Strain, Doping, and Electronic Transport of Large Area Monolayer MoS₂ Exfoliated on Gold and Transferred to an Insulating Substrate.

ABSTRACT: Gold-assisted mechanical exfoliation currently represents a promising method to separate ultralarge (centimeter scale) transition metal dichalcogenide (TMD) monolayers (1L) with excellent electronic and optical properties from the parent van der Waals (vdW) crystals. The strong interaction between Au and chalcogen atoms is key to achieving this nearly perfect 1L exfoliation yield. On the other hand, it may significantly affect the doping and strain of 1L TMDs in contact with Au. In this paper, we systematically investigated the morphology, strain, doping, and electrical properties of large area 1L MoS₂ exfoliated on ultraflat Au films (0.16-0.21 nm roughness) and finally transferred to an insulating Al₂O₃ substrate. Raman mapping and correlative analysis of the E' and A₁' peak positions revealed a moderate tensile strain (ε ≈ 0.2%) and p-type doping (n ≈ -0.25 × 10¹³ cm^-2) of 1L MoS₂ in contact with Au. Nanoscale resolution current mapping and current-voltage (I-V) measurements by conductive atomic force microscopy (C-AFM) showed direct tunneling across the 1L MoS₂ on Au, with a broad distribution of tunneling barrier values (Φ_B from 0.7 to 1.7 eV) consistent with p-type doping of MoS₂. After the final transfer of 1L MoS₂ on Al₂O₃/Si, the strain was converted to compressive strain (ε ≈ -0.25%). Furthermore, an n-type doping (n ≈ 0.5 × 10¹³ cm^-2) was deduced by Raman mapping and confirmed by electrical measurements of an Al₂O₃/Si back-gated 1L MoS₂ transistor. These results provide a deeper understanding of the Au-assisted exfoliation mechanism and can contribute to its widespread application for the realization of novel devices and artificial vdW heterostructures.

SUBMITTER: Panasci SE 

PROVIDER: S-EPMC9280715 | biostudies-literature |

REPOSITORIES: biostudies-literature