Microstructure and Mechanical Behavior of Porous Ti-6Al-4V Processed by Spherical Powder Sintering.

ABSTRACT: Reducing the stiffness of titanium is an important issue to improve the behavior of this material when working together with bone, which can be achieved by generating a porous structure. The aim of this research was to analyze the porosity and mechanical behavior of Ti-6Al-4V porous samples developed by spherical powder sintering. Four different microsphere sizes were sintered at temperatures ranging from 1300 to 1400 °C for 2, 4 and 8 h. An open, interconnected porosity was obtained, with mean pore sizes ranging from 54.6 to 140 µm. The stiffness of the samples diminished by as much as 40% when compared to that of solid material and the mechanical properties were affected mainly by powder particles size. Bending strengths ranging from 48 to 320 MPa and compressive strengths from 51 to 255 MPa were obtained.

SUBMITTER: Reig L

PROVIDER: S-EPMC5452833 | biostudies-other | 2013 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Chemical analysis on laser processed Ultrahydrophobic Ti-6Al-4V surface by high vacuum Process.

Project description:A technique has been developed for fabrication of ultrahydrophobic Ti-6Al-4V surface by vacuum process. This report has the data related to the article "Hybrid laser and vacuum process for rapid ultrahydrophobic Ti-6Al-4 V surface formation" on the fabrication of ultrahydrophobic Ti-6Al-4V by Vacuum process (Jagdheesh et al., 2019). The present data consist of X-ray photo electron spectroscopy spectrums recorded for the laser patterned ultrahydrophobic samples, droplet image and surface chemical composition of laser patterned Ti-6Al-4V samples before vacuum process(b. v. p.) and after vacuum process (a. v. p.) for 120 min. The presented data give a clear idea about the chemical modification evolved during the vacuum process.

| S-EPMC6355998 | biostudies-literature

Effect of powder oxidation on the impact toughness of electron beam melt Ti-6Al-4V.

Project description:Powder quality in additive manufacturing (AM) electron beam melt (EBM) of Ti-6Al-4V components is crucial in determining the critical material properties of the end item. In this study, we report on the effect of powder oxidation on the Charpy impact energy of Ti-6Al-4V parts manufactured using EBM. In addition to oxidation, the effects on impact energy due to hot isostatic pressing (HIP), specimen orientation, and EBM process defects were also investigated. This research has shown that excessive powder oxidation (oxygen mass fraction above 0.25 % and up to 0.46 %) dramatically decreases the impact energy. It was determined that the room temperature impact energy of the parts after excessive oxidation was reduced by about seven times. We also report that HIP post-processing significantly increases the impact toughness, especially for specimens with lower or normal oxygen content. The specimen orientation effect was found to be more significant for low oxidation levels.

| S-EPMC10941301 | biostudies-literature

Surface chemistry in Ti-6Al-4V feedstock as influenced by powder reuse in electron beam additive manufacturing

Project description:X-ray photoelectron spectroscopy (XPS) as well as scanning and transmission electron microscopy (SEM/TEM) analysis was carried out on four Ti-6Al-4V powders used in electron beam powder-bed fusion (PBF-EB) production environments: virgin low oxygen (0.080 wt% O), reused medium oxygen (0.140 wt% O), reused high oxygen (0.186 wt% O), and virgin high oxygen (0.180 wt% O). The two objectives of this comparative analyses were to (1) investigate high oxygen containing Grade 23 Ti-6Al-4V powders which were further oxidized as a function of reuse and (2) comparing the two virgin Grade 23 and Grade 5 powders of similar oxygen content. The microstructure of the low oxygen virgin Grade 23 powder was consistent with martensitic α′ microstructure, whereas the reused powder displayed tempered α/β Widmänstatten microstructure. XPS revealed a decrease in TiO2 at the surface of the reused powders with an increase in Al2O3. This trend is energetically favorable at the temperatures and pressures in PBF-EB machines, and it is consistent with the thermodynamics of Al2O3 vs. TiO2 reactions. An unexpected amount of nitrogen was measured on the titanium powder, with a general increase in nitride on the surface of the particles as a function of reuse in the Grade 23 powder.1

| S-EPMC9901169 | biostudies-literature

Data on the influence of TiN on wear and corrosion behavior of Ti-6Al-4V alloy fabricated through spark plasma sintering.

Project description:Data about bulk properties of Ti-6Al-4V based composites specimen achieved by powder metallurgy route using spark plasma sintering (SPS) technique is presented, with focus on the effect of TiN particles on wear and corrosion behavior of the resultant composites. Two microsized kind of powders are combined; Ti-6Al-4V and TiN. The powder mixing and SPS processing has been enhanced and consolidated.

| S-EPMC6141763 | biostudies-literature

Sintering Mechanism, Microstructure Evolution, and Mechanical Properties of Ti-Added Mo2FeB2-Based Cermets.

Project description:Four series of Mo2FeB2-based cermets with Ti contents between 0 wt.% and 1.5 wt.% in 0.5 wt.% increments were prepared by in situ reaction and liquid phase sintering technology. Influences of Ti on microstructure and mechanical properties of cermets were studied. It was found that Ti addition increases formation temperatures of liquid phases in liquid-phase stage. Ti atoms replace a fraction of Mo atoms in Mo2FeB2 and the solution of Ti atoms causes the Mo2FeB2 crystal to be equiaxed. In addition, the cermets with 1.0 wt.% Ti content exhibit the smallest particle size. The solution of Ti atoms in Mo2FeB2 promotes the transformation of Mo2FeB2 particles from elongated shape to equiaxed shape. With Ti content increasing from 0 wt.% to 1.5 wt.%, the hardness and transverse rupture strength (TRS) first increase and then decrease. The maximum hardness and TRS occur with 1.0 wt.% Ti content. However, the fracture toughness decreases as Ti content increases. The cermets with 1.0 wt.% Ti content show excellent comprehensive mechanical properties, and the hardness, fracture toughness, and TRS are HRA 89.5, 12.9 MPa?m1/2, and 1612.6 MPa, respectively.

| S-EPMC7215874 | biostudies-literature

Pandora's Box-Influence of Contour Parameters on Roughness and Subsurface Residual Stresses in Laser Powder Bed Fusion of Ti-6Al-4V.

Project description:The contour scan strategies in laser powder bed fusion (LPBF) of Ti-6Al-4V were studied at the coupon level. These scan strategies determined the surface qualities and subsurface residual stresses. The correlations to these properties were identified for an optimization of the LPBF processing. The surface roughness and the residual stresses in build direction were linked: combining high laser power and high scan velocities with at least two contour lines substantially reduced the surface roughness, expressed by the arithmetic mean height, from values as high as 30 µm to 13 µm, while the residual stresses rose from ~340 to about 800 MPa. At this stress level, manufactured rocket fuel injector components evidenced macroscopic cracking. A scan strategy completing the contour region at 100 W and 1050 mm/s is recommended as a compromise between residual stresses (625 MPa) and surface quality (14.2 µm). The LPBF builds were monitored with an in-line twin-photodiode-based melt pool monitoring (MPM) system, which revealed a correlation between the intensity quotient I2/I1, the surface roughness, and the residual stresses. Thus, this MPM system can provide a predictive estimate of the surface quality of the samples and resulting residual stresses in the material generated during LPBF.

| S-EPMC7436019 | biostudies-literature

Wire-Based Additive Manufacturing of Ti-6Al-4V Using Electron Beam Technique.

Project description:Electron beam freeform fabrication is a wire feed direct energy deposition additive manufacturing process, where the vacuum condition ensures excellent shielding against the atmosphere and enables processing of highly reactive materials. In this work, this technique is applied for the α + β-titanium alloy Ti-6Al-4V to determine suitable process parameter for robust building. The correlation between dimensions and the dilution of single beads based on selected process parameters, leads to an overlapping distance in the range of 70%-75% of the bead width, resulting in a multi-bead layer with a uniform height and with a linear build-up rate. Moreover, the stacking of layers with different numbers of tracks using an alternating symmetric welding sequence allows the manufacturing of simple structures like walls and blocks. Microscopy investigations reveal that the primary structure consists of epitaxial grown columnar prior β-grains, with some randomly scattered macro and micropores. The developed microstructure consists of a mixture of martensitic and finer α-lamellar structure with a moderate and uniform hardness of 334 HV, an ultimate tensile strength of 953 MPa and rather low fracture elongation of 4.5%. A subsequent stress relief heat treatment leads to a uniform hardness distribution and an extended fracture elongation of 9.5%, with a decrease of the ultimate strength to 881 MPa due to the fine α-lamellar structure produced during the heat treatment. Residual stresses measured by energy dispersive X-ray diffraction shows after deposition 200-450 MPa in tension in the longitudinal direction, while the stresses reach almost zero when the stress relief treatment is carried out.

| S-EPMC7435555 | biostudies-literature

Impact of surface and pore characteristics on fatigue life of laser powder bed fusion Ti-6Al-4V alloy described by neural network models.

Project description:In this study, the effects of surface roughness and pore characteristics on fatigue lives of laser powder bed fusion (LPBF) Ti-6Al-4V parts were investigated. The 197 fatigue bars were printed using the same laser power but with varied scanning speeds. These actions led to variations in the geometries of microscale pores, and such variations were characterized using micro-computed tomography. To generate differences in surface roughness in fatigue bars, half of the samples were grit-blasted and the other half were machined. Fatigue behaviors were analyzed with respect to surface roughness and statistics of the pores. For the grit-blasted samples, the contour laser scan in the LPBF strategy led to a pore-depletion zone isolating surface and internal pores with different features. For the machined samples, where surface pores resemble internal pores, the fatigue life was highly correlated with the average pore size and projected pore area in the plane perpendicular to the stress direction. Finally, a machine learning model using a drop-out neural network (DONN) was employed to establish a link between surface and pore features to the fatigue data (logN), and good prediction accuracy was demonstrated. Besides predicting fatigue lives, the DONN can also estimate the prediction uncertainty.

| S-EPMC8516886 | biostudies-literature

Understanding the hot isostatic pressing effectiveness of laser powder bed fusion Ti-6Al-4V by in-situ X-ray imaging and diffraction experiments.

Project description:In the present study, in-situ observation of Hot Isostatic Pressure (HIP) procedure of laser powder bed fusion manufactured Ti-6Al-4V parts was performed to quantitatively estimate the densification rate of the material and the influence of the defect initial size and shape on such rate. The observations were performed in-situ using the Ultrafast Tomography Paris-Edinburgh Cell and the combination of fast phase-contrast synchrotron X-ray tomography and energy dispersive diffraction. With this strategy, we could quantify how the effectiveness of HIP depends on the characteristics of a defect. Smaller defects showed a higher densification rate, while the defect shape did not have significant effect on such rate.

| S-EPMC10611763 | biostudies-literature

Notch Corrosion Fatigue Behavior of Ti-6Al-4V.

Project description:The aim of this paper is to map the corrosion fatigue characteristics of Ti-6Al-4V alloy through the evaluation of the corrosion fatigue initiation and failure mechanisms. The study included the effect of the stress concentration factor at very high Kt values and the role of different inert or corrosive environments. This alloy is widely used in naval-structures and aero-engine communities and the outcomes of the work will have direct relevance to industrial service operations. Axial fatigue tests (R = 0.1; 2 × 10⁵ cycles; f = 10 Hz) were carried out on smooth and high notched (Ktmax = 18.65) flat specimens in laboratory air, paraffin oil, laboratory air + beeswax coating, recirculated 3.5% NaCl solution. The step loading procedure was used to perform the fatigue tests and the surface replica method and crack propagation gages were used to check crack nucleation and propagation until failure. Log-Log plots of σmaxvs.Kt showed a bilinear behavior and enabled the demonstration of the presence of a threshold stress intensity factor (Kt = 8-9), after which the environment has no effect on the fatigue damage for all the tested environments.

| S-EPMC5455940 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data