Nanoscale Wear and Mechanical Properties of Calcite: Effects of Stearic Acid Modification and Water Vapor.

ABSTRACT: Understanding the wear of mineral fillers is crucial for controlling industrial processes, and in the present work, we examine the wear resistance and nanomechanical properties of bare calcite and stearic acid-modified calcite surfaces under dry and humid conditions at the nanoscale. Measurements under different loads allow us to probe the situation in the absence and presence of abrasive wear. The sliding motion is in general characterized by irregular stick-slip events that at higher loads lead to abrasion of the brittle calcite surface. Bare calcite is hydrophilic, and under humid conditions, a thin water layer is present on the surface. This water layer does not affect the friction force. However, it slightly decreases the wear depth and strongly influences the distribution of wear particles. In contrast, stearic acid-modified surfaces are hydrophobic. Nevertheless, humidity affects the wear characteristics by decreasing the binding strength of stearic acid at higher humidity. A complete monolayer coverage of calcite by stearic acid results in a significant reduction in wear but only a moderate reduction in friction forces at low humidity and no reduction at 75% relative humidity (RH). Thus, our data suggest that the wear reduction does not result from a lowering of the friction force but rather from an increased ductility of the surface region as offered by the stearic acid layer. An incomplete monolayer of stearic acid on the calcite surface provides no reduction in wear regardless of the RH investigated. Clearly, the wear properties of modified calcite surfaces depend crucially on the packing density of the surface modifier and also on the air humidity.

SUBMITTER: Wojas NA

PROVIDER: S-EPMC8397405 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Molecular Dynamics: Investigating the Self-Association of Stearic Acid and Heteroassociation of Stearic Acid-Water in Cyclohexane.

Project description:The self-association of molecular additives determines the chemical potential in the bulk and, in turn, the adsorbed amount onto a surface for a number of important commercial applications such as wind turbines. Molecular dynamics simulations have been utilized as a technique to study the self-association of model additive, stearic acid, and heteroassociation of stearic acid-water, in cyclohexane as a function of temperature. Reasonable values of the enthalpies and equilibrium constants were determined for stearic acid in cyclohexane. The role of water, nearly always present in commercial systems, in solution association was also studied to determine the thermodynamics parameters of hydration (i.e., acid-water heteroassociation). There are very few other studies reporting on these important heteroassociation parameters. The association constants and enthalpies of association obtained from molecular dynamics are in good agreement with experimental data in the literature. A combination of Fourier transform infrared (FTIR) data and molecular dynamics simulation results allows the fraction of open dimers (single hydrogen-bonded dimers) to be estimated in cyclohexane (which is not possible from the experimental FTIR data alone). The fraction of open dimers of stearic acid in cyclohexane at room temperature is ∼1.5% at 25 °C and ∼4% at 70 °C.

| S-EPMC10633822 | biostudies-literature

Effect of Clay Nanofillers on the Mechanical and Water Vapor Permeability Properties of Xylan-Alginate Films.

Project description:In this study, xylan-alginate-based films were reinforced with nanoclays (bentonite or halloysite) by the solvent casting technique. The effect of the nanoclay loadings (1-5 wt %) on various properties-mechanical, optical, thermal, solubility, water sorption, and water vapor permeability (WVP)-of the xylan-alginate films were examined for their application as food packaging materials. A 5 wt % loading of either bentonite or halloysite resulted in a 49% decrease of the WVP due to the impermeable nature of the silicate layers that make up both bentonite and halloysite. Thermal stability and solubility of the nanocomposite films were not significantly influenced by the presence of the nanoclays, whereas the optical properties were significantly improved when compared to neat xylan-alginate blend. In general, films reinforced with bentonite exhibited superior mechanical and optical properties when compared to both halloysite-based nanocomposite and neat films.

| S-EPMC7601507 | biostudies-literature

Nanoscale Bilayer Mechanical Lithography Using Water as Developer.

Project description:Sustainability has become a critical concern in the semiconductor industry as hazardous wastes released during the manufacturing process of semiconductor devices have an adverse impact on human beings and the environment. The use of hazardous solvents in existing fabrication processes also restricts the use of polymer substrates because of their low chemical resistance to such solvents. Here, we demonstrate an environmentally friendly mechanical, bilayer lithography that uses just water for development and lift-off. We show that we are able to create arbitrary patterns achieving resolution down to 310 nm. We then demonstrate the use of this technique to create functional devices by fabricating a MoS2 photodetector on a polyethylene terephthalate (PET) substrate with measured response times down to 42 ms.

| S-EPMC8289280 | biostudies-literature

The effect of surface wettability on water vapor condensation in nanoscale.

Project description:The effect of surface wettability on condensation heat transfer in a nanochannel is studied with the molecular dynamics simulations. Different from the conventional size, the results show that the filmwise mode leads to more efficient heat transfer than the dropwise mode, which is attributed to a lower interfacial thermal resistance between the hydrophilic surface and the condensed water compared with the hydrophobic case. The observed temperature jump at the solid-liquid surface confirms that the hydrophilic properties of the solid surface can suppress the interfacial thermal resistance and improve the condensation heat transfer performance effectively.

| S-EPMC4709718 | biostudies-other

Large datasets of water vapor sorption, mass diffusion immersed in water, hygroscopic expansion and mechanical properties of flax fibre/shape memory epoxy hygromorph composites.

Project description:This data article presents four experimental sets of results related to flax fibre composites with epoxy shape memory polymer matrix: water vapor absorption, mass diffusion immersed in water, hygroscopic expansion, mechanical properties. The water vapor absorption tests are described in raw data related to four types of laminates with weights measured at different relative humidity (0%, 9%, 33%, 44%,75%, 85% and 100%). The mass diffusion experiments are related to weights of immersed samples over time. The unidirectional composite hygroscopic expansion is also measured along the fibre longitude and transverse directions. The mechanical properties of flax composite at various temperatures (20°C, 40°C, 60°C, 80°C and 100°C) and humidity environments (50% and immersed) are also described. Load-displacement diagrams of the hygromorph composites are converted into stress-strain diagrams via a compliance calibration, from which the tensile moduli are extracted. The data presented in this article can provide a benchmark for the development of new models, or for the determination of other properties via post processing. The detailed interpretation of the data can be found in [1]. The data is available in the Mendeley Data repository at [2].

| S-EPMC9234088 | biostudies-literature

Enzymatic Synthesis and Characterization of Hydrophilic Sugar Based Polyesters and Their Modification with Stearic Acid.

Project description:Biodegradable and hydrophilic functional polyesters were synthesized enzymatically using xylitol or d-sorbitol together with divinyl adipate and lipase B from Candida antartica (CAL-B). The resulting polyesters had pendant OH-groups from their sugar units which were esterified to different degrees with stearic acid chloride. The structure and the degrees of polymerization of the resulting graft copolymers based on poly(xylitol adipate) and poly(d-sorbitol adipate) were characterized by ¹H NMR spectroscopy and SEC. DSC, WAXS and SAXS measurements indicated that a phase separation between polymer backbone and stearoyl side chains occurred in the graft copolymers, and, additionally, the side chains were able to crystallize which resulted in the formation of a lamellar morphology. Additionally, nanoparticles of the graft copolymers in an aqueous environment were studied by DLS and negative stain TEM.

| S-EPMC6432536 | biostudies-literature

Nanoscale mechanical properties of chitosan hydrogels as revealed by AFM.

Project description:In the context of tissue engineering, chitosan hydrogels are attractive biomaterials because they represent a family of natural polymers exhibiting several suitable features (cytocompatibility, bioresorbability, wound healing, bacteriostatic and fungistatic properties, structural similarity with glycosaminoglycans), and tunable mechanical properties. Optimizing the design of these biomaterials requires fine knowledge of its physical characteristics prior to assessment of the cell-biomaterial interactions. In this work, using atomic force microscopy (AFM), we report a characterization of mechanical and topographical properties at the submicron range of chitosan hydrogels, depending on physico-chemical parameters such as their polymer concentration (1.5%, 2.5% and 3.5%), their degree of acetylation (4% and 38.5%), and the conditions of the gelation process. Well-known polyacrylamide gels were used to validate the methodology approach for the determination and analysis of elastic modulus (i.e., Young's modulus) distribution at the gel surface. We present elastic modulus distribution and topographical and stiffness maps for different chitosan hydrogels. For each chitosan hydrogel formulation, AFM analyses reveal a specific asymmetric elastic modulus distribution that constitutes a useful hallmark for chitosan hydrogel characterization. Our results regarding the local mechanical properties and the topography of chitosan hydrogels initiate new possibilities for an interpretation of the behavior of cells in contact with such soft materials.

| S-EPMC7718388 | biostudies-literature

PVA-PDMS-Stearic acid composite nanofibrous mats with improved mechanical behavior for selective filtering applications.

Project description:In this work, we report a facile way to fabricate composite nanofibrous mats of polyvinyl alcohol (PVA), polydimethylsiloxane (PDMS), and stearic acid (SA) by employing the electrospinning-technique, with PDMS fraction ranging from 40w% to nearly 80w%. The results show that for a predetermined fraction of PVA and SA, incorporation of an optimal amount of PDMS is necessary for which the mats exhibit the best mechanical behavior. Beyond this optimal PDMS fraction, the mechanical properties of the composite mats deteriorate. This result has been attributed to the ability of the SA molecules to mediate binding between the PVA and PDMS long-chain molecules via van-der-Waals bonding. The morphological, structural, mechanical, and thermal characterizations respectively using SEM, XRD, DMA/tensile test, and DSC lend support to this explanation. By this method, it is possible to control the hydrophilicity/oleophilicity of the mats, and the mats show an excellent selective permeability to oil as compared to water and successfully filter water from a water-in-oil emulsion. Incorporation of SA not only serves to aid in electrospinning of a PDMS-rich nanofibrous mat with good mechanical strength and control over hydrophilicity/oleophilicity, but also has a potential use in fabricating sheets impregnated with phase change materials for thermal energy storage.

| S-EPMC6207706 | biostudies-literature

Water Orientation at the Calcite-Water Interface.

Project description:Mineral-water interfaces play an important role in many natural as well as technological fields. Fundamental properties of these interfaces are governed by the presence of the interfacial water and its specific structure at the surface. Calcite is particularly interesting as a dominant rock-forming mineral in the earth's crust. Here, we combine atomic force microscopy, sum-frequency generation spectroscopy, and molecular dynamics simulations to determine the position and orientation of the water molecules in the hydration layers of the calcite surface with high resolution. While atomic force microscopy provides detailed information about the position of the water molecules at the interface, sum-frequency generation spectroscopy can deduce the orientation of the water molecules. Comparison of the calcite-water interface to the interfaces of magnesite-water, magnesite-ethanol, and calcite-ethanol reveals a comprehensive picture with opposite water orientations in the first and second layer of the interface, which is corroborated by the molecular dynamics simulations.

| S-EPMC8365774 | biostudies-literature

Vitamin C/Stearic Acid Hybrid Monolayer Adsorption at Air-Water and Air-Solid Interfaces.

Project description:Because of the antioxidant activity of vitamin C (Vit C) polar heads, they can be used as a protective agent for fatty acids. Hence, the study on the growth of Vit C/stearic acid (SA) mixed binary films at air-water interface (known as Langmuir monolayer) and air-solid interface (known as Langmuir-Blodgett films) is of paramount interest. Although Vit C is situated at subsurface beneath SA molecules and interacts via hydrogen bonding between the hydroxyl groups of Vit C and SA, several Vit C molecules may infiltrate within SA two-dimensional matrix at the air-water interface. The increased mole fraction of Vit C (0.125-0.5) and the reduction of temperature (from 22 to 10 °C) of the subphase water result in an increase in the amount of adsorbed Vit C at the air-water interface. The surface pressure (π)-area (A) isotherms illustrate that such inclusion of Vit C provokes a spreading out of Vit C/SA binary monolayers, which leads to an alteration of different physicochemical parameters such as elasticity, Gibbs free energy of mixing, enthalpy, entropy, interaction energy parameter, and activity coefficient. However, being polar in nature, the transfer of pure Vit C on substrates gets affected. It can be transferred onto substrate by mixing suitably with SA as confirmed by infrared spectra. Their structures, extracted X-ray reflectivity, and atomic force microscopy (topography and phase imaging) are found to be strongly dependent on the nature of the substrate (hydrophilic and hydrophobic).

| S-EPMC6644023 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data