Mechanical and Microstructural Evaluations of Lightweight Aggregate Geopolymer Concrete before and after Exposed to Elevated Temperatures.

ABSTRACT: This paper presents the mechanical and microstructural characteristics of a lightweight aggregate geopolymer concrete (LWAGC) synthesized by the alkali-activation of a fly ash source (FA) before and after being exposed to elevated temperatures, ranging from 100 to 800 °C. The results show that the LWAGC unexposed to the elevated temperatures possesses a good strength-to-weight ratio compared with other LWAGCs available in the published literature. The unexposed LWAGC also shows an excellent strength development versus aging times, up to 365 days. For the exposed LWAGC to the elevated temperatures of 100 to 800 °C, the results illustrate that the concretes gain compressive strength after being exposed to elevated temperatures of 100, 200 and 300 °C. Afterward, the strength of the LWAGC started to deteriorate and decrease after being exposed to elevated temperatures of 400 °C, and up to 800 °C. Based on the mechanical strength results of the exposed LWAGCs to elevated temperatures of 100 °C to 800 °C, the relationship between the exposure temperature and the obtained residual compressive strength is statistically analyzed and achieved. In addition, the microstructure investigation of the unexposed LWAGC shows a good bonding between aggregate and mortar at the interface transition zone (ITZ). However, this bonding is subjected to deterioration as the LWAGC is exposed to elevated temperatures of 400, 600 and 800 °C by increasing the microcrack content and swelling of the unreacted silicates.

SUBMITTER: Abdulkareem OA

PROVIDER: S-EPMC5452862 | biostudies-other | 2013 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Mechanical Properties of Chopped Basalt Fiber-Reinforced Lightweight Aggregate Concrete and Chopped Polyacrylonitrile Fiber Reinforced Lightweight Aggregate Concrete.

Project description:In this study, an experimental investigation was conducted on the mechanical properties of lightweight aggregate concrete (LWAC) with different chopped fibers, including basalt fiber (BF) and polyacrylonitrile fiber (PANF). The LWAC performance was studied in regard to compressive strength, splitting tensile strength and shear strength at age of 28 days. In addition, the oven-dried density and water absorption were measured as well to confirm whether the specimens match the requirement of standard. In total, seven different mixture groups were designed and approximately 104 LWAC samples were tested. The test results showed that the oven-dried densities of the LWAC mixtures were in range of 1.819-1.844 t/m3 which satisfied the definition of LWAC by Chinese Standard. Additionally, water absorption decreased with the increasing of fiber content. The development tendency of the specific strength of LWAC was the same as that of the cube compressive strength. The addition of fibers had a significant effect on reducing water absorption. Adding BF and PANF into concrete had a relatively slight impact on the compressive strength but had an obvious effect on splitting tensile strength, flexural strength and shear strength enhancement, respectively. In that regard, a 1.5% fiber volume fraction of BF and PANF showed the maximum increase in strength. The use of BF and PANF could change the failure morphologies of splitting tensile and flexural destruction but almost had slight impact on the shear failure morphology. The strength enhancement parameter ? was proposed to quantify the improvement effect of fibers on cube compressive strength, splitting tensile strength, flexural strength and shear strength, respectively. And the calculation results showed good agreement with test value.

| S-EPMC7178649 | biostudies-literature

Properties of Lightweight Aggregate Concrete Reinforced with Carbon and/or Polypropylene Fibers.

Project description:The impact of carbon and polypropylene fibers in both single and hybrid forms on the properties of lightweight aggregate concrete (LWAC), including the slump, density, segregation resistance, compressive strength, splitting tensile strength, flexural strength, and compressive stress-strain behavior, were experimentally investigated. The toughness ratio and ductility index were introduced for quantitatively evaluating the energy-absorbing capacity and post-peak ductility. A positive synergistic effect of hybrid carbon and polypropylene fibers was obtained in terms of higher tensile strength, toughness, and ductility. The toughness ratio and ductility index of hybrid fiber-reinforced LWAC were increased by 26%-37% and 12%-27% compared with plain LWAC, respectively. The fiber in both single and hybrid forms had a smaller effect on the linearity ascending branch of the stress-strain curves, whereas the post-peak patterns in terms of the toughness and ductility for the hybrid fiber-reinforced LWAC were significantly improved when the fiber in hybrid form.

| S-EPMC7041369 | biostudies-literature

Effect of Aggregate Size on Strength Characteristics of High Strength Lightweight Concrete.

Project description:Effects of aggregate size on the mechanical properties of lightweight concrete (LC) were investigated. Four gradings of lightweight aggregate (LWA) were designed and used to prepare the specimens for compressive strength, splitting tensile strength, and flexural strength tests. An estimating method for compressive strength of LC was then established. The compressive strength of tested LC was up to 95 MPa at 90-day curing time. The test results suggested that the absence of medium-size particles decreased the compaction of LC, therefore the density and compressive strength were negatively affected. Specimens having single size of aggregate showed lower splitting tensile and flexural strengths than that having three sizes of LWA. The parameters of the estimating model were determined according to the test results, and the compressive strength predictions of estimation model were compared with the results from other literature.

| S-EPMC7143055 | biostudies-literature

A New Composite Slab Using Crushed Waste Tires as Fine Aggregate in Self-Compacting Lightweight Aggregate Concrete.

Project description:A composite slab comprised of self-compacting rubber lightweight aggregate concrete (SCRLC) and profiled steel sheeting is a new type of structural element with a series of superior properties. This paper presents an experimental research and finite element analysis (FEA) of the flexural behavior of composite slabs consisting of SCRLC to develop a new floor system. Four composite slabs specimens with different shear spans (450 mm and 800 mm) and SCRLC (0% and 30% in rubber particles substitution ratio) are prepared, and the flexural properties including failure modes, deflection at mid-span, profiled steel sheeting, and concrete surface stain at mid-span and end slippage are investigated by four-point bending tests. The experimental results indicate that applying SCRLC30 in composites slabs will improve the anti-cracking ability under the loading of composite slabs compared with composite slabs consisting of self-compacting lightweight aggregate concrete (SCLC). FEM on the flexural properties of SCRLC composites slabs show that the yield load, ultimate load, and deflection corresponding to the yield load and the ultimate load of composite slabs drop as the rubber particles content increases in SCRLC. The variation of SCRLC strength has less impact on the flexural bearing capacity of corresponding composite slabs. Based on the traditional calculated method of the ultimate bending moment of normal concrete (NC) composite slabs, a modified calculated method for the ultimate bending moment of SCRLC composite slabs is proposed.

| S-EPMC7321477 | biostudies-literature

Size Effect in Compressive Strength Tests of Cored Specimens of Lightweight Aggregate Concrete.

Project description:The aim of this paper is to discuss the unrecognized problem of the scale effect in compressive strength tests determined for cored specimens of lightweight aggregate concrete (LWAC) against the background of available data on the effect for normal-weight concrete (NWAC). The scale effect was analyzed taking into consideration the influence of slenderness (? = 1.0, 1.5, 2.0) and diameter (d = 80, 100, 125, and 150 mm) of cored specimens, as well as the type of lightweight aggregate (expanded clay and sintered fly ash) and the type of cement matrix (w/c = 0.55 and 0.37). The analysis of the results for four lightweight aggregate concretes revealed no scale effect in compressive strength tests determined on cored specimens. Neither the slenderness, nor the core diameter seemed to affect the strength results. This fact should be explained by the considerably better structural homogeneity of the tested lightweight concretes in comparison to normal-weight ones. Nevertheless, there were clear differences between the results obtained on molded and cored specimens of the same shape and size.

| S-EPMC7085069 | biostudies-literature

Mechanical and Physical Properties of Hydrophobized Lightweight Aggregate Concrete with Sewage Sludge.

Project description:This article is focused on lightweight aggregate-concrete modified by municipal sewage sludge and lightweight aggregate-concrete obtained from light aggregates. The article presents laboratory examinations of material physical parameters. Water absorptivity of the examined material was decreased by the admixture of water emulsion of reactive polysiloxanes. Water transport properties were determined using Time Domain Reflectometry, an indirect technique for moisture detection in porous media. Together with basic physical parameters, the heat conductivity coefficient λ was determined for both types of lightweight aggregate-concrete. Analysis of moisture and heat properties of the examined materials confirmed the usefulness of light aggregates supplemented with sewage sludge for prospective production.

| S-EPMC5503055 | biostudies-other

Fracture Properties of Polystyrene Aggregate Concrete after Exposure to High Temperatures.

Project description:This paper mainly reports an experimental investigation on the residual mechanical and fracture properties of polystyrene aggregate concrete (PAC) after exposure to high temperatures up to 800 degrees Celsius. The fracture properties namely, the critical stress intensity factor ( K I C S ), the critical crack tip opening displacement (CTODC) for the Two-Parameter Model, and the fracture energy (GF) for the Fictitious Crack Model were examined using the three-point bending notched beam test, according to the RILEM recommendations. The effects of polystyrene aggregate (PA) content and temperature levels on the fracture and mechanical properties of concrete were investigated. The results showed that the mechanical properties of PAC significantly decreased with increase in temperature level and the extent of which depended on the PA content in the mixture. However, at a very high temperature of 800 °C, all samples showed 80 percent reduction in modulus of elasticity compared to room temperature, regardless of the level of PA content. Fracture properties of control concrete (C) and PAC were influenced by temperature in a similar manner. Increasing temperature from 25 °C to 500 °C caused almost 50% reduction of the fracture energy for all samples while 30% increase in fracture energy was occurred when the temperature increased from 500 °C to 800 °C. It was found that adding more PA content in the mixture lead to a more ductile behaviour of concrete.

| S-EPMC5509076 | biostudies-other

Axial Compressive Behavior of Geopolymer Recycled Lump Concrete.

Project description:To reduce the environmental pollution from cement production and the damage to natural resources from aggregate mining in the concrete industry, a relatively new concrete, termed geopolymer recycled lump concrete (GRLC), which uses geopolymer as the binding material to replace traditional cement and uses large demolished concrete lumps (DCLs) to partly replace concrete, is prepared in this study. Cubic and cylindrical GRLC specimens containing fresh geopolymer concrete and DCLs were tested under axial compression with various parameters, including the compressive strength levels of both fresh geopolymer concrete and DCLs, and the replacement ratio of DCLs. The compressive behavior of the GRLC specimens was compared with traditional cement recycled lump concrete (CRLC) specimens, with test results showing that GRLC specimens possess higher compressive strength than CRLC specimens under the same experimental conditions, which is due to the strengthening effect that fresh geopolymer concrete has on the DCLs. From the scanning electron microscope pattern of the GRLC specimen, it is found that the geopolymer bonds well with the old mortar attached to DCLs. As the replacement ratio increases from 0% to 33%, the elastic modulus of GRLC increases by 5%-11% but Poisson's ratio remains almost constant (in the 0.16-0.17 range). Based on the measured strength and the predicted results, which coincide with one another well, a modified method for predicting the compressive strength of GRLC cubic and cylindrical specimens is proposed.

| S-EPMC7040574 | biostudies-literature

Creep Behavior of High-Strength Concrete Subjected to Elevated Temperatures.

Project description:Strain is generated in concrete subjected to elevated temperatures owing to the influence of factors such as thermal expansion and design load. Such strains resulting from elevated temperatures and load can significantly influence the stability of a structure during and after a fire. In addition, the lower the water-to-binder (W-B) ratio and the smaller the quantity of aggregates in high-strength concrete, the more likely it is for unstable strain to occur. Hence, in this study, the compressive strength, elastic modulus, and creep behavior were evaluated at target temperatures of 100, 200, 300, 500, and 800 °C for high-strength concretes with W-B ratios of 30%, 26%, and 23%. The loading conditions were set as non-loading and 0.33fcu. It was found that as the compressive strength of the concrete increased, the mechanical characteristics deteriorated and transient creep increased. Furthermore, when the point at which creep strain occurred at elevated temperatures after the occurrence of transient creep was considered, greater shrinkage strain occurred as the compressive strength of the concrete increased. At a heating temperature of 800 °C, the 80 and 100 MPa test specimens showed creep failure within a shrinkage strain range similar to the strain at the maximum load.

| S-EPMC5551824 | biostudies-other

Lightweight Concrete-From Basics to Innovations.

Project description:Lightweight concrete has a history of more than two-thousand years and its technical development is still proceeding. This review starts with a retrospective that gives an idea of the wide range of applications covered by lightweight concrete during the last century. Although lightweight concrete is well known and has proven its technical potential in a wide range of applications over the past decades, there are still hesitations and uncertainties in practice. For that reason, lightweight aggregate properties and the various types of lightweight concrete are discussed in detail with a special focus on current standards. The review is based on a background of 25 years of practical and theoretical experience in this field. One of the main challenges in designing lightweight concrete is to adapt most of design, production and execution rules since they often deviate from normal weight concrete. Therefore, aspects are highlighted that often are the cause of misunderstandings, such as nomenclature or the informational value of certain tests. Frequently occurring problems regarding the mix design and production of lightweight concrete are addressed and the unintended consequences are described. A critical view is provided on some information given in existing European concrete standards regarding the mechanical properties of structural lightweight concrete. Finally, the latest stage of development of very light lightweight concretes is presented. Infra-lightweight concrete is introduced as an innovative approach for further extending the range of applications of lightweight concrete by providing background knowledge and experiences from case records.

| S-EPMC7084983 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data