Cutting Modeling of Hybrid CFRP/Ti Composite with Induced Damage Analysis.

ABSTRACT: In hybrid carbon fiber reinforced polymer (CFRP)/Ti machining, the bi-material interface is the weakest region vulnerable to severe damage formation when the tool cutting from one phase to another phase and vice versa. The interface delamination as well as the composite-phase damage is the most serious failure dominating the bi-material machining. In this paper, an original finite element (FE) model was developed to inspect the key mechanisms governing the induced damage formation when cutting this multi-phase material. The hybrid composite model was constructed by establishing three disparate physical constituents, i.e., the Ti phase, the interface, and the CFRP phase. Different constitutive laws and damage criteria were implemented to build up the entire cutting behavior of the bi-material system. The developed orthogonal cutting (OC) model aims to characterize the dynamic mechanisms of interface delamination formation and the affected interface zone (AIZ). Special focus was made on the quantitative analyses of the parametric effects on the interface delamination and composite-phase damage. The numerical results highlighted the pivotal role of AIZ in affecting the formation of interface delamination, and the significant impacts of feed rate and cutting speed on delamination extent and fiber/matrix failure.

SUBMITTER: Xu J

PROVIDER: S-EPMC5456579 | biostudies-other | 2016 Jan

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Effects of the Electrophoretic Deposition of CNTs on the Mechanical Properties of Ti/CFRP Composite Laminates.

Project description:The interfacial performance between metals and resins significantly affects the mechanical properties of fiber-metal laminates. In this study, CNTs were deposited on a titanium surface via electrophoretic deposition (EPD) to improve the interfacial performance of Ti/carbon fiber-reinforced polymer composite laminates. Before EPD, the titanium plates were treated by either sandblasting, anodizing, or sandblasting/anodizing. A macroscopically rough surface and an oxide layer were formed by sandblasting and anodizing, then CNTs were deposited, and a porous layer was obtained, which improved the wettability and bonding strength. Finally, the static mechanical properties (single-lap properties, bending properties, and interlaminar shear properties) and dynamic mechanical properties (impact resistance) of the laminates were systematically explored. The introduction of CNTs played an important role in dispersing and carrying loads and providing a strong crack propagation resistance, which improved the laminates' static mechanical properties and reduced the delamination damage under dynamic impact. Compared with the original composite laminates, the bond strength, bending strength, and interlaminar shear strength of the laminates deposited with CNTs after sandblasting were increased by 117.94, 46.85, and 145.61%, respectively. When the impact energy was 35 J, the damage area of the composite laminate deposited with CNTs was decreased by 27.75%.

| S-EPMC8757327 | biostudies-literature

Evaluating the thermal damage resistance of graphene/carbon nanotube hybrid composite coatings.

Project description:We study laser irradiation behavior of multiwalled carbon nanotubes (MWCNT) and chemically modified graphene (rGO)-composite spray coatings for use as a thermal absorber material for high-power laser calorimeters. Spray coatings on aluminum test coupon were exposed to increasing laser irradiance for extended exposure times to quantify their damage threshold and optical absorbance. The coatings, prepared at varying mass % of MWCNTs in rGO, demonstrated significantly higher damage threshold values at 2.5 kW laser power at 10.6 μm wavelength than carbon paint or MWCNTs alone. Electron microscopy and Raman spectroscopy of irradiated specimens show that the coating prepared at 50% CNT loading endure at least 2 kW x cm(-2) for 10 seconds without significant damage. The improved damage resistance is attributed to the unique structure of the composite in which the MWCNTs act as an efficient absorber of laser light while the much larger rGO sheets surrounding them, dissipate the heat over a wider area.

| S-EPMC3945926 | biostudies-literature

Microwave Curing Characteristics of CFRP Composite Depending on Thickness Variation Using FBG Temperature Sensors.

Project description:Microwave curing technology, which has seen increased commercialization recently due to its ability to cut the curing time and ensure high quality, requires an understanding of the curing characteristics of composite materials of varying thickness. Therefore, this study aimed to perform cure monitoring to evaluate the effects of variations in thickness on the quality of microwave curing. For this study, a fiber Bragg grating sensor was used to measure temperature changes in specimens during the curing cycle for cure monitoring which is generally used for optimization of the curing cycle; then, the time taken for temperature increase and overshoot of the specimen, and the times at which the specimen thickness varied, were quantitatively evaluated. Testing confirmed that microwave curing reduced the curing time in the sections in which the temperature rose; also, the specimen thickness caused overshoot of up to approximately 40 °C at the side, which can affect the curing quality of the composite materials. Furthermore, voids were observed on the side of all specimens. The results indicated that, in order to improve the quality of microwave curing of composite materials, the curing cycle should be optimized by considering the characteristics of the microwave curing equipment.

| S-EPMC7178681 | biostudies-literature

Non-Destructive Thermography Analysis of Impact Damage on Large-Scale CFRP Automotive Parts.

Project description:Laminated composites are increasingly used in aeronautics and the wind energy industry, as well as in the automotive industry. In these applications, the construction and processing need to fulfill the highest requirements regarding weight and mechanical properties. Environmental issues, like fuel consumption and CO₂-footprint, set new challenges in producing lightweight parts that meet the highly monitored standards for these branches. In the automotive industry, one main aspect of construction is the impact behavior of structural parts. To verify the quality of parts made from composite materials with little effort, cost and time, non-destructive test methods are increasingly used. A highly recommended non-destructive testing method is thermography analysis. In this work, a prototype for a car's base plate was produced by using vacuum infusion. For research work, testing specimens were produced with the same multi-layer build up as the prototypes. These specimens were charged with defined loads in impact tests to simulate the effect of stone chips. Afterwards, the impacted specimens were investigated with thermography analysis. The research results in that work will help to understand the possible fields of application and the usage of thermography analysis as the first quick and economic failure detection method for automotive parts.

| S-EPMC5453135 | biostudies-other

Load-displacement experimental data from axial tensile loading of CFRP-SPCC hybrid laminates.

Project description:The current paper shows a data set of load-displacement output from axial tensile loading of CFRP-SPCC hybrid laminates. The specimen geometries are cut based on standard procedure from ASTM D-3039. At least 3 positions in each specimen, we measured its width and thickness. Data of the load and displacement were repeated at least 3 samples in each combination of hybrid laminates. Tensile test was conducted with a 1 mm/min of loading rate. The data were recorded from unloading until failure of specimens. The data gives information about the highest load and the behavior of load-displacement in axial tensile loading. By using width and thickness, normalized data can be obtained, the load can be calculated into stress (MPa) unit. The data are useful for researchers and structural engineers that deals with CFRP, SPCC, and hybrid CFRP-SPCC laminates.

| S-EPMC7058899 | biostudies-literature

Study on Damage Evaluation and Machinability of UD-CFRP for the Orthogonal Cutting Operation Using Scanning Acoustic Microscopy and the Finite Element Method.

Project description:Owing to high specific strength and designability, unidirectional carbon fiber reinforced polymer (UD-CFRP) has been utilized in numerous fields to replace conventional metal materials. Post machining processes are always required for UD-CFRP to achieve dimensional tolerance and assembly specifications. Due to inhomogeneity and anisotropy, UD-CFRP differs greatly from metal materials in machining and failure mechanism. To improve the efficiency and avoid machining-induced damage, this paper undertook to study the correlations between cutting parameters, fiber orientation angle, cutting forces, and cutting-induced damage for UD-CFRP laminate. Scanning acoustic microscopy (SAM) was employed and one-/two-dimensional damage factors were then created to quantitatively characterize the damage of the laminate workpieces. According to the 3D Hashin's criteria a numerical model was further proposed in terms of the finite element method (FEM). A good agreement between simulation and experimental results was validated for the prediction and structural optimization of the UD-CFRP.

| S-EPMC5459173 | biostudies-other

Bond Strength of Composite CFRP Reinforcing Bars in Timber.

Project description:The use of near-surface mounted (NSM) fibre-reinforced polymer (FRP) bars is an interesting method for increasing the shear and flexural strength of existing timber members. This article examines the behaviour of carbon FRP (CFRP) bars in timber under direct pull-out conditions. The objective of this experimental program is to investigate the bond strength between composite bars and timber: bars were epoxied into small notches made into chestnut and fir wood members using a commercially-available epoxy system. Bonded lengths varied from 150 to 300 mm. Failure modes, stress and strain distributions and the bond strength of CFRP bars have been evaluated and discussed. The pull-out capacity in NSM CFRP bars at the onset of debonding increased with bonded length up to a length of 250 mm. While CFRP bar's pull-out was achieved only for specimens with bonded lengths of 150 and 200 mm, bar tensile failure was mainly recorded for bonded lengths of 250 and 300 mm.

| S-EPMC5455648 | biostudies-other

Cutting Parameter Selection for Efficient and Sustainable Repair of Holes Made in Hybrid Mg?Ti?Mg Component Stacks by Dry Drilling Operations.

Project description:Drilling is one of the most common machining operations in the aeronautic and aerospace industries. For assembling parts, a large number of holes are usually drilled into the parts so that they can be joined later by rivets. As these holes are subjected to fatigue cycles, they have to be checked regularly for maintenance or repair, since small cracks or damage in its contour can quickly cause breakage of the part, which can have dangerous consequences. This paper focuses on finding the best combinations of cutting parameters to perform repair and maintenance operations of holes in stacked hybrid magnesium?titanium?magnesium components in an efficient, timely, and sustainable (without lubricants or coolants) manner, under dry drilling conditions. For the machining trials, experiments were designed and completed. A product of a full factorial 2³ and a block of two factors (3 × 2) was used with surface roughness as the response variable measured as the mean roughness average. Analysis of variance (ANOVA) was used to examine the results. A set of optimized tool and cutting conditions is presented for performing dry drilling repair operations.

| S-EPMC6119854 | biostudies-literature

Revealing extraordinary tensile plasticity in layered Ti-Al metal composite.

Project description:Layered Ti-Al metal composite (LMC) fabricated by hot-pressing and hot-rolling process displays higher ductility than that of both components. In this paper, a combination of digital image correlation (DIC) and X-ray tomography revealed that strain delocalization and constrained crack distribution are the origin of extraordinary tensile ductility. Strain delocalization was derived from the transfer of strain partitioning between Ti and Al layer, which relieved effectively the strain localization of LMC. Furthermore, the extensive cracks of LMC were restricted in the interface due to constraint effect. Layered architecture constrained the distribution of cracks and significantly relieved the strain localization. Meanwhile, the transfer of strain partitioning and constrained crack distribution were believed to inhibit the strain localization of Ti and change the deformation mechanisms of Ti. Our finding enriches current understanding about simultaneously improving the strength and ductility by structural design.

| S-EPMC5137039 | biostudies-literature

Stretchable Hybrid Bilayered Luminescent Composite Based on the Combination of Strain-Induced and Triboelectrification-Induced Electroluminescence.

Project description:High luminescence intensity from materials that are excited by external stimuli is highly desired. In this work, a stretchable hybrid luminescent composite (HLC) that has multiple luminescence modes is reported. The luminescence can be excited either by externally applied mechanical strain or by a moving object that slides against the HLC. When the HLC is deformed, such as being twisted or folded, the ZnS/Cu phosphor experiences mechanical strain that trigger the mechanoluminescence (ML) of the phosphors. Moreover, as the HLC slides against a contact object, the triboelectrification at the contact interface induces the electroluminescence of phosphor. Here, a series of internal and external factors were studied on how they influence the luminescent intensity. It is found that the luminescent intensity from the two modes can be superposed. The HLC material was used to fabricate a fiber-based luminescent device that can be driven by air flow. The overall luminescent intensity is enhanced by over 72% compared to that obtained solely from the ML. The HLC reported in this work has such potential applications as self-powered light sources and sensors as means of detecting dynamic motions and interaction.

| S-EPMC6906773 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data