Synergistic Effects of Ladder and Cage Structured Phosphorus-Containing POSS with Tetrabutyl Titanate on Flame Retardancy of Vinyl Epoxy Resins.

ABSTRACT: The cage and ladder structured phosphorus-containing polyhedral oligomeric silsesquioxanes (DOPO-POSS) have been synthesized through the hydrolytic condensation of 9,10-dihydro-9-oxa-10-phosphenanthrene-10-oxide (DOPO)-vinyl triethoxysilane (VTES). The unique ladder and cage-ladder structured components in DOPO-POSS endowed it with good solubility in vinyl epoxy resin (VE), and it was used with tetrabutyl titanate (TBT) to construct a phosphorus-silicon-titanium synergy system for the flame retardation of VE. Thermal stabilities, mechanical properties, and flame retardancy of the resultant VE composites were investigated by thermal gravimetric analysis (TGA), dynamic mechanical analysis (DMA), three-point bending tests, limiting oxygen index (LOI) measurement, and cone calorimetry. The experimental results showed that with the addition of only 4 wt% DOPO-POSS and 0.5 wt% TBT, the limiting oxygen index value (LOI) increased from 19.5 of pure VE to 24.2. With the addition of DOPO-POSS and TBT, the peak heat release rate (PHRR), total heat release (THR), smoke production rate (SPR), and total smoke production (TSP) were decreased significantly compared to VE-0. In addition, the VE composites showed improved thermal stabilities and mechanical properties comparable to that of the VE-0. The investigations on pyrolysis volatiles of cured VE further revealed that DOPO-POSS and TBT exerted flame retardant effects in gas phase. The results of char residue of the VE composites by SEM and XPS showed that TBT and DOPO-POSS can accelerate the char formation during the combustion, forming an interior char layer with the honeycomb cavity structure and dense exterior char layer, making the char strong with the formation of Si-O-Ti and Ti-O-P structures.

SUBMITTER: Han X

PROVIDER: S-EPMC8122454 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:A novel organic-inorganic hybrid containing allyl benzoxazine and polyhedral oligomeric silsesquioxane (POSS) was synthesized by the thiol-ene (click) reaction. The benzoxazine (BOZ)-containing POSS (SPOSS-BOZ) copolymerized with benzoxazine/epoxy resin was used to prepare composites of SPOSS-PBZ-E nanocomposites(NPs). The polymerization behavior was monitored by FTIR and non-isothermal differential scanning calorimetry (DSC), which showed that the composites had completely cured with multiple polymerization mechanisms according to the oxazine ring-opening and epoxy resin (EP) polymerization. The thermal properties of the organic-inorganic polybenzoxazine (PBZ) nanocomposites were analyzed by DSC and thermogravimetric analysis (TGA). Furthermore, the X-ray diffraction analysis and the scanning electron microscopy (SEM) micrographs of the SPOSS-PBZ-E nanocomposites indicated that SPOSS was chemically incorporated into the hybrid nanocomposites in the size range of 80-200 nm. The flame retardancy of the benzoxazine epoxy resin composites was investigated by limiting oxygen index (LOI), UL 94 vertical burn test, and cone calorimeter tests. When the amount of SPOSS reached 10% or more, the vertical burning rating of the curing system arrived at V-1, and when the SPOSS-BOZ content reached 20 wt %, the thermal stability and flame retardancy of the material were both improved. Moreover, in the cone calorimeter testing, the addition of SPOSS-BOZ hindered the decomposition of the composites and led to a reduction in the peak heat release rate (pHRR), the average heat release rate (aHRR), and the total heat release (THR) values by about 20%, 25%, and 25%, respectively. The morphologies of the chars were also studied by SEM and energy dispersive X-ray spectroscopy (EDX), and the flame-retardant mechanism of POSS was mainly a condensed-phase flame retardant. The ceramic layer was formed by the enrichment of silicon on the char surface. When there are enough POSS nanoparticles, it can effectively protect the combustion of internal polymers.

Project description:The effects of combining 0.1-5 wt % graphene nanoplatelet (GNP) and 3-30 wt % phosphorous flame retardant, 9,10- dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) as fillers in epoxy polymer on the mechanical, flame retardancy, and electrical properties of the epoxy nanocomposites was investigated. GNP was homogeneously dispersed into the epoxy matrix using a solvent-free three-roll milling process, while DOPO was incorporated into the epoxy resin by mechanical stirring at elevated temperature. The incorporation of DOPO reduced the crosslinking density of the epoxy resin. When using polyetheramine as a hardener, the structural rigidity effect of DOPO overshadowed the crosslinking effect and governed the flexural moduli of epoxy/DOPO resins. The flexural moduli of the nanocomposites were improved by adding GNP up to 5 wt % and DOPO up to 30 wt %, whereas the flexural strengths deteriorated when the GNP and DOPO loading were higher than 1 wt % and 10 wt %, respectively. Limited by the adverse effects on mechanical property, the loading combinations of GNP and DOPO within the range of 0-1 wt % and 0-10 wt %, respectively, in epoxy resin were further studied. Flame retardancy index (FRI), which depended on three parameters obtained from cone calorimetry, was considered to evaluate the flame retardancy of the epoxy composites. DOPO showed better performance than GNP as the flame retardant additive, while combining DOPO and GNP could further improve FRI to some extent. With the combination of 0.5 wt % GNP and 10 wt % DOPO, improvement in both mechanical properties and flame retardant efficiency of the nanocomposite was observed. Such a combination did not affect the electrical conductivity of the nanocomposites since the percolation threshold was at 1.6 wt % GNP. Our results enhance the understanding of the structure-property relationship of additive-filled epoxy resin composites and serve as a property constraining guidance for the composite manufacturing.

Dataset Information

Synergistic Effects of Ladder and Cage Structured Phosphorus-Containing POSS with Tetrabutyl Titanate on Flame Retardancy of Vinyl Epoxy Resins.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets