Thermophysical Characterization of MgCl₂·6H₂O, Xylitol and Erythritol as Phase Change Materials (PCM) for Latent Heat Thermal Energy Storage (LHTES).

ABSTRACT: The application range of existing real scale mobile thermal storage units with phase change materials (PCM) is restricted by the low phase change temperature of 58 ∘ C for sodium acetate trihydrate, which is a commonly used storage material. Therefore, only low temperature heat sinks like swimming pools or greenhouses can be supplied. With increasing phase change temperatures, more applications like domestic heating or industrial process heat could be operated. The aim of this study is to find alternative PCM with phase change temperatures between 90 and 150 ∘ C . Temperature dependent thermophysical properties like phase change temperatures and enthalpies, densities and thermal diffusivities are measured for the technical grade purity materials xylitol (C 5 H 12 O 5 ), erythritol (C 4 H 10 O 4 ) and magnesiumchloride hexahydrate (MCHH, MgCl 2 · 6H 2 O). The sugar alcohols xylitol and erythritol indicate a large supercooling and different melting regimes. The salt hydrate MgCl 2 · 6H 2 O seems to be a suitable candidate for practical applications. It has a melting temperature of 115.1 ± 0.1 ∘ C and a phase change enthalpy of 166.9 ± 1.2 J / g with only 2.8 K supercooling at sample sizes of 100 g . The PCM is stable over 500 repeated melting and solidification cycles at differential scanning calorimeter (DSC) scale with only small changes of the melting enthalpy and temperature.

SUBMITTER: Hohlein S

PROVIDER: S-EPMC5506912 | biostudies-other | 2017 Apr

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Fluidic phase-change materials with continuous latent heat from theoretically tunable ternary metals for efficient thermal management.

Project description:Phase-change materials (PCMs), as important energy storage materials (ESMs), have been widely used in heat dissipation for electronics. However, PCMs are encountering huge challenges since the extremely limited space in microelectronics largely suppresses the applied volume of PCMs, which demands excellent PCMs that can fully utilize the valuable latent heat. This work successfully found a universal strategy toward powerful ESMs from fluidic ternary metals (TMs, GaInSn as a representative TM in this work). TMs exhibit high thermal conductivity (20.3 W m-1 K-1) and significantly effective latent heat (115 J/cm3) and, more important, show continuous phase transition and full utilization of the valuable latent heat. Interestingly, theoretical prediction through ternary phase diagram is carried out to easily tune the melting range, latent heat, and fluidity (viscosity) of TMs to adapt with different service conditions. As a result, thermally conductive silicone grease can be conveniently fabricated via simple shear mixing of TM and polymers. Such thermally conductive TM grease inherits the merits of TM, exhibiting continuous thermal control over daily electronics according to thermal shock performance.

| S-EPMC9351464 | biostudies-literature

Data demonstrating the influence of the latent storage efficiency on the dynamic thermal characteristics of a PCM layer.

Project description:Dynamic thermal characteristics, for each month of the year, of PCM layers with different melting temperatures and thermophysical properties, in a steady periodic regime, were determined (Mazzeo et al., 2017 [1]). The layer is subjected to climatic conditions characterizing two locations, one with a continental climate and the second one with a Mediterranean climate. This data article provides detailed numerical data, as a function of the latent storage efficiency, including monthly average daily values: of the latent energy fraction, of the decrement factors of the temperature, of the heat flux and of the energy, and of the time lags of the maximum and minimum peaks of the temperature and of the heat flux.

| S-EPMC5403787 | biostudies-literature

Thermophysical and Mechanical Properties of Hardened Cement Paste with Microencapsulated Phase Change Materials for Energy Storage.

Project description:In this research, structural-functional integrated cement-based materials were prepared by employing cement paste and a microencapsulated phase change material (MPCM) manufactured using urea-formaldehyde resin as the shell and paraffin as the core material. The encapsulation ratio of the MPCM could reach up to 91.21 wt%. Thermal energy storage cement pastes (TESCPs) incorporated with different MPCM contents (5%, 10%, 15%, 20% and 25% by weight of cement) were developed, and their thermal and mechanical properties were studied. The results showed that the total energy storage capacity of the hardened cement specimens with MPCM increased by up to 3.9-times compared with that of the control cement paste. The thermal conductivity at different temperature levels (35-36 °C, 55-56 °C and 72-74 °C) decreased with the increase of MPCM content, and the decrease was the highest when the temperature level was 55-56 °C. Moreover, the compressive strength, flexural strength and density of hardened cement paste decreased with the increase in MPCM content linearly. Among the evaluated properties, the compressive strength of TESCPs had a larger and faster degradation with the increase of MPCM content.

| S-EPMC5456425 | biostudies-other

Synthesis and Thermophysical Characterization of Fatty Amides for Thermal Energy Storage.

Project description:Nine monoamides were synthesized from carboxylic acids (C8-C18) and crude glycerol. The final monoamides were the result of a rearrangement of the acyl chain during the final hydrogenation process. The purity of the final compounds was determined by spectroscopic and mass spectrometry (MS) techniques. The thermophysical properties of solid monoamides were investigated to determine their capability to act as phase change materials (PCM) in thermal energy storage. Thermophysical properties were determined with a differential scanning calorimeter (DSC). The melting temperatures of the analyzed material ranged from 62.2 °C to 116.4 °C. The analyzed enthalpy of these monoamides ranged from 25.8 kJ/kg to 149.7 kJ/kg. Enthalpy values are analyzed considering the carbon chain and the formation of hydrogen bonds.

| S-EPMC6832967 | biostudies-literature

Light-Responsive Solid–Solid Phase Change Materials for Photon and Thermal Energy Storage

Project description:We report a series of adamantane-functionalized azobenzenes

| S-EPMC9838185 | biostudies-literature

Optically-controlled long-term storage and release of thermal energy in phase-change materials.

Project description:Thermal energy storage offers enormous potential for a wide range of energy technologies. Phase-change materials offer state-of-the-art thermal storage due to high latent heat. However, spontaneous heat loss from thermally charged phase-change materials to cooler surroundings occurs due to the absence of a significant energy barrier for the liquid-solid transition. This prevents control over the thermal storage, and developing effective methods to address this problem has remained an elusive goal. Herein, we report a combination of photo-switching dopants and organic phase-change materials as a way to introduce an activation energy barrier for phase-change materials solidification and to conserve thermal energy in the materials, allowing them to be triggered optically to release their stored latent heat. This approach enables the retention of thermal energy (about 200?J?g-1) in the materials for at least 10?h at temperatures lower than the original crystallization point, unlocking opportunities for portable thermal energy storage systems.

| S-EPMC5684416 | biostudies-literature

Organic Phase Change Materials for Thermal Energy Storage: Influence of Molecular Structure on Properties.

Project description:Materials that change phase (e.g., via melting) can store thermal energy with energy densities comparable to batteries. Phase change materials will play an increasing role in reduction of greenhouse gas emissions, by scavenging thermal energy for later use. Therefore, it is useful to have summaries of phase change properties over a wide range of materials. In the present work, we review the relationship between molecular structure and trends in relevant phase change properties (melting temperature, and gravimetric enthalpy of fusion) for about 200 organic compounds from several chemical families, namely alkanes (paraffins), fatty acids, fatty alcohols, esters, diamines, dinitriles, diols, dioic acids, and diamides. We also review availability and cost, chemical compatibility, and thermal and chemical stabilities, to provide practical information for PCM selection. Compounds with even chain alkyl lengths generally give higher melting temperatures, store more thermal energy per unit mass due to more efficient packing, and are of lower cost than the comparable compounds with odd alkyl chains.

| S-EPMC8588044 | biostudies-literature

Biomass-Based Shape-Stabilized Composite Phase-Change Materials with High Solar-Thermal Conversion Efficiency for Thermal Energy Storage.

Project description:To alleviate the increasing energy crisis and achieve energy saving and consumption reduction in building materials, preparing shape-stabilized phase-change materials using bio-porous carbon materials from renewable organic waste to building envelope materials is an effective strategy. In this work, pine cone porous biomass carbon (PCC) was prepared via a chemical activation method using renewable biomaterial pine cone as a precursor and potassium hydroxide (KOH) as an activator. Polyethylene glycol (PEG) and octadecane (OD) were loaded into PCC using the vacuum impregnation method to prepare polyethylene glycol/pine cone porous biomass carbon (PEG/PCC) and octadecane/pine cone porous biomass carbon (OD/PCC) shape-stabilized phase-change materials. PCCs with a high specific surface area and pore volume were obtained by adjusting the calcination temperature and amount of KOH, which was shown as a caterpillar-like and block morphology. The shape-stabilized PEG/PCC and OD/PCC composites showed high phase-change enthalpies of 144.3 J/g and 162.3 J/g, and the solar-thermal energy conversion efficiencies of the PEG/PCC and OD/PCC reached 79.9% and 84.8%, respectively. The effects of the contents of PEG/PCC and OD/PCC on the temperature-controlling capability of rigid polyurethane foam composites were further investigated. The results showed that the temperature-regulating and temperature-controlling capabilities of the energy-storing rigid polyurethane foam composites were gradually enhanced with an increase in the phase-change material content, and there was a significant thermostatic plateau in energy absorption at 25 °C and energy release at 10 °C, which decreased the energy consumption.

| S-EPMC10534447 | biostudies-literature

Experimental Investigation on Mechanism of Latent Heat Reduction of Sodium Acetate Trihydrate Phase Change Materials.

Project description:Sodium acetate trihydrate (SAT) phase change material (PCM) has been well known for thermal energy storage due to its high latent heat and resource abundance. However, SAT suffers from severe latent heat reduction after heating and cooling cycles. Although a few of previous researches showed the reduction could be effectively inhibited by using thickeners, the mechanisms of the reduction process and thickeners' inhibition have not been deeply explored till now. In this work, SAT modified by 5 wt.% nucleating agent of disodium hydrogen phosphate dodecahydrate (SAT/5 wt.% DSP) was prepared and 200 thermal cycles were carried out. The differential scanning calorimeter, Rheometer, X-ray diffractometry, and scanning electron microscope were used to investigate the extent of latent heat reduction, viscosity, phase composition and microstructure, respectively, and the infrared thermal imaging method was used to evaluate heat storage capacity. It was found that the latent heat of SAT/5 wt.% DSP dropped dramatically and the relative decrease in latent heat was measured to be 22.44%. The lower layer of SAT/5 wt.% DSP contained 24.1 wt.% CH3COONa, which was quantitatively consistent with the reduction extent. Furthermore, the phase change endothermic time of the lower layer was only 44.1% of that of the upper. SAT/5 wt.% DSP was further modified by 3 wt.% thickener of carboxymethyl cellulose (SAT/5 wt.% DSP/3 wt.% CMC) and endured 200 thermal cycles. The extent of the latent heat reduction of SAT/5 wt.% DSP/3 wt.% CMC was only 9.29%, and phase compositions were more homogeneous. The 3 wt.% CMC increased viscosity by 14 times, which effectively prevented the Stokes sedimentation velocity of CH3COONa in melts and inhibited the final macroscopic phase separation.

| S-EPMC7040703 | biostudies-literature

Bio-based sunflower carbon/polyethylene glycol shape-stabilized phase change materials for thermal energy storage.

Project description:The exploitation of shape-stabilized phase change materials with high thermal conductivity and energy storage capacity is an effective strategy for improving energy efficiency. In this work, sunflower stem carbon/polyethylene glycol (SS-PEG) and sunflower receptacle carbon/polyethylene glycol (SR-PEG) shape-stabilized phase change materials, utilizing sunflower stem and receptacle biomass carbon with high specific surface area and pore volume obtained by carbonization as frameworks and polyethylene glycol as an energy storage material, were prepared by the vacuum impregnation method. The ability to load polyethylene glycol into the pore structure of carbon materials in different sunflower parts was mainly investigated, and the micro-morphology, compositional structure and thermal properties were characterized and analyzed using SEM, IR spectroscopy, XRD, DSC and TG techniques. The results showed that the carbonized sunflower stems maintained the sieve pore structure, and the carbonized sunflower receptacle was a macroporous structure containing a large number of three-dimensional interconnections. At the same time, the interaction between polyethylene glycol and each carbon material occurred through physisorption. The melting enthalpies of SS-PEG and SR-PEG shape-stabilized phase change materials were 153.4 J g-1 and 171.5 J g-1, respectively, and the loading rates reached 81.9% and 91.5%, with initial thermal decomposition temperatures (T 5%) of 344 °C and 368 °C.

| S-EPMC11294913 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data