Morphological, Rheological, and Mechanical Properties of Polyamide 6/Polypropylene Blends Compatibilized by Electron-Beam Irradiation in the Presence of a Reactive Agent.

ABSTRACT: An immiscible polyamide 6 (PA6)/polypropylene (PP) blend was compatibilized by electron-beam irradiation in the presence of reactive agent. Glycidyl methacrylate (GMA) was chosen as a reactive agent for interfacial cross-copolymerization between dispersed PP and continuous PA6 phases initiated by electron-beam irradiation. The PA6/PP (80/20) mixture containing GMA was prepared using a twin-screw extruder, and then exposed to an electron-beam at various doses at room temperature to produce compatibilized PA6/PP blends. The morphological, rheological, and mechanical properties of blends produced were investigated. Morphology analysis revealed that the diameter of PP particles dispersed in PA6 matrix was decreased with increased irradiation dose and interfacial adhesion increased due to high surface area of treated PP particles. Complex viscosities (η*) and storage moduli (G') of blends increased with increasing irradiation dose and were higher than those of PA6 and PP. The complex viscosity of the blend irradiated at 200 kGy was 64 and 8 times higher than PA6 and PP, respectively. The elongation at break of blend irradiated less than 100 kGy was about twice that of PA6. Electron beam treatment improved the compatibility at the interface between PA6 and PP matrix in the presence of GMA.

SUBMITTER: Shin BY

PROVIDER: S-EPMC5503080 | biostudies-other | 2016 May

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Novel compatibilized nylon-based ternary blends with polypropylene and poly(lactic acid): morphology evolution and rheological behaviour.

Project description:In this paper, the interaction between nylon 6 (PA6), polypropylene (PP) and poly(lactic acid) (PLA) is reported. To improve the compatibility between these immiscible polymers, a reactive compatibilization approach was used through extrusion with maleic anhydride grafted polypropylene (PP-g-MA). To further improve the compatibility of the phases, PLA was selected as a semi-polar polymer and a low molecular weight was used to assure a good droplet dispersion. All the blends were twin-screw extruded in the melt at different compositions. The morphologies of binary and ternary blends were investigated using microscopic techniques by means of scanning electron microscopy (SEM) and atomic force microscopy (AFM). The PP-g-MA grafting process was observed to have a dramatic effect on the compatibility of both the binary and ternary blends and while a drastic reduction of the PP dispersed phases particle size was observed, the affinity between PLA and PP was also highlighted. The surface tension of the homopolymers and the interfacial tension of the pairs of polymers were measured to characterize the interaction at their interfaces. The interaction of PA6/PLA appeared preferable to PLA/PP, explaining the thinner dispersion obtained for PLA phase. The morphologies observed were compared to the predictions of spreading coefficient and minimum free energy models. While both models predicted the encapsulation of PP by the PLA phase, disagreeing with the morphological results, the rheological measurement gave an explanation for this phase separation. Using rheology measurements, the interaction between the phases was further investigated and the viscosity ratios were measured for the different pairs of polymers, stressing the high interaction between PA6 and PLA with and without compatibilizer. The droplet size of the dispersed phases appeared to substantially influence the chain relaxations in the melt.

| S-EPMC9080108 | biostudies-literature

Rheological and Crystallization Properties of ABS/PA6-Compatibilized Blends via In Situ Reactive Extrusion.

Project description:ABS/PA6-compatibilized blends were prepared by in situ reactive extrusion method. The main objective was to evaluate the influences of the morphology and blend composition on the rheological and nonisothermal crystallization properties. The morphology of submicron-sized ABS droplets evenly dispersed in PA6 led to dilatant fluid behavior and a transition from elastic to viscous behavior in the low-frequency region. The crystallization results indicated that reactive blends had elevated crystallization temperatures and crystallization rates, which were due to the heterogeneous nucleation of the submicron-sized ABS particles. In addition, it was observed that the theory by Mo suitably described the nonisothermal crystallization process. The activation energy slightly decreased for ABS contents of 5 and 15 wt % and then increased for a content of 25 wt %, indicating that the ABS promoted the crystallization of the blends at appropriate contents.

| S-EPMC7331037 | biostudies-literature

Crystallization and Performance of Polyamide Blends Comprising Polyamide 4, Polyamide 6, and Their Copolymers.

Project description:Polyamide 4 (PA4) is a biobased and biodegradable polyamide. The high hydrogen bond density of PA4 bestows it with a high melting point that is close to its thermal decomposition temperature, thereby limiting the melt processing of PA4. In this study, PA4 was blended with polyamide 6 (PA6) and further modified with copolyamide 4/6 (R46). The effects of composition on the crystallization behavior of the blends were studied. The results demonstrated that the binary PA4/PA6 (B46) and ternary PA4/PA6/R46 (B46/R46) blends formed two crystalline phases (PA4- and PA6-rich phases) through crystallization-induced phase separation. With increasing PA6 content, the thermal stability and crystallinity of the B46 blend increased and decreased, respectively, and the contribution of PA6 toward the crystallization of the PA4-rich phase diminished. Molecular dynamics simulations showed the molecular chain orientation of the B46 blends well. The melting points, crystallinities, and grain sizes of the B46/R46 blends were lower than those of the B46 blends. The crystallization of the PA4-rich phase was restrained by the dilution effect of molten-state PA6, and the nucleation and crystallization of the PA6-rich phase were promoted by the presence of crystallized PA4. The B46 blends with 30-40 wt% PA6 had the best mechanical properties.

| S-EPMC10459628 | biostudies-literature

Prevention of peritoneal adhesions using polymeric rheological blends.

Project description:The effectiveness of rheological blends of high molecular weight hyaluronic acid (HA) and low molecular weight hydroxypropyl methylcellulose (HPMC) in the prevention of peritoneal adhesions post-surgery is demonstrated. The physical mixture of the two carbohydrates increased the dwell time in the peritoneum while significantly improving the injectability of the polymer compared with HA alone. HA-HPMC treatment decreased the total adhesion area by ∼ 70% relative to a saline control or no treatment in a repeated cecal injury model in the rabbit. No significant cytotoxicity and minimal inflammation were associated with the blend. Furthermore, no chemical or physical processing was required prior to their use beyond simple mixing.

| S-EPMC3929525 | biostudies-literature

Accelerated Laboratory Weathering of Polypropylene/Poly (Lactic Acid) Blends.

Project description:To solve the pollution problems that result from polypropylene (PP), suitable biopolymers such as poly (lactic acid) (PLA) were selected to blend with PP. Since PP/PLA blends are often exposed to the natural environment, it is necessary to study the photodegradation behavior of PP/PLA blends. In this paper, PP/PLA blends with different compositions were prepared by extrusion and subjected to the accelerated laboratory weathering equipment. The effects of compatibilizers on the degradation behavior of PP/PLA blends were also studied. The weatherability of PP/PLA blends was studied through weight loss, optical microscope, Fourier-transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). The results revealed that PP is easy to degrade than PLA during accelerated laboratory weathering. PP/PLA blends are susceptible to the accelerated laboratory weathering process, and PP-rich and PLA-rich blends reduce the weathering resistance. Moreover, the results indicate that the initial degradation temperature, melting temperature, and crystallization temperature decrease after weathering related to the decreased thermal stability of PP/PLA blends. For instance, the initial degradation temperature of PP/PLA8.2 reduces from 332.2 °C to 320.2 °C. Moreover, the compatibilized sample is generally more resistant to weathering conditions than the uncompatibilized one due to the higher compatibility of PP and PLA.

| S-EPMC9823939 | biostudies-literature

Towards High-performance Materials Based on Carbohydrate-Derived Polyamide Blends.

Project description:A bio-derived monomer called 2,3:4,5-di-O-isopropylidene-galactarate acid/ester (GalXMe) has great potential in polymer production. The unique properties of this molecule, such as its rigidity and bulkiness, contribute to the good thermal properties and appealing transparency of the material. The main problem, however, is that like other biobased materials, the polymers derived thereof are very brittle. In this study, we report on the melt blending of GalXMe polyamides (PAs) with different commercial PA grades using extrusion as well as blend characterization. Biobased PA blends showed limited to no miscibility with other polyamides. However, their incorporation resulted in strong materials with high Young moduli. The increase in modulus of the prepared GalXMe blends with commercial PAs ranged from up to 75% for blends with aliphatic polyamide composed of 1,6-diaminohexane and 1,12-dodecanedioic acid PA(6,12) to up to 82% for blends with cycloaliphatic polyamide composed of 4,4'-methylenebis(cyclohexylamine) and 1,12-dodecanedioic acid PA(PACM,12). Investigation into the mechanism of blending revealed that for some polyamides a transamidation reaction improved the blend compatibility. The thermal stability of the biobased PAs depended on which diamine was used. Polymers with aliphatic/aromatic or alicyclic diamines showed no degradation, whereas with fully aromatic diamines such as p-phenylenediamine, some degradation processes were observed under extrusion conditions (260/270 °C).

| S-EPMC6473389 | biostudies-literature

Mechanical Upcycling Immiscible Polyethylene Terephthalate-Polypropylene Blends with Carbon Fiber Reinforcement.

Project description:Ineffective sorting of post-consumer plastics remains one of the major obstacles in the recycling of plastics. Consequently, these highly heterogeneous, mixed post-consumer plastics will end up in landfill or have to be incinerated as repurposing them directly would lead to a polymer blend with inferior quality for many end-uses. In this work, we demonstrate the use of carbon fibers (CFs) to practically upgrade the mechanical properties of mixed plastics, adding value to them. This will create a stronger demand for mixed plastics to be used in various engineering applications. Using polyethylene terephthalate (PET) and polypropylene (PP) as the model immiscible polymer blend, we showed that the incorporation of CFs increased the tensile, flexural, and single-edge notched fracture toughness of the resulting CF-reinforced PET/PP composite blends. Despite the high environmental burden associated with the production of CFs, cradle-to-grave life-cycle analysis showed that CF-reinforced PET/PP composites have a lower environmental impact than the life-cycle scenarios of "doing nothing" and repurposing immiscible PET/PP blends as it is without CF reinforcement. This can be attributed to the weight saving achieved, a direct result of their higher mechanical performance. Our work opens up opportunities for the use of mixed plastics in various higher value applications such that they can be diverted away from landfill or incineration, in line with the concept of circular economy.

| S-EPMC9112279 | biostudies-literature

Thermomechanical Properties of Virgin and Recycled Polypropylene-High-Density Polyethylene Blends.

Project description:This paper provides evidence and discusses the variability in the thermomechanical behaviour of virgin and recycled polypropylene/high-density polyethylene blends without the addition of other components, which is sparse in the literature. Understanding the performance variability in recycled polymer blends is of critical importance in order to facilitate the re-entering of recycled materials to the consumer market and, thus, contribute towards a circular economy. This is an area that requires further research due to the inhomogeneity of recycled materials. Therefore, the thermal and mechanical properties of virgin and recycled polypropylene/high-density polyethylene blends were investigated systematically. Differential scanning calorimetry concludes that both the recycled and virgin blends are immiscible. Generally, recycled blends have lower overall crystallinity and melting temperatures compared with virgin blends while, remarkably, their crystallisation temperatures are compared favourably. Dynamical mechanical analysis showed little variation in the storage modulus of recycled and virgin blends. However, the alpha and beta relaxation temperatures are lower in recycled blends due to structural deterioration. Deterioration in the thermal and mechanical properties of recycled blends is thought to be caused by the presence of contaminants and structural degradation during reprocessing, resulting in shorter polymeric chains and the formation of imperfect crystallites. The tensile properties of recycled blends are also affected by the recycling process. The Young's modulus and yield strength of the recycled blends are inferior to those of virgin blends due to the deterioration during the recycling process. However, the elongation at break of the recycled blends is higher compared with the virgin blends, possibly due to the plasticity effect of the low-molecular-weight chain fragments.

| S-EPMC10647352 | biostudies-literature

Rheological Investigation of Relaxation Behavior of Polycarbonate/Acrylonitrile-Butadiene-Styrene Blends.

Project description:The rheological properties of polycarbonate/acrylonitrile-butadiene-styrene (PC/ABS) blends with various blend ratios are investigated at different temperatures to determine the shear dependent chain motions in a heterogeneous blend system. At low frequency levels under 0.1 rad/s, the viscosity of the material with a blend ratio of 3:7 (PC:ABS) is higher than that of pure ABS polymer. As the temperature increases, the viscosities of ABS-rich blends increase rather than decrease, whereas PC-rich blends exhibit decrease in viscosity. Results from the time sweep measurements indicate that ordered structures of PC and the formation and breakdown of internal network structures of ABS polymer occur simultaneously in the blend systems. Newly designed sequence test results show that the internal structures formed between PC and ABS polymers are dominant at low shear conditions for the blend ratio of 3:7 and effects of structural change and the presence of polybutadiene (PBD) become dominant at high shear conditions for pure ABS. The results of yield stress and relaxation time for PC/ABS blends support this phenomenon. The specimen with a blend ratio of 3:7 exhibited the highest value of yield stress at high temperature among others, which implies that the internal structure become stronger at higher temperature. The heterogeneity of ABS-rich blends increases whereas that of PC-rich blends decreases as temperature increases.

| S-EPMC7563493 | biostudies-literature

Rheological Behavior of Blends of Metallocene Catalyzed Long-Chain Branched Polyethylenes. Part I: Shear Rheological and Thermorheological Behavior.

Project description:Long-chain branched metallocene-catalyzed high-density polyethylenes (LCB-mHDPE) were solution blended to obtain blends with varying degrees of branching. A high molecular LCB-mHDPE was mixed with low molecular LCB-mHDPE at varying concentrations. The rheological behavior of those low molecular LCB-mHDPE is similar but their molar mass and molar mass distribution are significantly different. Those blends were characterized rheologically to study the effects of concentration, molar mass distribution, and long-chain branching level of the low molecular LCB-mHDPE. Owing to the ultra-long relaxation times of the high molecular LCB-mHDPE, the blends exhibited a clearly more long-chain branched behavior than the base materials. The thermorheological complexity analysis showed an apparent increase in the activation energies Ea determined from G', G″, and especially δ. Ea(δ), which for LCB-mHDPE is a peak function, turned out to produce even more pronounced peaks than observed for LCB-mPE with narrow molar mass distribution and also LCB-mPE with broader molar mass distribution. Thus, it is possible to estimate the molar mass distribution from the details of the thermorheological complexity.

| S-EPMC7864184 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data