Glucose-mediated template-free synthesis of hollow CuO microspheres.

ABSTRACT: In this work, we demonstrated a facile template-free method for the preparation of hollow CuO microspheres via a conventional hydrothermal reaction. The hollow architecture formed directly during the hydrothermal treatment of copper nitrate and glucose, without the use of template, precipitant and calcination process. The effects of reaction time, reaction temperature and glucose concentration were investigated in detail. On the basis of experimental results, the formation of hollow CuO microspheres probably proceeded via self-assemble process and the subsequent Ostwald's ripening. This synthetic strategy strongly depended on the characteristics of copper nitrate, which made it could not extend to other copper salts and/or nitrates. Even though, glucose still showed efficient morphology controlling ability with respect to nanosized transitional metal oxides, which could be used for the controllable synthesis of nanomaterials.

SUBMITTER: Zhou H

PROVIDER: S-EPMC9079924 | biostudies-literature | 2018 Apr

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Publications

Glucose-mediated template-free synthesis of hollow CuO microspheres.

Zhou Hai H Kang Min M Qin Biao B Zhao Ning N Wu Dong D Lv Baoliang B Wang Qingjie Q

RSC advances 20180417 26

In this work, we demonstrated a facile template-free method for the preparation of hollow CuO microspheres via a conventional hydrothermal reaction. The hollow architecture formed directly during the hydrothermal treatment of copper nitrate and glucose, without the use of template, precipitant and calcination process. The effects of reaction time, reaction temperature and glucose concentration were investigated in detail. On the basis of experimental results, the formation of hollow CuO m ...[more]

PMID: 35540754

Similar Datasets

Synthesis and Characterization of Gd₂O₃ Hollow Microspheres Using a Template-Directed Method.

Project description:Uniform rare-earth gadolinium oxide (Gd₂O₃) hollow microspheres, as formed through a urea-assisted homogenous precipitation process using carbon spheres as a template and a subsequent heat treatment, were characterized by using X-ray diffraction, Fourier transformed infared spectroscopy, thermogravimetry, X-ray photoelectron spectroscopy, scanning electron microscopy, transmission electron microscopy and Brunauer-Emmett-Tellet surface area measurement. The results indicate that the final products can be indexed to a cubic Gd₂O₃ phase with high purity and have a uniform morphology at 500 nm in diameter and 20 nm in shell thickness. The as-synthesized Gd₂O₃ hollow microspheres exhibited a superior photooxidation activity to that of Gd₂O₃ powder and an effect similar to P25, significantly broadening the potential of Gd₂O₃ hollow microspheres for many practical applications.

| S-EPMC5503032 | biostudies-other

Template-Free Synthesis of Sb2S3 Hollow Microspheres as Anode Materials for Lithium-Ion and Sodium-Ion Batteries.

Project description:Hierarchical Sb2S3 hollow microspheres assembled by nanowires have been successfully synthesized by a simple and practical hydrothermal reaction. The possible formation process of this architecture was investigated by X-ray diffraction, focused-ion beam-scanning electron microscopy dual-beam system, and transmission electron microscopy. When used as the anode material for lithium-ion batteries, Sb2S3 hollow microspheres manifest excellent rate property and enhanced lithium-storage capability and can deliver a discharge capacity of 674 mAh g-1 at a current density of 200 mA g-1 after 50 cycles. Even at a high current density of 5000 mA g-1, a discharge capacity of 541 mAh g-1 is achieved. Sb2S3 hollow microspheres also display a prominent sodium-storage capacity and maintain a reversible discharge capacity of 384 mAh g-1 at a current density of 200 mA g-1 after 50 cycles. The remarkable lithium/sodium-storage property may be attributed to the synergetic effect of its nanometer size and three-dimensional hierarchical architecture, and the outstanding stability property is attributed to the sufficient interior void space, which can buffer the volume expansion.

| S-EPMC6199062 | biostudies-literature

Microfluidics-mediated self-template synthesis of anisotropic hollow ellipsoidal mesoporous silica nanomaterials.

Project description:Herein, a facile strategy was firstly developed to synthesize ellipsoidal mesoporous silica nanomaterials (MSNs) with well-ordered parallel channels along the short axis. A miniaturized microfluidic device with spiral-shaped channels was then chosen as a straightforward and general platform to produce the corresponding hollow counterparts of MSNs under mild conditions. Such reaction process carried out in a microfluidic system was further demonstrated to be more rapid and efficient than conventional batch method under equivalent experimental conditions. The evolution of hollow structure can be well-tuned by flow rates (i.e., etching time), providing new paradigm for rational design and engineering of anisotropic nanostructures.

| S-EPMC6405212 | biostudies-literature

Template-mediated Synthesis of Hollow Microporous Organic Nanorods with Tunable Aspect Ratio.

Project description:Hollow microporous organic nanorods (HMORs) with hypercrosslinked polymer (HCPs) shells were synthesized through emulsion polymerization followed by hypercrosslinking. The HMORs have tunable aspect ratios, high BET surface areas and monodispersed morphologies, showing good performance in gas adsorpion.

| S-EPMC4979212 | biostudies-literature

Alkyldimethylbetaine-Assisted Development of Hollow Urchinlike CuO Microspheres and Application for High-Performance Battery Anodes.

Project description:A new approach to develop novel hollow urchinlike copper oxide (CuO) microspheres by the hydrothermal method was reported, and zwitterionic alkyldimethylbetaine (BS) surfactants were employed as templates in the classic copper-ammonia complex systems. Effects of numerous environmental factors on the morphology of CuO particles were studied systematically, in which the concentration and structure of BS predominantly affected the developed CuO materials. It was noticed that hollow urchinlike CuO microspheres were generally formed in the presence of BS regardless of the reaction temperature and time and the source of copper ions. Generally speaking, high concentrations of BS and BS with longer chain length strongly favored the formation of hollow urchinlike CuO microspheres. The microstructures of synthesized CuO particles were studied in detail, and the corresponding formation mechanism of hollow urchinlike CuO microspheres was also proposed based on the selective adsorption of BS on the particular crystal facets of CuO crystals. Moreover, hollow urchinlike CuO microspheres showed excellent performance in the lithium-ion batteries as anode materials with a reversible capability of 511 mA h·g-1 at 0.1 C after 40 charge-discharge cycles, which was one of the best values of CuO materials reported in this field.

| S-EPMC6644594 | biostudies-literature

Topological self-template directed synthesis of multi-shelled intermetallic Ni3Ga hollow microspheres for the selective hydrogenation of alkyne.

Project description:Multi-shelled hollow structured materials featuring large void volumes and high specific surface areas are very promising for a variety of applications. However, controllable synthesis of multi-shelled hollow structured intermetallic compounds remains a formidable challenge due to the high annealing temperature commonly required for the formation of intermetallic phases. Here, a topological self-template strategy was developed to solve this problem. Using this strategy, we prepared well-defined multi-shelled intermetallic Ni3Ga hollow microspheres (Ni3Ga-MIHMs) as disclosed by the HAADF-STEM, HRTEM, and EDS characterizations, and the BET specific surface areas of them measured as much as 153.4 m2 g-1. XRD and EXAFS spectral characterizations revealed the atomically ordered intermetallic phase nature of the Ni3Ga-MIHMs. The selective hydrogenation of acetylene catalytic evaluation results further demonstrated excellent catalytic properties of the Ni3Ga-MIHMs, which results from the more energetically facile reaction pathway for acetylene hydrogenation and ethylene desorption over it as revealed by DFT calculations. Besides, this strategy is also extendable to synthesize other multi-shelled intermetallic Ni3Sn4 hollow microspheres, and is expected to open up new opportunities for rational design and preparation of novel structured and highly efficient intermetallics.

| S-EPMC6334720 | biostudies-literature

Template-free Synthesis of Stable Cobalt Manganese Spinel Hollow Nanostructured Catalysts for Highly Water-Resistant CO Oxidation.

Project description:Development of spinel oxides as low-cost and high-efficiency catalysts is highly desirable; however, rational synthesis of efficient and stable spinel systems with precisely controlled structure and components remains challenging. We demonstrate the design of complex nanostructured cobalt-based bimetallic spinel catalysts for low-temperature CO oxidation by a simple template-free method. The self-assembled multi-shelled mesoporous spinel nanostructures provide high surface area (203.5 m2/g) and favorable unique surface chemistry for producing abundant active sites and lead to the creation of robust microsphere configured by 16-nm spinel nanosheets, which achieve satisfactory water-resisting property and catalytic activity. Theoretical models show that O vacancies at exposed {110} facets in cubic spinel phase guarantee the strong adsorption of reactive oxygen species on the surface of catalysts and play a key role in the prevention of deactivation under moisture-rich conditions. The design concept with architecture and composition control can be extended to other mixed transition metal oxide compositions.

| S-EPMC6820238 | biostudies-literature

Template synthesis of the Cu2O nanoparticle-doped hollow carbon nanofibres and their application as non-enzymatic glucose biosensors.

Project description:The cuprous oxide nanoparticle (Cu2O NP)-doped hollow carbon nanofibres (Cu2O/HCFs) were directly synthesized by the anodic aluminium oxide (AAO) template. The doped Cu2O NPs were formed by in situ deposition by direct reduction reaction of precursor carbonization in thermal decomposition and could act as functionalized nanoparticles. The synthesized Cu2O/HCFs were characterized in detail by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy and inductively coupled plasma mass spectrometry (ICP-MS). The results reveal that Cu2O/HCFs have a tubular structure with an average diameter of approximately 60 nm. The shape of the Cu2O/HCFs is straight and Cu2O NPs are uniformly distributed and highly dispersed in HCFs. Cu2O/HCFs have good dispersibility. The electrochemical activity of Cu2O/HCFs was investigated by cyclic voltammetry (CV), the glucose sensors display high electrochemical activity towards the oxidation of glucose. Cu2O/HCFs can effectively accelerate the transmission of electrons on the electrode surface. Cu2O/HCFs are applied in the detection of glucose with a detection limit of 0.48 µM, a linear detection range from 7.99 to 33.33 µM and with a high sensitivity of 1218.3 µA cm-2 mM-1. Moreover, the experimental results demonstrate that Cu2O/HCFs have good stability, reproducibility and selectivity. Our results suggest that Cu2O/HCFs could be a promising candidate for the construction of non-enzymatic sensor.

| S-EPMC6304140 | biostudies-literature

Template-free synthesis and lithium-ion storage performance of multiple ZnO nanoparticles encapsulated in hollow amorphous carbon shells.

Project description:Due to the limited utilization of electrode materials, the rational design and facile synthesis of composite structures are still challenging issues for lithium-ion batteries (LIBs). Herein, a simple approach has been developed to prepare multiple core-shell structures of ZnO nanoparticles (NPs) encapsulated in hollow amorphous carbon (AC) shells. The as-synthesized ZnO@AC composites showed a uniform dispersion of ZnO NPs, compliant buffer AC shells, and nanoscale void spaces between the ZnO NP cores and AC shells. As a result of their structural merits, the ZnO@AC composites were evaluated as anode materials for LIBs and delivered enhanced coulombic efficiency, high reversible capacity, high rate capability, and improved cycling stability.

| S-EPMC9054705 | biostudies-literature

Synthesis of Mesoporous CuO Hollow Sphere Nanozyme for Paper-Based Hydrogen Peroxide Sensor.

Project description:Point-of-care monitoring of hydrogen peroxide is important due to its wide usage in biomedicine, the household and industry. Herein, a paper sensor is developed for sensitive, visual and selective detection of H2O2 using a mesoporous metal oxide hollow sphere as a nanozyme. The mesoporous CuO hollow sphere is synthesized by direct decomposition of copper-polyphenol colloidal spheres. The obtained mesoporous CuO hollow sphere shows a large specific surface area (58.77 m2/g), pore volume (0.56 cm3/g), accessible mesopores (5.8 nm), a hollow structure and a uniform diameter (~100 nm). Furthermore, they are proven to show excellent peroxidase-like activities with Km and Vmax values of 120 mM and 1.396 × 10-5 M·s-1, respectively. Such mesoporous CuO hollow spheres are then loaded on the low-cost and disposable filter paper test strip. The obtained paper sensor can be effectively used for detection of H2O2 in the range of 2.4-150 μM. This work provides a new kind of paper sensor fabricated from a mesoporous metal oxide hollow sphere nanozyme. These sensors could be potentially used in bioanalysis, food security and environmental protection.

| S-EPMC8392683 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data