Nanofused Hierarchically Porous MIL-101(Cr) for Enhanced Methyl Orange Removal and Improved Catalytic Activity.

ABSTRACT: Hierarchically porous MIL-101(Cr) (H-MIL-101(Cr)) with meso/macro-pores was directly prepared via nanofusion progress by using butyric acid as a modulating agent. In the methyl orange (MO) adsorption experiments, H-MIL-101(Cr) showed a high adsorption capability of 369.8 mg g^-1, which was 1.52-fold greater than that of pristine MIL-101(Cr) (P-MIL-101(Cr)). While in the oxidation reaction of indene and 1-dodecene tests, H-MIL-101(Cr) presented much higher catalytic efficiency, with turnover frequency (TOF) values of 0.7242 mmol g^-1 min^-1 and 0.1492 mmol g^-1 min^-1, respectively, which were 28% and 34% greater than that in the case of P-MIL-101(Cr). Thus, compared with P-MIL-101(Cr), H-MIL-101(Cr) exhibited better removal efficiency and higher levels of activity in the oxidation reactions of indene and 1-dodecene. The unique structure of H-MIL-101(Cr) also contributed to its superior performance in these processes.

SUBMITTER: Zou M

PROVIDER: S-EPMC9146841 | biostudies-literature | 2022 May

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Nanofused Hierarchically Porous MIL-101(Cr) for Enhanced Methyl Orange Removal and Improved Catalytic Activity.

Zou Minmin M Dong Ming M Luo Mingliang M Zhu Hexin H Zhao Tian T

Materials (Basel, Switzerland) 20220519 10

Hierarchically porous MIL-101(Cr) (H-MIL-101(Cr)) with meso/macro-pores was directly prepared via nanofusion progress by using butyric acid as a modulating agent. In the methyl orange (MO) adsorption experiments, H-MIL-101(Cr) showed a high adsorption capability of 369.8 mg g<sup>-1</sup>, which was 1.52-fold greater than that of pristine MIL-101(Cr) (P-MIL-101(Cr)). While in the oxidation reaction of indene and 1-dodecene tests, H-MIL-101(Cr) presented much higher catalytic efficiency, with tur ...[more]

PMID: 35629671

Similar Datasets

Project description:In this study, hybrids of nanoporous MIL-101(Cr) and MIL-53(Al) were synthesized using a hydrothermal method for various time periods, ranging from 8 to 40 h. The prepared materials were characterized by powder X-ray diffraction (PXRD) and elemental analysis, and their specific surface areas were measured by N2 sorption at 77 K using the Brunauer-Emmett-Teller (BET) method. To investigate the practical application of these materials, the pure carbon dioxide and methane adsorption capacities of the samples were determined using the volumetric method. The Langmuir model was used to fit the CO2 and CH4 isotherms. Extended Langmuir (EL) equations and the ideal adsorbed solution theory (IAST) models were used to obtain the CO2/CH4 selectivity. The sample with the highest BET specific surface area was selected as a candidate for further investigations. The thermal stability of the selected sample was investigated by thermogravimetric analysis (TGA). Scanning electron microscopy (SEM) was used to characterize the sample morphology. XRD results showed that the sample synthesized over the shortest time corresponded to MIL-101(Cr), while the sample synthesized over the longest time was in agreement with MIL-53(Al). Samples synthesized for time periods between these two limits were assumed to be composites of both MIL-53(Al) and MIL-101(Cr). TGA results indicated that the hybrid materials were thermally stable at temperatures about 100 °C higher than for pure MIL-101(Cr). The BET specific surface area (1746 m2 g-1) and CO2 adsorption capacity (16 mmol g-1) of the selected hybrid sample were about 50% and 35% higher, respectively, compared with those of pure MIL-53(Al), but 30% and 20% lower, respectively, compared with those of pure MIL-101(Cr). Binary adsorption modeling showed the high selectivity of the MIL-101(Cr) and MIL-53(Al) hybrid material for CO2 with a minimum separation factor of about 60 at 298 K. This value was much higher than those reported previously and those observed in this work for the original MIL-101(Cr) or MIL-53(Al). These results demonstrated that the hybrid of MIL-101(Cr) and MIL-53(Al) was a promising material for selective CO2 capture from natural and biogas.

Dataset Information

Nanofused Hierarchically Porous MIL-101(Cr) for Enhanced Methyl Orange Removal and Improved Catalytic Activity.

Publications

Nanofused Hierarchically Porous MIL-101(Cr) for Enhanced Methyl Orange Removal and Improved Catalytic Activity.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets