Recovery of Green Polyols from Rigid Polyurethane Waste by Catalytic Depolymerization.

ABSTRACT: Polyurethane (PU) is one of the most versatile polymers available and can be found in an infinite number of formats ranging from rigid or flexible foams to elastomers. Currently, most Rigid PU Foam (RPUF) waste is landfilled, even though a small amount is mechanically recycled, in which the material is conditioned in size to a very fine powder, which is introduced as a filler. In this work, chemical recycling of two types of rigid PU foams is studied, the major difference being the aliphatic or aromatic nature of the isocyanate used in the synthesis. A solvolysis process is developed, a chemical depolymerization that breaks the chains by means of a chemical agent, a solvent, in the presence of a catalyst and under controlled process conditions. The glycolysis products are purified by vacuum distillation, centrifugation, and acid water treatment, depending on the most suitable process for each waste type. Optimal process conditions are established to obtain high-purity green polyols by performing a set of catalytic glycolysis reactions at laboratory scale with the previously conditioned RPUF waste samples. The physicochemical properties of the polyols, such as hydroxyl value, acid value, average molecular weight (M_n), and viscosity, are analyzed. The chemical structure and thermal stability of the polyols are studied by means of FTIR and TGA, respectively. Partial substitution of the commercial polyol (up to 15 wt.%) by the recycled polyols for RPUF synthesis is studied and characterized.

SUBMITTER: Miguel-Fernandez R

PROVIDER: S-EPMC9319047 | biostudies-literature |

REPOSITORIES: biostudies-literature

ACCESS DATA

Json Xml

Similar Datasets

Rigid Polyurethane Foams with Various Isocyanate Indices Based on Polyols from Rapeseed Oil and Waste PET.

Project description:Developing polyols derived from natural sources and recycling materials attracts great interest for use in replacing petroleum-based polyols in polyurethane production. In this study, rigid polyurethane (PUR) foams with various isocyanate indices were obtained from polyols based on rapeseed oil and polyethylene terephthalate (RO/PET). The various properties of the prepared PUR foams were investigated, and the effect of the isocyanate index was evaluated. The closed-cell content and water absorption were not impacted by the change of the isocyanate index. The most significant effect of increasing the isocyanate index was on the dimensional stability of the resulting foams. This is due to the increased crosslink density, as evidenced by the increased formation of isocyanurate and increase of the glass transition temperature. Additionally, the influence on compression strength, modulus, and long-term thermal conductivity were evaluated and compared with reference PUR foams from commercially available polyols. Rigid PUR foams from RO/PET polyol were found to be competitive with reference materials and could be used as thermal insulation material.

| S-EPMC7240454 | biostudies-literature

Effect of New Eco-Polyols Based on PLA Waste on the Basic Properties of Rigid Polyurethane and Polyurethane/Polyisocyanurate Foams.

Project description:The aim of the presented research was to obtain two new eco-polyols based on waste polylactide (PLA) and to check the effect on the properties of rigid polyurethane (RPU) foams and, based on these, rigid polyurethane/polyisocyanurate (RPU/PIR) foams. The synthesis of eco-polyols was based on the transesterification reaction of melted PLA with diethylene glycol in the presence of an organometallic catalyst. Properties of the obtained eco-polyols were examined for their potential as raw materials for synthesis of rigid polyurethane and polyisocyanurate foams, i.e., hydroxyl value, acid value, density, viscosity, pH, water content. Spectroscopic studies (FTIR, 1H NMR and 13C NMR) were also carried out. Results of these tests confirmed the assumed chemical structure of the new polyols. RPU and RPU/PIR foam formulations were developed based on the obtained analytical results. Partial replacement of petrochemical polyol by eco-polyols in RPU and RPU/PIR foams decreased the value of apparent density, compressive strength, brittleness and water absorption. Moreover, all foams modified by eco-polyols showed higher resistance to aging. All RPU/PIR foams and most PRU foams modified by eco-polyols from waste PLA had better functional properties than the reference foams based on petrochemical polyol.

| S-EPMC8396538 | biostudies-literature

High Functionality Bio-Polyols from Tall Oil and Rigid Polyurethane Foams Formulated Solely Using Bio-Polyols.

Project description:High-quality rigid polyurethane (PU) foam thermal insulation material has been developed solely using bio-polyols synthesized from second-generation bio-based feedstock. High functionality bio-polyols were synthesized from cellulose production side stream-tall oil fatty acids by oxirane ring-opening as well as esterification reactions with different polyfunctional alcohols, such as diethylene glycol, trimethylolpropane, triethanolamine, and diethanolamine. Four different high functionality bio-polyols were combined with bio-polyol obtained from tall oil esterification with triethanolamine to develop rigid PU foam formulations applicable as thermal insulation material. The developed formulations were optimized using response surface modeling to find optimal bio-polyol and physical blowing agent: c-pentane content. The optimized bio-based rigid PU foam formulations delivered comparable thermal insulation properties to the petro-chemical alternative.

| S-EPMC7215456 | biostudies-literature

Polyols from Microwave Liquefied Bagasse and Its Application to Rigid Polyurethane Foam.

Project description:Bagasse flour (BF) was liquefied using bi-component polyhydric alcohol (PA) as a solvent and phosphoric acid as a catalyst in a microwave reactor. The effect of BF to solvent ratio and reaction temperatures on the liquefaction extent and characteristics of liquefied products were evaluated. The results revealed that almost 75% of the raw bagasse was converted into liquid products within 9 min at 150 °C with a BF to solvent ratio of 1/4. The hydroxyl and acid values of the liquefied bagasse (LB) varied with the liquefied conditions. High reaction temperature combining with low BF to solvent ratio resulted in a low hydroxyl number for the LB. The molecular weight and polydispersity of the LB from reactions of 150 °C was lower compared to that from 125 °C. Rigid polyurethane (PU) foams were prepared from LB and methylene diphenyl diisocyanate (MDI), and the structural, mechanical and thermal properties of the PU foam were evaluated. The PU foams prepared using the LB from high reaction temperature showed better physical and mechanical performance in comparison to those from low reaction temperature. The amount of PA in the LB has the ability of increasing thermal stability of LB-PU foams. The results in this study may provide fundamental information on integrated utilizations of sugarcane bagasse via microwave liquefaction process.

| S-EPMC5458812 | biostudies-other

Producing Lignin-Based Polyols through Microwave-Assisted Liquefaction for Rigid Polyurethane Foam Production.

Project description:Lignin-based polyols were synthesized through microwave-assisted liquefaction under different microwave heating times (5-30 min). The liquefaction reactions were carried out using polyethylene glycol (PEG-400)/glycerol as liquefying solvents and 97 wt% sulfur acid as a catalyst at 140 °C. The polyols obtained were analyzed for their yield, composition and structural characteristics using gel permeation chromatography (GPC), Fourier transform infrared (FT-IR) and nuclear magnetic resonance (NMR) spectra. FT-IR and NMR spectra showed that the liquefying solvents reacted with the phenol hydroxyl groups of the lignin in the liquefied product. With increasing microwave heating time, the viscosity of polyols was slightly increased and their corresponding molecular weight (MW) was gradually reduced. The optimal condition at the microwave heating time (5 min) ensured a high liquefaction yield (97.47%) and polyol with a suitable hydroxyl number (8.628 mmol/g). Polyurethane (PU) foams were prepared by polyols and methylene diphenylene diisocyanate (MDI) using the one-shot method. With the isocyanate/hydroxyl group ([NCO]/[OH]) ratio increasing from 0.6 to 1.0, their mechanical properties were gradually increased. This study provided some insight into the microwave-assisted liquefied lignin polyols for the production of rigid PU foam.

| S-EPMC5455266 | biostudies-other

Catalytic Depolymerization of Waste Polyolefins by Induction Heating: Selective Alkane/Alkene Production.

Project description:Low- and high-density polyethylene (LDPE/HDPE) have been selectively depolymerized, without added H2, to C2-C20 + alkanes/alkenes via energy-efficient radio frequency induction heating, coupled with dual-functional heterogeneous Fe3O4 and Ni- or Pt-based catalysts. Fe3O4 was used to locally generate heat when exposed to magnetic fields. Initial results indicate that zeolite-based Ni catalysts are more selective to light olefins, while Ni supported on ceria catalysts are more selective to C7-C14 alkanes/alkenes. LDPE conversions up to 94% were obtained with minimal aromatic, coke, or methane formation which are typically observed with thermal heating. Two depolymerization mechanisms, a reverse Cossee-Arlman mechanism or a random cleavage process, were proposed to account for the different selectivities. The depolymerization process was also tested on commercial LDPE (grocery bags), polystyrene, and virgin HDPE using the Ni on Fe3O4 catalyst, with the LDPE resulting in similar product conversion (∼48%) and selectivity as for virgin LDPE.

| S-EPMC8554762 | biostudies-literature

Recovery of Waste Polyurethane from E-Waste-Part I: Investigation of the Oil Sorption Potential.

Project description:The shredding of end-of-life refrigerators produces every year in Italy 15,000 tons of waste polyurethane foam (PUF), usually destined for energy recovery. This work presents the results of the investigation of the oil sorption potential of waste PUF according to ASTM F726-17 standard. Three oils (diesel fuel and two commercial motor oils) having different densities (respectively, 0.83, 0.87, and 0.88 kg/dm3) and viscosities (respectively, 3, 95, and 140 mm2/s at 40 °C) were considered. The waste PUF was sampled in an Italian e-waste treatment plant, and its characterization showed 16.5 wt% particles below 0.71 mm and 13 wt% impurities (paper, plastic, aluminum foil), mostly having dimensions (d) above 5 mm. Sieving at 0.071 mm was applied to the waste PUF to obtain a "coarse" (d > 0.71 mm) and a "fine" fraction (d < 0.71 mm). Second sieving at 5 mm allowed an "intermediate" fraction to be obtained, with dimensions between 0.71 and 5 mm. The oil sorption tests involved the three fractions of waste PUF, and their performances were compared with two commercial oil sorbents (sepiolite and OKO-PUR). The results of the tests showed that the "fine" PUF was able to retain 7.1-10.3 g oil/g, the "intermediate" PUF, 4.2-7.4 g oil/g, and the "coarse" PUF, 4.5-7.0 g oil/g, while sepiolite and OKO-PUR performed worse (respectively, 1.3-1.6 and 3.3-5.3 g oil/g). In conclusion, compared with the actual management of waste PUF (100 wt% sent to energy recovery), the amount destined directly to energy recovery could be limited to 13 wt% (i.e., the impurities). The remaining 87 wt% could be diverted to reuse for oil sorption, and afterward directed to energy recovery, considered as a secondary option.

| S-EPMC8584342 | biostudies-literature

Fire Suppression and Thermal Behavior of Biobased Rigid Polyurethane Foam Filled with Biomass Incineration Waste Ash.

Project description:Currently, there is great demand to implement circular economy principles and motivate producers of building materials to integrate into a closed loop supply chain system and improve sustainability of their end-product. Therefore, it is of great interest to replace conventional raw materials with inorganic or organic waste-based and filler-type additives to promote sustainability and the close loop chain. This article investigates the possibility of bottom waste incineration ash (WA) particles to be used as a flame retardant replacement to increase fire safety and thermal stability under higher temperatures. From 10 wt.% to 50 wt.% WA particles do not significantly deteriorate performance characteristics, such as compressive strength, thermal conductivity, and water absorption after 28 days of immersion, and at 32 °C WA particles improve the thermal stability of resultant PU foams. Furthermore, 50 wt.% WA particles reduce average heat release by 69% and CO2 and CO yields during fire by 76% and 77%, respectively. Unfortunately, WA particles do not act as a smoke suppressant and do not reduce smoke release rate.

| S-EPMC7182938 | biostudies-literature

Recovery of Flexible Polyurethane Foam Waste for Efficient Reuse in Industrial Formulations.

Project description:Ester polyurethane (PU) foam waste was reacted at atmospheric pressure in an autoclave and using microwaves with diethylene glycol (DEG) at different PU/DEG ratios in the presence of diethanolamine as a catalyst to find the glycolysis conditions that allow for the improved recovery of the PU foam waste and enable the recycling of the whole glycolysis product in foam formulations suitable for industrial application. The recycled polyol was characterized by dynamic viscosity, hydroxyl number, water content, and density, while thermal stability was assessed using thermogravimetric analysis. In the PU foam formulation, 1% and 5% of the glycolyzed material was reused. The relationship between the reuse level of the recycled polyol and the physical properties of the foam was thoroughly investigated. It was observed that both hardness and air flow decreased with increasing recycled polyol content, particularly for the polyester type foam, while tensile strength and compression strength increased. Depending on the amount of recycled polyol and catalyst used, polyether-based foams could be obtained with a low air permeability, needed in special applications as sealed foams, or with higher air permeability desirable for comfort PU foams. The results open the way for further optimization studies of industrial polyurethane foam formulations using a glycolysis process without any separation stage.

| S-EPMC7407941 | biostudies-literature

Use of a Mixture of Polyols Based on Metasilicic Acid and Recycled PLA for Synthesis of Rigid Polyurethane Foams Susceptible to Biodegradation.

Project description:Two polyol raw materials were obtained in the conducted research, one based on metasilicic acid (MSA), the other based on poly(lactic acid) (PLA) waste. The obtained polyols were characterized in terms of their applicability for the production of rigid polyurethane foams (RPUFs). Their basic analytical properties (hydroxyl number, acid number, elemental analysis) and physicochemical properties (density, viscosity) were determined. The assumed chemical structure of the obtained new compounds was confirmed by performing FTIR and 1H NMR spectroscopic tests. Formulations for the synthesis of RPUFs were developed on the basis of the obtained research results. A mixture of polyols based on MSA and PLA in a weight ratio of 1:1 was used as the polyol component in the polyurethane formulation. The reference foam in these tests was a foam that was synthesized only on the basis of MSA-polyol. The obtained RPUFs were tested for basic functional properties (apparent density, compressive strength, water absorption, thermal conductivity coefficient etc.). Susceptibility to biodegradation in soil environment was also tested. It was found that the use of mixture of polyols based on MSA and PLA positively affected the properties of the obtained foam. The polyurethane foam based on this polyol mixture showed good thermal resistance and significantly reduced flammability in comparison with the foam based MSA-polyol. Moreover, it showed higher compressive strength, lower thermal conductivity and biodegradability in soil. The results of the conducted tests confirmed that the new foam was characterized by very good performance properties. In addition, this research provides information on new waste management opportunities and fits into the doctrine of sustainable resource management offered by the circular economy.

| S-EPMC7795053 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data