Study on the grain refinement mechanism of Mg-Al alloy based on carbon addition.

ABSTRACT: In this study, a comprehensive treatment process based on the rotary injection of Ar+CO2 Mg-Al alloy melt is proposed. The effect of carbon on the grain refinement of Mg-Al alloy is studied according to the proposed integrated treatment process. The regularity of carbon refinement in the Mg-Al alloy is examined by microstructural observation and theoretical calculation. The results show that carbon has no effect on the grain refinement of Mg-Al alloy when the Al content is less than 1wt.%. However, when the Al content reaches 2 wt.%, the refining effect is obvious, and the grain refinement efficiency is 62%. The refining effect increases with the increase in the Al content, and the refinement efficiency becomes 79% when the Al content reaches 9 wt.%. The size of Al-C-O in the matrix is approximately 5μm, which confirms the existence of Al4C3 phase exists as a heterogeneous nucleating agent. The theoretical calculations suggest that the Al4C3 heterogeneous nucleating agent cannot be formed when the Al content in the Mg alloy is less than 1.34%, so there is no thinning effect under such Al content. The crystallographic calculations reveal that the mismatch between the Al4C3 phase and Mg alloy matrix is only 4.05%, and Al4C3 can exist as a heterogeneous nucleating agent for α-Mg phase. Combining the measured solidification curves with the classical nucleation theory, the wetting angle of Mg-Al alloy on Al4C3 is calculated to be 24.3°.

SUBMITTER: Sun L

PROVIDER: S-EPMC9352047 | biostudies-literature | 2022

REPOSITORIES: biostudies-literature

ACCESS DATA

Publications

Study on the grain refinement mechanism of Mg-Al alloy based on carbon addition.

Sun Lifeng L Gao Zhongyu Z Hu Zhongchao Z Chen Huyan H Cai Jianwen J Cai Xiaoou X

PloS one 20220804 8

In this study, a comprehensive treatment process based on the rotary injection of Ar+CO2 Mg-Al alloy melt is proposed. The effect of carbon on the grain refinement of Mg-Al alloy is studied according to the proposed integrated treatment process. The regularity of carbon refinement in the Mg-Al alloy is examined by microstructural observation and theoretical calculation. The results show that carbon has no effect on the grain refinement of Mg-Al alloy when the Al content is less than 1wt.%. Howev ...[more]

PMID: 35926058

Similar Datasets

Project description:Al-Mg-Si series aluminum alloy is a heat-treatment-strengthened alloy. Research on the impact resistance of Al-Mg-Si series aluminum alloy is of great significance to expand its application in engineering. Taking 6082-T6 aluminum alloy as the concrete research object, using the split Hopkinson pressure bar (SHPB) device, the dynamic mechanical response of the material under different temperatures and average strain rates was studied, and the service performance of the material under extreme conditions was determined. The absolute temperature rise was introduced to optimize the existing constitutive model. The results show that when the environment temperature is 298.15~473.15 K under high-speed impact, the internal thermal softening effect of the material is dominant in the competition with the work hardening, resulting in a decrease in the flow stress of the material. Through the analysis of the real stress-strain curve, it was found that the elastic modulus of the material was negatively correlated with the strain rate, negatively correlated with the temperature, and showed an obvious temperature-softening effect. Yield strength was negatively correlated with temperature and positively correlated with strain rate, which showed an obvious strain rate hardening effect. Based on SEM microscopic analysis, it was found that under given conditions, adiabatic shear bands appeared in some samples, and their internal structures demonstrated obvious change. It was judged that when high-speed impact occurs, cracks are induced at the shear bands, and the cracks will continue to develop along the adiabatic shear bands, resulting in many oblique cracks which will gradually become larger and eventually lead to material failure. Finally, based on the model, the strain rate and temperature softening terms were improved, and a rise in adiabatic temperature rise was introduced. The improved model can better describe the strain rate effect of the material and accurately describe its flow stress. It provides a theoretical basis for the engineering application of materials.

Dataset Information

Study on the grain refinement mechanism of Mg-Al alloy based on carbon addition.

Publications

Study on the grain refinement mechanism of Mg-Al alloy based on carbon addition.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets