Synthesis and Evaluation of Thick Films of Electrochemically Deposited Bi₂Te₃ and Sb₂Te₃ Thermoelectric Materials.

ABSTRACT: This paper presents the results of the synthesis and evaluation of thick thermoelectric films that may be used for such applications as thermoelectric power generators. Two types of electrochemical deposition methods, constant and pulsed deposition with improved techniques for both N-type bismuth telluride (Bi₂Te₃) and P-type antimony telluride (Sb₂Te₃), are performed and compared. As a result, highly oriented Bi₂Te₃ and Sb₂Te₃ thick films with a bulk-like structure are successfully synthesized with high Seebeck coefficients and low electrical resistivities. Six hundred-micrometer-thick Bi₂Te₃ and 500-µm-thick Sb₂Te₃ films are obtained. The Seebeck coefficients for the Bi₂Te₃ and Sb₂Te₃ films are -150 ± 20 and 170 ± 20 µV/K, respectively. Additionally, the electrical resistivity for the Bi₂Te₃ is 15 ± 5 µΩm and is 25 ± 5 µΩm for the Sb₂Te₃. The power factors of each thermoelectric material can reach 15 × 10-4 W/mK² for Bi₂Te₃ and 11.2 × 10-4 W/mK² for Sb₂Te₃.

SUBMITTER: Trung NH

PROVIDER: S-EPMC5459149 | biostudies-other | 2017 Feb

REPOSITORIES: biostudies-other

ACCESS DATA

Similar Datasets

Project description:Conjugated polymers such as poly(3,4-ethylenedioxythiphene) (PEDOT) are of interest for a variety of applications including interfaces between electronic biomedical devices and living tissue. The mechanical properties, strength, and adhesion of these materials to solid substrates are all vital for long-term applications. We have been developing methods to quantify the mechanical properties of conjugated polymer thin films. In this paper, the stiffness, strength and the interfacial shear strength (adhesion) of electrochemically deposited PEDOT and PEDOT-co-1,3,5-tri[2-(3,4-ethylene dioxythienyl)]-benzene (EPh) were studied. The estimated Young's modulus of the PEDOT films was 2.6±1.4GPa, and the strain to failure was around 2%. The tensile strength was measured to be 56±27MPa. The effective interfacial shear strength was estimated with a shear-lag model by measuring the crack spacing as a function of film thickness. For PEDOT on gold/palladium-coated hydrocarbon film substrates an interfacial shear strength of 0.7±0.3MPa was determined. The addition of 5mole% of a tri-functional EDOT crosslinker (EPh) increased the tensile strength of the films to 283±67MPa, while the strain to failure remained about the same (2%). The effective interfacial shear strength was increased to 2.4±0.6MPa.Statement of significanceThis paper describes methods for estimating the ultimate mechanical properties of electrochemically deposited conjugated polymer (here PEDOT and PEDOT copolymers) films. Of particular interest and novelty is our implementation of a cracking test to quantify the shear strength of the PEDOT thin films on these solid substrates. There is considerable interest in these materials as interfaces between biomedical devices and living tissue, however potential mechanisms and modes of failure are areas of continuing concern, and establishing methods to quantify the strengths of these interfaces are therefore of particular current interest. We are confident that these results will be useful to the broader biological materials community and are worthy of broader dissemination.

Dataset Information

Synthesis and Evaluation of Thick Films of Electrochemically Deposited Bi₂Te₃ and Sb₂Te₃ Thermoelectric Materials.

Similar Datasets

OmicsDI is part of the ELIXIR infrastructure

Tweets