Influence of Different Solvents and High-Electric-Field Cycling on Morphology and Ferroelectric Behavior of Poly(Vinylidene Fluoride-Hexafluoropropylene) Films.

ABSTRACT: P(VdF-HFP) films are fabricated via a solution casting doctor blade method using high (HVS) and low (LVS) volatile solvents, respectively. The structural properties and the ferroelectric behavior are investigated. The surface structure and crystal phase composition are found to be strongly dependent on the type of solvent. LVS leads to a rougher copolymer surface structure with large spherulites and a lower crystallinity in contrast with HVS. The crystalline phase of copolymer films fabricated with HVS consists almost exclusively of α-phase domains, whereas films from LVS solution show a large proportion of γ-phase domains, as concluded from Raman and X-ray diffraction spectra. Virgin films show no ferroelectric (FE) switching polarization at electric field amplitudes below 180 MV/m, independent of the solvent type, observed in bipolar dielectric displacement-electric field measurements. After applying electric fields of above 180 MV/m, a FE behavior emerges, which is significantly stronger for LVS films. In a repeated measurement, FE polarization switching already occurs at lower fields. A shielding effect may be related to this observation. Additionally, Raman bands of polar γ-phase increase by high-electric-field cycling for the LVS sample. The solvent used and the resulting crystal phase composition of the virgin sample is crucial for the copolymer behavior during bipolar electrical cycling.

SUBMITTER: Malzer T

PROVIDER: S-EPMC8303348 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Nitric oxide (NO) releasing polymers have been widely applied as biomaterials for a variety of biomedical implants and devices. However, the chemical leaching of NO donors and their byproduct species is almost always observed during the application of polymers doped with NO donors, unless the donor is covalently linked to the polymer. Herein, we report the first NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluorinated copolymer prepared by incorporating a fluorinated S-nitrosothiol as the NO donor. Under physiological conditions, the resulting polymeric films can release NO for 16?days. Importantly, due to both fluorine-fluorine and electrostatic charge interactions between the fluorinated NO donor and the PVDF-HFP copolymer, the total chemical leaching of the fluorinated NO donor and its disulfide product after 9?day was only 0.6% (mol%) of the initial amount of NO donor loaded into the film. These new NO release PVDF-HFP films exhibit antimicrobial and anti-biofilm activities against both Gram positive S. aureus and Gram negative P. aeruginosa strains. The NO-releasing PVDF-HFP polymer can also be coated on Teflon tubing to release NO under physiological conditions for extended time periods. This NO-releasing PVDF-HFP copolymer with greatly reduced chemical leaching could help enhance the biocompatibility and antimicrobial activity of various biomedical devices. STATEMENT OF SIGNIFICANCE: Fluoropolymers have been widely used in creating various biomedical implants and devices. However, nitric oxide (NO) release fluoropolymers have not been well studied to date. Additionally, in the application of biomaterials doped with NO donors, a significant amount of NO donors and their byproducts almost always leach into aqueous environment. We now report an NO releasing poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) fluoropolymer by incorporating a new fluorinated S-nitrosothiol. The NO release can last for 16?days under physiological conditions. The total chemical leaching was determined to be only 0.6?mol% of the initial S-nitrosothiol loaded. As expected, significant antimicrobial/anti-biofilm activities of the NO release PVDF-HFP film were observed against Gram positive S. aureus and Gram negative P. aeruginosa bacterial strains.

Dataset Information

Influence of Different Solvents and High-Electric-Field Cycling on Morphology and Ferroelectric Behavior of Poly(Vinylidene Fluoride-Hexafluoropropylene) Films.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets