Griffiths phase behaviour in a frustrated antiferromagnetic intermetallic compound.

ABSTRACT: The rare coexistence of a Griffiths phase (GP) and a geometrically frustrated antiferromagnetism in the non-stoichiometric intermetallic compound GdFe0.17Sn2 (the paramagnetic Weiss temperature θp ~ -59 K) is reported in this work. The compound forms in the Cmcm space group with large structural anisotropy (b/c ~ 4). Interestingly, all the atoms in the unit cell possess the same point group symmetry (Wycoff position 4c), which is rather rare. The frustration parameter, f = |θp|/TN has been established as 3.6, with the Néel temperature TN and Griffiths temperature TG being 16.5 and 32 K, respectively. The TG has been determined from the heat capacity measurement and also from the magnetocaloric effect (MCE). It is also shown that substantial difference in GP region may exist between zero field and field cooled measurements - a fact hitherto not emphasized so far.

SUBMITTER: Ghosh K

PROVIDER: S-EPMC4626802 | biostudies-other | 2015

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Nucleation and growth of TiAl<sub>3</sub> intermetallic phase in diffusion bonded Ti/Al Metal Intermetallic Laminate.

Project description:A novel nucleation and growth phenomenon for TiAl3 intermetallic phase in Ti/Al diffusion couple is proposed based on diffusion kinetics. The interdiffusion and intrinsic diffusion co-efficients are calculated to make evident of dominant diffusion of Al towards Ti in Ti/Al diffusion couple obtained by solid state diffusion bonding. It was surprising to observe that the diffusion rate of Al was around 20 times higher than Ti with the formation of Kirkendall pores near the Al/TiAl3 interface. With such dominant diffusion of Al towards Ti, the nucleation and growth of TiAl3 intermetallic phase in Ti/Al couple happens mainly at the Ti/TiAl3 interface rather than Al/TiAl3 interface which is evident by the presence of very fine nearly nano-sized TiAl3 nuclei/grains near the Ti/TiAl3 interface. Even though the intermetallic phase is expected to nucleate at Al/TiAl3 interface, the relatively larger TiAl3 grains near that interface depicts grain growth with minimal nucleation. The theoretical calculations on diffusion parameters are in accordance with experimental observations of TiAl3 intermetallic growth phenomenon in Ti/Al system.

| S-EPMC6235842 | biostudies-literature

Thermodynamic phase transitions in a frustrated magnetic metamaterial.

Project description:Materials with interacting magnetic degrees of freedom display a rich variety of magnetic behaviour that can lead to novel collective equilibrium and out-of-equilibrium phenomena. In equilibrium, thermodynamic phases appear with the associated phase transitions providing a characteristic signature of the underlying collective behaviour. Here we create a thermally active artificial kagome spin ice that is made up of a large array of dipolar interacting nanomagnets and undergoes phase transitions predicted by microscopic theory. We use low energy muon spectroscopy to probe the dynamic behaviour of the interacting nanomagnets and observe peaks in the muon relaxation rate that can be identified with the critical temperatures of the predicted phase transitions. This provides experimental evidence that a frustrated magnetic metamaterial can be engineered to admit thermodynamic phases.

| S-EPMC4595626 | biostudies-literature

Experimental Investigation and Thermodynamic Verification for the Phase Relation around the ε-Mg23 (Al, Zn)30 Intermetallic Compound in the Mg-Zn-Al System.

Project description:The appearance of the ε phase during the welding process can severely weaken the welding strength of dissimilar metals of Mg-Zn-Al alloy systems. An understanding of the accurate phase diagram, especially the equilibrium phase relation around the ε phase, is thus of particular importance. However, the phase interrelation near the ε-Mg23(Al, Zn)30 phase has not yet been fully studied. In this work, the local phase diagrams of the ε phase and its surrounding phases in the Mg-Zn-Al system are systematically determined by experimental investigation and thermodynamic verification. Five Mg-Zn-Al alloys and one diffusion couple were fabricated and analyzed to get accurate phase constituents and relationships adjacent to ε phase. The current experimental data obtained from Scanning Electron Microscope (SEM), X-ray diffraction (XRD), Differential Scanning Calorimetry (DSC), and Electron Probe Micro Analysis (EPMA) were further compared with the thermodynamically computed phase relations around ε phase for verification, showing good agreements. Several important conclusions are drawn based on current experimental work, which can provide supporting information for the follow-up studies on ε phase in the Mg-Zn-Al alloy systems.

| S-EPMC8625525 | biostudies-literature

Antiferromagnetic Slater insulator phase of Na₂IrO₃.

Project description:Using a hybrid density-functional theory (DFT) calculation including spin-orbit coupling (SOC), we predict that the zigzag antiferromagnetic (AFM) ground state of the honeycomb layered compound Na₂IrO₃ opens the observed insulating gap through a long-range magnetic order. We show that the effect of SOC and the correction of self-interaction error inherent in previous local or semilocal DFT calculations play crucial roles in predicting the band gap formation in Na₂IrO₃. It is revealed that the itinerant AFM order with a strong suppression of the Ir magnetic moment is attributed to a considerable hybridization of the Ir 5d orbitals with the O 2p orbitals. Thus, our results suggest that the insulating phase of Na₂IrO₃ can be represented as a Slater insulator driven by itinerant magnetism.

| S-EPMC4052719 | biostudies-other

Steering the methanol steam reforming reactivity of intermetallic Cu-In compounds by redox activation: stability <i>vs.</i> formation of an intermetallic compound-oxide interface.

Project description:To compare the inherent methanol steam reforming properties of intermetallic compounds and a corresponding intermetallic compound-oxide interface, we selected the Cu-In system as a model to correlate the stability limits, self-activation and redox activation properties with the catalytic performance. Three distinct intermetallic Cu-In compounds - Cu7In3, Cu2In and Cu11In9 - were studied both in an untreated and redox-activated state resulting from alternating oxidation-reduction cycles. The stability of all studied intermetallic compounds during methanol steam reforming (MSR) operation is essentially independent of the initial stoichiometry and all accordingly resist substantial structural changes. The inherent activity under batch MSR conditions is highest for Cu2In, corroborating the results of a Cu2In/In2O3 sample accessed through reactive metal-support interaction. Under flow MSR operation, Cu7In3 displays considerable deactivation, while Cu2In and Cu11In9 feature stable performance at simultaneously high CO2 selectivity. The missing significant self-activation is most evident in the operando thermogravimetric experiments, where no oxidation is detected for any of the intermetallic compounds. In situ X-ray diffraction allowed us to monitor the partial decomposition and redox activation of the Cu-In intermetallic compounds into Cu0.9In0.1/In2O3 (from Cu7In3), Cu7In3/In2O3 (from Cu2In) and Cu7In3/Cu0.9In0.1/In2O3 (from Cu11In9) interfaces with superior MSR performance compared to the untreated samples. Although the catalytic profiles appear surprisingly similar, the latter interface with the highest indium content exhibits the least deactivation, which we explain by formation of stabilizing In2O3 patches under MSR conditions.

| S-EPMC8365629 | biostudies-literature

Increasing strength and conductivity of Cu alloy through abnormal plastic deformation of an intermetallic compound.

Project description:The precipitation strengthening of Cu alloys inevitably accompanies lowering of their electric conductivity and ductility. We produced bulk Cu alloys arrayed with nanofibers of stiff intermetallic compound through a precipitation mechanism using conventional casting and heat treatment processes. We then successfully elongated these arrays of nanofibers in the bulk Cu alloys to 400% of original length without breakage at room temperature using conventional rolling process. By inducing such an one-directional array of nanofibers of intermetallic compound from the uniform distribution of fine precipitates in the bulk Cu alloys, the trade-off between strength and conductivity and between strength and ductility could be significantly reduced. We observed a simultaneous increase in electrical conductivity by 1.3 times and also tensile strength by 1.3 times in this Cu alloy bulk compared to the conventional Cu alloys.

| S-EPMC4973219 | biostudies-literature

Nanostructured Molybdenum Oxides from Aluminium-Based Intermetallic Compound: Synthesis and Application in Hydrogen Evolution Reaction.

Project description:Characterized by a large surface area to volume ratio, nanostructured metal oxides possess unique chemical and physical properties with applications in electronics, catalysis, sensors, etc. In this study, Mo3Al8, an intermetallic compound, has been used as a precursor to obtain nanostructured molybdenum oxides. It was prepared into ribbons by arc-melting and melt-spinning techniques. Single and double-step free corrosion of the as-quenched material have been studied in 1 M KOH, 1 M HF and 1.25 M FeCl3 at room temperature. In both cases, nanostructured molybdenum oxides were obtained on a surface layer a few microns thick. Two of the as-prepared samples were tested for their electrocatalytic capability for hydrogen evolution reaction (HER) in 0.5 M H2SO4 giving low onset potential (-50 mV, -45 mV), small Tafel slopes (92 mV dec-1, 9 mV dec-1) and high exchange current densities (0.08 mA cm-2, 0.35 mA cm-2 respectively). The proposed nanostructured molybdenum oxides are cost-effective and sustainable due to the cheap and abundant starting material used and the simple synthetic route, paving the way for their possible application as HER electrocatalysts.

| S-EPMC8156916 | biostudies-literature

Evolutionary design of non-frustrated networks of phase-repulsive oscillators.

Project description:Evolutionary optimisation algorithm is employed to design networks of phase-repulsive oscillators that achieve an anti-phase synchronised state. By introducing the link frustration, the evolutionary process is implemented by rewiring the links with probability proportional to their frustration, until the final network displaying a unique non-frustrated dynamical state is reached. Resulting networks are bipartite and with zero clustering. In addition, the designed non-frustrated anti-phase synchronised networks display a clear topological scale. This contrasts usually studied cases of networks with phase-attractive dynamics, whose performance towards full synchronisation is typically enhanced by the presence of a topological hierarchy.

| S-EPMC3522069 | biostudies-literature

Defect-induced ferromagnetism in a S = 1/2 quasi-one-dimensional Heisenberg antiferromagnetic chain compound.

Project description:We present evidences that defects in the spin S = 1/2 Heisenberg antiferromagnetic chain (HAFC) compound can lead to ferromagnetism by studying the magnetic and thermal properties of the newly discovered quasi-one-dimensional (1D) metal-organic framework [CH3NH3][Cu(HCOO)3] (MACuF). Our findings suggest that the long-range ferromagnetic order at 3.7 K can be attributed to Cu2+ ions from the 2D networks constructed by the endpoints of the broken chains. In such a case, the intrinsic magnetism can emerge in this quasi-1D Heisenberg chain system at the background of the short-range antiferromagnetism. This unusual ferromagnetism found in HAFC not only enriches magnetic features in the low-dimensional systems, but helps to understand some of the exotic magnetic phenomena in other real quasi-1D magnetic materials.

| S-EPMC8280101 | biostudies-literature

Spin pumping during the antiferromagnetic-ferromagnetic phase transition of iron-rhodium.

Project description:FeRh attracts intensive interest in antiferromagnetic (AFM) spintronics due to its first-order phase transition between the AFM and ferromagnetic (FM) phase, which is unique for exploring spin dynamics in coexisting phases. Here, we report lateral spin pumping by which angular momentum is transferred from FM domains into the AFM matrix during the phase transition of ultrathin FeRh films. In addition, FeRh is verified to be both an efficient spin generator and an efficient spin sink, by electrically probing vertical spin pumping from FM-FeRh into Pt and from Py into FeRh, respectively. A dramatic enhancement of damping related to AFM-FeRh is observed during the phase transition, which we prove to be dominated by lateral spin pumping across the FM/AFM interface. The discovery of lateral spin pumping provides insight into the spin dynamics of magnetic thin films with mixed-phases, and the significantly modulated damping advances its potential applications, such as ultrafast spintronics.

| S-EPMC6959338 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data