Mechanical and Physical Properties of Hydrophobized Lightweight Aggregate Concrete with Sewage Sludge.
Ontology highlight
ABSTRACT:
SUBMITTER: Suchorab Z
PROVIDER: S-EPMC5503055 | biostudies-other | 2016 Apr
REPOSITORIES: biostudies-other
Similar Datasets
Project description:In this study, an experimental investigation was conducted on the mechanical properties of lightweight aggregate concrete (LWAC) with different chopped fibers, including basalt fiber (BF) and polyacrylonitrile fiber (PANF). The LWAC performance was studied in regard to compressive strength, splitting tensile strength and shear strength at age of 28 days. In addition, the oven-dried density and water absorption were measured as well to confirm whether the specimens match the requirement of standard. In total, seven different mixture groups were designed and approximately 104 LWAC samples were tested. The test results showed that the oven-dried densities of the LWAC mixtures were in range of 1.819-1.844 t/m3 which satisfied the definition of LWAC by Chinese Standard. Additionally, water absorption decreased with the increasing of fiber content. The development tendency of the specific strength of LWAC was the same as that of the cube compressive strength. The addition of fibers had a significant effect on reducing water absorption. Adding BF and PANF into concrete had a relatively slight impact on the compressive strength but had an obvious effect on splitting tensile strength, flexural strength and shear strength enhancement, respectively. In that regard, a 1.5% fiber volume fraction of BF and PANF showed the maximum increase in strength. The use of BF and PANF could change the failure morphologies of splitting tensile and flexural destruction but almost had slight impact on the shear failure morphology. The strength enhancement parameter ? was proposed to quantify the improvement effect of fibers on cube compressive strength, splitting tensile strength, flexural strength and shear strength, respectively. And the calculation results showed good agreement with test value.
| S-EPMC7178649 | biostudies-literature
Project description:The impact of carbon and polypropylene fibers in both single and hybrid forms on the properties of lightweight aggregate concrete (LWAC), including the slump, density, segregation resistance, compressive strength, splitting tensile strength, flexural strength, and compressive stress-strain behavior, were experimentally investigated. The toughness ratio and ductility index were introduced for quantitatively evaluating the energy-absorbing capacity and post-peak ductility. A positive synergistic effect of hybrid carbon and polypropylene fibers was obtained in terms of higher tensile strength, toughness, and ductility. The toughness ratio and ductility index of hybrid fiber-reinforced LWAC were increased by 26%-37% and 12%-27% compared with plain LWAC, respectively. The fiber in both single and hybrid forms had a smaller effect on the linearity ascending branch of the stress-strain curves, whereas the post-peak patterns in terms of the toughness and ductility for the hybrid fiber-reinforced LWAC were significantly improved when the fiber in hybrid form.
| S-EPMC7041369 | biostudies-literature
Project description:Effects of aggregate size on the mechanical properties of lightweight concrete (LC) were investigated. Four gradings of lightweight aggregate (LWA) were designed and used to prepare the specimens for compressive strength, splitting tensile strength, and flexural strength tests. An estimating method for compressive strength of LC was then established. The compressive strength of tested LC was up to 95 MPa at 90-day curing time. The test results suggested that the absence of medium-size particles decreased the compaction of LC, therefore the density and compressive strength were negatively affected. Specimens having single size of aggregate showed lower splitting tensile and flexural strengths than that having three sizes of LWA. The parameters of the estimating model were determined according to the test results, and the compressive strength predictions of estimation model were compared with the results from other literature.
| S-EPMC7143055 | biostudies-literature
Project description:A composite slab comprised of self-compacting rubber lightweight aggregate concrete (SCRLC) and profiled steel sheeting is a new type of structural element with a series of superior properties. This paper presents an experimental research and finite element analysis (FEA) of the flexural behavior of composite slabs consisting of SCRLC to develop a new floor system. Four composite slabs specimens with different shear spans (450 mm and 800 mm) and SCRLC (0% and 30% in rubber particles substitution ratio) are prepared, and the flexural properties including failure modes, deflection at mid-span, profiled steel sheeting, and concrete surface stain at mid-span and end slippage are investigated by four-point bending tests. The experimental results indicate that applying SCRLC30 in composites slabs will improve the anti-cracking ability under the loading of composite slabs compared with composite slabs consisting of self-compacting lightweight aggregate concrete (SCLC). FEM on the flexural properties of SCRLC composites slabs show that the yield load, ultimate load, and deflection corresponding to the yield load and the ultimate load of composite slabs drop as the rubber particles content increases in SCRLC. The variation of SCRLC strength has less impact on the flexural bearing capacity of corresponding composite slabs. Based on the traditional calculated method of the ultimate bending moment of normal concrete (NC) composite slabs, a modified calculated method for the ultimate bending moment of SCRLC composite slabs is proposed.
| S-EPMC7321477 | biostudies-literature
Project description:Sewage sludge is a high-volume and low-cost waste commonly generated worldwide, so its utilization is a vital issue. The application of this waste in the manufacturing of lightweight aggregates was investigated. The process was performed using intensive mixers with volumes of 5 and 30 L, as well as the industrial 500 L mixer. Then, granulates were sintered in a tube furnace. The influence of composition and mixer size on the particle size, microstructure, mechanical performance, and stability of lightweight aggregates in different environments was analyzed. The best results were obtained for a 500 L mixer, enhancing the industrial potential of the presented process. Increasing the share of sewage sludge in the composition of aggregates enhanced their porosity and reduced the specific weight, which caused a drop in compressive strength. Nevertheless, for all analyzed materials, the mechanical performance was superior compared to many commercial products. Therefore, sewage sludge can be efficiently applied as a raw material for the manufacturing of lightweight aggregates. The presented results confirm that a proper adjustment of composition allows easy the tailoring of aggregates' performance and cost.
| S-EPMC7764059 | biostudies-literature
Project description:The aim of this paper is to discuss the unrecognized problem of the scale effect in compressive strength tests determined for cored specimens of lightweight aggregate concrete (LWAC) against the background of available data on the effect for normal-weight concrete (NWAC). The scale effect was analyzed taking into consideration the influence of slenderness (? = 1.0, 1.5, 2.0) and diameter (d = 80, 100, 125, and 150 mm) of cored specimens, as well as the type of lightweight aggregate (expanded clay and sintered fly ash) and the type of cement matrix (w/c = 0.55 and 0.37). The analysis of the results for four lightweight aggregate concretes revealed no scale effect in compressive strength tests determined on cored specimens. Neither the slenderness, nor the core diameter seemed to affect the strength results. This fact should be explained by the considerably better structural homogeneity of the tested lightweight concretes in comparison to normal-weight ones. Nevertheless, there were clear differences between the results obtained on molded and cored specimens of the same shape and size.
| S-EPMC7085069 | biostudies-literature
Project description:This paper presents the mechanical and microstructural characteristics of a lightweight aggregate geopolymer concrete (LWAGC) synthesized by the alkali-activation of a fly ash source (FA) before and after being exposed to elevated temperatures, ranging from 100 to 800 °C. The results show that the LWAGC unexposed to the elevated temperatures possesses a good strength-to-weight ratio compared with other LWAGCs available in the published literature. The unexposed LWAGC also shows an excellent strength development versus aging times, up to 365 days. For the exposed LWAGC to the elevated temperatures of 100 to 800 °C, the results illustrate that the concretes gain compressive strength after being exposed to elevated temperatures of 100, 200 and 300 °C. Afterward, the strength of the LWAGC started to deteriorate and decrease after being exposed to elevated temperatures of 400 °C, and up to 800 °C. Based on the mechanical strength results of the exposed LWAGCs to elevated temperatures of 100 °C to 800 °C, the relationship between the exposure temperature and the obtained residual compressive strength is statistically analyzed and achieved. In addition, the microstructure investigation of the unexposed LWAGC shows a good bonding between aggregate and mortar at the interface transition zone (ITZ). However, this bonding is subjected to deterioration as the LWAGC is exposed to elevated temperatures of 400, 600 and 800 °C by increasing the microcrack content and swelling of the unreacted silicates.
| S-EPMC5452862 | biostudies-other
Project description:This research aims at clarifying the influence of the granulometry of expanded perlite, on the thermal conductivity, structural strength, density, and water absorption of lightweight mortars. Three original perlite gradations have been obtained and three pairs of twin test mortars have been tested with those gradations. SEM tests have also been run to clarify the interaction, at a microscopic level, between the expanded perlite and the cement grouting. The results indicate that the mere manipulation of the granulometry may have a considerable and very beneficial effect on the mixture's properties, such as thermal conductivity and water absorption.
| S-EPMC6926826 | biostudies-literature
Project description:The sustainable development of construction materials is an essential aspect of current worldwide trends. Reusing post-production waste in the building industry has numerous positive effects on the environment. Since concrete is one of the materials that people manufacture and use the most, it will continue to be an integral element of the surrounding reality. In this study, the relationship between the individual components and parameters of concrete and its compressive strength properties was assessed. In the experimental works, concrete mixes with different contents of sand, gravel, Portland cement CEM II/B-S 42.5 N, water, superplasticizer, air-entraining admixture, and fly ash from the thermal conversion of municipal sewage sludge (SSFA) were designed. According to legal requirements in the European Union, SSFA waste from the sewage sludge incineration process in a fluidized bed furnace should not be stored in landfills but processed in various ways. Unfortunately, its generated amounts are too large, so new management technologies should be sought. During the experimental work, the compressive strength of concrete samples of various classes, namely, C8/10, C12/15, C16/20, C20/25, C25/30, C30/37, and C35/45, were measured. The higher-class concrete samples that were used, the greater the compressive strength obtained, ranging from 13.7 to 55.2 MPa. A correlation analysis was carried out between the mechanical strength of waste-modified concretes and the composition of concrete mixes (the amount of sand and gravel, cement, and FA), as well as the water-to-cement ratio and the sand point. No negative effect of the addition of SSFA on the strength of concrete samples was demonstrated, which translates into economic and environmental benefits.
| S-EPMC10254342 | biostudies-literature
Project description:Currently, one of the topical areas of application of artificial intelligence methods in industrial production is neural networks, which allow for predicting the performance properties of products and structures that depend on the characteristics of the initial components and process parameters. The purpose of the study was to develop and train a neural network and an ensemble model to predict the mechanical properties of lightweight fiber-reinforced concrete using the accumulated empirical database and data from construction industry enterprises, and to improve production processes in the construction industry. The study applied deep learning and an ensemble of regression trees. The empirical base is the result of testing a series of experimental compositions of fiber-reinforced concrete. The predicted properties are cubic compressive strength, prismatic compressive strength, flexural tensile strength, and axial tensile strength. The quantitative picture of the accuracy of the applied methods for strength characteristics varies for the deep neural network method from 0.15 to 0.73 (MAE), from 0.17 to 0.89 (RMSE), and from 0.98% to 6.62% (MAPE), and for the ensemble of regression trees, from 0.11 to 0.62 (MAE), from 0.15 to 0.80 (RMSE), and from 1.30% to 3.4% (MAPE). Both methods have shown high efficiency in relation to such a hard-to-predict material as concrete, which is so heterogeneous in structure and depends on many factors. The value of the developed models lies in the possibility of obtaining additional useful information in the process of preparing highly functional lightweight fiber-reinforced concrete without additional experiments.
| S-EPMC9573277 | biostudies-literature