Cu-Doped ZnO Thin Films Deposited by a Sol-Gel Process Using Two Copper Precursors: Gas-Sensing Performance in a Propane Atmosphere.

ABSTRACT: A study on the propane gas-sensing properties of Cu-doped ZnO thin films is presented in this work. The films were deposited on glass substrates by sol-gel and dip coating methods, using zinc acetate as a zinc precursor, copper acetate and copper chloride as precursors for doping. For higher sensitivity values, two film thickness values are controlled by the six and eight dippings, whereas for doping, three dippings were used, irrespective of the Cu precursor. The film structure was analyzed by X-ray diffractometry, and the analysis of the surface morphology and film composition was made through scanning electron microscopy (SEM) and secondary ion mass spectroscopy (SIMS), respectively. The sensing properties of Cu-doped ZnO thin films were then characterized in a propane atmosphere, C₃H₈, at different concentration levels and different operation temperatures of 100, 200 and 300 °C. Cu-doped ZnO films doped with copper chloride presented the highest sensitivity of approximately 6 × 10⁴, confirming a strong dependence on the dopant precursor type. The results obtained in this work show that the use of Cu as a dopant in ZnO films processed by sol-gel produces excellent catalysts for sensing C₃H₈ gas.

SUBMITTER: Gomez-Pozos H

PROVIDER: S-EPMC5456497 | biostudies-other | 2016 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Sol-Gel-Deposited Ti-Doped ZnO: Toward Cell Fouling Transparent Conductive Oxides.

Project description:Ti-doped ZnO thin films were obtained with the aim of tailoring ZnO film bioadhesiveness and making the optoelectronic properties of ZnO materials transferable to biological environments. The films were prepared on silicon substrates by sol-gel spin-coating and subsequent annealing. A Ti-O segregation limits the ZnO crystallite growth and creates a buffer out-layer. Consequently, the Ti-doped ZnO presents slightly increased resistivity, which remains in the order of 10-3 Ω·cm. The strong biochemical interference of Zn2+ ions released from pure ZnO surfaces was evidenced by culturing Staphylococcus epidermidis with and without the Zn2+ coupling agent clioquinol. The Ti-doped ZnO surfaces showed a considerable increase of bacterial viability with respect to pure ZnO. Cell adhesion was assayed with human mesenchymal stem cells (hMSCs). Although hMSCs find difficulties to adhere to the pure ZnO surface, they progressively expand on the surface of ZnO when the Ti doping is increased. A preliminary microdevice has been built on the Si substrate with a ZnO film doped with 5% Ti. A one-dimensional micropattern with a zigzag structure shows the preference of hMSCs for adhesion on Ti-doped ZnO with respect to Si. The induced contrast of surface tension further induces a cell polarization effect on hMSCs. It is suggested that the presence of Ti-O covalent bonding on the doped surfaces provides a much more stable ground for bioadhesion. Such fouling behavior suggests an influence of Ti doping on film bioadhesiveness and sets the starting point for the selection of optimal materials for implantable optoelectronic devices.

| S-EPMC6682115 | biostudies-literature

Affinity of Electrochemically Deposited Sol⁻Gel Silica Films towards Catecholamine Neurotransmitters.

Project description:Dopamine, norepinephrine, and epinephrine neurotransmitters can be detected by electrochemical oxidation in conventional electrodes. However, their similar chemical structure and electrochemical behavior makes a difficult selective analysis. In the present work, glassy carbon electrodes have been modified with silica layers, which were prepared by electroassisted deposition of sol⁻gel precursors. These layers were morphologically and compositionally characterized using different techniques, such as field emission scanning electron microscopy (FESEM), TEM, FTIR, or thermogravimetric analysis⁻mass spectrometry (TG-MS). The affinity of silica for neurotransmitters was evaluated, exclusively, by means of electrochemical methods. It was demonstrated that silica adsorbs dopamine, norepinephrine, and epinephrine, showing different interaction with silica pores. The adsorption process is dominated by a hydrogen bond between silanol groups located at the silica surface and the amine groups of neurotransmitters. Because of the different interaction with neurotransmitters, electrodes modified with silica films could be used in electrochemical sensors for the selective detection of such molecules.

| S-EPMC6412732 | biostudies-literature

Comparative study on photocatalytic activity of transition metals (Ag and Ni)-doped ZnO nanomaterials synthesized via sol-gel method.

Project description:Ag and Ni/ZnO photocatalyst nanostructures were successfully synthesized by a sol-gel method. In this work, the photocatalyst sample was systematically studied based on several factors affecting the performance of photocatalyst, which are size, morphology, band gap, textural properties and the number of active sites presence on the surface of the nanocatalyst. X-ray diffraction revealed that Ag/ZnO nanomaterials experienced multiple phases, meanwhile for Ni/ZnO the phase of nanomaterials were pure and single phase for stoichiometry less than 5%. Field emission scanning electron microscope (FESEM) showed almost all of the synthesized nanomaterials possessed a mixture of nanorods and spherical-like shape morphology. The Ag/ZnO showed high photocatalytic activity, producing at least 14th trials of nanocatalyst reusability on degradation of methyl orange under UV irradiation. Interestingly, this phenomenon was not observed in larger surface area of Ni/ZnO nanomaterials which supposedly favour photocatalytic activity, but instead producing poor photocatalytic performance. The main reasons were studied and exposed by temperature-programmed desorption of carbon dioxide (TPD-CO2) which showed that incorporation of Ag into ZnO lattice has enhanced the number of active sites on the surface of the nanocatalyst. Whereas incorporation of Ni in ZnO has lowered the number of active sites with respect to undoped ZnO. Active sites measurement is effective and significant, providing opportunities in developing an intensive study as an additional factor.

| S-EPMC7062069 | biostudies-literature

Novel sol-gel precursors for thin mesoporous eu(3+)-doped silica coatings as efficient luminescent materials.

Project description:Europium(III) ions containing mesoporous silica coatings have been prepared via a solvent evaporation-induced self-assembly (EISA) approach of different single-source precursors (SSPs) in the presence of Pluronic P123 as a structure-directing agent, using the spin-coating process. A deliberate tailoring of the chemical composition of the porous coatings with various Si:Eu ratios was achieved by processing mixtures of tetraethylorthosilicate (TEOS) and Eu(3+)-coordinated SSPs. Small-angle X-ray scattering (SAXS) and transmission electron microscopy (TEM) analyses demonstrate that the thin metal oxide-doped silica coatings consist of a porous network with a short-range order of the pore structure, even at high europium(III) loadings. Furthermore, luminescence properties were investigated at different temperatures and different degrees of Eu(3+) contents. The photoluminescence spectra clearly show characteristic emission peaks corresponding to the (5)D0 → (7)FJ (J = 0-5) transitions resulting in a red luminescence visible by the eyes, although the films have a very low thickness (150-200 nm).

| S-EPMC3597185 | biostudies-other

Origin of ferromagnetism in Cu-doped ZnO.

Project description:It is widely reported during last decade on the observation of room temperature ferromagnetism (RTFM) in doped ZnO and other transition metal oxides. However, the origin of RTFM is not understood and highly debated. While investigating the origin of RTFM, magnetic ion doped oxides should be excluded because it is not yet settled whether RTFM is intrinsic or due to the magnetic ion cluster in ZnO. Hence, it is desirable to investigate the origin of RTFM in non-magnetic ion doped ZnO and Cu-doped ZnO will be most suitable for this purpose. The important features of ferromagnetism observed in doped ZnO are (i) observation of RTFM at a doping concentration much below than the percolation threshold of wurtzite ZnO, (ii) temperature independence of magnetization and (iii) almost anhysteretic magnetization curve. We show that all these features of ferromagnetism in ZnO are due to overlapping of bound magnetic polarons (BMPs) which are created by exchange interaction between the spin of Cu2+ ion and spin of the localized hole due to zinc vacancy [Formula: see text]. Both the experimental and theoretical investigation show that the exchange interaction between Cu2+-Cu2+ ions mediated by [Formula: see text] is responsible for RTFM in Cu-doped ZnO.

| S-EPMC6385290 | biostudies-literature

Hydrogen gas sensing using aluminum doped ZnO metasurfaces.

Project description:Hydrogen (H2) sensing is crucial in a wide variety of areas, such as industrial, environmental, energy and biomedical applications. However, engineering a practical, reliable, fast, sensitive and cost-effective hydrogen sensor is a persistent challenge. Here we demonstrate hydrogen sensing using aluminum-doped zinc oxide (AZO) metasurfaces based on optical read-out. The proposed sensing system consists of highly ordered AZO nanotubes (hollow pillars) standing on a SiO2 layer deposited on a Si wafer. Upon exposure to hydrogen gas, the AZO nanotube system shows a wavelength shift in the minimum reflectance by ∼13 nm within 10 minutes for a hydrogen concentration of 4%. These AZO nanotubes can also sense the presence of a low concentration (0.7%) of hydrogen gas within 10 minutes. Their rapid response time even for a low concentration, the possibility of large sensing area fabrication with good precision, and high sensitivity at room temperature make these highly ordered nanotube structures a promising miniaturized H2 gas sensor.

| S-EPMC9417916 | biostudies-literature

Comparative photocatalytic activity of sol-gel derived rare earth metal (La, Nd, Sm and Dy)-doped ZnO photocatalysts for degradation of dyes.

Project description:Rare earth metal doping into semiconductor oxides is considered to be an effective approach to enhance photocatalytic activity due to its ability to retard the electron-hole pair recombination upon excitation. Herein, we report the synthesis of different rare earth metal (La, Nd, Sm and Dy)-doped ZnO nanoparticles using a facile sol-gel route followed by evaluation of their photocatalytic activity by studying the degradation of methylene blue (MB) and Rhodamine B (RhB) under UV-light irradiation. Different standard analytical techniques were employed to investigate the microscopic structure and physiochemical properties of the prepared samples. The formation of the hexagonal wurtzite structure of ZnO was established by XRD and TEM analyses. In addition, the incorporation of rare earth metal into ZnO is confirmed by the shift of XRD planes towards lower theta values. All metal doped ZnO showed improved photocatalytic activity toward the degradation of MB, of which, Nd-doped ZnO showed the best activity with 98% degradation efficiency. In addition, mineralization of the dye was also observed, indicating 68% TOC removal in 180 min with Nd-doped ZnO nanoparticles. The influence of different operational parameters on the photodegradation of MB was also investigated and discussed in detail. Additionally, a possible photocatalytic mechanism for degradation of MB over Nd-doped ZnO nanoparticles has been proposed and involvement of hydroxyl radicals as reactive species is elucidated by radical trapping experiments.

| S-EPMC9080395 | biostudies-literature

Light-soaking free organic photovoltaic devices with sol–gel deposited ZnO and AZO electron transport layers† † Electronic supplementary information (ESI) available. See DOI: 10.1039/c8ra07071g

Project description:This paper investigates light-soaking effects in inverted organic photovoltaic (OPV) devices with zinc oxide (ZnO) and aluminum doped ZnO (AZO) electron transport layers (ETL), which is important for the development of low-cost and stable solar cells. The samples demonstrated high solar harvesting properties with power conversion efficiency up to 3.9%. Air-stability tests of up to 150 days were performed on devices with different Al doping levels. The devices maintained higher than 60% of the initial PCE after 50 days of open-air exposure. The light-soaking mechanism was investigated with experiments and simulations and shown to be eliminated when the Al fraction of the AZO is higher than 4%. The simulated band diagram of the OPV devices indicates that the low carrier density in the ZnO layer by virtue of depletion is the main reason of the light-soaking effect. Doping the ZnO layer as well as exposing the devices under UV irradiation will introduce additional free carriers into the ETL and reduce the width of the depletion region at both sides of the ETL. This paper investigates the mechanism of light-soaking effects in inverted organic photovoltaic devices with zinc oxide and aluminum doped ZnO electron transport layers, which is important for development of low-cost and stable solar cells.

| S-EPMC9088863 | biostudies-literature

Foliar Fertilization by the Sol-Gel Particles Containing Cu and Zn

Project description:Silica particles with the size of 150–200 nm containing Ca, P, Cu or Zn ions were synthesized with the sol-gel method and tested as a foliar fertilizer on three plant species: maize Zea mays, wheat Triticum sativum and rape Brassica napus L. var napus growing on two types of soils: neutral and acidic. The aqueous suspensions of the studied particles were sprayed on the chosen leaves and also on the whole tested plants. At a specific stage of plant development determined according to the BBCH (Biologische Bundesanstalt, Bundessortenamt und CHemische Industrie) scale, the leaves and the whole plants were harvested and dried, and the content of Cu and Zn was determined with the AAS (atomic absorption spectroscopy) method. The engineered particles were compared with a water solution of CuSO4 and ZnSO4 (0.1%) used as a conventional fertilizer. In many cases, the copper-containing particles improved the metal supply to plants more effectively than the CuSO4. The zinc-containing particles had less effect on both the growth of plants and the metal concentration in the plants. All the tested particles were not toxic to the examined plants, although some of them caused a slight reduction in plants growth.

| S-EPMC9824736 | biostudies-literature

Mesoporous Strontium-Doped Phosphate-Based Sol-Gel Glasses for Biomedical Applications.

Project description:Mesoporous phosphate-based glasses have great potential as biomedical materials being able to simultaneously induce tissue regeneration and controlled release of therapeutic molecules. In the present study, a series of mesoporous phosphate-based glasses in the P2O5-CaO-Na2O system, doped with 1, 3, and 5 mol% of Sr2+, were prepared using the sol-gel method combined with supramolecular templating. A sample without strontium addition was prepared for comparison. The non-ionic triblock copolymer EO20PO70EO20 (P123) was used as a templating agent. Scanning electron microscopy (SEM) images revealed that all synthesized glasses have an extended porous structure. This was confirmed by N2 adsorption-desorption analysis at 77 K that shows a porosity typical of mesoporous materials. 31P magic angle spinning nuclear magnetic resonance (31P MAS-NMR) and Fourier transform infrared (FTIR) spectroscopies have shown that the glasses are mainly formed by Q1 and Q2 phosphate groups. Degradation of the glasses in deionized water assessed over a 7-day period shows that phosphate, Ca2+, Na+, and Sr2+ ions can be released in a controlled manner over time. In particular, a direct correlation between strontium content and degradation rate was observed. This study shows that Sr-doped mesoporous phosphate-based glasses have great potential in bone tissue regeneration as materials for controlled delivery of therapeutic ions.

| S-EPMC7191082 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data