The Potential of Stereolithography for 3D Printing of Synthetic Trabecular Bone Structures.

ABSTRACT: Synthetic bone models are used to train surgeons as well as to test new medical devices. However, currently available models do not accurately mimic the complex structure of trabecular bone, which can provide erroneous results. This study aimed to investigate the suitability of stereolithography (SLA) to produce synthetic trabecular bone. Samples were printed based on synchrotron micro-computed tomography (micro-CT) images of human bone, with scaling factors from 1 to 4.3. Structure replicability was assessed with micro-CT, and mechanical properties were evaluated by compression and screw pull-out tests. The overall geometry was well-replicated at scale 1.8, with a volume difference to the original model of <10%. However, scaling factors below 1.8 gave major print artefacts, and a low accuracy in trabecular thickness distribution. A comparison of the model-print overlap showed printing inaccuracies of ~20% for the 1.8 scale, visible as a loss of smaller details. SLA-printed parts exhibited a higher pull-out strength compared to existing synthetic models (Sawbones ™), and a lower strength compared to cadaveric specimens and fused deposition modelling (FDM)-printed parts in poly (lactic acid). In conclusion, for the same 3D model, SLA enabled higher resolution and printing of smaller scales compared to results reported by FDM.

SUBMITTER: Grzeszczak A

PROVIDER: S-EPMC8269906 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Desktop-Stereolithography 3D Printing of a Polyporous Extracellular Matrix Bioink for Bone Defect Regeneration.

Project description:IntroductionDecellularized tendon extracellular matrix (tECM) perfectly provides the natural environment and holds great potential for bone regeneration in Bone tissue engineering (BTE) area. However, its densifying fiber structure leads to reduced cell permeability. Our study aimed to combine tECM with polyethylene glycol diacrylate (PEGDA) to form a biological scaffold with appropriate porosity and strength using stereolithography (SLA) technology for bone defect repair.MethodsThe tECM was produced and evaluated. Mesenchymal stem cell (MSC) was used to evaluate the biocompatibility of PEGDA/tECM bioink in vitro. Mineralization ability of the bioink was also evaluated in vitro. After preparing 3D printed polyporous PEGDA/tECM scaffolds (3D-pPES) via SLA, the calvarial defect generation capacity of 3D-pPES was assessed.ResultsThe tECM was obtained and the decellularized effect was confirmed. The tECM increased the swelling ratio and porosity of PEGDA bioink, both cellular proliferation and biomineralization in vitro of the bioink were significantly optimized. The 3D-pPES was fabricated. Compared to the control group, increased cell migration efficiency, up-regulation of osteogenic differentiation RNA level, and better calvarial defect repair in rat of the 3D-pPES group were observed.ConclusionThis study demonstrates that the 3D-pPES may be a promising strategy for bone defect treatment.

| S-EPMC7677189 | biostudies-literature

Biobased Acrylate Photocurable Resin Formulation for Stereolithography 3D Printing.

Project description:To facilitate the ongoing transition toward a circular economy, the availability of renewable materials for additive manufacturing becomes increasingly important. Here, we report the successful fabrication of complex shaped prototypes from biobased acrylate photopolymer resins, employing a commercial stereolithography apparatus (SLA) 3D printer. Four distinct resins with a biobased content ranging from 34 to 67% have been developed. All formulations demonstrated adequate viscosity and were readily polymerizable by the UV-laser-based SLA process. Increasing the double-bond concentration within the resin results in stiff and thermally resilient 3D printed products. High-viscosity resins lead to high-resolution prototypes with a complex microarchitecture and excellent surface finishing, comparable to commercial nonrenewable resins. These advances can facilitate the wide application of biobased resins for construction of new sustainable products via stereolithographic 3D printing methods.

| S-EPMC6641428 | biostudies-literature

3D printing of hollow geometries using blocking liquid substitution stereolithography.

Project description:Micrometer scale arbitrary hollow geometries within a solid are needed for a variety of applications including microfluidics, thermal management and metamaterials. A major challenge to 3D printing hollow geometries using stereolithography is the ability to retain empty spaces in between the solidified regions. In order to prevent unwanted polymerization of the trapped resin in the hollow spaces-known as print-through-significant constraints are generally imposed on the primary process parameters such as resin formulation, exposure conditions and layer thickness. Here, we report on a stereolithography process which substitutes the trapped resin with a UV blocking liquid to mitigate print-through. We investigate the mechanism of the developed process and determine guidelines for the formulation of the blocking liquid. The reported method decouples the relationship between the primary process parameters and their effect on print-through. Without having to optimize the primary process parameters to reduce print-through, hollow heights that exceed the limits of conventional stereolithography can be realized. We demonstrate fabrication of a variety of complex hollow geometries with cross-sectional features ranging from tens of micrometer to hundreds of micrometers in size. With the framework presented, this method may be employed for 3D printing functional hollow geometries for a variety of applications, and with improved freedom over the printing process (e.g. material choices, speed and resulting properties of the printed parts).

| S-EPMC9829859 | biostudies-literature

Stereolithography 3D Printing of Lignin-Reinforced Composites with Enhanced Mechanical Properties.

Project description:Due to the availability, biodegradability, and biological effects, lignin has emerged as an interesting alternative to petroleum-based compounds for developing sustainable chemicals, materials, and composites. In this study, lignin at various concentrations was incorporated into methacrylate resin via solution blending to fabricate lignin-reinforced composites using stereolithography apparatus three-dimensional printing. Softwood kraft lignin in the amounts of 0.2, 0.4, 0.5, 0.8, and 1.0 wt % in the methacrylate resin was used as a printing ink, and the gel contents and relative contents of the residual resin in the printed samples with various lignin concentrations were measured. The effects of the lignin on the ultimate mechanical properties of the non-postcured and postcured printed composites were determined. The tensile testing results revealed that the incorporation of lignin in the composite increased the tensile strength by 46-64% and Young's modulus by 13-37% for the postcured printed composites compared with that of the control sample (no lignin added). Employing a 0.4 wt % softwood kraft lignin, the tensile strength of the postcured printed composite reached the highest value of 49.0 MPa, which was a 60% increase in comparison to that of the control sample with 30.7 MPa. Scanning electron microscopy images of the fracture samples illustrated that the lignin-incorporated composites exhibited a rougher fracture surface that can presumably dissipate the stress, which could be a contributing factor for the mechanical enhancement.

| S-EPMC6893962 | biostudies-literature

Projection-based stereolithography for direct 3D printing of heterogeneous ultrasound phantoms.

Project description:Modern ultrasound (US) imaging is increasing its clinical impact, particularly with the introduction of US-based quantitative imaging biomarkers. Continued development and validation of such novel imaging approaches requires imaging phantoms that recapitulate the underlying anatomy and pathology of interest. However, current US phantom designs are generally too simplistic to emulate the structure and variability of the human body. Therefore, there is a need to create a platform that is capable of generating well-characterized phantoms that can mimic the basic anatomical, functional, and mechanical properties of native tissues and pathologies. Using a 3D-printing technique based on stereolithography, we fabricated US phantoms using soft materials in a single fabrication session, without the need for material casting or back-filling. With this technique, we induced variable levels of stable US backscatter in our printed materials in anatomically relevant 3D patterns. Additionally, we controlled phantom stiffness from 7 to >120 kPa at the voxel level to generate isotropic and anisotropic phantoms for elasticity imaging. Lastly, we demonstrated the fabrication of channels with diameters as small as 60 micrometers and with complex geometry (e.g., tortuosity) capable of supporting blood-mimicking fluid flow. Collectively, these results show that projection-based stereolithography allows for customizable fabrication of complex US phantoms.

| S-EPMC8659365 | biostudies-literature

Micro 3D Printing of a Temperature-Responsive Hydrogel Using Projection Micro-Stereolithography.

Project description:Stimuli-responsive hydrogels exhibiting physical or chemical changes in response to environmental conditions have attracted growing attention for the past few decades. Poly(N-isopropylacrylamide) (PNIPAAm), a temperature responsive hydrogel, has been extensively studied in various fields of science and engineering. However, manufacturing of PNIPAAm has been heavily relying on conventional methods such as molding and lithography techniques that are inherently limited to a two-dimensional (2D) space. Here we report the three-dimensional (3D) printing of PNIPAAm using a high-resolution digital additive manufacturing technique, projection micro-stereolithography (P?SL). Control of the temperature dependent deformation of 3D printed PNIPAAm is achieved by controlling manufacturing process parameters as well as polymer resin composition. Also demonstrated is a sequential deformation of a 3D printed PNIPAAm structure by selective incorporation of ionic monomer that shifts the swelling transition temperature of PNIPAAm. This fast, high resolution, and scalable 3D printing method for stimuli-responsive hydrogels may enable many new applications in diverse areas, including flexible sensors and actuators, bio-medical devices, and tissue engineering.

| S-EPMC5792483 | biostudies-literature

UV-Light Curing of 3D Printing Inks from Vegetable Oils for Stereolithography.

Project description:Typical resins for UV-assisted additive manufacturing (AM) are prepared from petroleum-based materials and therefore do not contribute to the growing AM industry trend of converting to sustainable bio-based materials. To satisfy society and industry's demand for sustainability, renewable feedstocks must be explored; unfortunately, there are not many options that are applicable to photopolymerization. Nevertheless, some vegetable oils can be modified to be suitable for UV-assisted AM technologies. In this work, extended study, through FTIR and photorheology measurements, of the UV-curing of epoxidized acrylate from soybean oil (AESO)-based formulations has been performed to better understand the photopolymerization process. The study demonstrates that the addition of appropriate functional comonomers like trimethylolpropane triacrylate (TMPTA) and the adjusting of the concentration of photoinitiator from 1% to 7% decrease the needed UV-irradiation time by up to 25%. Under optimized conditions, the optimal curing time was about 4 s, leading to a double bond conversion rate (DBC%) up to 80% and higher crosslinking density determined by the Flory-Rehner empirical approach. Thermal and mechanical properties were also investigated via TGA and DMA measurements that showed significant improvements of mechanical performances for all formulations. The properties were improved further upon the addition of the reactive diluents. After the thorough investigations, the prepared vegetable oil-based resin ink formulations containing reactive diluents were deemed suitable inks for UV-assisted AM, giving their appropriate viscosity. The validation was done by printing different objects with complex structures using a laser based stereolithography apparatus (SLA) printer.

| S-EPMC8068002 | biostudies-literature

Towards the Development of Artificial Bone Grafts: Combining Synthetic Biomineralisation with 3D Printing.

Project description:A synthetic technique inspired by the biomineralisation process in nacre has been previously reported to be effective in replicating the nanostructural elements of nacre in 2D chitosan hydrogel films. Here we evaluate the applicability of this synthetic biomineralisation technique, herein called the McGrath method, in replicating the flat tabular morphology of calcium carbonate and other nanostructural elements obtained when 2D chitosan hydrogel films were used, on a 3D porous chitosan hydrogel-based scaffold, hence developing 3D chitosan-calcium carbonate composites. Nozzle extrusion-based 3D printing technology was used to develop 3D porous scaffolds using chitosan hydrogel as the printing ink in a custom-designed 3D printer. The rheology of the printing ink and print parameters were optimised in order to fabricate 3D cylindrical structures with a cubic lattice-based internal structure. The effects of various dehydration techniques, including air-drying, critical point-drying and freeze-drying, on the structural integrity of the as-printed scaffolds from the nano to macroscale, were evaluated. The final 3D composite materials were characterised using scanning electron microscopy, X-ray diffraction and energy dispersive X-ray spectroscopy. The study has shown that McGrath method can be used to develop chitosan-calcium carbonate composites wherein the mineral and matrix are in intimate association with each other at the nanoscale. This process can be successfully integrated with 3D printing technology to develop 3D compartmentalised polymer-mineral composites.

| S-EPMC6462944 | biostudies-literature

Synthetic Polymers for Organ 3D Printing.

Project description:Three-dimensional (3D) printing, known as the most promising approach for bioartificial organ manufacturing, has provided unprecedented versatility in delivering multi-functional cells along with other biomaterials with precise control of their locations in space. The constantly emerging 3D printing technologies are the integration results of biomaterials with other related techniques in biology, chemistry, physics, mechanics and medicine. Synthetic polymers have played a key role in supporting cellular and biomolecular (or bioactive agent) activities before, during and after the 3D printing processes. In particular, biodegradable synthetic polymers are preferable candidates for bioartificial organ manufacturing with excellent mechanical properties, tunable chemical structures, non-toxic degradation products and controllable degradation rates. In this review, we aim to cover the recent progress of synthetic polymers in organ 3D printing fields. It is structured as introducing the main approaches of 3D printing technologies, the important properties of 3D printable synthetic polymers, the successful models of bioartificial organ printing and the perspectives of synthetic polymers in vascularized and innervated organ 3D printing areas.

| S-EPMC7466039 | biostudies-literature

Effect of Printing Direction on the Accuracy of 3D-Printed Dentures Using Stereolithography Technology.

Project description:This study evaluated the effects of the differences in the printing directions of stereolithography (SLA) three-dimensional (3D)-printed dentures on accuracy (trueness and precision). The maxillary denture was designed using computer-aided design (CAD) software with an STL file (master data) as the output. Three different printing directions (0°, 45°, and 90°) were used. Photopolymer resin was 3D-printed (n = 6/group). After scanning all dentures, the scanning data were saved/output as STL files (experimental data). For trueness, the experimental data were superimposed on the master data sets. For precision, the experimental data were selected from six dentures with three different printing directions and superimposed. The root mean square error (RMSE) and color map data were obtained using a deviation analysis. The averages of the RMSE values of trueness and precision at 0°, 45°, and 90° were statistically compared. The RMSE of trueness and precision were lowest at 45°, followed by 90°; the highest occurred at 0°. The RMSE of trueness and precision were significantly different among all printing directions (p < 0.05). The highest trueness and precision and the most favorable surface adaptation occurred when the printing direction was 45°; therefore, this may be the most effective direction for manufacturing SLA 3D-printed dentures.

| S-EPMC7435373 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data