Continuous and controllable electro-fabrication of antimicrobial copper-alginate dressing for infected wounds treatment.

ABSTRACT: The contamination of chronic wound with bacteria especially methicillin-resistant Staphylococcus aureus (MRSA) is considered as the major factor interferencing normal wound healing. There still remain great challenges in developing safe and effective wound dressings with wide-spectrum antibacterial functions. Alginate hydrogel is a common dressing for wound treatment. Copper is one of the trace elements in human body with inherent antibacterial activity. Traditional methods for preparing a structure-controlled copper-alginate antibacterial matrix are difficult however, due to the fast and uncontrolled gelation between alginate and metal ions. In this work, we report an electrodeposition method for rapid fabrication of copper cross-linked alginate antibacterial films (Cu²⁺-Alg) with controlled structure and copper content, which is relied on an electrical signal controlled release of copper ions from the reaction of insoluble salt Cu₂(OH)₂CO₃ and the generated protons via water electrolysis on anode. The results prove that the physical structure and chemical composition of the electrodeposited Cu²⁺-Alg films can be continuously modulated by the imposed charges during electrodeposition. In vitro tests demonstrate the film has Cu²⁺ content-dependent bactericidal activities. Film's cytocompatibility is well controlled by the imposed charges for Cu²⁺-Alg fabrication. The MRSA infected wound model in vivo also indicates that Cu²⁺-Alg film can effectively eliminate bacterial infection and suppress host inflammatory responses. We believe this study demonstrates a convenient and controllable strategy to fabricate alginate antibacterial dressings with potential applications for infected wound treatment. More broadly, our work reveals electrodeposition is a general and simple platform to design alginate films with versatile functions.

SUBMITTER: Wang S

PROVIDER: S-EPMC8613166 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Similar Datasets

Project description:Wound infections are serious medical complications that can endanger human health. Latest researches show that conductive composite materials may make endogenous/exogenous electrical stimulation more effective, guide/comb cell migration to the wound, and subsequently promote wound healing. To accelerate infected wound healing, a novel medical silver nanoparticle-doped conductive polymer-based hydrogel system (Ag NPs/CPH) dressing with good conductivity, biocompatibility, and mechanical and antibacterial properties was fabricated. For the hydrogel dressing, Ag NPs/CPH, polyvinyl alcohol (PVA), and gelatin were used as the host matrix materials, and phytic acid (PA) was used as the cross-linking agent to introduce conductive polyaniline into the matrix, with antibacterial Ag NPs loaded via impregnation. After a series of analyses, the material containing 5 wt% of PVA by concentration, 1.5 wt% gelatin, 600 μL of AN reactive volume, and 600 μL of PA reactive volume was chosen for Ag NPs/CPH preparation. XPS and FTIR analysis had been further used to characterize the composition of the prepared Ag NPs/CPH. The test on the swelling property showed that the hydrogels had abundant pores with good water absorption (≈140% within 12 h). They can be loaded and continuously release Ag NPs. Thus, the prepared Ag NPs/CPH showed excellent antibacterial property with increasing duration of immersion of Ag NPs. Additionally, to evaluate in vivo safety, CCK-8 experiments of HaCat, LO2 and 293T cells were treated with different concentrations of the Ag NPs/CPH hydrogel soaking solution. The experimental results showed the Ag NPs/CPH had no significant inhibitory effect on any of the cells. Finally, an innovative infection and inflammation model was designed to evaluate the prepared Ag NPs/CPH hydrogel dressing for the treatment of severely infected wounds. The results showed that even when infected with bacteria for long periods of time (more than 20 h), the proposed conductive antibacterial hydrogel could treat severely infected wounds.

Project description:Background and aimsDressings containing silver ions are an accepted and common option for wound treatment. However, some wounds fail to heal at the desired rate despite optimal management. The aim of the study was to examine the effect of copper dressings in noninfected wounds.MethodsThe study included 20 patients aged 18-85 years with 2-30 cm2 noninfected wounds treated for 17-41 days with silver wound dressings that failed to reduce by >50% the wound size, who were then treated with copper dressings. Ten patients were diabetics, 10 suffered from hypertension, and six suffered from peripheral vascular disease (PVD). Two patients suffered from two wounds. Most were amputation wounds below the knee.ResultsFive patients dropped out from the study due to complications not related to the wound. The mean period of silver and copper dressings treatment was 25.6 and 29.6 days, respectively (p = 0.25; t test). None of the wounds became infected. Comparing a period of 25 days, during the copper dressings treatment, the mean wound area reduction was ~2.4 times higher than during the silver dressing treatment, 87.35 ± 22.4% versus 37.02 ± 25.11% (mean ± SD; p < 0.001; paired t test), respectively. The average decline during the silver and copper treatments were 1.2% and 2.14% per day (p = 0.002; multiple regression analysis), respectively.ConclusionsThe enhanced wound healing process observed with the copper dressings may be explained by the integral role of copper throughout all physiological skin repair processes. Silver in contrast has no physiological role in wound healing. The results of our study confirm case reports showing enhanced wound healing of hard-to-heal wounds with copper dressings, both of infected and noninfected wounds. Taken together, the results of the current study support the hypothesis that the application of copper dressings in situ for noninfected wounds results in the stimulation of the wound healing processes, as opposed to silver dressings.

Dataset Information

Continuous and controllable electro-fabrication of antimicrobial copper-alginate dressing for infected wounds treatment.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets