Surface Functionalization of Black Phosphorus via Amine Compounds and Its Impacts on the Flame Retardancy and Thermal Decomposition Behaviors of Epoxy Resin

ABSTRACT: Recently, lots of effort has been placed into stabilizing black phosphorus (BP) in the air to improve its compatibility with polymers. Herein, BP was chemically functionalized by aliphatic amine (DETA), aromatic amine (PPDA) and cyclamine (Pid) via a nucleophilic substitution reaction, aiming to develop an intensively reactive BP flame retardant for epoxy resin (EP). The -NH2 group on BP-DETA, BP-PPDA and BP-Pid reacted with the epoxide group at different temperatures. The lowest temperature was about 150 °C for BP-DETA. The impacts of three BP-NH2 were compared on the flame retardancy and thermal decomposition of EP. At 5 wt% loading, EP/BP-NH2 all passed UL 94 V 0 rating. The limiting oxygen index (LOI) of EP/BP-PPDA was as high as 32.3%. The heat release rate (HRR) of EP/BP-DETA greatly decreased by 46% and char residue increased by 73.8%, whereas HRR of EP/BP-Pid decreased by 11.5% and char residue increased by 50.8%, compared with EP. Average effective heat of combustion (av-EHC) of EP/BP-Pid was lower than that of EP/BP-DETA and EP/BP-PPDA. In view of the flame-retardant mechanism, BP nanosheets functionalized with aliphatic amine and aromatic amine played a dominant role in the condensed phase, while BP functionalized with cyclamine was more effective in the gas phase.

SUBMITTER: Lin S

PROVIDER: S-EPMC8588435 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:A novel organic-inorganic hybrid containing allyl benzoxazine and polyhedral oligomeric silsesquioxane (POSS) was synthesized by the thiol-ene (click) reaction. The benzoxazine (BOZ)-containing POSS (SPOSS-BOZ) copolymerized with benzoxazine/epoxy resin was used to prepare composites of SPOSS-PBZ-E nanocomposites(NPs). The polymerization behavior was monitored by FTIR and non-isothermal differential scanning calorimetry (DSC), which showed that the composites had completely cured with multiple polymerization mechanisms according to the oxazine ring-opening and epoxy resin (EP) polymerization. The thermal properties of the organic-inorganic polybenzoxazine (PBZ) nanocomposites were analyzed by DSC and thermogravimetric analysis (TGA). Furthermore, the X-ray diffraction analysis and the scanning electron microscopy (SEM) micrographs of the SPOSS-PBZ-E nanocomposites indicated that SPOSS was chemically incorporated into the hybrid nanocomposites in the size range of 80-200 nm. The flame retardancy of the benzoxazine epoxy resin composites was investigated by limiting oxygen index (LOI), UL 94 vertical burn test, and cone calorimeter tests. When the amount of SPOSS reached 10% or more, the vertical burning rating of the curing system arrived at V-1, and when the SPOSS-BOZ content reached 20 wt %, the thermal stability and flame retardancy of the material were both improved. Moreover, in the cone calorimeter testing, the addition of SPOSS-BOZ hindered the decomposition of the composites and led to a reduction in the peak heat release rate (pHRR), the average heat release rate (aHRR), and the total heat release (THR) values by about 20%, 25%, and 25%, respectively. The morphologies of the chars were also studied by SEM and energy dispersive X-ray spectroscopy (EDX), and the flame-retardant mechanism of POSS was mainly a condensed-phase flame retardant. The ceramic layer was formed by the enrichment of silicon on the char surface. When there are enough POSS nanoparticles, it can effectively protect the combustion of internal polymers.

Dataset Information

Surface Functionalization of Black Phosphorus via Amine Compounds and Its Impacts on the Flame Retardancy and Thermal Decomposition Behaviors of Epoxy Resin

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets