Paper Sludge Reuse in Lightweight Aggregates Manufacturing.

ABSTRACT: The lightweight aggregates used by the civil engineering market are sintered at a high temperature, about 1200 °C. In times of high energy prices and regulation of carbon dioxide emissions, lightweight aggregate products of the high-temperature process in sales marketing are not readily accepted. This study developed a sintered-type paper sludge lightweight aggregate. In order to reduce energy consumption, substitution of some reservoir sediment clay in paper sludge substitutes is to be expected. The study used two types of paper sludge (green clay paper sludge and paper pulp sludge). The sintering temperature was reduced effectively as the green clay paper sludge was substituted for some of the reservoir sediment clay, and the optimum substitute ranges of green clay paper sludge were 10%-50%. The optimum substitute ranges of the paper pulp sludge were 10%-40%. Test results show that the properties of aggregates have a particle density of 0.66-1.69 g/cm³, a water absorption of 5%-30%, and a loss on ignition of 10%-43%. The loss on ignition of aggregate became greater with the increase in paper sludge content. This means that the calorific value provided by the paper sludge will increase as paper sludge content increases. Paper sludge can therefore be considered a good material to provide heat energy for sintering lightweight aggregate.

SUBMITTER: Chen HJ

PROVIDER: S-EPMC5457188 | biostudies-other | 2016 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Manufacturing of Lightweight Aggregates as an Auspicious Method of Sewage Sludge Utilization.

Project description:Sewage sludge is a high-volume and low-cost waste commonly generated worldwide, so its utilization is a vital issue. The application of this waste in the manufacturing of lightweight aggregates was investigated. The process was performed using intensive mixers with volumes of 5 and 30 L, as well as the industrial 500 L mixer. Then, granulates were sintered in a tube furnace. The influence of composition and mixer size on the particle size, microstructure, mechanical performance, and stability of lightweight aggregates in different environments was analyzed. The best results were obtained for a 500 L mixer, enhancing the industrial potential of the presented process. Increasing the share of sewage sludge in the composition of aggregates enhanced their porosity and reduced the specific weight, which caused a drop in compressive strength. Nevertheless, for all analyzed materials, the mechanical performance was superior compared to many commercial products. Therefore, sewage sludge can be efficiently applied as a raw material for the manufacturing of lightweight aggregates. The presented results confirm that a proper adjustment of composition allows easy the tailoring of aggregates' performance and cost.

| S-EPMC7764059 | biostudies-literature

Coal Combustion Wastes Reuse in Low Energy Artificial Aggregates Manufacturing.

Project description:Sustainable building material design relies mostly on energy saving processes, decrease of raw materials consumption, and increase of waste and by-products recycling. Natural and lightweight artificial aggregates production implies relevant environmental impact. This paper addresses both the issues of residues recycling and energy optimization. Particularly, three coal combustion wastes (Weathered Fly Ash, WFA; Wastewater Treatment Sludge, WTS; Desulfurization Device Sludge, DDS) supplied by the Italian electric utility company (ENEL) have been employed in the manufacture of cold bonded artificial aggregates. Previously, the residues have been characterized in terms of chemical and mineralogical compositions, water content, particle size distribution, and heavy metal release behavior. These wastes have been used in the mix design of binding systems with the only addition of lime. Finally, the artificial aggregates have been submitted to physical, mechanical, and leaching testing, revealing that they are potentially suitable for many civil engineering applications.

| S-EPMC5452781 | biostudies-other

Paper sludge

Project description:Paper sludge Metagenome

| PRJNA437549 | ENA

Accurate additive manufacturing of lightweight and elastic carbons using plastic precursors.

Project description:Despite groundbreaking advances in the additive manufacturing of polymers, metals, and ceramics, scaled and accurate production of structured carbons remains largely underdeveloped. This work reports a simple method to produce complex carbon materials with very low dimensional shrinkage from printed to carbonized state (less than 4%), using commercially available polypropylene precursors and a fused filament fabrication-based process. The control of macrostructural retention is enabled by the inclusion of fiber fillers regardless of the crosslinking degree of the polypropylene matrix, providing a significant advantage to directly control the density, porosity, and mechanical properties of 3D printed carbons. Using the same printed plastic precursors, different mechanical responses of derived carbons can be obtained, notably from stiff to highly compressible. This report harnesses the power of additive manufacturing for producing carbons with accurately controlled structure and properties, while enabling great opportunities for various applications.

| S-EPMC10825225 | biostudies-literature

Pulp-Paper Sludge

Project description:Profiling of bacterial communities grown in secondary sludge of pulp paper mill

| PRJNA1090633 | ENA

Bioconversion of paper sludge to biofuel by simultaneous saccharification and fermentation using a cellulase of paper sludge origin and thermotolerant Saccharomyces cerevisiae TJ14.

Project description:BackgroundEthanol production from paper sludge (PS) by simultaneous saccharification and fermentation (SSF) is considered to be the most appropriate way to process PS, as it contains negligible lignin. In this study, SSF was conducted using a cellulase produced from PS by the hypercellulase producer, Acremonium cellulolyticus C-1 for PS saccharification, and a thermotolerant ethanol producer Saccharomyces cerevisiae TJ14 for ethanol production. Using cellulase of PS origin minimizes biofuel production costs, because the culture broth containing cellulase can be used directly.ResultsWhen 50 g PS organic material (PSOM)/l was used in SSF, the ethanol yield based on PSOM was 23% (g ethanol/g PSOM) and was two times higher than that obtained by a separate hydrolysis and fermentation process. Cellulase activity throughout SSF remained at around 60% of the initial activity. When 50 to 150 g PSOM/l was used in SSF, the ethanol yield was 21% to 23% (g ethanol/g PSOM) at the 500 ml Erlenmeyer flask scale. Ethanol production and theoretical ethanol yield based on initial hexose was 40 g/l and 66.3% (g ethanol/g hexose) at 80 h, respectively, when 161 g/l of PSOM, 15 filter paper units (FPU)/g PSOM, and 20% inoculum were used for SSF, which was confirmed in the 2 l scale experiment. This indicates that PS is a good raw material for bioethanol production.ConclusionsEthanol concentration increased with increasing PSOM concentration. The ethanol yield was stable at PSOM concentrations of up to 150 g/l, but decreased at concentrations higher than 150 g/l because of mass transfer limitations. Based on a 2 l scale experiment, when 1,000 kg PS was used, 3,182 kFPU cellulase was produced from 134.7 kg PS. Produced cellulase was used for SSF with 865.3 kg PS and ethanol production was estimated to be 51.1 kg. Increasing the yeast inoculum or cellulase concentration did not significantly improve the ethanol yield or concentration.

| S-EPMC3203334 | biostudies-literature

Modification of Lightweight Aggregates' Microstructure by Used Motor Oil Addition.

Project description:An admixture of lightweight aggregate substrates (beidellitic clay containing 10 wt % of natural clinoptilolite or Na-P1 zeolite) with used motor oil (1 wt %-8 wt %) caused marked changes in the aggregates' microstructure, measured by a combination of mercury porosimetry (MIP), microtomography (MT), and scanning electron microscopy. Maximum porosity was produced at low (1%-2%) oil concentrations and it dropped at higher concentrations, opposite to the aggregates' bulk density. Average pore radii, measured by MIP, decreased with an increasing oil concentration, whereas larger (MT) pore sizes tended to increase. Fractal dimension, derived from MIP data, changed similarly to the MIP pore radius, while that derived from MT remained unaltered. Solid phase density, measured by helium pycnometry, initially dropped slightly and then increased with the amount of oil added, which was most probably connected to changes in the formation of extremely small closed pores that were not available for He atoms.

| S-EPMC5456622 | biostudies-other

Mechanical and Physical Properties of Hydrophobized Lightweight Aggregate Concrete with Sewage Sludge.

Project description:This article is focused on lightweight aggregate-concrete modified by municipal sewage sludge and lightweight aggregate-concrete obtained from light aggregates. The article presents laboratory examinations of material physical parameters. Water absorptivity of the examined material was decreased by the admixture of water emulsion of reactive polysiloxanes. Water transport properties were determined using Time Domain Reflectometry, an indirect technique for moisture detection in porous media. Together with basic physical parameters, the heat conductivity coefficient λ was determined for both types of lightweight aggregate-concrete. Analysis of moisture and heat properties of the examined materials confirmed the usefulness of light aggregates supplemented with sewage sludge for prospective production.

| S-EPMC5503055 | biostudies-other

Feasible and effective reuse of municipal sludge for vegetation restoration: physiochemical characteristics and microbial diversity.

Project description:The large volume of municipal sludge causes environmental problems in cities worldwide. In this study, municipal sludge, mixed with construction waste residue, was used as substrate to plant Ailanthus altissima. The growth of A. altissima, the substrate characteristics, and substrate microbial diversity were measured to investigate potential recycling and reusing pathways of municipal sludge. The obtained results showed that compared to garden soil, the mixed substrate was weakly alkaline, and had higher nutrient contents, which is beneficial for A. altissima, and results in better growth in mixed substrate. Although the contents of the main heavy metals in the mixed substrate were significantly higher than in garden soil, the values met the criterion of Class II soil in the Environmental Quality Standard for the Soils of China (GB15618-1995). Different substrates showed a variety of microbial diversities. Proteobacteria was the top microbial phylum in all samples, and higher relative abundances were found in samples containing municipal sludge. After growing A. altissima, the relative abundances of Acidobacteria and Gemmatimonadetes increased in the mixed substrate. Therefore, addition of construction waste residue and growth of A. altissima caused a difference. The microbial communities in the mixed substrate with A. altissima are both plant friendly and environmentally friendly. These results suggest this mixed substrate as a potentially feasible and effective pathway for the reuse and recycling of municipal sludge for vegetation restoration.

| S-EPMC6351607 | biostudies-literature

Surface chemistry in Ti-6Al-4V feedstock as influenced by powder reuse in electron beam additive manufacturing

Project description:X-ray photoelectron spectroscopy (XPS) as well as scanning and transmission electron microscopy (SEM/TEM) analysis was carried out on four Ti-6Al-4V powders used in electron beam powder-bed fusion (PBF-EB) production environments: virgin low oxygen (0.080 wt% O), reused medium oxygen (0.140 wt% O), reused high oxygen (0.186 wt% O), and virgin high oxygen (0.180 wt% O). The two objectives of this comparative analyses were to (1) investigate high oxygen containing Grade 23 Ti-6Al-4V powders which were further oxidized as a function of reuse and (2) comparing the two virgin Grade 23 and Grade 5 powders of similar oxygen content. The microstructure of the low oxygen virgin Grade 23 powder was consistent with martensitic α′ microstructure, whereas the reused powder displayed tempered α/β Widmänstatten microstructure. XPS revealed a decrease in TiO2 at the surface of the reused powders with an increase in Al2O3. This trend is energetically favorable at the temperatures and pressures in PBF-EB machines, and it is consistent with the thermodynamics of Al2O3 vs. TiO2 reactions. An unexpected amount of nitrogen was measured on the titanium powder, with a general increase in nitride on the surface of the particles as a function of reuse in the Grade 23 powder.1

| S-EPMC9901169 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data