Radio Frequency Induction Welding of Silver Nanowire Networks for Transparent Heat Films.

ABSTRACT: Transparent heat films (THFs) are attracting increasing attention for their usefulness in various applications, such as vehicle windows, outdoor displays, and biosensors. In this study, the effects of induction power and radio frequency on the welding characteristics of silver nanowires (Ag NWs) and Ag NW-based THFs were investigated. The results showed that higher induction frequency and higher power increased the welding of the Ag NWs through the nano-welding at the junctions of the Ag NWs, which produced lower sheet resistance, and improved the adhesion of the Ag NWs. Using the inductive welding condition of 800 kHz and 6 kW for 60 s, 100 ohm/sq of Ag NW thin film with 95% transmittance at 550 nm after induction heating could be decreased to 56.13 ohm/sq, without decreasing the optical transmittance. In addition, induction welding of the Ag NW-based THFs improved haziness, increased bending resistance, enabled higher operating temperature at a given voltage, and improved stability.

SUBMITTER: Oh J

PROVIDER: S-EPMC8400299 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Flash-induced nanowelding of silver nanowire networks for transparent stretchable electrochromic devices.

Project description:Electrochromic devices (ECDs) are emerging as a novel technology for various applications like commercialized smart window glasses, and auto-dimming rear-view mirrors. Recently, the development of low-power, lightweight, flexible, and stretchable devices has been accelerated to meet the growing demand in the new wearable devices market. Silver nanowires (AgNWs) can become new primary transparent conducting electrode (TCE) materials to replace indium tin oxide (ITO) for ECDs. However, issues such as substrate adhesion, delamination, and higher resistance still exist with AgNWs. Herein, we report a high-performance stretchable flash-induced AgNW-network-based TCE on surface-treated polydimethylsiloxane (PDMS) substrates. A Xe flash light method was used to create nanowelded networks of AgNWs. Surface silane treatments increased the adhesion and durability of the films as well. Finally, ECDs were fabricated under the optimal conditions and examined under strained conditions to demonstrate the resistance and mechanical behaviours of the devices. Results showed a flexible and durable film maintaining a high level of conductivity and reversible resistance behaviour, beyond those currently achievable with standard ITO/PET flexible TCEs.

| S-EPMC5807424 | biostudies-literature

Enhancement of Antibacterial Performance of Silver Nanowire Transparent Film by Post-Heat Treatment.

Project description:Silver nanomaterials (AgNMs) have been applied as antibacterial agents to combat bacterial infections that can cause disease and death. The antibacterial activity of AgNMs can be improved by increasing the specific surface area, so significant efforts have been devoted to developing various bottom-up synthesis methods to control the size and shape of the particles. Herein, we report on a facile heat-treatment method that can improve the antibacterial activity of transparent silver nanowire (AgNW) films in a size-controllable, top-down manner. AgNW films were fabricated via spin-coating and were then heated at different temperatures (230 and 280 °C) for 30 min. The morphology and the degree of oxidation of the as-fabricated AgNW film were remarkably sensitive to the heat-treatment temperature, while the transparency was insensitive. As the heat-treatment temperature increased, the AgNWs spontaneously broke into more discrete wires and droplets, and oxidation proceeded faster. The increase in the heat-treatment temperature further increased the antibacterial activity of the AgNW film, and the heat treatment at 280 °C improved the antibacterial activity from 31.7% to 94.7% for Staphylococcus aureus, and from 57.0% to 98.7% for Escherichia coli. Following commonly accepted antibacterial mechanisms of AgNMs, we present a correlation between the antibacterial activity and surface observations of the AgNW film.

| S-EPMC7279492 | biostudies-literature

Tackling the Stability Issues of Silver Nanowire Transparent Conductive Films through FeCl₃ Dilute Solution Treatment.

Project description:Silver nanowires (AgNWs) have been investigated as alternatives to indium tin oxide in transparent conductive films (TCFs) for electronics. However, AgNW TCFs still pose stability issues when exposed to thermal, chemical, and mechanical stimuli. Herein, we demonstrate a facile and effective route to improve stability by treating the films with dilute ferric chloride solution. Our results indicate that after treatment the films exhibit a dramatically enhanced stability against aging, high temperature oxidation, chemical etching, sulfurization, and mechanical straining. Size-dependent instability is fully explored and explained regarding surface atomic diffusion, which could be blocked by enhancing the activation energy of surface diffusion through forming a AgCl cap under ferric chloride solution treatment. Chemisorption-related Fermi level shift of silver nanowires is applied to tune their chemical reactivity to ferric chloride solution for balancing between size-dependent stability improvement and maintaining optoelectrical properties. Owing to the dilute treatment solution, the treated films exhibit a negligible change in light transmittance, whereas sheet resistance decreases by 30% and flexibility increases because of capillary-force-induced welding of contacting AgNWs and AgCl layer mediated tightening. These findings are significant for real-world applications of AgNW TCFs.

| S-EPMC6523130 | biostudies-literature

Scalable Solution-Processed Fabrication Approach for High-Performance Silver Nanowire/MXene Hybrid Transparent Conductive Films.

Project description:The transparent conductive films (TCFs) based on silver nanowires are expected to be a next-generation electrode for flexible electronics. However, their defects such as easy oxidation and high junction resistance limit its wide application in practical situations. Herein, a method of coating Ti3C2Tx with different sizes was proposed to prepare silver nanowire/MXene composite films. The solution-processed silver nanowire (AgNW) networks were patched and welded by capillary force effect through the double-coatings of small and large MXene nanosheets. The sheet resistance of the optimized AgNW/MXene TCFs was 15.1 Ω/sq, the optical transmittance at 550 nm was 89.3%, and the figure of merit value was 214.4. Moreover, the AgNW/MXene TCF showed higher stability at 1600 mechanical bending, annealing at 100 °C for 50 h, and exposure to ambient air for 40 days. These results indicate that the novel AgNW/MXene TCFs have a great potential for high-performance flexible optoelectronic devices.

| S-EPMC8224074 | biostudies-literature

Screen-Printed Fabrication of PEDOT:PSS/Silver Nanowire Composite Films for Transparent Heaters.

Project description:A transparent and flexible film heater was fabricated; based on a hybrid structure of poly(3,4-ethylenedioxythiophene) poly(styrenesulfonate) (PEDOT:PSS) and silver nanowires (Ag NWs) using a screen printing; which is a scalable production technology. The resulting film integrates the advantages of the two conductive materials; easy film-forming and strong adhesion to the substrate of the polymer PEDOT:PSS; and high conductivity of the Ag NWs. The fabricated composite films with different NW densities exhibited the transmittance within the range from 82.3% to 74.1% at 550 nm. By applying 40 V potential on the films; a stable temperature from 49 °C to 99 °C was generated within 30 s to 50 s. However; the surface temperature of the pristine PEDOT:PSS film did not increase compared to the room temperature. The composite film with the transmittance of 74.1% could be heated to the temperatures from 41 °C to 99 °C at the driven voltages from 15 V to 40 V; indicating that the film heater exhibited uniform heating and rapid thermal response. Therefore; the PEDOT:PSS/Ag NW composite film is a promising candidate for the application of the transparent and large-scale film heaters.

| S-EPMC5503381 | biostudies-other

Transparent Electrodes Based on Silver Nanowire Networks: From Physical Considerations towards Device Integration.

Project description:The past few years have seen a considerable amount of research devoted to nanostructured transparent conducting materials (TCM), which play a pivotal role in many modern devices such as solar cells, flexible light-emitting devices, touch screens, electromagnetic devices, and flexible transparent thin film heaters. Currently, the most commonly used TCM for such applications (ITO: Indium Tin oxide) suffers from two major drawbacks: brittleness and indium scarcity. Among emerging transparent electrodes, silver nanowire (AgNW) networks appear to be a promising substitute to ITO since such electrically percolating networks exhibit excellent properties with sheet resistance lower than 10 Ω/sq and optical transparency of 90%, fulfilling the requirements of most applications. In addition, AgNW networks also exhibit very good mechanical flexibility. The fabrication of these electrodes involves low-temperature processing steps and scalable methods, thus making them appropriate for future use as low-cost transparent electrodes in flexible electronic devices. This contribution aims to briefly present the main properties of AgNW based transparent electrodes as well as some considerations relating to their efficient integration in devices. The influence of network density, nanowire sizes, and post treatments on the properties of AgNW networks will also be evaluated. In addition to a general overview of AgNW networks, we focus on two important aspects: (i) network instabilities as well as an efficient Atomic Layer Deposition (ALD) coating which clearly enhances AgNW network stability and (ii) modelling to better understand the physical properties of these networks.

| S-EPMC5552077 | biostudies-other

Nanoscale Chemical and Electrical Stabilities of Graphene-covered Silver Nanowire Networks for Transparent Conducting Electrodes.

Project description:The hybrid structure of Ag nanowires (AgNWs) covered with graphene (Gr) shows synergetic effects on the performance of transparent conducting electrodes (TCEs). However, these effects have been mainly observed via large-scale characterization, and precise analysis at the nanoscale level remains inadequate. Here, we present the nanoscale verification and visualization of the improved chemical and electrical stabilities of Gr-covered AgNW networks using conductive atomic force microscopy (C-AFM), Auger electron spectroscopy (AES), and X-ray photoelectron spectroscopy (XPS) combined with the gas cluster ion beam (GCIB) sputtering technique. Specifically by transferring island Gr on top of the AgNW network, we were able to create samples in which both covered and uncovered AgNWs are simultaneously accessible to various surface-characterization techniques. Furthermore, our ab initio molecular dynamics (AIMD) simulation elucidated the specific mechanistic pathway and a strong propensity for AgNW sulfidation, even in the presence of ambient oxidant gases.

| S-EPMC5020617 | biostudies-literature

Improved Flexible Transparent Conductive Electrodes based on Silver Nanowire Networks by a Simple Sunlight Illumination Approach.

Project description:Silver nanowire (Ag NW) networks have attracted wide attention as transparent electrodes for emerging flexible optoelectronics. However, the sheet resistance is greatly limited by large wire-to-wire contact resistances. Here, we propose a simple sunlight illumination approach to remarkably improve their electrical conductivity without any significant degradation of the light transmittance. Because the power density is extremely low (0.1?W/cm2, 1-Sun), only slight welding between Ag NWs has been observed. Despite this, a sheet resistance of <20??/sq and transmittance of ~87% at wavelength of 550?nm as well as excellent mechanical flexibility have still been achieved for Ag NW networks after sunlight illumination for 1?hour or longer, which are significant upgrades over those of ITO. Slight plasmonic welding together with the associated self-limiting effect has been investigated by numerical simulations and further verified experimentally through varied solar concentrations. Due to the reduced resistance, high-performance transparent film heaters as well as efficient defrosters have been demonstrated, which are superior to the previously-reported Ag NW based film heaters. Since the sunlight is environmentally friendly and easily available, sophisticated or expensive facilities are not necessary. Our findings are particularly meaningful and show enormous potential for outdoor applications.

| S-EPMC5294563 | biostudies-literature

The effect of rod orientation on electrical anisotropy in silver nanowire networks for ultra-transparent electrodes.

Project description:Two-dimensional networks made of metal nanowires are excellent paradigms for the experimental observation of electrical percolation caused by continuous jackstraw-like physical pathways. Such systems became very interesting as alternative material in transparent electrodes, which are fundamental components in display devices. This work presents the experimental characterization of low-haze and ultra-transparent electrodes based on silver nanowires. The films are created by dip-coating, a feasible and scalable liquid film coating technique. We have found dominant alignment of the silver nanowires in withdrawal direction. The impact of this structural anisotropy on electrical anisotropy becomes more pronounced for low area coverage. The rod alignment does not influence the technical usability of the films as significant electrical anisotropy occurs only at optical transmission higher than 99 %. For films with lower transmission, electrical anisotropy becomes negligible. In addition to the experimental work, we have carried out computational studies in order to explain our findings further and compare them to our experiments and previous literature. This paper presents the first experimental observation of electrical anisotropy in two-dimensional silver nanowire networks close at the percolation threshold.

| S-EPMC5039631 | biostudies-literature

Thermal stability data of silver nanowire transparent conducting electrode.

Project description:The authors have recently reported the enhanced thermal stability of silver nanowire (AgNW) network transparent electrodes by electrodeposition method [1]. AgNW networks are known to break into droplets at elevated temperatures (spherodization temperature) that are still much lower than the bulk Ag melting temperature. This phenomenon is known as Rayleigh instability. As the diameter of individual AgNW in the network increases by electrodeposited Ag on the AgNW surface, the thermal stability of AgNW network can be enhanced. Here, we provide the data on the spherodization temperature depending on AgNW diameter. We also report the calculated activation energy required to induce the spherodization of AgNW network.

| S-EPMC7109625 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data