Annealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding.

ABSTRACT: Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mechanical properties was monitored by microhardness measurements. The microhardness increases when the material is annealed up to 160 °C. Above this temperature a fast drop of microhardness occurs followed by a negligible variation at annealing temperatures exceeding 300 °C. In order to map continuously the microstructure changes during annealing, the in situ TEM experiments in the heating stage were performed as a supplement to post-mortem TEM observations.

SUBMITTER: Cieslar M

PROVIDER: S-EPMC5456430 | biostudies-other | 2014 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Novel twin-roll-cast Ti/Al clad sheets with excellent tensile properties.

Project description:Pure Ti or Ti alloys are recently spot-lighted in construction industries because they have excellent resistance to corrosions, chemicals, and climates as well as various coloring characteristics, but their wide applications are postponed by their expensiveness and poor formability. We present a new fabrication process of Ti/Al clad sheets by bonding a thin Ti sheet on to a 5052 Al alloy melt during vertical-twin-roll casting. This process has merits of reduced production costs as well as improved tensile properties. In the as-twin-roll-cast clad sheet, the homogeneously cast microstructure existed in the Al alloy substrate side, while the Ti/Al interface did not contain any reaction products, pores, cracks, or lateral delamination, which indicated the successful twin-roll casting. When this sheet was annealed at 350 °C~600 °C, the metallurgical bonding was expanded by interfacial diffusion, thereby leading to improvement in tensile properties over those calculated by a rule of mixtures. The ductility was also improved over that of 5052-O Al alloy (25%) or pure Ti (25%) by synergic effect of homogeneous deformation due to excellent Ti/Al bonding. This work provides new applications of Ti/Al clad sheets to lightweight-alloy clad sheets requiring excellent formability and corrosion resistance as well as alloy cost saving.

| S-EPMC5556021 | biostudies-other

Cyclic Deformation of Ultra-Fine Grained Commercial Purity Aluminum Processed by Accumulative Roll-Bonding.

Project description:Accumulative Roll-Bonding (ARB) is one of the more recently developed techniques capable of producing bulk ultra-fine grained (ufg) metals. There are still many aspects of the behavior of ufg metals that lacks an in-depth understanding, such as a generalized view of the factors that govern the cyclic deformation mechanism(s). This study aims to advance the understanding of the cyclic deformation behavior of ufg metals through the systematic investigation of ARB processed aluminum upon cyclic loading. It was found that the cyclic softening response often reported for ufg metals is largely influenced by the microstructure stability as the cyclic softening response is facilitated by grain coarsening which becomes inhibited with highly stable microstructure. On one hand, shear bands resembling braids of dislocations trespassing multiple grains have been observed to operate for the accommodation of the imposed cyclic strain in cases where grain coarsening is largely restricted. On the other hand, it was found that the microstructure stability can be overcome at higher applied cyclic plastic strain levels, leading to grain coarsening and thus a cyclic softening response. The findings in this study have further confirmed that the cyclic softening behavior found in many ufg metals, which may be detrimental in practical applications, can be inhibited by improvements in the microstructure stability.

| S-EPMC5521316 | biostudies-other

A crystal plasticity FEM study of through-thickness deformation and texture in a {112} <111> aluminium single crystal during accumulative roll-bonding.

Project description:In this study, a crystal plasticity finite element method (CPFEM) model was used to study the deformation behaviour in an aluminium single crystal (1 1 2)[1 1 -1] processed by accumulative roll-bonding (ARB) up to 9 cycles. The simulation followed the real ARB process based on the developed finite element model. The predicted through-thickness texture matches well with the experimental observations. The deformation behaviours, in terms of crystal rotation, shear strain and slip system activation, in the first and second cycles (conventional rolling) were unidirectional, but the deformation was altered after ARB was applied from the third cycle onwards. Such alteration was found to be caused by the thickness position change and deformation discontinuity at interfaces, which were investigated in detail. The role that interfaces play became dominant over thickness position change as increasing ARB cycles.

| S-EPMC6399260 | biostudies-literature

Fabrication of ultra-thin nanostructured bimetallic foils by Accumulative Roll Bonding and Asymmetric Rolling.

Project description:This paper reports a new technique that combines the features of Accumulative Roll Bonding (ARB) and Asymmetric Rolling (AR). This technique has been developed to enable production of ultra-thin bimetallic foils. Initially, 1.5 mm thick AA1050 and AA6061 foils were roll-bonded using ARB at 200°C, with 50% reduction. The resulting 1.5 mm bimetallic foil was subsequently thinned to 0.04 mm through four AR passes at room temperature. The speed ratio between the upper and lower AR rolls was 1:1.3. The tensile strength of the bimetallic foil was seen to increase with reduction in thickness. The ductility of the foil was seen to reduce upon decreasing the foil thickness from 1.5 mm to 0.14 mm, but increase upon further reduction in thickness from 0.14 mm to 0.04 mm. The grain size was about 140 nm for the AA6061 layer and 235 nm for the AA1050 layer, after the third AR pass.

| S-EPMC3734478 | biostudies-other

Fabrication of Al/Mg/Al Composites via Accumulative Roll Bonding and Their Mechanical Properties.

Project description:Al(1060)/Mg(AZ31)/Al(1060) multilayered composite was successfully produced using an accumulative roll bonding (ARB) process for up to four cycles at an elevated temperature (400 °C). The microstructure evolution of the composites and the bonding characteristics at the interfaces between Al and Mg layers with increasing ARB cycles were characterized through optical microscopy, field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). It was found that the grains of Al and Mg layers were significantly refined and Al₃Mg₂ and Al12 Mg17 intermetallic compound layers formed at the Al/Mg bonding interfaces. The strength increased gradually and the ultimate tensile strength (UTS) reached a maximum value of about 240 MPa at the third pass. Furthermore, the strengthening mechanism of the composite was analyzed based on the fracture morphologies.

| S-EPMC5457262 | biostudies-other

Microstructure and Hot Deformation Behavior of Twin Roll Cast Mg-2Zn-1Al-0.3Ca Alloy.

Project description:In the present work, the microstructure, texture, mechanical properties as well as hot deformation behavior of a Mg-2Zn-1Al-0.3Ca sheet manufactured by twin roll casting were investigated. The twin roll cast state reveals a dendritic microstructure with intermetallic compounds predominantly located in the interdendritic areas. The twin roll cast samples were annealed at 420 °C for 2 h followed by plane strain compression tests in order to study the hardening and softening behavior. Annealing treatment leads to the formation of a grain structure, consisting of equiaxed grains with an average diameter of approximately 19 µm. The twin roll cast state reveals a typical basal texture and the annealed state shows a weakened texture, by spreading basal poles along the transverse direction. The twin roll cast Mg-2Zn-1Al-0.3Ca alloy offers a good ultimate tensile strength of 240 MPa. The course of the flow curves indicate that dynamic recrystallization occurs during hot deformation. For the validity range from 250 °C to 450 °C as well as equivalent logarithmic strain rates from 0.01 s-1 to 10 s-1 calculated model coefficients are shown. The average activation energy for plastic flow of the twin roll cast and annealed Mg-2Zn-1Al-0.3Ca alloy amounts to 180.5 kJ/mol. The processing map reveals one domain with flow instability at temperatures above 370 °C and strain rates ranging from 3 s-1 to 10 s-1. Under these forming conditions, intergranular cracks arose and grew along the grain boundaries.

| S-EPMC6479906 | biostudies-other

Novel strip-cast Mg/Al clad sheets with excellent tensile and interfacial bonding properties.

Project description:In order to broaden industrial applications of Mg alloys, as lightest-weight metal alloys in practical uses, many efforts have been dedicated to manufacture various clad sheets which can complement inherent shortcomings of Mg alloys. Here, we present a new fabrication method of Mg/Al clad sheets by bonding thin Al alloy sheet on to Mg alloy melt during strip casting. In the as-strip-cast Mg/Al clad sheet, homogeneously distributed equi-axed dendrites existed in the Mg alloy side, and two types of thin reaction layers, i.e., γ (Mg17Al12) and β (Mg2Al3) phases, were formed along the Mg/Al interface. After post-treatments (homogenization, warm rolling, and annealing), the interfacial layers were deformed in a sawtooth shape by forming deformation bands in the Mg alloy and interfacial layers, which favorably led to dramatic improvement in tensile and interfacial bonding properties. This work presents new applications to multi-functional lightweight alloy sheets requiring excellent formability, surface quality, and corrosion resistance as well as tensile and interfacial bonding properties.

| S-EPMC4888122 | biostudies-other

High Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing.

Project description:Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstructure changes depends on chemical and phase composition. Better stability is observed in the Al-Mn-Zr-based alloy. High temperature tensile tests reveal that equal channel angular pressing results in a softening of all studied materials at high temperatures. This can be explained by an active role of grain boundaries in the deformation process. The maximum values of ductility and strain rate sensitivity parameter m found in the Al-Mn-Zr-based alloy are below the bottom limit of superplasticity (155%, m = 0.25). However, some features typical for superplastic behavior were observed-the strain rate dependence of the parameter m, the strengthening with increasing grain size, and the fracture by diffuse necking. Grain boundary sliding is believed to contribute partially to the overall strain in specimens where the grain size remained in the microcrystalline range.

| S-EPMC5458924 | biostudies-other

Enhanced Mechanical Properties and Microstructure of Accumulative Roll-Bonded Co/Pb Nanocomposite.

Project description:Lead composites have been used as anodes in the electrowinning process to produce metals such as copper and zinc. Manufacturing stable lead anodes with appropriate mechanical and chemical properties is required to improve the performance of the electrowinning process. In this study, an accumulative roll bonding (ARB) method was used to fabricate a Co/Pb nanocomposite. Utilizing the ARB method can help us to achieve a uniform structure with enhanced mechanical properties via severe plastic deformation. The results showed that suitable tensile properties were obtained in Pb-0.5%Co-10pass samples. The tensile strength and strain of these samples were 2.51 times higher and 83.7% lower than that of as-cast pure Pb. They also showed creep resistance and hardness up to 1.8 and 2.5 times more than that of as-cast pure Pb. The ARB technique uniformly distributed Co particles in the Pb matrix. The enhanced strength of Pb samples was observed in the composite including grain sizes of less than 50 nm as a result of hindering the recovery phenomenon. The particle size of the Co distributed in the Pb matrix was 353 ± 259 nm. Compared to conventional methods, the ARB process improved the mechanical properties of Co/Pb composites and can open a new horizon to fabricating this composite in metal industries.

| S-EPMC8147126 | biostudies-literature

Microstructure Evolution and Mechanical Properties of Al-TiB₂/TiC In Situ Aluminum-Based Composites during Accumulative Roll Bonding (ARB) Process.

Project description:In this study, a kind of Al-TiB₂/TiC in situ composite was successfully prepared using the melt reaction method and the accumulative roll-bonding (ARB) technique. The microstructure evolution of the composites with different deformation treatments was characterized using field emission scanning electron microscopy (FESEM) and a transmission electron microscope (TEM). The mechanical properties of the Al-TiB₂/TiC in situ composite were also studied with tensile and microhardness tests. It was found that the distribution of reinforcement particles becomes more homogenous with an increasing ARB cycle. Meanwhile, the mechanical properties showed great improvement during the ARB process. The ultimate tensile strength (UTS) and microhardness of the composites were increased to 173.1 MPa and 63.3 Hv after two ARB cycles, respectively. Furthermore, the strengthening mechanism of the composite was analyzed based on its fracture morphologies.

| S-EPMC5459192 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data