Photoluminescence studies of a perceived white light emission from a monolithic InGaN/GaN quantum well structure.

ABSTRACT: In this work we demonstrate by photoluminescence studies white light emission from a monolithic InGaN/GaN single quantum well structure grown by metal organic chemical vapour deposition. As-grown and thermally annealed samples at high temperature (1000 °C, 1100 °C and 1200 °C) and high pressure (1.1 GPa) were analysed by spectroscopic techniques, and the annealing effect on the photoluminescence is deeply explored. Under laser excitation of 3.8 eV at room temperature, the as-grown structure exhibits two main emission bands: a yellow band peaked at 2.14 eV and a blue band peaked at 2.8 eV resulting in white light perception. Interestingly, the stability of the white light is preserved after annealing at the lowest temperature (1000 °C), but suppressed for higher temperatures due to a deterioration of the blue quantum well emission. Moreover, the control of the yellow/blue bands intensity ratio, responsible for the white colour coordinate temperatures, could be achieved after annealing at 1000 °C. The room temperature white emission is studied as a function of incident power density, and the correlated colour temperature values are found to be in the warm white range: 3260-4000 K.

SUBMITTER: Ben-Sedrine N

PROVIDER: S-EPMC4559898 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

A novel model on time-resolved photoluminescence measurements of polar InGaN/GaN multi-quantum-well structures.

Project description:Based on carrier rate equation, a new model is proposed to explain the non-exponential nature of time-resolved photoluminescence (TRPL) decay curves in the polar InGaN/GaN multi-quantum-well structures. From the study of TRPL curves at different temperatures, it is found that both radiative and non-radiative recombination coefficients vary from low temperature to room temperature. The variation of the coefficients is compatible with the carrier density of states distribution as well as the carrier localization process. These results suggest that there is a novel method to calculate the internal quantum efficiency, which is a complement to the traditional one based on temperature dependent photoluminescence measurement.

| S-EPMC5361181 | biostudies-literature

Monolithic multiple colour emission from InGaN grown on patterned non-polar GaN.

Project description:A novel overgrowth approach has been developed in order to create a multiple-facet structure consisting of only non-polar and semi-polar GaN facets without involving any c-plane facets, allowing the major drawbacks of utilising c-plane GaN for the growth of III-nitride optoelectronics to be eliminated. Such a multiple-facet structure can be achieved by means of overgrowth on non-polar GaN micro-rod arrays on r-plane sapphire. InGaN multiple quantum wells (MQWs) are then grown on the multiple-facet templates. Due to the different efficiencies of indium incorporation on non-polar and semi-polar GaN facets, multiple-colour InGaN/GaN MQWs have been obtained. Photoluminescence (PL) measurements have demonstrated that the multiple-colour emissions with a tunable intensity ratio of different wavelength emissions can be achieved simply through controlling the overgrowth conditions. Detailed cathodoluminescence measurements and excitation-power dependent PL measurements have been performed, further validating the approach of employing the multiple facet templates for the growth of multiple colour InGaN/GaN MQWs. It is worth highlighting that the approach potentially paves the way for the growth of monolithic phosphor-free white emitters in the future.

| S-EPMC6353934 | biostudies-literature

Linearly polarized photoluminescence of InGaN quantum disks embedded in GaN nanorods.

Project description:We have investigated the emission from InGaN/GaN quantum disks grown on the tip of GaN nanorods. The emission at 3.21?eV from the InGaN quantum disk doesn't show a Stark shift, and it is linearly polarized when excited perpendicular to the growth direction. The degree of linear polarization is about 39.3% due to the anisotropy of the nanostructures. In order to characterize a single nanostructure, the quantum disks were dispersed on a SiO2 substrate patterned with a metal reference grid. By rotating the excitation polarization angle from parallel to perpendicular relative to the nanorods, the variation of overall PL for the 3.21?eV peak was recorded and it clearly showed the degree of linear polarization (DLP) of 51.5%.

| S-EPMC5970171 | biostudies-literature

3D fluorescence confocal microscopy of InGaN/GaN multiple quantum well nanorods from a light absorption perspective.

Project description:A nanostructure of In0.18Ga0.82N/GaN multiple quantum well (MQW) nanorods (NRs) was fabricated using top-down etching with self-organized nickel (Ni) nanoparticles as masks on the wafer. The optical properties of In0.18Ga0.82N/GaN MQW NRs were discussed by experiment and theory from a light absorption perspective. Three-dimensional (3D) optical images of NRs were successfully obtained by confocal laser scanning microscopy (CLSM) for physical observation of the optical phenomenon of InGaN/GaN MQW NRs. Moreover, optical simulations were performed by COMSOL Multiphysics via the three-dimensional finite-element method to explore the influences of NR geometrical parameters on optical absorption. The simulated results demonstrate that the absorption of NRs is higher than that of the film due to the waveguide properties of NRs resulting from their higher refractive index than embedding medium and higher aspect ratio than bulk. In addition, an increase in the diameter results in a red-shift of the absorption peak position of In0.18Ga0.82N/GaN MQW NRs. The smaller pitch enhances the near-field coupling of the nanorods and broadens the absorption peak. These results clearly illustrate the optical properties of In0.18Ga0.82N/GaN MQW NRs from the perspective of 3D confocal laser scanning microscopy. This work is promising for the applications of III-V optoelectronic devices.

| S-EPMC9417793 | biostudies-literature

Stretchable Transparent Light-Emitting Diodes Based on InGaN/GaN Quantum Well Microwires and Carbon Nanotube Films.

Project description:We propose and demonstrate both flexible and stretchable blue light-emitting diodes based on core/shell InGaN/GaN quantum well microwires embedded in polydimethylsiloxane membranes with strain-insensitive transparent electrodes involving single-walled carbon nanotubes. InGaN/GaN core-shell microwires were grown by metal-organic vapor phase epitaxy, encapsulated into a polydimethylsiloxane film, and then released from the growth substrate. The fabricated free-standing membrane of light-emitting diodes with contacts of single-walled carbon nanotube films can stand up to 20% stretching while maintaining efficient operation. Membrane-based LEDs show less than 15% degradation of electroluminescence intensity after 20 cycles of stretching thus opening an avenue for highly deformable inorganic devices.

| S-EPMC8230151 | biostudies-literature

Study on spin and optical polarization in a coupled InGaN/GaN quantum well and quantum dots structure.

Project description:The spin and optical polarization based on a coupled InGaN/GaN quantum well (QW) and quantum dots (QDs) structure is investigated. In this structure, spin-electrons can be temporarily stored in QW, and spin injection from the QW into QDs via spin-conserved tunneling is enabled. Spin relaxation can be suppressed owing to the small energy difference between the initial state in the QW and the final states in the QDs. Photoluminescence (PL) and time-resolved photoluminescence (TRPL) measurements are carried out on optical spin-injection and -detection. Owing to the coupled structure, spin-conserved tunneling mechanism plays a significant role in preventing spin relaxation process. As a result, a higher circular polarization degree (CPD) (~49.1%) is achieved compared with conventional single layer of QDs structure. Moreover, spin relaxation time is also extended to about 2.43 ns due to the weaker state-filling effect. This coupled structure is believed an appropriate candidate for realization of spin-polarized light source.

| S-EPMC5069675 | biostudies-literature

Highly polarized photoluminescence from c-plane InGaN/GaN multiple quantum wells on stripe-shaped cavity-engineered sapphire substrate.

Project description:Highly polarized photoluminescence (PL) from c-plane InGaN/GaN multiple quantum wells (MQWs) grown on stripe-shaped cavity-engineered sapphire substrate (SCES) was realized. The polarization ratio was as high as 0.74 at room temperature. High-resolution X-ray reciprocal space mapping measurements revealed that the InGaN quantum wells on GaN/SCES template were under considerable anisotropic in-plane strain states of -1.178% and -1.921% along the directions perpendicular and parallel to the stripe-pattern, respectively. The anisotropic strain states were attributed to the anisotropic alignment of cavity-incorporated sapphire nano-membranes, which accommodated both anisotropic elastic relaxation in the InGaN quantum well plane as well as the graded elastic relaxation along the vertical direction in the GaN template adjacent to the InGaN/GaN MQWs. The partial strain relaxation in the InGaN wells also contributed to reduction of quantum confined Stark effect, resulting in four times higher PL intensity than InGaN/GaN MQWs on planar sapphire substrate. From theoretical calculations based on k∙p perturbation theory, it was found that fundamental origin of the polarized optical emission was strain-induced modification of valence band structures of the InGaN/GaN MQWs on the SCES. This study will allow us to realize light emitting diodes with highly polarized emission with conventional c-plane sapphire substrates by strain-induced valence band modification.

| S-EPMC6547675 | biostudies-literature

Strain-induced yellow to blue emission tailoring of axial InGaN/GaN quantum wells in GaN nanorods synthesized by nanoimprint lithography.

Project description:GaN nanorods (NRds) with axial InGaN/GaN MQWs insertions are synthesized by an original cost-effective and large-scale nanoimprint-lithography process from an InGaN/GaN MQWs layer grown on c-sapphire substrates. By design, such NRds exhibit a single emission due to the c-axis MQWs. A systematic study of the emission of the NRds by time-resolved luminescence (TR-PL) and power dependence PL shows a diameter-controlled luminescence without significant degradation of the recombination rate thanks to the diameter-controlled strain tuning and QSCE. A blueshift up to 0.26 eV from 2.28 to 2.54 eV (543 nm to 488 nm) is observed for 3.2 nm thick InGaN/GaN QWs with an In composition of 19% when the NRds radius is reduced from 650 to 80 nm. The results are consistent with a 1-D based strain relaxation model. By combining state of the art knowledge of c-axis growth and the strong strain relieving capability of NRds, this process enables multiple and independent single-color emission from a single uniform InGaN/GaN MQWs layer in a single patterning step, then solving color mixing issue in InGaN based nanorods LED devices.

| S-EPMC7990954 | biostudies-literature

Carrier localization in In-rich InGaN/GaN multiple quantum wells for green light-emitting diodes.

Project description:Carrier localization phenomena in indium-rich InGaN/GaN multiple quantum wells (MQWs) grown on sapphire and GaN substrates were investigated. Temperature-dependent photoluminescence (PL) spectroscopy, ultraviolet near-field scanning optical microscopy (NSOM), and confocal time-resolved PL (TRPL) spectroscopy were employed to verify the correlation between carrier localization and crystal quality. From the spatially resolved PL measurements, we observed that the distribution and shape of luminescent clusters, which were known as an outcome of the carrier localization, are strongly affected by the crystalline quality. Spectroscopic analysis of the NSOM signal shows that carrier localization of MQWs with low crystalline quality is different from that of MQWs with high crystalline quality. This interrelation between carrier localization and crystal quality is well supported by confocal TRPL results.

| S-EPMC4366764 | biostudies-literature

Room-temperature continuous-wave electrically pumped InGaN/GaN quantum well blue laser diode directly grown on Si.

Project description:Current laser-based display and lighting applications are invariably using blue laser diodes (LDs) grown on free-standing GaN substrates, which are costly and smaller in size compared with other substrate materials.1-3 Utilizing less expensive and large-diameter Si substrates for hetero-epitaxial growth of indium gallium nitride/gallium nitride (InGaN/GaN) multiple quantum well (MQW) structure can substantially reduce the cost of blue LDs and boost their applications. To obtain a high crystalline quality crack-free GaN thin film on Si for the subsequent growth of a blue laser structure, a hand-shaking structure was formed by inserting Al-composition step down-graded AlN/AlxGa1-xN buffer layers between GaN and Si substrate. Thermal degradation in InGaN/GaN blue MQWs was successfully suppressed with indium-rich clusters eliminated by introducing hydrogen during the growth of GaN quantum barriers (QBs) and lowering the growth temperature for the p-type AlGaN/GaN superlattice optical cladding layer. A continuous-wave (CW) electrically pumped InGaN/GaN quantum well (QW) blue (450 nm) LD grown on Si was successfully demonstrated at room temperature (RT) with a threshold current density of 7.8 kA/cm2.

| S-EPMC6106987 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data