Experimental Study on the Electrochemical Anti-Corrosion Properties of Steel Structures Applying the Arc Thermal Metal Spraying Method.

ABSTRACT: The arc thermal metal spraying method (ATMSM) provides proven long-term protective coating systems using zinc, aluminum and their alloys for steel work in a marine environment. This paper focuses on studying experimentally the anti-corrosion criteria of ATMSM on steel specimens. The effects of the types of spraying metal and the presence or absence of sealing treatment from the thermal spraying of film on the anti-corrosion performance of TMSM were quantitatively evaluated by electrochemical techniques. The results showed that ATMSM represented a sufficient corrosion resistance with the driving force based on the potential difference of more than approximately 0.60 V between the thermal spraying layer and the base substrate steel. Furthermore, it was found that the sealing treatment of specimens had suppressed the dissolution of metals, increased the corrosion potential, decreased the corrosion current density and increased the polarization resistance. Metal alloy Al-Mg (95%:5%) by mass with epoxy sealing coating led to the most successful anti-corrosion performance in these electrochemical experiments.

SUBMITTER: Choe HB

PROVIDER: S-EPMC5456417 | biostudies-other | 2014 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Protection of Reinforced Concrete Structures of Waste Water Treatment Reservoirs with Stainless Steel Coating Using Arc Thermal Spraying Technique in Acidified Water.

Project description:Waste water treatment reservoirs are contaminated with many hazardous chemicals and acids. Reservoirs typically comprise concrete and reinforcement steel bars, and the main elements responsible for their deterioration are hazardous chemicals, acids, and ozone. Currently, a variety of techniques are being used to protect reservoirs from exposure to these elements. The most widely used techniques are stainless steel plating and polymeric coating. In this study, a technique known as arc thermal spraying was used. It is a more convenient and economical method for protecting both concrete and reinforcement steel bar from deterioration in waste water treatment reservoirs. In this study, 316L stainless steel coating was applied to a concrete surface, and different electrochemical experiments were performed to evaluate the performance of coatings in different acidic pH solutions. The coating generated from the arc thermal spraying process significantly protected the concrete surface from corrosion in acidic pH solutions, owing to the formation of a double layer capacitance-a mixture of Cr3+ enriched with Cr₂O₃ and Cr-hydroxide in inner and Fe3+ oxide on the outer layer of the coating. The formation of this passive film is defective owing to the non-homogeneous 316L stainless steel coating surface. In the pH 5 solution, the growth of a passive film is adequate due to the presence of un-dissociated water molecules in the aqueous sulfuric acid solution. The coated surface is sealed with alkyl epoxide, which acts as a barrier against the penetration of acidic solutions. This coating exhibits higher impedance values among the three studied acidic pH solutions.

| S-EPMC5457078 | biostudies-other

Study on the Shielding Effectiveness of an Arc Thermal Metal Spraying Method against an Electromagnetic Pulse.

Project description:An electromagnetic pulse (EMP) explodes in real-time and causes critical damage within a short period to not only electric devices, but also to national infrastructures. In terms of EMP shielding rooms, metal plate has been used due to its excellent shielding effectiveness (SE). However, it has difficulties in manufacturing, as the fabrication of welded parts of metal plates and the cost of construction are non-economical. The objective of this study is to examine the applicability of the arc thermal metal spraying (ATMS) method as a new EMP shielding method to replace metal plate. The experimental parameters, metal types (Cu, Zn-Al), and coating thickness (100-700 μm) used for the ATMS method were considered. As an experiment, a SE test against an EMP in the range of 103 to 1010 Hz was conducted. Results showed that the ATMS coating with Zn-Al had similar shielding performance in comparison with metal plate. In conclusion, the ATMS method is judged to have a high possibility of actual application as a new EMP shielding material.

| S-EPMC5666961 | biostudies-literature

Corrosion mechanism and kinetics of Al-Zn coating deposited by arc thermal spraying process in saline solution at prolong exposure periods.

Project description:Steel structures significantly degrades owing to corrosion especially in coastal and industrial areas where significant amounts of aggressive ions are present. Therefore, anodic metals such as Al and Zn are used to protect steel. In the present study, we provide insights for the corrosion mechanism and kinetics of Al-Zn pseudo alloy coating deposited on mild steel plate via an arc thermal spraying process in 3.5 wt.% NaCl solution in terms of its improved corrosion resistance properties at prolonged exposure durations. Electrochemical studies including open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) on the deposited coating at longer exposure durations revealed enhanced corrosion resistance properties while the morphology of corrosion products through field emission-scanning electron microscopy (FE-SEM) indicated their compactness and adherence. Furthermore, atomic force microscopy (AFM) confirmed reduced roughness when compared with that of unexposed coating. Additionally, X-ray diffraction (XRD) and Raman spectroscopy results confirmed the formation of protective, adherent, and sparingly soluble Simonkolleite (Zn5(OH)8Cl2.H2O) after 55 d of exposure in 3.5 wt.% NaCl solution. A schematic is proposed that explains the corrosion process of Al-Zn pseudo alloy coating in 3.5 wt.% NaCl solution from the deposition of coating and initiation of corrosion to longer exposure durations.

| S-EPMC6399354 | biostudies-literature

Chemical, electrochemical and surface studies of new metal-organic frameworks (MOF) as corrosion inhibitors for carbon steel in sulfuric acid environment.

Project description:The effects of [Co2 (SCN) 4(hmt)2(H2O)6. H2O] (SC1) and [Co (CN)6 (Me3Sn)3(H2O). (qox)] (SCP2) MOF as corrosion inhibitors on C-steel in 0.5 M sulfuric acid solutions are illustrated utilizing mass reduction (MR), electrochemical [potentiodynamic polarization (PP), and AC electrochemical impedance (EIS)]. The experiments revealed that as the dose of these compounds rose, the inhibition efficacy (IE percent) of C-steel corrosion improved, reaching 80.7-93.1% at dose 25 × 10-6 M for SC1 and SCP2, respectively. IE percent, on the other hand, dropped as the temperature range grew. SC1was adsorbed physically and chemically (mixed adsorption) but SCP2 was adsorbed physically on the surface of C-steel and conformed to the Langmuir adsorption isotherm equation. The PP studies revealed that these compounds act as mixed kind inhibitors. To establish the morphology of the inhibited C-steel surface, scanning electron microscopy (SEM), energy transmitted X-ray (EDX), and atomic force microscopy (AFM) studies were used. All tested experiments were in good agreement.

| S-EPMC8511119 | biostudies-literature

Dataset of manual metal arc welded heterogeneous thin steel plates AISI1018 AND AISI4340

Project description: Not available

| S-EPMC10519823 | biostudies-literature

Monitoring corrosion of steel bars in reinforced concrete structures.

Project description:Corrosion of steel bars embedded in reinforced concrete (RC) structures reduces the service life and durability of structures causing early failure of structure, which costs significantly for inspection and maintenance of deteriorating structures. Hence, monitoring of reinforcement corrosion is of significant importance for preventing premature failure of structures. This paper attempts to present the importance of monitoring reinforcement corrosion and describes the different methods for evaluating the corrosion state of RC structures, especially hal-cell potential (HCP) method. This paper also presents few techniques to protect concrete from corrosion.

| S-EPMC3914605 | biostudies-other

Chromeno-carbonitriles as corrosion inhibitors for mild steel in acidic solution: electrochemical, surface and computational studies.

Project description:Three novel N-hydrospiro-chromeno-carbonitriles namely, 2-amino-7,7-dimethyl-1',3',5-trioxo-1',3',5,6,7,8-hexahydrospiro[chromene-4,2'-indene]-3-carbonitrile (INH-1), 3-amino-7,7-dimethyl-2',5-dioxo-5,6,7,8-tetrahydrospiro[chromene-4,3'-indoline]-2-carbonitrile (INH-2) and 3'-amino-7',7'-dimethyl-2,5'-dioxo-5',6',7',8'-tetrahydro-2H-spiro[acenaphthylene-1,4'-chromene]-2'-carbonitrile (INH-3) were synthesized using the principles of green chemistry and applied as corrosion inhibitors for mild steel in acidic medium using computational simulations and experimental methods. Experimental and computational studies revealed that inhibition effectiveness of the INHs followed the sequence: INH-3 (95.32%) > INH-2 (93.02%) > INH-1 (89.16%). The investigated compounds exhibit mixed-type corrosion inhibition characteristics by blocking the active sites on the surface of mild steel. EIS study revealed that the INHs behave as interface-type corrosion inhibitors. EDX analyses supported the adsorption mechanism of corrosion inhibition. A DFT study carried out for gaseous and aqueous forms of inhibitor molecules indicated that interactions of INHs with the mild steel surface involve charge transfer phenomenon or donor-acceptor interactions. A Monte Carlo (MC) simulation study revealed that only a fractional segment of the molecule lies parallel to the steel surface, since the INH molecules are not completely planar. The results of computational studies and experimental analyses were in good agreement.

| S-EPMC8693851 | biostudies-literature

Corrosion of steel in groundwater

Project description:Microbially-induced corrosion of carbon steel in anoxic groundwater

| PRJEB19087 | ENA

Electrochemical and quantum mechanical investigation of various small molecule organic compounds as corrosion inhibitors in mild steel.

Project description:The corrosion inhibition property of selected small organic compounds was investigated using electrochemical measurements, including potentiodynamic polarization (PDP), linear polarization resistance (LPR), electrochemical impedance spectroscopy (EIS), and density functional theory (DFT) calculations. The inhibition efficiency (IE %) of the inhibitor on mild steel (MS) in 1 M HCl was then determined. Results show that the presence of the inhibitors resulted in decreased corrosion current density (I corr) values and increased polarization resistance (R p). Furthermore, the use of higher concentrations of inhibitors led to an increased inhibition efficiency. Tafel slopes and shifts in the E corr values suggested that the inhibitors tested are mixed-type inhibitors that form a protective layer on the surface of the substrate. Of the organic compound inhibitors tested, the inhibitor 4-ethylpyridine (EP) exhibited the highest R p values and inhibition efficiency values from the PDP, LPR, and EIS analyses, respectively. DFT calculations showed negative adsorption energies and confirmed the chemisorption of the inhibitors allowing for the formation of a hydrophobic protective film against corrosion and correlations between the quantum chemical values and electrochemical data were demonstrated. The results show the influence of the presence of electronegative O, S, and N atoms, as well as the role of aromatic rings in the promotion of surface protection by preventing aggressive ionic species from binding onto MS.

| S-EPMC8441079 | biostudies-literature

Crystallographic orientation data from chloride-induced stress corrosion crack (CISCC) paths in gas tungsten arc welded (GTAW) austenitic stainless steel 304L.

Project description:This Data in Brief article presents crystallographic data collected along chloride-induced stress corrosion cracks (CISCC) in a gas tungsten arc welded (GTAW) austenitic stainless steel (AuSS) 304L. The experimental setup involved a welded stainless steel 304L coupon of dimensions 105 mm × 18.5 mm × 3 mm, loaded in a 4-point bending fixture with a maximum tensile stress of 380 MPa. The fixtured specimen was immersed in boiling magnesium chloride (MgCl2) solution until a through-crack was observed on the specimen surface after 17 hours of boiling. The cross-section was subsequently polished, and 37 cracks of interest in the heat affected zone (HAZ) and weld zone (WZ) were selected for crystallographic characterization. Scanning electron microscopy (SEM) based electron backscatter diffraction (EBSD) was used to map the grain orientations along and surrounding each crack path. The obtained orientation imaging microscopy (OIM) datasets were post-processed using EDAX OIM V8 proprietary software to generate inverse pole figures (IPF), image quality (IQ) figures, detector signal (SEM) images, and to determine the Taylor factor and Schmid factor of mapped grains. This dataset can be used to understand CISCC crack initiation, propagation, and termination behaviors, as has been reported in the accompanying original research article. This data article providing the raw EBSD OIM datasets and processed images formatted for accessibility in future studies. This comprehensive EBSD dataset can further be used to extract grain boundary misorientation information; benchmark comparative studies of SCC/CISCC in AuSS and other Fe or Ni alloys; and provide critical validation data on grain morphology, misorientation, and crystallography for GTAW and CISCC models.

| S-EPMC8956886 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data