Few-quintuple Bi₂Te₃ nanofilms as potential thermoelectric materials.

ABSTRACT: The thermoelectric transport properties of p-type Bi₂Te₃ nanofilms with various quintuple layers (QL) were systematically investigated based on ab initio electronic structure calculations and Boltzmann transport equations. Our results demonstrated that p-type few-quintuple Bi₂Te₃ nanofilms could exhibit high thermoelectric performance. It was found out that the 1QL Bi₂Te₃ nanofilm had the highest ZT value as compared with other nanofilms, which is mainly attributed to the significant enhancement of the density of states near the edge of the valence band resulting from the strong coupling between the top and bottom electronic states and the quantum confinement effect. The dependence of the thermoelectric transport properties on carrier concentration and temperature was also discussed in detail, which can be useful for searching high-efficiency few-quintuple Bi₂Te₃ thermoelectric nanofilms.

SUBMITTER: Zhou G

PROVIDER: S-EPMC4309965 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Synthesis and Evaluation of Thick Films of Electrochemically Deposited Bi₂Te₃ and Sb₂Te₃ Thermoelectric Materials.

Project description:This paper presents the results of the synthesis and evaluation of thick thermoelectric films that may be used for such applications as thermoelectric power generators. Two types of electrochemical deposition methods, constant and pulsed deposition with improved techniques for both N-type bismuth telluride (Bi₂Te₃) and P-type antimony telluride (Sb₂Te₃), are performed and compared. As a result, highly oriented Bi₂Te₃ and Sb₂Te₃ thick films with a bulk-like structure are successfully synthesized with high Seebeck coefficients and low electrical resistivities. Six hundred-micrometer-thick Bi₂Te₃ and 500-µm-thick Sb₂Te₃ films are obtained. The Seebeck coefficients for the Bi₂Te₃ and Sb₂Te₃ films are -150 ± 20 and 170 ± 20 µV/K, respectively. Additionally, the electrical resistivity for the Bi₂Te₃ is 15 ± 5 µΩm and is 25 ± 5 µΩm for the Sb₂Te₃. The power factors of each thermoelectric material can reach 15 × 10-4 W/mK² for Bi₂Te₃ and 11.2 × 10-4 W/mK² for Sb₂Te₃.

| S-EPMC5459149 | biostudies-other

Thermoelectric Properties of Highly-Crystallized Ge-Te-Se Glasses Doped with Cu/Bi.

Project description:Chalcogenide semiconducting systems are of growing interest for mid-temperature range (~500 K) thermoelectric applications. In this work, Ge20Te77Se₃ glasses were intentionally crystallized by doping with Cu and Bi. These effectively-crystallized materials of composition (Ge20Te77Se₃)100-xMx (M = Cu or Bi; x = 5, 10, 15), obtained by vacuum-melting and quenching techniques, were found to have multiple crystalline phases and exhibit increased electrical conductivity due to excess hole concentration. These materials also have ultra-low thermal conductivity, especially the heavily-doped (Ge20Te77Se₃)100-xBix (x = 10, 15) samples, which possess lattice thermal conductivity of ~0.7 Wm-1 K-1 at 525 K due to the assumable formation of nano-precipitates rich in Bi, which are effective phonon scatterers. Owing to their high metallic behavior, Cu-doped samples did not manifest as low thermal conductivity as Bi-doped samples. The exceptionally low thermal conductivity of the Bi-doped materials did not, alone, significantly enhance the thermoelectric figure of merit, zT. The attempt to improve the thermoelectric properties by crystallizing the chalcogenide glass compositions by excess doping did not yield power factors comparable with the state of the art thermoelectric materials, as these highly electrically conductive crystallized materials could not retain the characteristic high Seebeck coefficient values of semiconducting telluride glasses.

| S-EPMC5506923 | biostudies-literature

Semi-metals as potential thermoelectric materials.

Project description:The best thermoelectric materials are believed to be heavily doped semiconductors. The presence of a band gap is assumed to be essential to achieve large thermoelectric power factor and figure of merit. In this work, we propose semi-metals with large asymmetry between conduction and valence bands as an alternative class of thermoelectric materials. To illustrate the idea, we study semi-metallic HgTe in details experimentally and theoretically. We employ ab initio calculations with hybrid exchange-correlation functional to accurately describe the electronic band structure in conjunction with the Boltzmann Transport theory to investigate the electronic transport properties. We calculate the lattice thermal conductivity using first principles calculations and evaluate the overall figure of merit. To validate our theoretical approach, we prepare semi-metallic HgTe samples and characterize their transport properties. Our first-principles calculations agree well with the experimental data. We show that intrinsic HgTe, a semimetal with large disparity in its electron and hole masses, has a high thermoelectric power factor that is comparable to the best known thermoelectric materials. Finally, we propose other possible materials with similar band structures as potential candidates for thermoelectric applications.

| S-EPMC6026171 | biostudies-literature

Few-Layer PdSe2 Sheets: Promising Thermoelectric Materials Driven by High Valley Convergence.

Project description:Herein, we report a comprehensive study on the structural and electronic properties of bulk, monolayer, and multilayer PdSe2 sheets. First, we present a benchmark study on the structural properties of bulk PdSe2 by using 13 commonly used density functional theory (DFT) functionals. Unexpectedly, the most commonly used van der Waals (vdW)-correction methods, including DFT-D2, optB88, and vdW-DF2, fail to provide accurate predictions of lattice parameters compared to experimental data (relative error > 15%). On the other hand, the PBE-TS series functionals provide significantly improved prediction with a relative error of <2%. Unlike hexagonal two-dimensional materials like graphene, transition metal dichalcogenides, and h-BN, the conduction band minimum of monolayer PdSe2 is not located along the high symmetry lines in the first Brillouin zone; this highlights the importance of the structure-property relationship in the pentagonal lattice. Interestingly, high valley convergence is found in the conduction and valence bands in monolayer, bilayer, and trilayer PdSe2 sheets, suggesting promising application in thermoelectric cooling.

| S-EPMC6644379 | biostudies-literature

Tuning of the Thermoelectric Properties of Bi2Te3 Nanorods Using Helium Ion Irradiation.

Project description:The present study reports an enhancement of the power factor of Bi2Te3 nanorods NRs) by helium (He+) ion irradiation. High-resolution transmission electron microscopy studies revealed the formation of amorphous layers on the surface of the NRs at the high ion fluence. This amorphous nature is due to the accumulation of migrating point defect clusters at the surface of the NRs. Raman scattering experiments provide further insight to the observed structural modifications. At higher ion fluence, impurity-dominated scattering processes significantly enhance the value of the Seebeck coefficient of Bi2Te3 NRs. The He+ ion irradiation up to the ion fluence of 1 × 1016 ions/cm2 improves the thermoelectric transport properties with the highest power factor, 8.2 ?W/m K2, at 390 K. Further investigations may result in the possibility of fabricating the Bi2Te3 NRs as thermoelectric generators with a high power factor for space applications.

| S-EPMC6643506 | biostudies-literature

Direct measurement of the thermoelectric properties of electrochemically deposited Bi2Te3 thin films.

Project description:The best known thermoelectric material for near room temperature heat-to-electricity conversion is bismuth telluride. Amongst the possible fabrication techniques, electrodeposition has attracted attention due to its simplicity and low cost. However, the measurement of the thermoelectric properties of electrodeposited films is challenging because of the conducting seed layer underneath the film. Here, we develop a method to directly measure the thermoelectric properties of electrodeposited bismuth telluride thin films, grown on indium tin oxide. Using this technique, the temperature dependent thermoelectric properties (Seebeck coefficient and electrical conductivity) of electrodeposited thin films have been measured down to 100 K. A parallel resistor model is employed to discern the signal of the film from the signal of the seed layer and the data are carefully analysed and contextualized with literature. Our analysis demonstrates that the thermoelectric properties of electrodeposited films can be accurately evaluated without inflicting any damage to the films.

| S-EPMC7578806 | biostudies-literature

Optimizing Room-Temperature Thermoelectric Performance of n-Type Bi2Te2.7Se0.3.

Project description:Bi2Te3-based compounds are exclusive commercial thermoelectric materials around room temperature. For n-type compounds, optimal thermoelectric properties are normally obtained at temperatures higher than room temperature to suppress the bipolar effect through increased carrier concentration. We find that doping with trace amounts of Cd and the addition of excess Bi are effective ways to optimize carrier concentration and achieve enhanced room-temperature thermoelectric performance for the Bi2Te2.7Se0.3 alloy in this work. For the Cd-doped samples, the replacement of Cd with Bi leads to not only a significant decrease in electron concentration but also apparently reduces the total thermal conductivity. The addition of excess Bi in the samples creates a Bi-rich synthetic atmosphere during the synthesis process, leading to increased BiTe antisite defects, decreased electron concentration, and reduced total thermal conductivity. Doping a small amount of Cd or adding excess Bi causes optimal thermoelectric performance of the n-type Bi2Te2.7Se0.3 sample shifts obviously toward low temperatures, and the samples with 0.4 atom % Cd and 0.8 atom % excess Bi achieve maximum zT of ∼0.97 at 448 K and ∼0.88 at 348 K, respectively.

| S-EPMC8675032 | biostudies-literature

A facile energy-saving route of fabricating thermoelectric Sb2Te3-Te nanocomposites and nanosized Te.

Project description:A facile energy-saving route is developed for fabricating Sb2Te3-Te nanocomposites and nanosized Te powders. The fabrication route not only avoids using organic chemicals, but also keeps the energy consumption to a minimum. The fabrication procedure involves two steps. Energetic precursors of nanosized powders of Sb and Te are produced at room temperature followed by hot pressing at 400°C under 70 MPa for 1 h. The resulting Sb2Te3-Te nanocomposite exhibits enhanced power factor. The dimensionless figure of merit zT value of the Sb2Te3-Te nanocomposite is 0.29 at 475 K.

| S-EPMC6227969 | biostudies-literature

Surrounding sensitive electronic properties of Bi?Te? nanoplates-potential sensing applications of topological insulators.

Project description:Significant efforts have been paid to exploring the fundamental properties of topological insulators (TIs) in recent years. However, the investigation of TIs as functional materials for practical device applications is still quite limited. In this work, electronic sensors based on Bi2Te3 nanoplates were fabricated and the sensing performance was investigated. On exposure to different surrounding environments, significant changes in the conducting properties were observed by direct electrical measurements. These results suggest that nanostructured TIs hold great potential for sensing applications.

| S-EPMC3982166 | biostudies-literature

Te Nanoneedles Induced Entanglement and Thermoelectric Improvement of SnSe.

Project description:Chalcogenide-based materials have attracted widespread interest in high-performance thermoelectric research fields. A strategy for the application of two types of chalcogenide for improved thermoelectric performance is described herein. Tin selenide (SnSe) is used as a base material, and Te nanoneedles are crystallized in the SnSe, resulting in the generation of a composite structure of SnSe with Te nanoneedles. The thermoelectric properties with various reaction times are investigated to reveal the optimum conditions for enhanced thermoelectric performance. A reaction time of 4 h at 450 K generated a composite Te nanoneedles/SnSe sample with the maximum ZT value, 3.2 times larger than that of the pristine SnSe. This result is attributed to both the reduced thermal conductivity from the effective phonon scattering of heterointerfaces and the improved electrical conductivity value due to the introduction of Te nanoparticles. This strategy suggests an approach to generating high-performance practical thermoelectric materials.

| S-EPMC7321485 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data