Porous Materials Based on Poly(methylvinylsiloxane) Cross-Linked with 1,3,5,7-Tetramethylcyclotetrasiloxane in High Internal Phase Emulsion as Precursors to Si-C-O and Si-C-O/Pd Ceramics.

ABSTRACT: Polysiloxane networks were prepared by hydrosilylation of poly(methylvinylsiloxane) (V₃ polymer) with 1,3,5,7-tetramethylcyclotetrasiloxane (D₄^H) at various Si-Vinyl: Si-H groups molar ratios in water-in-oil high internal phase emulsion (HIPE). Curing the emulsions followed by removal of water led to foamed cross-linked polysiloxane systems differing in the cross-linking degrees, as well as residual Si-H and Si-Vinyl group concentrations. Treatment of thus obtained materials in Pd(OAc)₂ solution in tetrahydrofuran resulted in the formation of porous palladium/polymer nanocomposites with different Pd contents (1.09-1.70 wt %). Conducted investigations showed that pyrolysis of the studied materials at 1000 °C in argon atmosphere leads to porous Si-C-O and Si-C-O/Pd ceramics containing amorphous carbon and graphitic phases. Thermogravimetric (TG) analysis of the starting cross-linked polymer materials and those containing Pd nanoparticles revealed that the presence of palladium deteriorates thermal stability and decreases ceramic yields of preceramic networks. The extent of this effect depends on polymer cross-linking density in the system.

SUBMITTER: Mrowka J

PROVIDER: S-EPMC8510497 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Poly(methylvinylsiloxane)-Based High Internal Phase Emulsion-Templated Materials (polyHIPEs)-Preparation, Incorporation of Palladium, and Catalytic Properties.

Project description:Poly(methylvinylsiloxane) (V3 polymer) obtained by kinetically controlled anionic ring-opening polymerization of 1,3,5-trimethyl-1,3,5-trivinylcyclotrisiloxane was cross-linked with various amounts of 1,3,5,7-tetramethylcyclotetrasiloxane (D4 H) in w/o high internal phase emulsions (HIPEs). PolyHIPEs thus prepared differed in the polymer cross-linking degree, which affected their porous morphology and total porosity. The obtained V3 polymer-based polyHIPEs were applied as matrices for the incorporation of Pd from the Pd(OAc)2 solution in tetrahydrofuran. This process involved the conversion of Si-H groups remaining in the polymer networks and resulted in the formation of crystalline, metallic Pd in the systems. Mean sizes of the generated Pd crystallites were lower in polyHIPEs of higher than in those of lower polymer cross-linking degrees and porosities (∼5 nm vs ∼8 nm, respectively). The Pd-containing polyHIPEs showed activity in catalytic hydrogenation of the triple carbon-carbon bond in phenylacetylene giving the unsaturated product, styrene with a selectivity of ca. 80%. To the best of our knowledge, this is the first work devoted to polysiloxane-based polyHIPEs with dispersed metallic particles.

| S-EPMC7660935 | biostudies-literature

Cross-linked poly(ionic liquid) as precursors for nitrogen-doped porous carbons.

Project description:A soluble and easily dispersive cross-linked poly(ionic liquid), copolymer of 1-vinyl-3-butylimidazolium bromide ([VBIM][Br]) and divinylbenzene (DVB), was used as a precursor for nitrogen doped porous carbons (NPCs) with SiO2 (from tetraethyl orthosilicate) as a template. The NPCs were characterized by infrared (IR) spectroscopy, nitrogen adsorption-desorption, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy, thermo gravimetric analysis (TGA), elemental analysis and X-ray photoelectron spectroscopy (XPS). The specific surface area and porosity of NPCs depended on the carbonization temperature, the SiO2/[VBIM][Br] ratio and the precursors. Under the optimized conditions, the NPC prepared from cross-linked poly(ionic liquid), P([VBIM][Br]-0.1DVB), gave a high specific surface area up to 1324 m2 g-1. XRD indicated that amorphous and disordered graphitic layers were dominant in NPCs. The nitrogen content was about 4-5 wt% in NPCs, and the nitrogen bonding state observed using XPS analysis was mainly pyridinic- and pyrrolic-N. Meanwhile, the cyclic voltammetry, gravimetric charge-discharge curves and electrochemical impedance spectroscopy of the NPCs were also investigated, the specific capacitance was up to 243 F g-1 at 0.1 A g-1, and the retention ratio was nearly 100% after charge-discharge cycling 2400 times at 2 A g-1 in 6 M KOH electrolyte.

| S-EPMC9061521 | biostudies-literature

Emulsion Gels as Precursors for Porous Silicones and All-Polymer Composites-A Proof of Concept Based on Siloxane Stabilizers.

Project description:In spite of its versatility, the emulsion templating method is rather uncommon for the preparation of porous silicones. In this contribution, two siloxane-containing stabilizers, designed to be soluble in polar (water) and non-polar (toluene) solvents, respectively, were used in low concentrations to produce stable emulsions, wherein polysiloxane gels were obtained by UV-photoinitiated thiol-ene click cross-linking. The stabilizers exhibited negative interfacial tension, as measured by Wilhelmy plate tensiometry. The emulsion gels evolved into porous silicones (xerogels), with tunable morphology and properties. According to TEM and SEM investigations, the emulsion template was preserved in the final materials. Several parameters (e.g., the structure of the polysiloxane precursors, composition of the emulsion gels, nature of the continuous phase, cross-linking conditions, or additives) can be varied in order to obtain porous elastic materials with desired properties, such as Janus membranes, absorbent monoliths, all-polymer porous composites, or silicone-swollen gels. The feasibility of these types of materials was tested, and exemplary porous silicones were briefly characterized by contact angle measurements, mechanical testing, and absorption tests. The proposed method is simple, fast, and economic, uses very little amounts of stabilizers, and can be adjusted as a green technique. In this contribution, all the silicon-based materials with a convenient design were prepared in house.

| S-EPMC9222695 | biostudies-literature

Materials Precursor Score: Modeling Chemists' Intuition for the Synthetic Accessibility of Porous Organic Cage Precursors.

Project description:Computation is increasingly being used to try to accelerate the discovery of new materials. One specific example of this is porous molecular materials, specifically porous organic cages, where the porosity of the materials predominantly comes from the internal cavities of the molecules themselves. The computational discovery of novel structures with useful properties is currently hindered by the difficulty in transitioning from a computational prediction to synthetic realization. Attempts at experimental validation are often time-consuming, expensive, and frequently, the key bottleneck of material discovery. In this work, we developed a computational screening workflow for porous molecules that includes consideration of the synthetic difficulty of material precursors, aimed at easing the transition between computational prediction and experimental realization. We trained a machine learning model by first collecting data on 12,553 molecules categorized either as "easy-to-synthesize" or "difficult-to-synthesize" by expert chemists with years of experience in organic synthesis. We used an approach to address the class imbalance present in our data set, producing a binary classifier able to categorize easy-to-synthesize molecules with few false positives. We then used our model during computational screening for porous organic molecules to bias toward precursors whose easier synthesis requirements would make them promising candidates for experimental realization and material development. We found that even by limiting precursors to those that are easier-to-synthesize, we are still able to identify cages with favorable, and even some rare, properties.

| S-EPMC8479809 | biostudies-literature

Electrochemical Performance Enhancement of Micro-Sized Porous Si by Integrating with Nano-Sn and Carbonaceous Materials.

Project description:Silicon is investigated as one of the most prospective anode materials for next generation lithium ion batteries due to its superior theoretical capacity (3580 mAh g-1), but its commercial application is hindered by its inferior dynamic property and poor cyclic performance. Herein, we presented a facile method for preparing silicon/tin@graphite-amorphous carbon (Si/Sn@G-C) composite through hydrolyzing of SnCl2 on etched Fe-Si alloys, followed by ball milling mixture and carbon pyrolysis reduction processes. Structural characterization indicates that the nano-Sn decorated porous Si particles are coated by graphite and amorphous carbon. The addition of nano-Sn and carbonaceous materials can effectively improve the dynamic performance and the structure stability of the composite. As a result, it exhibits an initial columbic efficiency of 79% and a stable specific capacity of 825.5 mAh g-1 after 300 cycles at a current density of 1 A g-1. Besides, the Si/Sn@G-C composite exerts enhanced rate performance with 445 mAh g-1 retention at 5 A g-1. This work provides an approach to improve the electrochemical performance of Si anode materials through reasonable compositing with elements from the same family.

| S-EPMC7919461 | biostudies-literature

Facile synthesis of hierarchically porous carbonaceous materials derived from olefin/aldehyde precursors using silica as templates.

Project description:Porous carbon is exceptionally useful, but it remains a great challenge to develop a facile route to prepare porous carbon materials with hierarchical structure and enhanced porosity. This work demonstrates a novel synthetic pathway for hierarchical carbonaceous materials (HCM) using isobutene and formaldehyde as carbon precursors via silica templates impregnated with phosphorus. Different from the traditional nanocasting method, the formation of the carbon structure is caused by heavy coke deposits on the solid catalyst in the course of the olefin/aldehyde vapor reaction. The coke-derived carbonaceous materials indicated by transmission electron microscopy (TEM) and nitrogen adsorption-desorption measurement are hierarchically mesoporous structures with a large surface area (971 m2 g-1) and pore volume (1.91 cm3 g-1). We have demonstrated for the first time that the olefin/aldehyde reaction may provide a convenient route to develop a porous carbon texture. The newly developed method may lead to porous carbon having scientific and technological importance in adsorption and catalysis applications.

| S-EPMC9079135 | biostudies-literature

Nanostructure of Porous Si and Anodic SiO2 Surface Passivation for Improved Efficiency Porous Si Solar Cells.

Project description:The photovoltaic effect in the anodic formation of silicon dioxide (SiO2) on porous silicon (PS) surfaces was investigated toward developing a potential passivation technique to achieve high efficiency nanostructured Si solar cells. The PS layers were prepared by electrochemical anodization in hydrofluoric acid (HF) containing electrolyte. An anodic SiO2 layer was formed on the PS surface via a bottom-up anodization mechanism in HCl/H2O solution at room temperature. The thickness of the oxide layer for surface passivation was precisely controlled by adjusting the anodizing current density and the passivation time, for optimal oxidation on the PS layer while maintaining its original nanostructure. HRTEM characterization of the microstructure of the PS layer confirms an atomic lattice matching at the PS/Si interface. The dependence of photovoltaic performance, series resistance, and shunt resistance on passivation time was examined. Due to sufficient passivation on the PS surface, a sample with anodization duration of 30 s achieved the best conversion efficiency of 10.7%. The external quantum efficiency (EQE) and internal quantum efficiency (IQE) indicate a significant decrease in reflectivity due to the PS anti-reflection property and indicate superior performance due to SiO2 surface passivation. In conclusion, the surface of PS solar cells could be successfully passivated by electrochemical anodization.

| S-EPMC7916900 | biostudies-literature

Porous Zirconia/Magnesia Ceramics Support Osteogenic Potential In Vitro.

Project description:Porous zirconia (ZrO2), magnesia (MgO) and zirconia/magnesia (ZrO2/MgO) ceramics were synthesised by sintering and designated as ZrO2(100), ZrO2(75)MgO(25), ZrO2(50)MgO(50), ZrO2(25)MgO(75), MgO(100) based on their composition. The ceramic samples were characterised by means of scanning electron microscopy, X-ray diffraction, energy-dispersive X-ray spectroscopy and atomic absorption spectrometry to explore the incorporation of Mg atoms into the zirconia lattice. The resulting porosity of the samples was calculated based on the composition and density. The final porosity of the cylinder-shaped ceramic samples ranged between 30 and 37%. The mechanical analysis exhibited that the Young modulus increased and the microstress decreased with increasing magnesia amount, with values ranging from 175 GPa for zirconia to 301 GPa for magnesia. The adhesion, viability, proliferation and osteogenic activity of MC3T3-E1 pre-osteoblastic cells cultured on the zirconia/magnesia ceramics was found to increase, with the magnesia-containing ceramics exhibiting higher values of calcium mineralisation. The results from the mechanical analysis, the ALP activity, the calcium and collagen production demonstrate that the zirconia/magnesia ceramics possess robust osteoinductive capacity, therefore holding great potential for bone tissue engineering.

| S-EPMC7926502 | biostudies-literature

Materials Research & Measurement Needs for Ceramics Additive Manufacturing.

Project description:We report on a recent workshop dedicated to additive manufacturing (AM) of ceramics that was held at the National Institute of Standards and Technology (NIST) in November 2019. This two-day all-invited meeting brought together experts from industry, government agencies and academia to review the state of the field and identify the most pressing applied materials research and metrology issues which, if addressed, could accelerate the incorporation of AM methods into commercial ceramic manufacturing. Besides the AM technologies, the discussions included consideration of the necessary post-processing steps. We highlight some of the successes and challenges for the adoption of ceramics AM on an industrial scale, as viewed by the workshop participants. We also propose actions for the ceramic community to facilitate the wider commercialization of these fabrication methods.

| S-EPMC7923907 | biostudies-literature

Preparation of fluoropolymer materials with different porous morphologies by an emulsion template method using supercritical carbon dioxide as a medium.

Project description:The choice of a suitable surfactant is key to the formation of a stable water-in-CO2 (W/C) or CO2-in-water (C/W) emulsion. It is even more critical in stabilization of the emulsion containing carbon dioxide (CO2). In this study, the successful preparation of W/C emulsion was achieved by using the amphiphilic block polymer poly(ethylene glycol) methyl ether-b-poly(trifluoroethyl methacrylate) (mPEG45-b-(TFEMA) n ) as a surfactant, in which CO2 was used as a solvent for the fluoromonomer, trifluoroethyl methacrylate (TFEMA). In the case of the W/C emulsion, CO2 and TFEMA were used as the continuous phase and water as the internal phase of the emulsion system. It has been found that in the length of the block polymer mPEG45-b-(TFEMA) n , the fluorine-containing chain end has a significant effect on the morphology of the polymer and the type of emulsion formed. The morphology of the polymer was observed by scanning electron microscopy which confirmed the type of emulsion formed. With the fluorine-containing end segment, the morphology of the polymer changes from a small hollow sphere in a large hollow sphere to a hollow spherical to a porous structure. Correspondingly, it could be concluded that the type of emulsion could go through the process from water-in-CO2-in-water-in-CO2 (W/C/W/C) emulsion to water-in-CO2-in-water (W/C/W) emulsion to water-in-CO2 (W/C) emulsion. Also, suitable co-surfactants were identified in this study. Investigations were also attempted to check the effect of the amount of surfactant, cross-linker and water/CO2 ratio on the type of emulsion formed as well as the morphology of the resultant polymer.

| S-EPMC9063414 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data