Damage Evolution and Life Prediction of Cross-Ply C/SiC Ceramic-Matrix Composite under Cyclic Fatigue Loading at Room Temperature and 800 °C in Air.

ABSTRACT: The damage evolution and life prediction of cross-ply C/SiC ceramic-matrix composite (CMC) under cyclic-fatigue loading at room temperature and 800 °C in air have been investigated using damage parameters derived from fatigue hysteresis loops, i.e., fatigue hysteresis modulus and fatigue hysteresis loss energy. The experimental fatigue hysteresis modulus and fatigue hysteresis loss energy degrade with increasing applied cycles attributed to transverse cracks in the 90° plies, matrix cracks and fiber/matrix interface debonding in the 0° plies, interface wear at room temperature, and interface and carbon fibers oxidation at 800 °C in air. The relationships between fatigue hysteresis loops, fatigue hysteresis modulus and fatigue hysteresis loss energy have been established. Comparing experimental fatigue hysteresis loss energy with theoretical computational values, the fiber/matrix interface shear stress corresponding to different cycle numbers has been estimated. It was found that the degradation rate at 800 °C in air is much faster than that at room temperature due to serious oxidation in the pyrolytic carbon (PyC) interphase and carbon fibers. Combining the fiber fracture model with the interface shear stress degradation model and the fibers strength degradation model, the fraction of broken fibers versus the cycle number can be determined for different fatigue peak stresses. The fatigue life S-N curves of cross-ply C/SiC composite at room temperature and 800 °C in air have been predicted.

SUBMITTER: Li L

PROVIDER: S-EPMC5458855 | biostudies-other | 2015 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Fatigue Damage and Lifetime of SiC/SiC Ceramic-Matrix Composite under Cyclic Loading at Elevated Temperatures.

Project description:In this paper, the fatigue damage and lifetime of 2D SiC/SiC ceramic-matrix composites (CMCs) under cyclic fatigue loading at 750, 1000, 1100, 1200 and 1300 °C in air and in steam atmosphere have been investigated. The damage evolution versus applied cycles of 2D SiC/SiC composites were analyzed using fatigue hysteresis dissipated energy, fatigue hysteresis modulus, fatigue peak strain and interface shear stress. The presence of steam accelerated the damage development inside of SiC/SiC composites, which increased the increasing rate of the fatigue hysteresis dissipated energy and the fatigue peak strain, and the decreasing rate of the fatigue hysteresis modulus and the interface shear stress. The fatigue life stress-cycle (S-N) curves and fatigue limit stresses of 2D SiC/SiC composites at different temperatures in air and in steam condition have been predicted. The fatigue limit stresses approach 67%, 28%, 39% 17% and 28% tensile strength at 750, 1000, 1100, 1200 and 1300 °C in air, and 49%, 10%, 9% and 19% tensile strength at 750, 1000, 1200 and 1300 °C in steam conditions, respectively.

| S-EPMC5506978 | biostudies-other

Comparisons of Damage Evolution between 2D C/SiC and SiC/SiC Ceramic-Matrix Composites under Tension-Tension Cyclic Fatigue Loading at Room and Elevated Temperatures.

Project description:In this paper, comparisons of damage evolution between 2D C/SiC and SiC/SiC ceramic-matrix composites (CMCs) under tension-tension cyclic fatigue loading at room and elevated temperatures have been investigated. Fatigue hysteresis loops models considering multiple matrix cracking modes in 2D CMCs have been developed based on the damage mechanism of fiber sliding relative to the matrix in the interface debonded region. The relationships between the fatigue hysteresis loops, fatigue hysteresis dissipated energy, fatigue peak stress, matrix multiple cracking modes, and interface shear stress have been established. The effects of fiber volume fraction, fatigue peak stress and matrix cracking mode proportion on fatigue hysteresis dissipated energy and interface debonding and sliding have been analyzed. The experimental fatigue hysteresis dissipated energy of 2D C/SiC and SiC/SiC composites at room temperature, 550 °C, 800 °C, and 1100 °C in air, and 1200 °C in vacuum corresponding to different fatigue peak stresses and cycle numbers have been analyzed. The interface shear stress degradation rate has been obtained through comparing the experimental fatigue hysteresis dissipated energy with theoretical values. Fatigue damage evolution in C/SiC and SiC/SiC composites has been compared using damage parameters of fatigue hysteresis dissipated energy and interface shear stress degradation rate. It was found that the interface shear stress degradation rate increases at elevated temperature in air compared with that at room temperature, decreases with increasing loading frequency at room temperature, and increases with increasing fatigue peak stress at room and elevated temperatures.

| S-EPMC5456581 | biostudies-other

Comparison of Cyclic Hysteresis Behavior between Cross-Ply C/SiC and SiC/SiC Ceramic-Matrix Composites.

Project description:In this paper, the comparison of cyclic hysteresis behavior between cross-ply C/SiC and SiC/SiC ceramic-matrix composites (CMCs) has been investigated. The interface slip between fibers and the matrix existed in the matrix cracking mode 3 and mode 5, in which matrix cracking and interface debonding occurred in the 0° plies are considered as the major reason for hysteresis loops of cross-ply CMCs. The hysteresis loops of cross-ply C/SiC and SiC/SiC composites corresponding to different peak stresses have been predicted using present analysis. The damage parameter, i.e., the proportion of matrix cracking mode 3 in the entire matrix cracking modes of the composite, and the hysteresis dissipated energy increase with increasing peak stress. The damage parameter and hysteresis dissipated energy of C/SiC composite under low peak stress are higher than that of SiC/SiC composite; However, at high peak stress, the damage extent inside of cross-ply SiC/SiC composite is higher than that of C/SiC composite as more transverse cracks and matrix cracks connect together.

| S-EPMC5456556 | biostudies-other

Fatigue Life Prediction of Fiber-Reinforced Ceramic-Matrix Composites with Different Fiber Preforms at Room and Elevated Temperatures.

Project description:In this paper, the fatigue life of fiber-reinforced ceramic-matrix composites (CMCs) with different fiber preforms, i.e., unidirectional, cross-ply, 2D (two dimensional), 2.5D and 3D CMCs at room and elevated temperatures in air and oxidative environments, has been predicted using the micromechanics approach. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. The statistical matrix multicracking model and fracture mechanics interface debonding criterion were used to determine the matrix crack spacing and interface debonded length. Under cyclic fatigue loading, the fiber broken fraction was determined by combining the interface wear model and fiber statistical failure model at room temperature, and interface/fiber oxidation model, interface wear model and fiber statistical failure model at elevated temperatures, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfies the Global Load Sharing (GLS) criterion. When the broken fiber fraction approaches the critical value, the composites fatigue fracture.

| S-EPMC5456649 | biostudies-other

Porous SiC and SiC/Cf Ceramic Microspheres Derived from Polyhydromethylsiloxane by Carbothermal Reduction.

Project description:A simple and inexpensive method for the preparation of porous SiC microspheres is presented. Polysiloxane microspheres derived from polyhydromethylsiloxane (PHMS) cross-linked with divinylbenzene (DVB) were ceramized under conditions leading to the removal of oxygen from the material. The content of free carbon (Cf) in highly crystalline silicon carbide (SiC) particles can be controlled by using various proportions of DVB in the synthesis of the pre-ceramic material. The chemical structure of the ceramic microspheres was studied by elemental analysis for carbon and oxygen, 29Si MAS NMR, 13C MAS NMR, SEM/EDS, XRD and Raman spectroscopies, and their morphology by SEM, nitrogen adsorption and mercury intrusion porosimetries. The gaseous products of the thermal reduction processes formed during ceramization created a porous structure of the microspheres. In the SiC/Cf microspheres, meso/micro pores were formed, while in carbon-free SiC, microspheres macroporosity dominated.

| S-EPMC8745781 | biostudies-literature

In Situ Polymerization on a 3D Ceramic Framework of Composite Solid Electrolytes for Room-Temperature Solid-State Batteries.

Project description:Solid-state batteries (SSBs) are ideal candidates for next-generation high-energy-density batteries in the Battery of Things era. Unfortunately, SSB application is limited by their poor ionic conductivity and electrode-electrolyte interfacial compatibility. Herein, in situ composite solid electrolytes (CSEs) are fabricated by infusing vinyl ethylene carbonate monomer into a 3D ceramic framework to address these challenges. The unique and integrated structure of CSEs generates inorganic, polymer, and continuous inorganic-polymer interphase pathways that accelerate ion transportation, as revealed by solid-state nuclear magnetic resonance (SSNMR) analysis. In addition, the mechanism and activation energy of Li+ transportation are studied and visualized by performing density functional theory calculations. Furthermore, the monomer solution can penetrate and polymerize in situ to form an excellent ionic conductor network inside the cathode structure. This concept is successfully applied to both solid-state lithium and sodium batteries. The Li|CSE|LiNi0.8 Co0.1 Mn0.1 O2 cell fabricated herein delivers a specific discharge capacity of 118.8 mAh g-1 after 230 cycles at 0.5 C and 30 °C. Meanwhile, the Na|CSE|Na3 Mg0.05 V1.95 (PO4 )3 @C cell fabricated herein maintains its cycling stability over 3000 cycles at 2 C and 30 °C with zero-fading. The proposed integrated strategy provides a new perspective for designing fast ionic conductor electrolytes to boost high-energy solid-state batteries.

| S-EPMC10375120 | biostudies-literature

High-performance ceramic/epoxy composite adhesives enabled by rational ceramic bandgaps.

Project description:High over-all properties, including low dielectric loss, high breakdown strength, high mechanical shock strength, high thermal conductivity and high weight stability, are very difficult to simultaneously achieve in electrical-insulation applicable cured potting-adhesive materials. To deal with this challenge, in this work, we have designed and fabricated a series of epoxy based composite potting-adhesives filled with low-cost and high-performance inorganic micro-particles including alpha-silica, alpha-alumina and alpha-SiC. Combination employment of high-molecular-weight and low-molecular-weight epoxy resins as matrices has been made. Heat-induced curing or crosslink of resin matrices has been carried out. Large band gap of silica filler has endowed the cured composite with high breakdown strength and ageing breakdown strength, and meanwhile relatively high deformation trait of silica has led to high shock strength of cured composite. Silica filler has been found to be superior to other two fillers, namely, optimal over-all properties such as dielectric, breakdown, mechanical and thermal features have been obtained in silica filled cured composite. High breakdown strength of ~48?MV m-1 and shock strength of ~9950?J?m-2 have been achieved in silica loaded composite. This work might open up the way for large-scale fabrication of promising epoxy-based hybrid potting-adhesives.

| S-EPMC6965657 | biostudies-literature

Next Generation Ceramic Substrate Fabricated at Room Temperature.

Project description:A ceramic substrate must not only have an excellent thermal performance but also be thin, since the electronic devices have to become thin and small in the electronics industry of the next generation. In this manuscript, a thin ceramic substrate (thickness: 30-70 µm) is reported for the next generation ceramic substrate. It is fabricated by a new process [granule spray in vacuum (GSV)] which is a room temperature process. For the thin ceramic substrates, AlN GSV films are deposited on Al substrates and their electric/thermal properties are compared to those of the commercial ceramic substrates. The thermal resistance is significantly reduced by using AlN GSV films instead of AlN bulk-ceramics in thermal management systems. It is due to the removal of a thermal interface material which has low thermal conductivity. In particular, the dielectric strengths of AlN GSV films are much higher than those of AlN bulk-ceramics which are commercialized, approximately 5 times. Therefore, it can be expected that this GSV film is a next generation substrate in thermal management systems for the high power application.

| S-EPMC5529459 | biostudies-literature

The Oxidation Behavior of ZrB2-SiC Ceramic Composites Fabricated by Plasma Spray Process.

Project description:Our goal is to develop a structural ceramic for high-temperature applications in which silicon carbide-based materials (SiCs) are used as matrix composites. The potential of SiCs to deposit a mixture of SiC and zirconium diboride (ZrB2) plasma spray coating is analyzed. To deposit thermal barrier layers containing up to 50 vol.% SiC, a high-pressure plasma spray (HPPS) process was used. Although the SiC cannot be deposited by thermal spray, a mixture of SiC and zirconium diboride (ZrB2) was deposited because these two compounds form a eutectic phase at a temperature below SiC decomposition. The preference was two different forms, 3 mm and 1 mm, of graphite substrates with different thickness values. A comparison of the morphology of SiC-ZrB2 coatings before and after thermal treatment was performed by applying heat to the surface of a gas torch and traditional furnace between 800 °C and 1200 °C. The growth of the oxide scale was calculated with X-ray diffraction (XRD), scanning electron microscopy (SEM)/energy dispersive X-ray analysis (EDX), transmission electron microscopy (TEM), and density. The oxide scale consists of a SiO2 layer with ZrO2 groups. The findings indicate a greater potential for the studied material in protecting against high-temperature oxidation and in a wide variety of aerospace applications.

| S-EPMC7830389 | biostudies-literature

Sliding contact fatigue damage in layered ceramic structures.

Project description:Porcelain-veneered restorations often chip and fracture from repeated occlusal loading, making fatigue studies relevant. Most fatigue studies are limited to uni-axial loading without sliding motion. We hypothesized that bi-axial loading (contact-load-slide-liftoff, simulating a masticatory cycle), as compared with uni-axial loading, accelerates the fatigue of layered ceramics. Monolithic glass plates were epoxy-joined to polycarbonate substrates as a transparent model for an all-ceramic crown on dentin. Uni-and bi-axial cyclic contact was applied through a hard sphere in water, by means of a mouth-motion simulator apparatus. The uni-axial (contact-load-hold-liftoff) and traditional R-ratio fatigue (indenter never leaves the specimen surface) produced similar lifespans, while bi-axial fatigue was more severe. The accelerated crack growth rate in bi-axial fatigue is attributed to enhanced tensile stresses at the trailing edges of a moving indenter. Fracture mechanics descriptions for damage evolution in brittle materials loaded repeatedly with a sliding sphere are provided. Clinical relevance is addressed.

| S-EPMC4708265 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data