Mechanical Properties and Durability of CNT Cement Composites.
Ontology highlight
ABSTRACT:
SUBMITTER: Del Carmen Camacho M
PROVIDER: S-EPMC5453286 | biostudies-other | 2014 Feb
REPOSITORIES: biostudies-other
Similar Datasets
Project description:High-performance fiber-reinforced cement composites (HPFRCCs) have been widely used in structural engineering due to their excellent performance. With the trend of lightweight construction, these materials, which can be used in prefabricated components, are becoming more and more important. This study investigated the influence of the water-cement (w/c) ratio, within the 0.19-0.28 range, on the rheological and mechanical properties of HPFRCCs; the pore structure and microstructure were observed to evaluate its effect. An elastic modulus test showed that a smaller w/c ratio would result in a higher rigidity of the material. Both the yield shear stress and plastic viscosity decreased to significantly different degrees with an increasing w/c ratio; a decrease in the yield shear stress and plastic viscosity was conducive to air discharge from the composite and, hence, reduced the air content. Most of the internal pores had a diameter of 20-100 nm or larger than 200 nm, while the proportion of those with a diameter of 100-200 nm was relatively low. When the w/c ratio was below 0.22, the flexural and compressive strengths barely increased due to an increment in the number of larger pores (i.e., diameter >200 nm). The results showed that the yield shear stress, plastic viscosity, pore uniformity, and the number of pores with a diameter above 200 nm are the dominant factors affecting the HPFRCC performance at a low w/c ratio.
| S-EPMC8945063 | biostudies-literature
Project description:The data presented herein are compiled of the research summary of "Staple-wire-reinforced high-volume fly-ash cement paste composites" (Aydin, in preparation) [1]. This data article provides general information about the novel high volume fly ash cement paste composites composed of various volume of staple wires. The dataset here also helps the readers to understand the mechanisms of staple wires on physical and mechanical properties of pure cement paste composites.
| S-EPMC5544468 | biostudies-literature
Project description:This paper reports the effects of carbon nanofibers (CNFs) on nanoscaled mechanical properties of cement composites. CNFs were added to cement composites at the filler loading of 0.2 wt % (by wt. of cement). Micrographs based on scanning electron microscopy (SEM) show that CNFs are capable of forming strong interfacial bonding with cement matrices. Experimental results using nanoindentation reveal that the addition of CNFs in cement composites increases the proportions of high-density calcium-silicate-hydrate gel (HD-CSH) compared to low-density CSH gel. It was also found that the inclusion of CNFs increases the compressive strength of cement composites.
| S-EPMC5554043 | biostudies-other
Project description:The data presented herein are compiled of the research summary of "Characterization of High-Volume Fly-Ash Cement Paste for Sustainable Construction Application" (Aydin and Arel, 2017) [1]. This data article provides general information about the ASTM Class C and Class F fly ash cement paste composites composed of silica fume, lime, water reducing admixtures in three different level of workability (0 mm, 100 mm and 200 mm). The dataset here also helps the readers to understand the links with the basic properties of the ingredients, for example, how can porosity be predicted based on the mixture design? how can the strength of the material be linked with the basic strengths of the constituent ingredients?.
| S-EPMC5711659 | biostudies-literature
Project description:The durability of a cement-based material is mainly dependent on its permeability. Modifications of porosity, pore-structure and pore-connectivity could have significant impacts on permeability improvement, which eventually leads to more durable materials. One of the most efficient solutions in this regard is to use permeability reducing admixtures (PRA). Among these admixtures for those structures exposed to hydro-static pressure, crystalline waterproofing admixtures (CWA) have been serving in the construction industries for decades and according to ACI 212-chemical admixtures' report, it has proven its capability in permeability reduction and durability-enhancement. However, there is substantial research being done on its durability properties at the macro level but very limited information available regarding its microstructural features and chemical characteristics at the micro level. Hence, this paper presents one of the first reported attempts to characterize microstructural and chemical elements of hydration products for cementitious composites with CWA called K, P and X using Scanning Electron Microscopy (SEM). Backscattered SEM images taken from a polished-section of one CWA type-K-admixture were analyzed in ImageJ to obtain paste matrix porosity, indicating a lower value for the CWA-K mixture. X-ray analysis and SEM micrographs of polished sections were examined to identify chemical compositions based on atomic ratio plots and brightness differences in backscatter-SEM images. To detect chemical elements and the nature of formed crystals, the fractured surfaces of three different CWA mixtures were examined. Cementitious composites with K admixture indicated needle-like crystal formation-though different from ettringite; X and P admixtures showed sulfur peaks in Energy Dispersive Spectrum (EDS) spectra, like ettringite. SEM images and X-ray analyses of mixtures incorporating Portland Limestone Cement (PLC) indicated lower-than-average porosity but showed different Si/Ca and Al/Ca atomic ratios.
| S-EPMC7143351 | biostudies-literature
Project description:PURPOSE:A strong isotropic material that is both biocompatible and biodegradable is desired for many biomedical applications, including rotator cuff repair, tendon and ligament repair, vascular grafting, among others. Recently, we developed a technique, called "bioskiving" to create novel 2D and 3D constructs from decellularized tendon, using a combination of mechanical sectioning, and layered stacking and rolling. The unidirectionally aligned collagen nanofibers (derived from sections of decellularized tendon) offer good mechanical properties to the constructs compared with those fabricated from reconstituted collagen. METHODS:In this paper, we studied the effect that several variables have on the mechanical properties of structures fabricated from tendon slices, including crosslinking density and the orientation in which the fibers are stacked. RESULTS:We observed that following stacking and crosslinking, the strength of the constructs is significantly improved, with crosslinked sections having an ultimate tens ile strength over 20 times greater than non-crosslinked samples, and a modulus nearly 50 times higher. The mechanism of the mechanical failure mode of the tendon constructs with or without crosslinking was also investigated. CONCLUSIONS:The strength and fiber organization, combined with the ability to introduce transversely isotropic mechanical properties makes the laminar tendon composites a biocompatiable material that may find future use in a number of biomedical and tissue engineering applications.
| S-EPMC4327911 | biostudies-literature
Project description:Most of the currently used concretes are based on ordinary Portland cement (OPC) which results in a high carbon dioxide footprint and thus has a negative environmental impact. Replacing OPCs, partially or fully by ecological binders, i.e., supplementary cementitious materials (SCMs) or alternative binders, aims to decrease the carbon dioxide footprint. Both solutions introduced a number of technological problems, including their performance, when exposed to low, subfreezing temperatures during casting operations and the hardening stage. This review indicates that the present knowledge enables the production of OPC-based concretes at temperatures as low as -10 °C, without the need of any additional measures such as, e.g., heating. Conversely, composite cements containing SCMs or alkali-activated binders (AACs) showed mixed performances, ranging from inferior to superior in comparison with OPC. Most concretes based on composite cements require pre/post heat curing or only a short exposure to sub-zero temperatures. At the same time, certain alkali-activated systems performed very well even at -20 °C without the need for additional curing. Chemical admixtures developed for OPC do not always perform well in other binder systems. This review showed that there is only a limited knowledge on how chemical admixtures work in ecological concretes at low temperatures and how to accelerate the hydration rate of composite cements containing high amounts of SCMs or AACs, when these are cured at subfreezing temperatures.
| S-EPMC7476010 | biostudies-literature
Project description:The aim of this study is to develop a process to produce high-performance cement-based composites reinforced with flax nonwoven fabrics, analyzing the influence of the fabric structure-thickness and entanglement-on mechanical behavior under flexural and tensile loadings. For this purpose, composite with flax nonwoven fabrics with different thicknesses were first prepared and their cement infiltration was evaluated with backscattered electron (BSE) images. The nonwoven fabrics with the optimized thickness were then subjected to a water treatment to improve their stability to humid environments and the fiber-matrix adhesion. For a fixed thickness, the effect of the nonwoven entanglement on the mechanical behavior was evaluated under flexural and direct tension tests. The obtained results indicate that the flax nonwoven fabric reinforcement leads to cement composites with substantial enhancement of ductility.
| S-EPMC5459217 | biostudies-literature
Project description:Since ash from wood biomass mostly ends up in landfills, recent research has focused on finding its economic and environmental added value as a potential new raw material in the construction industry. However, for wood ash to be used on an industrial scale in construction, a strategy for its proper storage must be defined. Proper storage of WBA is important to ensure quality control for applications in cementitious composites. This work investigated the aging of wood biomass ash (WBA) collected from five different power plants in Croatia and its influence on the performance of cementitious composites. WBA and cement pastes were investigated at different aging times (up to one year) using thermogravimetric analysis (TGA), powder X-ray diffraction (XRD), isothermal calorimetry and initial and final setting times. The results showed that storage of WBA in closed and open containers resulted in carbonation and hydration of mainly free lime and periclase, respectively, which affected the reactivity and setting times of WBA cement pastes.
| S-EPMC8036677 | biostudies-literature
Project description:The antagonism between strength and corrosion resistance in graphene-reinforced aluminum matrix composites is an inherent challenge to designing reliable structural components. Heteroatom microstructural modification is highly appreciated to conquer the obstacle. Here, a bottom-up strategy to exploit the heterogeneous phase interface to enable high corrosion durability is proposed. Deformation-driven metallurgy derived from severe plastic deformation is developed to produce Mg-alloyed fluorinated graphene structures with homogeneous dispersion. These structures allow for absorbing corrosion products, forming a dense protective layer against corrosion, and local micro-tuning of the suppression of charge transfer. This results in superior corrosion resistance with an outstanding strength-ductility balance of the composites via ultrafine-grained and precipitation strengthening. The anti-corrosion polarization resistance remains 89% of the initial state after 2-month immersion in chloride-containing environment, while the ultra-tensile strength and elongation of 532 ± 39 MPa and 17.3 ± 1.2% are obtained. The economical strategy of heteroatom modification broadens the horizon for anti-corrosion engineering in aluminum matrix composites, which is critical for the design of carbonaceous nanomaterial-reinforced composites to realize desired performances for practical applications.
| S-EPMC9376822 | biostudies-literature