Multi-barrier field-emission behavior in PBTTT thin films at low temperatures.

ABSTRACT: We investigated the low-temperature transport mechanism for poly[2,5-bis(3-alkylthiophen-2-yl)thieno(3,2-b)thiophene] (PBTTT). The temperature-dependent transport behavior was studied by varying the drain-source electric field and gate bias. The results suggest that low-temperature charge transport is dominated by direct tunneling at low electric fields, while field emission is prevailing for high electric fields with high carrier densities. However, the obtained barrier heights are remarkably greater than expected in a conventional field emission. We propose a simplified model of field emission through quasi-one-dimensional path with multiple barriers which shows good agreement with the results more clearly. Field emission across the domain boundaries may assist in overcoming the transport barriers induced by the interchain disorder, which results in the weak temperature dependence of conductivities and nonlinear current-voltage relation at low temperatures.

SUBMITTER: Kang ES

PROVIDER: S-EPMC4323663 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Low Temperature Synthesis of Lithium-Doped Nanocrystalline Diamond Films with Enhanced Field Electron Emission Properties.

Project description:Low temperature (350 °C) grown conductive nanocrystalline diamond (NCD) films were realized by lithium diffusion from Cr-coated lithium niobate substrates (Cr/LNO). The NCD/Cr/LNO films showed a low resistivity of 0.01 Ω·cm and excellent field electron emission characteristics, viz. a low turn-on field of 2.3 V/µm, a high-current density of 11.0 mA/cm² (at 4.9 V/m), a large field enhancement factor of 1670, and a life-time stability of 445 min (at 3.0 mA/cm²). The low temperature deposition process combined with the excellent electrical characteristics offers a new prospective for applications based on temperature sensitive materials.

| S-EPMC6164399 | biostudies-literature

Low-Temperature Emission Dynamics of Methylammonium Lead Bromide Hybrid Perovskite Thin Films at the Sub-Micrometer Scale.

Project description:We study the low-temperature (T = 4.7 K) emission dynamics of a thin film of methylammonium lead bromide (MAPbBr3), prepared via the anti-solvent method. Using intensity-dependent (over 5 decades) hyperspectral microscopy under quasi-resonant (532 nm) continuous wave excitation, we revealed spatial inhomogeneities in the thin film emission. This was drastically different at the band-edge (∼550 nm, sharp peaks) than in the emission tail (∼568 nm, continuum of emission). We are able to observe regions of the film at the micrometer scale where emission is dominated by excitons, in between regions of trap emission. Varying the density of absorbed photons by the MAPbBr3 thin films, two-color fluorescence lifetime imaging microscopy unraveled the emission dynamics: a fast, resolution-limited (∼200 ps) monoexponential tangled with a stretched exponential decay. We associate the first to the relaxation of excitons and the latter to trap emission dynamics. The obtained stretching exponents can be interpreted as the result of a two-dimensional electron diffusion process: Förster resonant transfer mechanism. Furthermore, the non-vanishing fast monoexponential component even in the tail of the MAPbBr3 emission indicates the subsistence of localized excitons. Finally, we estimate the density of traps in MAPbBr3 thin films prepared using the anti-solvent method at n∼1017 cm-3.

| S-EPMC10458237 | biostudies-literature

Nanopatterning of Perovskite Thin Films for Enhanced and Directional Light Emission.

Project description:Lead-halide perovskites offer excellent properties for lighting and display applications. Nanopatterning perovskite films could enable perovskite-based devices with designer properties, increasing their performance and adding novel functionalities. We demonstrate the potential of nanopatterning for achieving light emission of a perovskite film into a specific angular range by introducing periodic sol-gel structures between the injection and emissive layer by using substrate conformal imprint lithography (SCIL). Structural and optical characterization reveals that the emission is funnelled into a well-defined angular range by optical resonances, while the emission wavelength and the structural properties of the perovskite film are preserved. The results demonstrate a flexible and scalable approach to the patterning of perovskite layers, paving the way toward perovskite LEDs with designer angular emission patterns.

| S-EPMC9412957 | biostudies-literature

Low Gilbert damping and high thermal stability of Ru-seeded L10-phase FePd perpendicular magnetic thin films at elevated temperatures.

Project description:Bulk perpendicular magnetic anisotropy materials are proposed to be a promising candidate for next-generation ultrahigh density and ultralow energy-consumption spintronic devices. In this work, we experimentally investigate the structure, thermal stability, and magnetic properties of FePd thin films seeded by a Ru layer. An fcc-phase Ru layer induces the highly-ordered L10-phase FePd thin films with perpendicular magnetic anisotropy (Ku ~ 10.1 Merg/cm3). The thermal stability of FePd samples is then studied through the annealing process. It is found that a Ku ~ 6.8 Merg/cm3 can be obtained with the annealing temperature of 500 °C. In addition, the damping constant α, an important parameter for switching current density, is determined as a function of the testing temperature. We observe that α increases from 0.006 to 0.009 for as-deposited FePd sample and from 0.006 to 0.012 for 400 °C-annealed FePd sample as the testing temperature changes from 25 °C to 150 °C. These results suggest that Ru-seeded FePd provides great potential in scaling perpendicular magnetic tunnel junctions below 10 nm for applications in ultralow energy-consumption spintronic devices.

| S-EPMC7909870 | biostudies-literature

Near-Field Optical Drilling of Sub-? Pits in Thin Polymer Films.

Project description:Under UV illumination, polymer films can undergo chain scission and contract. Using this effect, tightly focused laser light is shown to develop runaway near-field concentration that drills sub-100 nm pits through a thin film. This subwavelength photolithography can be controlled in real time by monitoring laser scatter from the evolving holes, allowing systematic control of the void diameter. Our model shows how interference between the substrate and film together with near-field focusing by the evolving crevice directs this formation and predicts minimum pit sizes in films of 100 nm thickness on gold substrates. The smallest features so far are 60 nm diameter pits using 447 nm light focused onto polystyrene through a ×100 objective (NA = 0.8). Such arrays of pits can be easily used as masks for fabricating more complex nanostructures, such as plasmonic nanostructures and biomicrofluidic devices. This demonstration shows the potential for harnessing near-field feedback in optical direct-writing for nanofabrication.

| S-EPMC5578361 | biostudies-literature

Electric Field Assisted Self-Assembly of Viruses into Colored Thin Films.

Project description:Filamentous viruses called M13 bacteriophages are promising materials for devices with thin film coatings because phages are functionalizable, and they can self-assemble into smectic helicoidal nanofilament structures. However, the existing "pulling" approach to align the nanofilaments is slow and limits potential commercialization of this technology. This study uses an applied electric field to rapidly align the nanostructures in a fixed droplet. The electric field reduces pinning of the three-phase contact line, allowing it to recede at a constant rate. Atomic force microscopy reveals that the resulting aligned structures resemble those produced via the pulling method. The field-assisted alignment results in concentric color bands quantified with image analysis of red, green, and blue line profiles. The alignment technique shown here could reduce self-assembly time from hours to minutes and lend itself to scalable manufacturing techniques such as inkjet printing.

| S-EPMC6781059 | biostudies-literature

High field superconducting properties of Ba(Fe1-xCox)2As2 thin films.

Project description:In general, the critical current density, Jc, of type II superconductors and its anisotropy with respect to magnetic field orientation is determined by intrinsic and extrinsic properties. The Fe-based superconductors of the '122' family with their moderate electronic anisotropies and high yet accessible critical fields (Hc2 and Hirr) are a good model system to study this interplay. In this paper, we explore the vortex matter of optimally Co-doped BaFe2As2 thin films with extended planar and c-axis correlated defects. The temperature and angular dependence of the upper critical field is well explained by a two-band model in the clean limit. The dirty band scenario, however, cannot be ruled out completely. Above the irreversibility field, the flux motion is thermally activated, where the activation energy U0 is going to zero at the extrapolated zero-kelvin Hirr value. The anisotropy of the critical current density Jc is both influenced by the Hc2 anisotropy (and therefore by multi-band effects) as well as the extended planar and columnar defects present in the sample.

| S-EPMC4661601 | biostudies-literature

Ultra-low damping insulating magnetic thin films get perpendicular.

Project description:A magnetic material combining low losses and large perpendicular magnetic anisotropy (PMA) is still a missing brick in the magnonic and spintronic fields. We report here on the growth of ultrathin Bismuth doped Y3Fe5O12 (BiYIG) films on Gd3Ga5O12 (GGG) and substituted GGG (sGGG) (111) oriented substrates. A fine tuning of the PMA is obtained using both epitaxial strain and growth-induced anisotropies. Both spontaneously in-plane and out-of-plane magnetized thin films can be elaborated. Ferromagnetic Resonance (FMR) measurements demonstrate the high-dynamic quality of these BiYIG ultrathin films; PMA films with Gilbert damping values as low as 3?×?10-4 and FMR linewidth of 0.3?mT at 8?GHz are achieved even for films that do not exceed 30?nm in thickness. Moreover, we measure inverse spin hall effect (ISHE) on Pt/BiYIG stacks showing that the magnetic insulator's surface is transparent to spin current, making it appealing for spintronic applications.

| S-EPMC6105659 | biostudies-literature

Gas Permeation of Sulfur Thin-Films and Potential as a Barrier Material.

Project description:Elemental sulfur was formed into poly(ether sulfone)-supported thin-films (ca. 10 µm) via a melt-casting process. Observed permeabilities of C2H4, CO2, H2, He, and N2 through the sulphur thin-films were <1 barrer. The sulfur thin-films were observed to age over a period of ca. 15 days, related to the reversion of polymerized sulfur to the S8 allotrope. This structural conversion was observed to correlate with an increase in the permeability of all gases.

| S-EPMC6631778 | biostudies-literature

Photoluminescence and Stoichiometry Correlation in Nanocrystalline EuO x Thin Films: Tunable Color Emission.

Project description:The development of broadband and ultracompact optoelectronic devices relies on the possibility of fabricating bright and tunable emitters at the nanoscale. Here, we show emission from EuO x (1 ? x < 1.4) thin films on silicon formed by nanocrystals with average sizes in the range of 5 nm. The photoluminescence emission of the nano-EuO x films is tunable as a function of the oxygen concentration changing from a green broadband Eu2+-related emission to a narrow red Eu3+-related emission. To reach these results has been instrumental through the use of a new methodology specially designed to achieve high-quality europium oxide films whose compositional properties are controlled by the growth base pressure and preserved thanks to a chemically stable and transparent cover layer of Al2O3. Our findings confirm the outstanding potential of nanostructured EuO x films as "one-compound" optical elements with tunable emission properties for their implementation in integrated silicon-based devices.

| S-EPMC7370298 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data