Hierarchically Porous, Biphasic, and C-Doped TiO₂ for Solar Photocatalytic Degradation of Dyes and Selective Oxidation of Benzyl Alcohol.

ABSTRACT: Macroporous TiO₂ monoliths were synthesized by self-sustained combustion reactions of molded pellets made up of a mixture of TiCl₄ as a precursor, urea as a fuel, ammonium nitrate as an oxidizer, and starch as a binder. The porous TiO₂ monoliths were found to be a heterostructure of anatase and rutile phases, in addition to being doped with carbon. Variation in the amount of starch yielded porous monoliths of different anatase-rutile ratios (increasing rutile component from 0 to 40%) but comparable Brunauer-Emmett-Teller (BET) surface area (∼30 m² g^-1). The porous monoliths obtained, where the TiCl₄/starch mass ratio was 2.17, exhibit exceptional photocatalytic activity in the degradation of dyes (methylene blue and methyl orange) and selective oxidation of benzyl alcohol to benzaldehyde under natural sunlight. The synergistic combination of high surface area, porous network, lowered band gap due to heterostructured anatase-rutile polymorphs, and the presence of doped carbon renders the macroporous TiO₂ an efficient photocatalyst.

SUBMITTER: Ragesh Nath R

PROVIDER: S-EPMC8154131 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Spent Coffee Grounds Derived Carbon Loading C, N Doped TiO2 for Photocatalytic Degradation of Organic Dyes.

Project description:Titanium dioxide (TiO2) is an ideal photocatalyst candidate due to its high activity, low toxicity and cost, and high chemical stability. However, its practical application in photocatalysis is seriously hindered by the wide band gap energy of TiO2 and the prone recombination of electron-hole pairs. In this study, C, N doped TiO2 were supported on spent coffee grounds-derived carbon (ACG) via in situ formation, which was denoted as C, N-TiO2@ACG. The obtained C, N-TiO2@ACG exhibits increased light absorption efficiency with the band gap energy decreasing from 3.31 eV of TiO2 to 2.34 eV, a higher specific surface area of 145.8 m2/g, and reduced recombination rates attributed to the synergistic effect of a spent coffee grounds-derived carbon substrate and C, N doping. Consequently, the optimal 1:1 C, N-TiO2@ACG delivers considerable photocatalytic activity with degradation efficiencies for methylene blue (MB) reaching 96.9% within 45 min, as well as a high reaction rate of 0.06348 min-1, approximately 4.66 times that of TiO2 (0.01361 min-1). Furthermore, it also demonstrated greatly enhanced photocatalytic efficiency towards methyl orange (MO) in the presence of MB compared with a single MO solution. This work provides a feasible and universal strategy of synchronous introducing nonmetal doping and biomass-derived carbon substrates to promote the photocatalytic performance of TiO2 for the degradation of organic dyes.

| S-EPMC10385829 | biostudies-literature

Enhanced Solar Light Photocatalytic Activity of Ag Doped TiO2-Ag3PO4 Composites.

Project description:Composites comprised of Ag3PO4 and bare TiO2 (TiO2@Ag3PO4) or silver doped TiO2 (Ag@TiO2-Ag3PO4) have been synthesized by coupling sol-gel and precipitation methods. For the sake of comparison, also the bare components have been similarly prepared. All the samples have been characterized by X-ray diffraction (XRD), UV-vis diffuse reflectance spectroscopy (DRS), scanning electron microscopy (SEM), Fourier transformed infrared spectroscopy (FTIR), photoelectrochemical measurements, and specific surface area (SSA) analysis. The optoelectronic and structural features of the samples have been related to their photocatalytic activity for the degradation of 4-nitrophenol under solar and UV light irradiation. Coupling Ag3PO4 with silver doped TiO2 mitigates photocorrosion of the Ag3PO4 counterpart, and remarkably improves the photocatalytic activity under solar light irradiation with respect to the components, to the TiO2-Ag3PO4 sample, and to the benchmark TiO2 Evonik P25. These features open the route to future applications of this material in the field of environmental remediation.

| S-EPMC7221970 | biostudies-literature

Enhanced photocatalytic activity of Se-doped TiO2 under visible light irradiation.

Project description:Anatase TiO2 is a typical photocatalyst, and its excellent performance is limited in ultraviolet light range due to its wide band gap of 3.2?eV. A series of Se-doped TiO2 nanoparticles in anatase structure with various Se concentrations up to 17.1?at.% were prepared using sol-gel method. The doped Se ions are confirmed to be mainly in the valence state of?+?4, which provides extra electronic states in the band gap of TiO2. The band gap is effectively narrowed with the smallest gap energy of 2.17?eV, and the photocatalytic activity is effectively improved due to the extended absorption range. The photocatalytic activity was evaluated by the degradation of Rhodamine B (RhB) in aqueous solution under visible light irradiation. The results show that Se doping significantly improves the photocatalytic activity of TiO2 and 13.63?at.% Se-doped TiO2 has the best performance.

| S-EPMC5993730 | biostudies-literature

One-Pot Route towards Active TiO₂ Doped Hierarchically Porous Cellulose: Highly Efficient Photocatalysts for Methylene Blue Degradation.

Project description:In this study, novel photocatalyst monolith materials were successfully fabricated by a non-solvent induced phase separation (NIPS) technique. By adding a certain amount of ethyl acetate (as non-solvent) into a cellulose/LiCl/N,N-dimethylacetamide (DMAc) solution, and successively adding titanium dioxide (TiO₂) nanoparticles (NPs), cellulose/TiO₂ composite monoliths with hierarchically porous structures were easily formed. The obtained composite monoliths possessed mesopores, and two kinds of macropores. Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS), Fourier Transform Infrared Spectroscopy (FT-IR), X-ray Diffraction (XRD), Brunauer-Emmett-Teller (BET), and Ultraviolet-visible Spectroscopy (UV-Vis) measurements were adopted to characterize the cellulose/TiO₂ composite monolith. The cellulose/TiO₂ composite monoliths showed high efficiency of photocatalytic activity in the decomposition of methylene blue dye, which was decomposed up to 99% within 60 min under UV light. Moreover, the composite monoliths could retain 90% of the photodegradation efficiency after 10 cycles. The novel NIPS technique has great potential for fabricating recyclable photocatalysts with highly efficiency.

| S-EPMC5506969 | biostudies-other

Efficient Photocatalytic Degradation of Organic Dyes by AgNPs/TiO2/Ti3C2T x MXene Composites under UV and Solar Light.

Project description:Due to their broad applications in various industrial activities, and their well-known negative impacts on the aquatic environment, organic dyes have been continuously identified as serious threat to the quality of ecosystems. The photocatalytic degradation process in aqueous solutions has emerged as an efficient and reliable approach for the removal of organic dyes. MXenes, a new class of two-dimensional (2D) nanomaterials, possess unique chemical composition, surface functionalities, and physicochemical properties. Such characteristics enable MXenes to act as efficient catalysts or cocatalysts to photodegrade organic molecules. This work explores the application of Ti3C2T x MXene decorated with silver and palladium nanoparticles, using a simple hydrothermal treatment method, for the photocatalytic degradation of methylene blue (MB) and rhodamine B (RhB). The chemical composition of these photocatalysts, as well as their structural properties and morphology, was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) techniques. The photocatalytic degradation abilities of the pristine MXene and the synthesized MXene composites were investigated under ultraviolet and solar light irradiation. A significant improvement in the photocatalytic performances was observed for all oxidized MXene composites when compared to pristine MXene, with a superior degradation efficiency achieved for AgNPs/TiO2/Ti3C2T x . This work broadens the application range of oxidized MXene composites, providing an alternative material for degrading organics dyes and wastewater treatment applications.

| S-EPMC8674905 | biostudies-literature

Porous TiO2/Carbon Dot Nanoflowers with Enhanced Surface Areas for Improving Photocatalytic Activity.

Project description:Electron-hole recombination and the narrow-range utilization of sunlight limit the photocatalytic efficiency of titanium oxide (TiO2). We synthesized carbon dots (CDs) and modified TiO2 nanoparticles (NPs) with a flower-like mesoporous structure, i.e., porous TiO2/CDs nanoflowers. Among such hybrid particles, the CDs worked as photosensitizers for the mesoporous TiO2 and enabled the resultant TiO2/CDs nanoflowers with a wide-range light absorption. Rhodamine B (Rh-B) was employed as a model organic pollutant to investigate the photocatalytic activity of the TiO2/CDs nanoflowers. The results demonstrated that the decoration of the CDs on both the TiO2 nanoflowers and the (commercially available AEROXIDE TiO2) P25 NPs enabled a significant improvement in the photocatalytic degradation efficiency compared with the pristine TiO2. The TiO2/CDs nanoflowers, with their porous structure and larger surface areas compared to P25, showed a higher efficiency to prevent local aggregation of carbon materials. All of the results revealed that the introduced CDs, with the unique mesoporous structure, large surface areas and loads of pore channels of the prepared TiO2 NPs, played important roles in the enhancement of the photocatalytic efficiency of the TiO2/CDs hybrid nanoflowers.

| S-EPMC9331435 | biostudies-literature

Soft Zr-doped TiO2 Nanofibrous Membranes with Enhanced Photocatalytic Activity for Water Purification.

Project description:Self-standing photocatalytic membranes constructed from TiO2 nanofibers hold great promise in environmental remediation; however, challenges still remained for the poor mechanical properties of polycrystalline TiO2 nanofibers. Herein, soft Zr-doped TiO2 (TZ) nanofibrous membranes with robust mechanical properties and enhanced photocatalytic activity were fabricated via electrospinning technique. The Zr4+ incorporation could effectively inhibit the grain growth and reduce the surface defects and breaking point of TiO2 nanofiber. The as-prepared TZ membranes were composed of well-interconnected nanofibers with a high aspect ratios, small grain size and pore size, which exhibited good tensile strength (1.32?MPa) and showed no obvious damage after 200 cycles of bending to a radius of 2?mm. A plausible bending deformation mechanism of the soft TZ membranes was proposed from microscopic single nanofiber to macroscopical membranes. Moreover, the resultant TZ membranes displayed better photocatalytic performance for methylene blue degradation compared to a commercial catalyst (P25), including high degradation degree of 95.4% within 30?min, good reusability in 5 cycles, and easiness of recycling. The successful preparation of such fascinating materials may open up new avenues for the design and development of soft TiO2-based membranes for various application.

| S-EPMC5431652 | biostudies-literature

Photocatalytic and Antibacterial Properties of Doped TiO2 Nanopowders Synthesized by Sol-Gel Method.

Project description:For environmental applications, nanosized TiO2-based materials are known as the most important photocatalyst and are intensively studied for their advantages such as their higher activity, lower price, and chemical and photoresist properties. Zn or Cu doped TiO2 nanoparticles with anatase crystalline structure were synthesized by sol-gel process. Titanium (IV) butoxide was used as a TiO2 precursor, with parental alcohol as a solvent, and a hydrolysing agent (ammonia-containing water) was added to obtain a solution with pH 10. The gels were characterized by TG/DTA analysis, SEM, and XPS. Based on TG/DTA results, the temperature of 500 °C was chosen for processing the powders in air. The structure of the samples thermally treated at 500 °C was analysed by XRD and the patterns show crystallization in a single phase of TiO2 (anatase). The surface of the samples and the oxidation states was investigated by XPS, confirming the presence of Ti, O, Zn and Cu. The antibacterial activity of the nanoparticle powder samples was verified using the gram-positive bacterium Staphylococcus aureus. The photocatalytic efficiency of the doped TiO2 nanopowders for degradation of methyl orange (MO) is here examined in order to evaluate the potential applications of these materials for environmental remediation.

| S-EPMC9601293 | biostudies-literature

CdSe nanorod/TiO2 nanoparticle heterojunctions with enhanced solar- and visible-light photocatalytic activity.

Project description:CdSe nanorods (NRs) with an average length of ≈120 nm were prepared by a solvothermal process and associated to TiO2 nanoparticles (Aeroxide® P25) by annealing at 300 °C for 1 h. The content of CdSe NRs in CdSe/TiO2 composites was varied from 0.5 to 5 wt %. The CdSe/TiO2 heterostructured materials were characterized by XRD, TEM, SEM, XPS, UV-visible spectroscopy and Raman spectroscopy. TEM images and XRD patterns show that CdSe NRs with wurtzite structure are associated to TiO2 particles. The UV-visible spectra demonstrate that the narrow bandgap of CdSe NRs serves to increase the photoresponse of CdSe/TiO2 composites until ≈725 nm. The CdSe (2 wt %)/TiO2 composite exhibits the highest photocatalytic activity for the degradation of rhodamine B in aqueous solution under simulated sunlight or visible light irradiation. The enhancement in photocatalytic activity likely originates from CdSe sensitization of TiO2 and the heterojunction between these materials which facilitates electron transfer from CdSe to TiO2. Due to its high stability (up to ten reuses without any significant loss in activity), the CdSe/TiO2 heterostructured catalysts show high potential for real water decontamination.

| S-EPMC5753051 | biostudies-literature

Synthesis and Characterization of N-Doped Porous TiO₂ Hollow Spheres and Their Photocatalytic and Optical Properties.

Project description:Three kinds of N-doped mesoporous TiO₂ hollow spheres with different N-doping contents, surface area, and pore size distributions were prepared based on a sol-gel synthesis and combined with a calcination process. Melamine formaldehyde (MF) microspheres have been used as sacrificial template and cetyltrimethyl ammonium bromide (CTAB) or polyvinylpyrrolidone (PVP) was selected as pore-directing agent. Core-shell intermediate spheres of titania-coated MF with diameters of 1.2-1.6 μm were fabricated by varying the volume concentration of TiO₂ precursor from 1 to 3 vol %. By calcining the core-shell composite spheres at 500 °C for 3 h in air, an in situ N-doping process occurred upon the decomposition of the MF template and CTAB or PVP pore-directing surfactant. N-doped mesoporous TiO₂ hollow spheres with sizes in the range of 0.4-1.2 μm and shell thickness from 40 to 110 nm were obtained. The composition and N-doping content, thermal stability, morphology, surface area and pore size distribution, wall thickness, photocatalytic activities, and optical properties of the mesoporous TiO₂ hollow spheres derived from different conditions were investigated and compared based on Fourier-transformation infrared (FTIR), SEM, TEM, thermogravimetric analysis (TGA), nitrogen adsorption-desorption, and UV-vis spectrophotoscopy techniques. The influences of particle size, N-doping, porous, and hollow characteristics of the TiO₂ hollow spheres on their photocatalytic activities and optical properties have been studied and discussed based on the composition analysis, structure characterization, and optical property investigation of these hollow spherical TiO₂ matrices.

| S-EPMC5456619 | biostudies-other