Colloidal Bismuth Chalcohalide Nanocrystals.

ABSTRACT: Here we present a colloidal approach to synthesize bismuth chalcohalide nanocrystals (BiEX NCs, in which E=S, Se and X=Cl, Br, I). Our method yields orthorhombic elongated BiEX NCs, with BiSCl crystallizing in a previously unknown polymorph. The BiEX NCs display a composition-dependent band gap spanning the visible spectral range and absorption coefficients exceeding 10⁵ cm^-1 . The BiEX NCs show chemical stability at standard laboratory conditions and form colloidal inks in different solvents. These features enable the solution processing of the NCs into robust solid films yielding stable photoelectrochemical current densities under solar-simulated irradiation. Overall, our versatile synthetic protocol may prove valuable in accessing colloidal metal chalcohalide nanomaterials at large and contributes to establish metal chalcohalides as a promising complement to metal chalcogenides and halides for applied nanotechnology.

SUBMITTER: Quarta D

PROVIDER: S-EPMC9311208 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Laser Fragmentation Synthesis of Colloidal Bismuth Ferrite Particles.

Project description:Laser fragmentation of colloidal submicron-sized bismuth ferrite particles was performed by irradiating a liquid jet to synthesize bismuth ferrite nanoparticles. This treatment achieved a size reduction from 450 nm to below 10 nm. A circular and an elliptical fluid jet were compared to control the energy distribution within the fluid jet and thereby the product size distribution and educt decomposition. The resulting colloids were analysed via UV-VIS, XRD and TEM. All methods were used to gain information on size distribution, material morphology and composition. It was found that using an elliptical liquid jet during the laser fragmentation leads to a slightly smaller and narrower size distribution of the resulting product compared to the circular jet.

| S-EPMC7075302 | biostudies-literature

Electron transfer between colloidal ZnO nanocrystals.

Project description:Colloidal ZnO nanocrystals capped with dodecylamine and dissolved in toluene can be charged photochemically to give stable solutions in which electrons are present in the conduction bands of the nanocrystals. These conduction-band electrons are readily monitored by EPR spectroscopy, with g* values that correlate with the nanocrystal sizes. Mixing a solution of charged small nanocrystals (e(-)(CB):ZnO-S) with a solution of uncharged large nanocrystals (ZnO-L) caused changes in the EPR spectrum indicative of quantitative electron transfer from small to large nanocrystals. EPR spectra of the reverse reaction, e(-)(CB):ZnO-L + ZnO-S, showed that electrons do not transfer from large to small nanocrystals. Stopped-flow kinetics studies monitoring the change in the UV band-edge absorption showed that reactions of 50 ?M nanocrystals were complete within the 5 ms mixing time of the instrument. Similar results were obtained for the reaction of charged nanocrystals with methyl viologen (MV(2+)). These and related results indicate that the electron-transfer reactions of these colloidal nanocrystals are quantitative and very rapid, despite the presence of ~1.5 nm long dodecylamine capping ligands. These soluble ZnO nanocrystals are thus well-defined redox reagents suitable for studies of electron transfer involving semiconductor nanostructures.

| S-EPMC3073092 | biostudies-literature

Colloidal CdSe nanocrystals are inherently defective.

Project description:Colloidal CdSe nanocrystals (NCs) have shown promise in applications ranging from LED displays to medical imaging. Their unique photophysics depend sensitively on the presence or absence of surface defects. Using simulations, we show that CdSe NCs are inherently defective; even for stoichiometric NCs with perfect ligand passivation and no vacancies or defects, we still observe that the low energy spectrum is dominated by dark, surface-associated excitations, which are more numerous in larger NCs. Surface structure analysis shows that the majority of these states involve holes that are localized on two-coordinate Se atoms. As chalcogenide atoms are not passivated by any Lewis base ligand, varying the ligand should not dramatically change the number of dark states, which we confirm by simulating three passivation schemes. Our results have significant implications for understanding CdSe NC photophysics, and suggest that photochemistry and short-range photoinduced charge transfer should be much more facile than previously anticipated.

| S-EPMC7873310 | biostudies-literature

Fluorine-Doped Tin Oxide Colloidal Nanocrystals.

Project description:Fluorine-doped tin oxide (FTO) is one of the most studied and established materials for transparent electrode applications. However, the syntheses for FTO nanocrystals are currently very limited, especially for stable and well-dispersed colloids. Here, we present the synthesis and detailed characterization of FTO nanocrystals using a colloidal heat-up reaction. High-quality SnO2 quantum dots are synthesized with a tuneable fluorine amount up to ~10% atomic, and their structural, morphological and optical properties are fully characterized. These colloids show composition-dependent optical properties, including the rise of a dopant-induced surface plasmon resonance in the near infrared.

| S-EPMC7712819 | biostudies-literature

Surface engineering of bismuth nanocrystals to counter dissolution.

Project description:Rapid dissolution of Bi Nanocrystals (NCs) in lysosomal conditions results in poor biocompatibility. We report that an in situ surface coating of Bi nanocrystals with Ganex® V216, a cosmetic dispersant, limits its dissolution under physiological conditions. These Bi Ganex (BiG) NCs are readily encapsulated in FDA approved polymer poly(dl-lactic-co-glycolic acid) (PLGA) by an oil-in-water emulsion technique and also undergo facile SiO2 coating. BiG NCs in BiG@PLGA and BiG@SiO2 nanoparticles dissolve slowly under physiological conditions and exhibit excellent biocompatibility, as opposed to uncoated Bi NCs. Finally, these Bi nanoconstructs are shown to be strong CT CAs, even at relatively low Bi concentrations.

| S-EPMC5817880 | biostudies-literature

Colloidal nanocrystals fluoresced by surface coordination complexes.

Project description:Colloidal Nanocrystals (NCs) with fluorescence originating from surface complexes are successfully prepared. The components of these NCs range from insulator, semiconductor to metal, with either pure phase, doped or core/shell structures. The photoluminescence of these NCs can be reversibly tuned across the visible to infrared spectrum, and even allow multi-color emission. A light emitting device is fabricated and a new in vivo cell imaging method is performed to demonstrate the power of this technology for emerging applications.

| S-EPMC4073169 | biostudies-literature

Tunability Limit of Photoluminescence in Colloidal Silicon Nanocrystals.

Project description:Luminescent silicon nanocrystals (Si NCs) have attracted tremendous research interest. Their size dependent photoluminescence (PL) shows great promise in various optoelectronic and biomedical applications and devices. However, it remains unclear why the exciton emission is limited to energy below 2.1?eV, no matter how small the nanocrystal is. Here we interpret a nanosecond transient yellow emission band at 590?nm (2.1?eV) as a critical limit of the wavelength tunability in colloidal silicon nanocrystals. In the "large size" regime (d?>?~3?nm), quantum confinement dominantly determines the PL wavelength and thus the PL peak blue shifts upon decreasing the Si NC size. In the "small size" regime (d?<?~2?nm) the effect of the yellow band overwhelms the effect of quantum confinement with distinctly increased nonradiative trapping. As a consequence, the photoluminescence peak does not exhibit any additional blue shift and the quantum yield drops abruptly with further decreasing the size of the Si NCs. This finding confirms that the PL originating from the quantum confined core states can only exist in the red/near infrared with energy below 2.1?eV; while the blue/green PL originates from surface related states and exhibits nanosecond transition.

| S-EPMC4510486 | biostudies-literature

Colloidal Synthesis of Bulk-Bandgap Lead Selenide Nanocrystals.

Project description:Lead selenide quantum dots (QDs) are low-bandgap IV-VI semiconducting nanomaterials that have been studied for a variety of applications. Their preparation using colloidal methods can create small spherical to larger cubic nanocrystals, with an upper limit of ~17 nm reported to date. Here we describe methods for preparing cubic PbSe nanocrystals over a 20-40 nm size range using a twostep procedure. Specifically, ~10 nm PbSe QDs are generated using the rapid injection method, the products from which are overcoated with additional lead and selenium precursors. The use of two lead reagents were studied; lead oleate resulted in a maximum of 20 nm cubes, while more reactive lead hexyldecanoate resulted in much larger nanomaterials with bulk bandgaps. However, PbSe samples prepared with lead hexyldecanoate also contained agglomerates. Special care must be taken when characterizing larger strained nanomaterials with X-ray powder diffraction, for which the Scherrer equation is inadequate. A more rigorous approach using the Williamson-Hall method provides characterizations that are consistent with electron microscopy analysis.

| S-EPMC6261983 | biostudies-literature

Colloidal Synthesis of CsX Nanocrystals (X = Cl, Br, I).

Project description:A facile colloidal synthesis of highly ionic cesium halide nanocrystals is reported. Colloidal nanocrystals of CsI, CsCl and CsBr with unprecedentedly small dimensions are obtained using oleylammonium halides and cesium oleate as precursors. The ease and adaptability of our method enables its universalization for the formation of other highly ionic nanocrystals.

| S-EPMC6070971 | biostudies-literature

Galvanic Exchange in Colloidal Metal/Metal-Oxide Core/Shell Nanocrystals.

Project description:While galvanic exchange is commonly applied to metallic nanoparticles, recently its applicability was expanded to metal-oxides. Here the galvanic exchange is studied in metal/metal-oxide core/shell nanocrystals. In particular Sn/SnO2 is treated by Ag(+), Pt(2+), Pt(4+), and Pd(2+). The conversion dynamics is monitored by in situ synchrotron X-ray diffraction. The Ag(+) treatment converts the Sn cores to the intermetallic Ag x Sn (x ? 4) phase, by changing the core's crystal structure. For the analogous treatment by Pt(2+), Pt(4+), and Pd(2+), such a galvanic exchange is not observed. This different behavior is caused by the semipermeability of the naturally formed SnO2 shell, which allows diffusion of Ag(+) but protects the nanocrystal cores from oxidation by Pt and Pd ions.

| S-EPMC5018861 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data