Effects of waste glass and waste marble on mechanical and durability performance of concrete

ABSTRACT: Industrial waste has been rapidly increased day by day because of the fast-growing population which results environmental pollutions. It has been recommended that the disposal of industrial waste would be greatly reduced if it could be incorporated in concrete production. In cement concrete technology, there are many possibilities to use waste materials either as cement replacement or aggregate in concrete production. Two major industrials waste are glass and marble waste. The basic objective of this investigation is to examine the characteristics of concrete waste glass (WG) as binding material in proportions 10%, 20% and 30% by weight of cement. Furthermore, to obtain high strength concrete, waste marble in proportion of 40%, 50% and 60% by weight cement as fine aggregate were used as a filler material to fill the voids between concrete ingredients. Fresh properties were evaluated through slump cone test while mechanical performance was evaluated through compressive strength and split tensile strength which were performed after 7 days, 28 days and 56 days curing. Results show that, workability of concrete decreased with incorporation of waste glass and marble waste. Furthermore, mechanical performance improved considerably up 20% and 50% substitution of waste glass and waste marble respectively. Statistical approach of Response Surface Methodology (RSM) was used optimize both waste materials in concrete. Results indicate better agreement between statistical and experimental results.

SUBMITTER: Ahmad J

PROVIDER: S-EPMC8564529 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:The aim of this study was to develop new sulfur-copolymer concrete composites using waste compounds that have good mechanical characteristics and show a resistance to biocorrosion. The comonomers used to synthesize the sulfur-organic copolymers were-90 wt. % sulfur; 5 wt. % dicyclopentadiene (DCPD); 5 wt. % organic monomers, styrene (SDS), 1-decene (SDD), turpentine (SDT), and furfural (SDF). The concrete composites based on sulfur-organic copolymers were filled with aggregates, sand, gravel, as well as additives and industrial waste such as fly ash or phosphogypsum. The sulfur-organic copolymers were found to be chemically stable (softening temperature, thermal stability, melting temperature, amount of recrystallized sulfur, and shore D hardness). Partial replacement of DCPD with other organic comonomers did not change the thermal stability markedly but did make the copolymers more elastic. However, the materials became significantly stiffer after repeated melting. All the tested copolymers were found to be resistant to microbial corrosion. The highest resistance was exhibited by the SDS-containing polymer, while the SDF polymer exhibited the greatest change due to the activity of the microorganisms (FTIR analysis and sulfur crystallization). The concrete composites with sulfur-organic copolymers containing DCPD, SDS, SDF, fly ash, and phosphogypsum were mechanically resistant to compression and stretching, had low water absorbance, and were resistant to factors, such as temperature and salt. Resistance to freezing and thawing (150 cycles) was not confirmed. The concrete composites with sulfur-organic copolymers showed resistance to bacterial growth and acid activity during 8 weeks of incubation with microorganisms. No significant structural changes were observed in the SDS composites after incubation with bacteria, whereas composites containing SDF showed slight changes (FTIR and microscopic analysis). The concrete composite containing sulfur, DCPD, SDS, sand, gravel, and fly ash was the most resistant to microbiological corrosion, based on the metabolic activity of the bacteria and the production of ergosterol by the molds after eight weeks of incubation. It was found that Thiobacillus thioparus was the first of the acidifying bacteria to colonize the sulfur concrete, decreasing the pH of the environment. The molds Penicillium chrysogenum, Aspergillus versicolor and Cladosporium herbarum were able to grow on the surface of the tested composites only in the presence of an organic carbon source (glucose). During incubation, they produced organic acids and acidified the environment. However, no morphological changes in the concretes were observed suggesting that sulfur-organic copolymers containing styrene could be used as engineering materials or be applied as binders in sulfur-concretes.

Dataset Information

Effects of waste glass and waste marble on mechanical and durability performance of concrete

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets