded in the EP phase and the PDVB lobe being pushed toward the AR phase. The TETA-SiO2@PDVB JPs anchored at the interface of AR and EP increase their interfacial adhesion, decrease the domain phase size and distribution of dispersed AR, and improve the compatibility of AR/EP composites. The compatibilization of nanoparticles (NPs) is realized by the cavitation and blunting of different scaled AR phase domain distributions and that of JPs is realized by the strong interfacial force originated by JPs. Moreover, the desorption energy of TETA-SiO2@PDVB JPs is higher than that of SiO2-TETA; so the glass transition temperature (T g) of AR/EP/JP composites is higher than that of AR/EP/NP composites. The strong interfacial adhesion and high desorption energy endow TETA-SiO2@PDVB JPs with a toughening effect and enhancing effect. The impact strength and the tensile strength of AR/EP/TETA-SiO2@PDVB composites are 16.03 kJ/m2 and 63.12 MPa, which are 9.91 kJ/m2 and 16.32 MPa higher than those of AR/EP composites, respectively. JPs used in the thermosetting EP is benefit to its toughening study and the new anisotropic Janus compatibilizer.

| S-EPMC6822127 | biostudies-literature

One-Pot Synthesis of α-Alkyl Styrene Derivatives.

Project description:There is a significant need to develop more rapid and efficient routes to styrene derivatives, since they are extensively used in polymer sciences. This manuscript reports a one-pot synthesis of an array of α-alkyl styrene derivatives from readily available natural products (i.e., estragole and safrole). This method is regioselective, producing a rearranged adduct, under transition metal-free conditions. This methodology has broad nucleophile scope, even tolerating sterically hindered nucleophiles; it is general for carbon, nitrogen, oxygen, and sulfur nucleophiles.

| S-EPMC8359136 | biostudies-literature

Hybrid Silica-Based Fillers in Nanocomposites: Influence of Isotropic/Isotropic and Isotropic/Anisotropic Fillers on Mechanical Properties of Styrene-Butadiene (SBR)-Based Rubber.

Project description:The improvement of mechanical properties of polymer-based nanocomposites is usually obtained through a strong polymer-silica interaction. Most often, precipitated silica nanoparticles are used as filler. In this work, we study the synergetic effect occurring between dual silica-based fillers in a styrene-butadiene rubber (SBR)/polybutadiene (PBD) rubber matrix. Precipitated Highly Dispersed Silica (HDS) nanoparticles (10 nm) have been associated with spherical Stöber silica nanoparticles (250 nm) and anisotropic nano-Sepiolite. By imaging filler at nano scale through Scanning Transmission Electron Microscopy, we have shown that anisotropic fillers align only in presence of a critical amount of HDS. The dynamic mechanical analysis of rubber compounds confirms that this alignment leads to a stiffer nanocomposite when compared to Sepiolite alone. On the contrary, spherical 250 nm nanoparticles inhibit percolation network and reduce the nanocomposite stiffness.

| S-EPMC8348337 | biostudies-literature

Investigation of five α-hydroxy acids for enamel and dentin etching: Demineralization depth, resin adhesion and dentin enzymatic activity.

Project description:ObjectivesSurface conditioning of enamel and dentin is a key step during adhesive restorative procedures and strategies. The aim of this study was to investigate the effectiveness of five α-hydroxy-acids (AHAs) as enamel and dentin surface etchants.MethodsEnamel and dentin specimens were prepared from human molars to determine the depth of demineralization by optical profilometry (Δz), the resin bond strength to enamel and dentin (μTBS), the micro-permeability of dentin-resin interfaces, and the gelatinolytic activity of dentin matrix induced by AHAs [glycolic (GA), lactic (LA), citric (CA), malic (MI) and tartaric (TA)] and controls [phosphoric (PA) and maleic (MA)]. All acids were prepared at 35% concentration. Adhesion studies employed Adper Single Bond Plus bonding system. Data were individually processed and analyzed by ANOVA, post-hoc tests and Pearson correlations (α = 0.05).ResultsAHA exhibited statistically lower depth of demineralization of enamel and dentin (average 4 fold) than controls (p < 0.001). In enamel, MA and PA etching resulted in higher μTBS than AHA groups (p < 0.001). In dentin, GA, TA, CI and LA etching resulted in statistically similar μTBS than PA (p < 0.05). The hybrid-layer (HL) thickness and interfacial micro-permeability intensity were statistically lower for AHA groups (p < 0.05). A significant positive correlation was observed between the intensity of micro-permeability and the thickness of HL (p < 0.05). AHA etchants elicited lower dentin enzymatic activity than controls (p < 0.05).SignificanceAHAs effectively etched enamel and dentin surfaces. In particular, GA and TA resulted in suitable μTBS and sealing ability as well as induced less gelatinolytic activity in dentin than PA and MA.

| S-EPMC6513690 | biostudies-literature

A Theoretical Investigation of the Ni(II)-Catalyzed Hydrovinylation of Styrene.

Project description:We report a detailed and full computational investigation on the hydrovinylation reaction of styrene with the Ni(II)-phospholane catalytic system, which was originally presumed to proceed through a cationic mechanism involving a nickel hydride intermediate. The following general features emerge from this study on a specific catalyst complex that was found to give quantitative yield and moderate selectivity: (a) the activation barrier for the initiation (18.8 kcal/mol) is higher than that for the reaction due to a low-lying square-planar pentenyl chelate intermediate originating from a Ni(II)-allyl catalyst precursor. Consequently there is an induction period for the catalysis; (b) the exit of product from the catalyst is via a ?-H-transfer step instead of the usual ?-H elimination pathway, which has a very high activation energy due to a trans effect of the phospholane ligand; (c) the turnover-limiting and enantio- determining transition state is also the ?-H-transfer; (d) because of the absence of a hydride intermediate, the unwanted isomerization of the product is prevented; (e) since the enantio-discrimination is decided at the H-transfer stage itself, the configuration of the product in a catalytic cycle influences the enantioselectivity in the subsequent cycle; (f) the trans effect of the sole strong ligand in the d8 square-planar Ni(II), the stability of the ?(3)-benzyl intermediate, and the availability of three coordination sites enable regioselective hydrovinylation over the possible oligomerization/polymerization of the olefin substrates and linear hydrovinylation. This work has also confirmed the previously recognized role of the hemilabile group at various stages in the mechanism.

| S-EPMC3083920 | biostudies-literature

Rheological Investigation of Relaxation Behavior of Polycarbonate/Acrylonitrile-Butadiene-Styrene Blends.

Project description:The rheological properties of polycarbonate/acrylonitrile-butadiene-styrene (PC/ABS) blends with various blend ratios are investigated at different temperatures to determine the shear dependent chain motions in a heterogeneous blend system. At low frequency levels under 0.1 rad/s, the viscosity of the material with a blend ratio of 3:7 (PC:ABS) is higher than that of pure ABS polymer. As the temperature increases, the viscosities of ABS-rich blends increase rather than decrease, whereas PC-rich blends exhibit decrease in viscosity. Results from the time sweep measurements indicate that ordered structures of PC and the formation and breakdown of internal network structures of ABS polymer occur simultaneously in the blend systems. Newly designed sequence test results show that the internal structures formed between PC and ABS polymers are dominant at low shear conditions for the blend ratio of 3:7 and effects of structural change and the presence of polybutadiene (PBD) become dominant at high shear conditions for pure ABS. The results of yield stress and relaxation time for PC/ABS blends support this phenomenon. The specimen with a blend ratio of 3:7 exhibited the highest value of yield stress at high temperature among others, which implies that the internal structure become stronger at higher temperature. The heterogeneity of ABS-rich blends increases whereas that of PC-rich blends decreases as temperature increases.

| S-EPMC7563493 | biostudies-literature

Bacillus sp. PS35 Lipase-Immobilization on Styrene-Divinyl Benzene Resin and Application in Fatty Acid Methyl Ester Synthesis.

Project description:BACKGROUND:Lipase is an enzyme with immense application potential. Ester synthesis by lipase catalysis in organic media is an area of key industrial relevance. Enzymatic preparations with traits that cater to the needs of this function are hence being intensely researched. OBJECTIVE:The objectives of the study were to immobilize the lipase from Bacillus sp. PS35 by cross-linking and adsorption onto styrene-divinyl benzene (Sty-Dvb) hydrophobic resin and to comparatively characterize the free and immobilized lipase preparations. The work also aimed to apply the immobilized lipase for catalysing the fatty acid methyl ester (FAME) synthesis from palm oil and optimize the process parameters for maximizing the yield. MATERIALS AND METHODS:In this study, the purified lipase from Bacillus sp. PS35 was immobilized by adsorption onto styrene-divinyl benzene hydrophobic resin with gluteraldehyde cross-linking. RESULTS:The immobilized enzyme showed better pH and temperature stabilities than the free lipase. Organic solvent stability was also enhanced, with the relative activity in the presence of methanol being shifted from 53% to 81%, thereby facilitating the enzyme's application in fatty acid methyl ester synthesis. It exhibited remarkable storage stability over a 30-day period and after 20 repetitive uses. Cross-linking also reduced enzyme leakage by 49%. The immobilized lipase was then applied for biodiesel production from palm oil. Methanol and oil molar ratio of 5:1, three step methanol additions, and an incubation temperature of 50°C were established to be the ideal conditions favoring the transesterification reaction, resulting in 97% methyl ester yield. CONCLUSIONS:These promising results offer scope for further investigation and process scale up, permitting the enzyme's commercial application in a practically feasible and economically agreeable manner.

| S-EPMC5435022 | biostudies-literature

Investigation of Parameters that Affect Resin Swelling in Green Solvents.

Project description:The influence of various physical and chemical factors on the swelling of polystyrene and PEG based resins in greener organic solvents has been systematically investigated. In general, chemical factors: the nature of the functionality/linker and the degree of loading were found to have a far larger influence on the swelling of the resins than physical parameters such as bead size. The results are interpreted in terms of Hansen solubility parameters for the solvents and there is evidence that some solvents interact with the polymeric core of a resin whilst others interact with the functionality. The results are extended to a study of the changes in resin swelling observed during both deprotection and chain elongation reactions during solid phase peptide synthesis.

| S-EPMC7121665 | biostudies-literature

Numerical evidence for thermally induced monopoles.

Project description:Electric charges are conserved. The same would be expected to hold for magnetic charges, yet magnetic monopoles have never been observed. It is therefore surprising that the laws of nonequilibrium thermodynamics, combined with Maxwell's equations, suggest that colloidal particles heated or cooled in certain polar or paramagnetic solvents may behave as if they carry an electric/magnetic charge. Here, we present numerical simulations that show that the field distribution around a pair of such heated/cooled colloidal particles agrees quantitatively with the theoretical predictions for a pair of oppositely charged electric or magnetic monopoles. However, in other respects, the nonequilibrium colloidal particles do not behave as monopoles: They cannot be moved by a homogeneous applied field. The numerical evidence for the monopole-like fields around heated/cooled colloidal particles is crucial because the experimental and numerical determination of forces between such colloidal particles would be complicated by the presence of other effects, such as thermophoresis.

| S-EPMC5441697 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data