Modification of Lightweight Aggregates' Microstructure by Used Motor Oil Addition.

ABSTRACT: An admixture of lightweight aggregate substrates (beidellitic clay containing 10 wt % of natural clinoptilolite or Na-P1 zeolite) with used motor oil (1 wt %-8 wt %) caused marked changes in the aggregates' microstructure, measured by a combination of mercury porosimetry (MIP), microtomography (MT), and scanning electron microscopy. Maximum porosity was produced at low (1%-2%) oil concentrations and it dropped at higher concentrations, opposite to the aggregates' bulk density. Average pore radii, measured by MIP, decreased with an increasing oil concentration, whereas larger (MT) pore sizes tended to increase. Fractal dimension, derived from MIP data, changed similarly to the MIP pore radius, while that derived from MT remained unaltered. Solid phase density, measured by helium pycnometry, initially dropped slightly and then increased with the amount of oil added, which was most probably connected to changes in the formation of extremely small closed pores that were not available for He atoms.

SUBMITTER: Franus M

PROVIDER: S-EPMC5456622 | biostudies-other | 2016 Oct

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Paper Sludge Reuse in Lightweight Aggregates Manufacturing.

Project description:The lightweight aggregates used by the civil engineering market are sintered at a high temperature, about 1200 °C. In times of high energy prices and regulation of carbon dioxide emissions, lightweight aggregate products of the high-temperature process in sales marketing are not readily accepted. This study developed a sintered-type paper sludge lightweight aggregate. In order to reduce energy consumption, substitution of some reservoir sediment clay in paper sludge substitutes is to be expected. The study used two types of paper sludge (green clay paper sludge and paper pulp sludge). The sintering temperature was reduced effectively as the green clay paper sludge was substituted for some of the reservoir sediment clay, and the optimum substitute ranges of green clay paper sludge were 10%-50%. The optimum substitute ranges of the paper pulp sludge were 10%-40%. Test results show that the properties of aggregates have a particle density of 0.66-1.69 g/cm³, a water absorption of 5%-30%, and a loss on ignition of 10%-43%. The loss on ignition of aggregate became greater with the increase in paper sludge content. This means that the calorific value provided by the paper sludge will increase as paper sludge content increases. Paper sludge can therefore be considered a good material to provide heat energy for sintering lightweight aggregate.

| S-EPMC5457188 | biostudies-other

A lightweight YOLOv3 algorithm used for safety helmet detection.

Project description:YOLOv3 is a popular and effective object detection algorithm. However, YOLOv3 has a complex network, and floating point operations (FLOPs) and parameter sizes are large. Based on this, the paper designs a new YOLOv3 network and proposes a lightweight object detection algorithm. First, two excellent networks, the Cross Stage Partial Network (CSPNet) and GhostNet, are integrated to design a more efficient residual network, CSP-Ghost-Resnet. Second, combining CSPNet and Darknet53, this paper designs a new backbone network, the ML-Darknet, to realize the gradient diversion of the backbone network. Finally, we design a lightweight multiscale feature extraction network, the PAN-CSP-Network. The newly designed network is named mini and lightweight YOLOv3 (ML-YOLOv3). Based on the helmet dataset, the FLPSs and parameter sizes of ML-YOLOv3 are only 29.7% and 29.4% of those of YOLOv3. Compared with YOLO5, ML-YOLOv3 also exhibits obvious advantages in calculation cost and detection effect.

| S-EPMC9243020 | biostudies-literature

Manufacturing of Lightweight Aggregates as an Auspicious Method of Sewage Sludge Utilization.

Project description:Sewage sludge is a high-volume and low-cost waste commonly generated worldwide, so its utilization is a vital issue. The application of this waste in the manufacturing of lightweight aggregates was investigated. The process was performed using intensive mixers with volumes of 5 and 30 L, as well as the industrial 500 L mixer. Then, granulates were sintered in a tube furnace. The influence of composition and mixer size on the particle size, microstructure, mechanical performance, and stability of lightweight aggregates in different environments was analyzed. The best results were obtained for a 500 L mixer, enhancing the industrial potential of the presented process. Increasing the share of sewage sludge in the composition of aggregates enhanced their porosity and reduced the specific weight, which caused a drop in compressive strength. Nevertheless, for all analyzed materials, the mechanical performance was superior compared to many commercial products. Therefore, sewage sludge can be efficiently applied as a raw material for the manufacturing of lightweight aggregates. The presented results confirm that a proper adjustment of composition allows easy the tailoring of aggregates' performance and cost.

| S-EPMC7764059 | biostudies-literature

Diesel fuel from used frying oil.

Project description:New conversion technologies of used edible oils and waste animal fats into a biofuel appropriate for use in standard diesel engines have been developed, taking into consideration environmental requirements and improvement in the economics of current trans-esterification technologies. The variation in the properties of substrates made from used rape oil after treatment with mixed adsorbents (active carbon, magnesium silicate) was studied in this work. The obtained results are compared with the quality requirements for the substrates used in Vogel & Noot GmbH technology for transesterification of oils and fats.

| S-EPMC3915488 | biostudies-other

Wobble tRNA modification dependent protein aggregates modification

Project description:We want to assess the features of proteins whose aggregation depends on defects in traslation by the loss of the mcm5s2 modification on the urifdine in position 34 of some tRNAs.

2021-02-24 | PXD019590 | Pride

Short- and Long-Term Epoxy Modification of Bitumen: Modification Kinetics, Rheological Properties, and Microstructure.

Project description:Aiming to gain knowledge in the epoxy-bitumen modification mechanisms, this work explores the effects that epoxy concentration and ambient curing exert on the physico-chemistry and thermo-rheological properties of epoxy-modified binders. Process rheokinetics of epoxy-bitumen blends indicates that binder short-term modification (i.e., during processing) is accelerated by epoxy concentration. Furthermore, a synergistic effect of epoxy concentration and ambient curing is found during long-term modification (i.e., during curing at ambient conditions). As a result, viscous and viscoelastic rheological properties of binders are enhanced at medium/high in-service temperatures, at least, after one month of curing. FTIR (Fourier Transform Infrared spectroscopy) tests and SARAs (Saturates, Aromatics, Resins and Asphaltenes) analysis confirm the existence of esterification/etherification reactions between epoxy oxirane groups and the carbonyl groups available in aromatic and resin molecules. Thus, the new high molecular weight compounds increase the asphaltenic fraction of modified bitumen. Likewise, nonreversing heat flow curves obtained by modulated calorimetry corroborate the formation of such highly structured domains responsible for the final binder performance.

| S-EPMC7182878 | biostudies-literature

Surface Modification of Lightweight Mortars by Nanopolymers to Improve Their Water-Repellency and Durability.

Project description:The paper explores the possibility of covering the mortar with the lightweight aggregate by the nanopolymer silane and siloxane as surface hydrophobisation. The investigation involved the mortars with two types of hydrophobic agents diluted with water in a ratio of 1:4 and 1:8. Mortar wetting properties were determined by measuring the absorbability, water vapor diffusion, contact angle (CA) and surface free energy (SFE) of their structure. Surface micro-roughness and 2D topography were evaluated. Scanning electron microscopy (SEM) has shown the microstructure and distribution of pores in mortars. The reduction in absorbency after the first day of testing by 87% was shown. An improvement in frost resistance after 25 cycles by 97% and an 18-fold decrease in weight loss after the sulphate crystallization test were observed. The hydrophobic coating reduces the SFE of mortars and increases the CA. In the case of using silanes, a 9-fold increase CA was observed.

| S-EPMC7143614 | biostudies-literature

Effects of Wastes from the Brewing Industry in Lightweight Aggregates Manufactured with Clay for Green Roofs.

Project description:This study investigates the effects of sieved wastes generated from the brewing industry on lightweight aggregates manufactured with clay. Sludge from a wastewater treatment plant, bagasse and diatomaceous earth were used to obtain the samples. These wastes are usually dumped in landfills, but the current increase in restrictions on dumping and interest in improving the environment make our proposal for gaining value from these wastes a significant contribution. Laboratory tests show that the new aggregate has low bulk density and increased water absorption and porosity. The thermographic camera results provide evidence that new aggregates have significant insulating properties and are suitable for use on green roofs.

| S-EPMC5459013 | biostudies-other

Efficient Addition of Waste Glass in MK-Based Geopolymers: Microstructure, Antibacterial and Cytotoxicity Investigation.

Project description:Reuse of waste glass can significantly decrease the quantity of waste to be treated or disposed of in landfills, allowing to both diminish the ecological damage and to reduce the costs of transportation for removal. Geopolymer mixes with diverse percentages (20, 50 and 60 wt%) and with different grain size ranges (37 μm < diam < 53 μm; 75 μm < diam < 105 μm) of waste glass and the residual part of pure metakaolin were prepared by addition of NaOH and sodium silicate as alkaline activator solutions. The effect of waste glass on the mechanical and microstructure of new geopolymers has been explored in this study. Fourier transform infrared spectroscopy (FTIR) evidenced the reactivity of waste glass in terms of Si-O and Si-O-Al bonds, more evident for the finer waste glass powder. The consolidation of the materials has been established by reduced weight loss in water and decreased pH and ionic conductivity of the eluate after 7, 14 and 28 days of curing at room temperature. The decrease of the mechanical properties with waste glass content was less evident for the finer glassy powders, yet the value of about 4-5 MPa indicates their potential use as non-structural materials. The consolidated final materials were tested for their effects on the microbial growth of Escherichia coli and Enterococcus faecalis after 24 and 48 h, respectively. The samples showed a very limited and absent inhibition zone, for fine and coarse grain size ranges, respectively. Finally, the cytotoxicity tests accomplished the ecological valuation of the final consolidated products.

| S-EPMC8124374 | biostudies-literature

Modification of Honeybee Silk by the Addition of Antimicrobial Agents.

Project description:Honeybee silk proteins can be produced at high levels in recombinant systems, fabricated into materials, and are tolerant of amino acid modifications: properties that make them exciting templates for designing new functional materials. Here, we explore the properties of materials either made from silk-antimicrobial peptide (AMP) fusion proteins or silk containing entrapped AMPs or silver nanoparticles. Inclusion of AMP within the silk protein sequence did not affect our ability to express the proteins or process them into films. When AMP-silk proteins and Escherichia coli cells were coincubated in solution, a reduction in cell numbers was observed after degradation of the chimeric protein to release a truncated version of the AMP. In films, the AMP was retained in the silk with leaching rates of <1% per day. Films containing silver nanoparticles were antimicrobial, with the silk preventing aggregation of nanoparticles and slowing the rate of dissolution of the particles.

| S-EPMC6044942 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data