Mechanical and Thermal Properties of Polypropylene Composites Reinforced with Lignocellulose Nanofibers Dried in Melted Ethylene-Butene Copolymer.

ABSTRACT: Lignocellulose nanofibers were prepared by the wet disk milling of wood flour. First, an ethylene-butene copolymer was pre-compounded with wood flour or lignocellulose nanofibers to prepare master batches. This process involved evaporating the water of the lignocellulose nanofiber suspension during compounding with ethylene-butene copolymer by heating at 105 °C. These master batches were compounded again with polypropylene to obtain the final composites. Since ethylene-butene copolymer is an elastomer, its addition increased the impact strength of polypropylene but decreased the stiffness. In contrast, the wood flour- and lignocellulose nanofiber-reinforced composites showed significantly higher flexural moduli and slightly higher flexural yield stresses than did the ethylene-butene/polypropylene blends. Further, the wood flour composites exhibited brittle fractures during tensile tests and had lower impact strengths than those of the ethylene-butene/polypropylene blends. On the other hand, the addition of the lignocellulose nanofibers did not decrease the impact strength of the ethylene-butene/polypropylene blends. Finally, the addition of wood flour and the lignocellulose nanofibers increased the crystallization temperature and crystallization rate of polypropylene. The increases were more remarkable in the case of the lignocellulose nanofibers than for wood flour.

SUBMITTER: Iwamoto S

PROVIDER: S-EPMC5456022 | biostudies-other | 2014 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Sustainable Development of Hot-Pressed All-Lignocellulose Composites-Comparing Wood Fibers and Nanofibers.

Project description:Low-porosity materials based on hot-pressed wood fibers or nanocellulose fibrils (no polymer matrix) represent a new concept for eco-friendly materials with interesting mechanical properties. For the replacement of fossil-based materials, physical properties of wood fiber materials need to be improved. In addition, the carbon footprint and cumulative energy required to produce the material also needs to be reduced compared with fossil-based composites, e.g., glass fiber composites. Lignin-containing fibers and nanofibers are of high yield and special interest for development of more sustainable materials technologies. The present mini-review provides a short analysis of the potential. Different extraction routes of lignin-containing wood fibers are discussed, different processing methods, and the properties of resulting fiber materials. Comparisons are made with analogous lignin-containing nanofiber materials, where mechanical properties and eco-indicators are emphasized. Higher lignin content may promote eco-friendly attributes and improve interfiber or interfibril bonding in fiber materials, for improved mechanical performance.

| S-EPMC8399967 | biostudies-literature

Migration Behavior of Lubricants in Polypropylene Composites under Accelerated Thermal Aging.

Project description:The surface migration of lubricants degrades the quality of thermoplastic polymer composites. In this study, the surface migration of lubricants in polypropylene composites were studied to improve the quality of the composites. Polypropylene (PP)/lubricant composites were manufactured using a co-rotating twin-screw extruder and injection molding, and the migration phenomena of the lubricant in the PP/lubricant composites were investigated under accelerated aging conditions with temperatures in the range of 20 to 90 °C and humidity of 100% for 72 h. The interrelation between the surface migration properties of PP/lubricant composites were investigated by considering their microstructural and morphological features, which were influenced by the thermal aging conditions. Further, the microstructural and morphological features were examined by contact angle, surface energy, attenuated total reflectance Fourier-transform infrared spectrometry, X-ray photoelectron spectroscopy, close-up digital imaging, and atomic force microscopy analyses. The polypropylene composites containing the magnesium stearate as the lubricant were found to exhibit a more stable migration behavior than the polypropylene composites containing a calcium stearate lubricant. This is attributed to multiple synergistic factors, such as interfacial tension and work of adhesion between PP and the lubricant. The findings of this study can be utilized to effectively manufacture high-quality thermoplastic composites for the fourth industrial revolution.

| S-EPMC8197380 | biostudies-literature

Nanoscaled Mechanical Properties of Cement Composites Reinforced with Carbon Nanofibers.

Project description:This paper reports the effects of carbon nanofibers (CNFs) on nanoscaled mechanical properties of cement composites. CNFs were added to cement composites at the filler loading of 0.2 wt % (by wt. of cement). Micrographs based on scanning electron microscopy (SEM) show that CNFs are capable of forming strong interfacial bonding with cement matrices. Experimental results using nanoindentation reveal that the addition of CNFs in cement composites increases the proportions of high-density calcium-silicate-hydrate gel (HD-CSH) compared to low-density CSH gel. It was also found that the inclusion of CNFs increases the compressive strength of cement composites.

| S-EPMC5554043 | biostudies-other

Thermal Conductivity Performance of Polypropylene Composites Filled with Polydopamine-Functionalized Hexagonal Boron Nitride.

Project description:Mussel-inspired approach was attempted to non-covalently functionalize the surfaces of boron nitride (BN) with self-polymerized dopamine coatings in order to reduce the interfacial thermal barrier and enhance the thermal conductivity of BN-containing composites. Compared to the polypropylene (PP) composites filled with pristine BN at the same filler content, thermal conductivity was much higher for those filled with both functionalized BN (f-BN) and maleic anhydride grafted PP (PP-g-ma) due to the improved filler dispersion and better interfacial filler-matrix compatibility, which facilitated the development of more thermal paths. Theoretical models were also applied to predict the composite thermal conductivity in which the Nielsen model was found to fit well with the experimental results, and the estimated effective aspect ratio of fillers well corresponded to the degree of filler aggregation as observed in the morphological study.

| S-EPMC5249180 | biostudies-literature

Thermal and Mechanical Interfacial Behaviors of Graphene Oxide-Reinforced Epoxy Composites Cured by Thermal Latent Catalyst.

Project description:A series of composites was prepared from a diglycidyl ether of bisphenol A (DGEBA) with different graphene filler contents to improve their mechanical performance and thermal stability. Graphene oxide (GO) and GO modified with hexamethylene tetraamine (HMTA) were selected as reinforcing agents. As a latent cationic initiator and curing agent, N-benzylepyrizinium hexafluoroantimonate (N-BPH) was used. The effect of fillers and their contents on the mechanical properties and thermal stability of the composites were studied. Fracture toughness improved by 23% and 40%, and fracture energy was enhanced by 1.94- and 2.27-fold, for the composites containing 0.04 wt.% GO and HMTA-GO, respectively. The gradual increase in fracture toughness at higher filler contents was attributed to both crack deflection and pinning mechanisms. Maximum thermal stability in the composites was achieved by using up to 0.1 wt.% graphene fillers.

| S-EPMC6515424 | biostudies-literature

Synergetic Toughening Effect of Carbon Nanotubes and β-Nucleating Agents on the Polypropylene Random Copolymer/Styrene-Ethylene-Butylene- Styrene Block Copolymer Blends.

Project description:Polypropylene random co-polymer (PPR)/styrene-ethylene-butylene-styrene (SBS) block copolymer blends with high toughness and favorable tensile properties were successfully obtained by blending with traces of multi-wall carbon nanotubes (MWCNTs) and β-nucleating agents (β-NAs). β-NAs can effectively induce the ductile β-form crystal in the PPR matrix. Although the addition of MWCNTs was reported to be only benefit for the tensile strength of PPR and relatively disadvantageous for the toughness, the obviously synergistic toughening effect in PPR/SBS blends was found when MWCNTs and β-NAs coexisted. The notched izod impact strength of PPR/30 wt % SBS blend with MWCNTs and β-NAs increased from 11.3 to 58.9 kJ/m²; more than 5-fold increment compared with pure PPR. Meanwhile, the tensile strength retention of this PPR blend is still above 72.2%. The micro-morphology indicated that the MWCNTs can act as bridges between SBS particle and PPR matrix, effectively transferring the stress and absorbing impact energy among SBS particles.

| S-EPMC6401747 | biostudies-literature

Acoustic, Mechanical and Thermal Properties of Green Composites Reinforced with Natural Fibers Waste.

Project description:The use of acoustic panels is one of the most important methods for sound insulation in buildings. Moreover, it has become increasingly important to use green/natural origin materials in this area to reduce environmental impact. This study focuses on the investigation of acoustic, mechanical and thermal properties of natural fiber waste reinforced green epoxy composites. Three different types of fiber wastes were used, e.g., cotton, coconut and sugarcane with epoxy as the resin. Different fiber volume fractions, i.e., 10%, 15% and 20% for each fiber were used with a composite thickness of 3 mm. The sound absorption coefficient, impact strength, flexural strength, thermal conductivity, diffusivity, coefficient of thermal expansion and thermogravimetric properties of all samples were investigated. It has been found that by increasing the fiber content, the sound absorption coefficient also increases. The coconut fiber-based composites show a higher sound absorption coefficient than in the other fiber-reinforced composites. The impact and flexural strength of the cotton fiber-reinforced composite samples are higher than in other samples. The coefficient of thermal expansion of the cotton fiber-based composite is also higher than the other composites. Thermogravimetric analysis revealed that all the natural fiber-reinforced composites can sustain till 300 °C with a minor weight loss. The natural fiber-based composites can be used in building interiors, automotive body parts and household furniture. Such composite development is an ecofriendly approach to the acoustic world.

| S-EPMC7183085 | biostudies-literature

Silica-Based Aerogel Composites Reinforced with Reticulated Polyurethane Foams: Thermal and Mechanical Properties.

Project description:In this work, silica aerogel composites reinforced with reticulated polyurethane (PU) foams have been manufactured having densities in the range from 117 to 266 kg/m3 and porosities between 85.7 and 92.3%. Two different drying processes were employed (ambient pressure drying and supercritical drying) and a surface modification step was applied to some of the silica formulations. These composites, together with the reference PU foam and the monolithic silica aerogels, were fully characterized in terms of their textural properties, mechanical properties and thermal conductivities. The surface modification with hexamethyldisilazane (HMDZ) proved to improve the cohesion between the reticulated foam and the silica aerogels, giving rise to a continuous network of aerogel reinforced by a polyurethane porous structure. The samples dried under supercritical conditions showed the best interaction between matrixes as well as mechanical and insulating properties. These samples present better mechanical properties than the monolithic aerogels having a higher elastic modulus (from 130 to 450 kPa), a really exceptional flexibility and resilience, and the capacity of being deformed without breaking. Moreover, these silica aerogel-polyurethane foam (Sil-PU) composites showed an excellent insulating capacity, reaching thermal conductivities as low as 14 mW/(m·K).

| S-EPMC9318614 | biostudies-literature

Phlogopite-Reinforced Natural Rubber (NR)/Ethylene-Propylene-Diene Monomer Rubber (EPDM) Composites with Aminosilane Compatibilizer.

Project description:Rubber compounding with two or more components has been extensively employed to improve various properties. In particular, natural rubber (NR)/ethylene-propylene-diene monomer rubber (EPDM) blends have found use in tire and automotive parts. Diverse fillers have been applied to NR/EPDM blends to enhance their mechanical properties. In this study, a new class of mineral filler, phlogopite, was incorporated into an NR/EPDM blend to examine the mechanical, curing, elastic, and morphological properties of the resulting material. The combination of aminoethylaminopropyltrimethoxysilane (AEAPS) and stearic acid (SA) compatibilized the NR/EPDM/phlogopite composite, further improving various properties. The enhanced properties were compared with those of NR/EPDM/fillers composed of silica or carbon black (CB). Compared with the NR/EPDM/silica composite, the incompatibilized NR/EPDM/phlogopite composite without AEAPS exhibited poorer properties, but NR/EPDM/phlogopite compatibilized by AEAPS and SA showed improved properties. Most properties of the compatibilized NR/EPDM/phlogopite composite were similar to those of the NR/EPDM/CB composite, except for the lower abrasion resistance. The NR/EPDM/phlogopite/AEAPS rubber composite may potentially be used in various applications by replacing expensive fillers, such as CB.

| S-EPMC8309489 | biostudies-literature

Kinetics of Crystallization and Thermal Degradation of an Isotactic Polypropylene Matrix Reinforced with Graphene/Glass-Fiber Filler.

Project description:Polypropylene composites reinforced with a filler mixture of graphene nanoplatelet-glass fiber were prepared by melt mixing, while conventional composites containing graphene nanoplatelet and glass fiber were prepared for comparative reasons. An extensive study of thermally stimulated processes such as crystallization, nucleation, and kinetics was carried out using Differential Scanning Calorimetry and Thermogravimetric Analysis. Moreover, effective activation energy and kinetic parameters of the thermal decomposition process were determined by applying Friedman's isoconversional differential method and multivariate non-linear regression method. It was found that the graphene nanoplatelets act positively towards the increase in crystallization rate and nucleation phenomena under isothermal conditions due to their large surface area, inherent nucleation activity, and high filler content. Concerning the thermal degradation kinetics of polypropylene graphene nanoplatelets/glass fibers composites, a change in the decomposition mechanism of the matrix was found due to the presence of graphene nanoplatelets. The effect of graphene nanoplatelets dominates that of the glass fibers, leading to an overall improvement in performance.

| S-EPMC6572227 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data