Uniform and Conformal Carbon Nanofilms Produced Based on Molecular Layer Deposition.

ABSTRACT: Continuous and uniform carbon nanofilms (CNFs) are prepared by pyrolysis of polyimide films which are produced by molecular layer deposition (MLD). The film thickness can be easily controlled at nanometer scale by altering the cycle numbers. During the annealing process at 600 °C, the polyimide film is subject to shrinkage of 70% in thickness. The obtained CNFs do not exhibit a well-graphitized structure due to the low calcination temperature. No clear pore structures are observed in the produced films. CNFs grown on a glass substrate with a thickness of about 1.4 nm shows almost 98% optical transmittance in the visible spectrum range. Au nanoparticles coated with CNFs are produced by this method. Carbon nanotubes with uniform wall thickness are obtained using anodic aluminum oxide as a template by depositing polyimide films into its pores. Our results demonstrate that this method is very effective to coat conformal and uniform CNFs on various substrates, such as nanoparticles and porous templates, to produce functional composite nanomaterials.

SUBMITTER: Yang P

PROVIDER: S-EPMC5452762 | biostudies-other | 2013 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

F-Doped Carbon Nanoparticles-Based Nucleation Assistance for Fast and Uniform Three-Dimensional Zn Deposition.

Project description:Aqueous Zn metal-based batteries have considerable potential as energy storage system; however, their application is extremely limited by dendrite development and poor reversibility. In this study, to overcome both challenges, F-doped carbon nanoparticles (FCNPs) are uniformly constructed on substrates (Ti, Zn, Cu, and steel) by a plasma-assisted surface modification, which endows reversible and uniform deposition of Zn metal. FCNPs with high surface charge density act as nucleation assistors and form numerous homogenous Zn nucleation sites toward Zn 3D growth, which improves Zn plating kinetic and results in uniform Zn deposition. Furthermore, the ZnF2 solid electrolyte interface generated during cycling contributes to rapid mass transfer and enhances Zn reversibility, but also suppresses the side reaction. Accordingly, the half-cell of P-Ti coupled with Zn exhibits an average Coulombic efficiency of 99.47% with 500 cycles. The symmetric cell of the P-Zn anode presents a lifespan of over 1500 h at the current density of 5 mA cm-2 . Notably, the cell works for 100 h at 50 mA cm-2 . It is believed that this ingenious surface modification broadens revolutionary methods for uniform metallic deposition, as well as the dendrite-free rechargeable batteries system.

| S-EPMC10238181 | biostudies-literature

Nanometer-thick conformal pore sealing of self-assembled mesoporous silica by plasma-assisted atomic layer deposition.

Project description:On a porous substrate, regular atomic layer deposition (ALD) not only takes place on top of the substrate but also penetrates into the internal porosity. Here we report a plasma-assisted process in which the ALD precursors are chosen to be nonreactive unless triggered by plasma, so that ALD can be spatially defined by the supply of plasma irradiation. Since plasma cannot penetrate within the internal porosity, ALD has been successfully confined to the immediate surface. This not only gives a possible solution for sealing of porous low dielectric constant films with a conformal layer of nm-scale thickness but also enables us to progressively reduce the pore size of mesoporous materials in a sub-A/cycle fashion for membrane formation.

| S-EPMC2707262 | biostudies-literature

Large-scale synthesis of uniform hexagonal boron nitride films by plasma-enhanced atomic layer deposition.

Project description:Hexagonal boron nitride (h-BN) has been previously manufactured using mechanical exfoliation and chemical vapor deposition methods, which make the large-scale synthesis of uniform h-BN very challenging. In this study, we produced highly uniform and scalable h-BN films by plasma-enhanced atomic layer deposition, which were characterized by various techniques including atomic force microscopy, transmission electron microscopy, Raman spectroscopy, and X-ray diffraction. The film composition studied by X-ray photoelectron spectroscopy and Auger electron spectroscopy corresponded to a B:N stoichiometric ratio close to 1:1, and the band-gap value (5.65?eV) obtained by electron energy loss spectroscopy was consistent with the dielectric properties. The h-BN-containing capacitors were characterized by highly uniform properties, a reasonable dielectric constant (3), and low leakage current density, while graphene on h-BN substrates exhibited enhanced electrical performance such as the high carrier mobility and neutral Dirac voltage, which resulted from the low density of charged impurities on the h-BN surface.

| S-EPMC5214515 | biostudies-literature

Tandem Si Micropillar Array Photocathodes with Conformal Copper Oxide and a Protection Layer by Pulsed Laser Deposition.

Project description:This work demonstrates the influence of high-quality protection layers on Si-Cu2O micropillar arrays created by pulsed laser deposition (PLD), with the goal to overcome photodegradation and achieve long-term operation during photoelectrochemical (PEC) water splitting. Sequentially, we assessed planar and micropillar device designs with various design parameters and their influence on PEC hydrogen evolution reaction. On the planar device substrates, a Cu2O film thickness of 600 nm and a Cu2O/CuO heterojunction layer with a 5:1 thickness ratio between Cu2O to CuO were found to be optimal. The planar Si/Cu2O/CuO heterostructure showed a higher PV performance (Jsc = 20 mA/cm2) as compared to the planar Si/Cu2O device, but micropillar devices did not show this improvement. Multifunctional overlayers of ZnO (25 nm) and TiO2 (100 nm) were employed by PLD on Si/Cu2O planar and micropillar arrays to provide a hole-selective passivation layer that acts against photocorrosion. A micropillar Si/ITO-Au/Cu2O/ZnO/TiO2/Pt stack was compared to a planar device. Under optimized conditions, the Si/Cu2O photocathode with Pt as a HER catalyst displayed a photocurrent of 7.5 mA cm-2 at 0 V vs RHE and an onset potential of 0.85 V vs RHE, with a stable operation for 75 h.

| S-EPMC6838789 | biostudies-literature

Soap-film coating: high-speed deposition of multilayer nanofilms.

Project description:The coating of thin films is applied in numerous fields and many methods are employed for the deposition of these films. Some coating techniques may deposit films at high speed; for example, ordinary printing paper is coated with micrometre-thick layers of clay at a speed of tens of meters per second. However, to coat nanometre thin films at high speed, vacuum techniques are typically required, which increases the complexity of the process. Here, we report a simple wet chemical method for the high-speed coating of films with thicknesses at the nanometre level. This soap-film coating technique is based on forcing a substrate through a soap film that contains nanomaterials. Molecules and nanomaterials can be deposited at a thickness ranging from less than a monolayer to several layers at speeds up to meters per second. We believe that the soap-film coating method is potentially important for industrial-scale nanotechnology.

| S-EPMC3600599 | biostudies-literature

MoS<sub>2</sub> /MXene Aerogel with Conformal Heterogeneous Interfaces Tailored by Atomic Layer Deposition for Tunable Microwave Absorption.

Project description:In the design of electromagnetic (EM) wave absorbing materials, it is still a great challenge to optimize the relationship between the attenuation capability and impedance matching synergistically. Herein, a 3D porous MoS2 /MXene hybrid aerogel architecture with conformal heterogeneous interface has been built by atomic layer deposition (ALD) based on specific porous templates to optimize the microwave absorption (MA) performance comprehensively. The original porous structure of pristine Ti3 C2 Tx aerogel used as templates can be preserved well during ALD fabrication, which prolongs the reflection and scattering path and ameliorates the dielectric loss. Meanwhile, plenty of heterointerfaces between MoS2 and Ti3 C2 Tx have been fabricated based on conformally ALD-deposited MoS2 with controlled thickness on the porous surfaces of the templates, which can effectively optimize the impedance matching and transform its response to EM waves from shielding into absorbing. Moreover, the interaction between the attenuation capability and impedance matching can also be modulated by the number of ALD cycle in MoS2 fabrication. After optimization, MoS2 /MXene hybrid aerogel obtained under 300 ALD cycles shows a minimum reflection loss of -61.65 dB at the thickness of 4.53 mm. In addition, its preferable lightweight, high surface area, mechanical, and hydrophobicity properties will also be conducive to further practical applications.

| S-EPMC8895119 | biostudies-literature

CO<sub>2</sub>-based atomic/molecular layer deposition of lithium ethylene carbonate thin films.

Project description:When a conventional lithium-ion battery (LIB) is cycled, a solid electrolyte interphase (SEI) forms on the surface of a negative electrode, passivating it but also depleting the capacity of the battery. Most commercial LIBs utilize a carbonate-based electrolyte, which at least temporarily leads to the formation of lithium alkyl carbonates (ROCO2Li) as the main organic SEI component. Here, we pioneer the use of atomic/molecular layer deposition (ALD/MLD) for the fabrication of lithium ethyl glycoxide (LiEG) and lithium ethylene carbonate (LiEGCO) thin films, to mimic the lithium alkyl carbonate component of the SEI. For the in situ growth of LiEGCO, we employ for the first time CO2 as an ALD/MLD precursor. The films are characterized using XRR, GIXRD, FTIR, AFM and SEM.

| S-EPMC9417553 | biostudies-literature

Biocompatible organic-inorganic hybrid materials based on nucleobases and titanium developed by molecular layer deposition.

Project description:We have constructed thin films of organic-inorganic hybrid character by combining titanium tetra-isopropoxide (TTIP) and the nucleobases thymine, uracil or adenine using the molecular layer deposition (MLD) approach. Such materials have potential as bioactive coatings, and the bioactivity of these films is described in our recent work [Momtazi, L.; Dartt, D. A.; Nilsen, O.; Eidet, J. R. J. Biomed. Mater. Res., Part A 2018, 106, 3090-3098. doi:10.1002/jbm.a.36499]. The growth was followed by in situ quartz crystal microbalance (QCM) measurements and all systems exhibited atomic layer deposition (ALD) type of growth. The adenine system has an ALD temperature window between 250 and 300 °C, while an overall reduction in growth rate with increasing temperature was observed for the uracil and thymine systems. The bonding modes of the films have been further characterized by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and X-ray diffraction, confirming the hybrid nature of the as-deposited films with an amorphous structure where partial inclusion of the TTIP molecule occurs during growth. The films are highly hydrophilic, while the nucleobases do leach in water providing an amorphous structure mainly of TiO2 with reduced density and index of refraction.

| S-EPMC6369986 | biostudies-literature

A Novel Carbon-Assisted Chemical Vapor Deposition Growth of Large-Area Uniform Monolayer MoS2 and WS2.

Project description:Monolayer MoS2 can be used for various applications such as flexible optoelectronics and electronics due to its exceptional optical and electronic properties. For these applications, large-area synthesis of high-quality monolayer MoS2 is highly desirable. However, the conventional chemical vapor deposition (CVD) method using MoO3 and S powder has shown limitations in synthesizing high-quality monolayer MoS2 over a large area on a substrate. In this study, we present a novel carbon cloth-assisted CVD method for large-area uniform synthesis of high-quality monolayer MoS2. While the conventional CVD method produces thick MoS2 films in the center of the substrate and forms MoS2 monolayers at the edge of the thick MoS2 films, our carbon cloth-assisted CVD method uniformly grows high-quality monolayer MoS2 in the center of the substrate. The as-synthesized monolayer MoS2 was characterized in detail by Raman/photoluminescence spectroscopy, atomic force microscopy, and transmission electron microscopy. We reveal the growth process of monolayer MoS2 initiated from MoS2 seeds by synthesizing monolayer MoS2 with varying reaction times. In addition, we show that the CVD method employing carbon powder also produces uniform monolayer MoS2 without forming thick MoS2 films in the center of the substrate. This confirms that the large-area growth of monolayer MoS2 using the carbon cloth-assisted CVD method is mainly due to reducing properties of the carbon material, rather than the effect of covering the carbon cloth. Furthermore, we demonstrate that our carbon cloth-assisted CVD method is generally applicable to large-area uniform synthesis of other monolayer transition metal dichalcogenides, including monolayer WS2.

| S-EPMC8468553 | biostudies-literature

Atomic/molecular layer deposition of europium-organic thin films on nanoplasmonic structures towards FRET-based applications.

Project description:We present a novel atomic/molecular layer deposition (ALD/MLD) process for europium-organic thin films based on Eu(thd)3 and 2-hydroxyquinoline-4-carboxylic acid (HQA) precursors. The process yields with appreciably high growth rate luminescent Eu-HQA thin films in which the organic HQA component acts as a sensitizer for the red Eu3+ luminescence, extending the excitation wavelength range up to ca. 400 nm. We moreover deposit these films on nanoplasmonic structures to achieve a twentyfold enhanced emission intensity. Finally, we demonstrate the FRET-type energy transfer process for our Eu-HQA coated nanoplasmonic structures in combination with commercial Alexa647 fluorophor, underlining their potential towards novel bioimaging applications.

| S-EPMC10551872 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data