Facile metal-free reduction-based synthesis of pristine and cation-doped conductive mayenite.

ABSTRACT: In the present study we synthesized conductive nanoscale [Ca₂₄Al₂₈O₆₄]⁴⁺(4e^-) (hereafter denoted as C₁₂A₇:e^-) material, and reduced graphene oxide (rGO) was produced, which was unexpected; graphene oxide was removed after melting the sample. The conductivity of C₁₂A₇:e^- composites synthesized at 1550 °C was 1.25 S cm^-1, and the electron concentration was 5.5 × 10¹⁹ cm^-3. The estimated BET specific surface area of the highly conductive sample was 20 m² g^-1. Pristine C₁₂A₇:e^- electride was obtained by melting the composite powder, but the nano size of C₁₂A₇:e^- particles could not be preserved; the value of conductivity was ∼28 S cm^-1, electron concentration was ∼1.9 × 10²¹ cm^-3, and mass density was 93%. For C₁₂A_7-x V _x :e^-, where x = 0.25 to 1, the conductivity improved to a maximum value of 40 S cm^-1, and the electron density improved to ∼2.2 × 10²¹ cm^-3; this enhancement in conductivity was also proposed by a theoretical study but lacked any associated experimental support.

SUBMITTER: Khan K 

PROVIDER: S-EPMC9082041 | biostudies-literature | 2018 Jul

REPOSITORIES: biostudies-literature