Thermophysical and Mechanical Properties of Hardened Cement Paste with Microencapsulated Phase Change Materials for Energy Storage.

ABSTRACT: In this research, structural-functional integrated cement-based materials were prepared by employing cement paste and a microencapsulated phase change material (MPCM) manufactured using urea-formaldehyde resin as the shell and paraffin as the core material. The encapsulation ratio of the MPCM could reach up to 91.21 wt%. Thermal energy storage cement pastes (TESCPs) incorporated with different MPCM contents (5%, 10%, 15%, 20% and 25% by weight of cement) were developed, and their thermal and mechanical properties were studied. The results showed that the total energy storage capacity of the hardened cement specimens with MPCM increased by up to 3.9-times compared with that of the control cement paste. The thermal conductivity at different temperature levels (35-36 °C, 55-56 °C and 72-74 °C) decreased with the increase of MPCM content, and the decrease was the highest when the temperature level was 55-56 °C. Moreover, the compressive strength, flexural strength and density of hardened cement paste decreased with the increase in MPCM content linearly. Among the evaluated properties, the compressive strength of TESCPs had a larger and faster degradation with the increase of MPCM content.

SUBMITTER: Cui H

PROVIDER: S-EPMC5456425 | biostudies-other | 2014 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Thermophysical Characterization of MgCl₂·6H₂O, Xylitol and Erythritol as Phase Change Materials (PCM) for Latent Heat Thermal Energy Storage (LHTES).

Project description:The application range of existing real scale mobile thermal storage units with phase change materials (PCM) is restricted by the low phase change temperature of 58 ∘ C for sodium acetate trihydrate, which is a commonly used storage material. Therefore, only low temperature heat sinks like swimming pools or greenhouses can be supplied. With increasing phase change temperatures, more applications like domestic heating or industrial process heat could be operated. The aim of this study is to find alternative PCM with phase change temperatures between 90 and 150 ∘ C . Temperature dependent thermophysical properties like phase change temperatures and enthalpies, densities and thermal diffusivities are measured for the technical grade purity materials xylitol (C 5 H 12 O 5 ), erythritol (C 4 H 10 O 4 ) and magnesiumchloride hexahydrate (MCHH, MgCl 2 · 6H 2 O). The sugar alcohols xylitol and erythritol indicate a large supercooling and different melting regimes. The salt hydrate MgCl 2 · 6H 2 O seems to be a suitable candidate for practical applications. It has a melting temperature of 115.1 ± 0.1 ∘ C and a phase change enthalpy of 166.9 ± 1.2 J / g with only 2.8 K supercooling at sample sizes of 100 g . The PCM is stable over 500 repeated melting and solidification cycles at differential scanning calorimeter (DSC) scale with only small changes of the melting enthalpy and temperature.

| S-EPMC5506912 | biostudies-other

Thermal Energy Storage and Mechanical Performance of Crude Glycerol Polyurethane Composite Foams Containing Phase Change Materials and Expandable Graphite.

Project description:The aim of this study was to enhance the thermal comfort properties of crude glycerol (CG) derived polyurethane foams (PUFs) using phase change materials (PCMs) (2.5⁻10.0% (wt/wt)) to contribute to the reduction of the use of non-renewable resources and increase energy savings. The main challenge when adding PCM to PUFs is to combine the low conductivity of PUFs whilst taking advantage of the heat released/absorbed by PCMs to achieve efficient thermal regulation. The solution considered to overcome this limitation was to use expandable graphite (EG) (0.50⁻1.50% (wt/wt)). The results obtained show that the use of PCMs increased the heterogeneity of the foams cellular structure and that the incorporation of PCMs and EG increased the stiffness of the ensuing composite PUFs acting as filler-reinforcing materials. However, these fillers also caused a substantial increase of the thermal conductivity and density of the ensuing foams which limited their thermal energy storage. Therefore, numerical simulations were carried using a single layer panel and the thermal and physical properties measured to evaluate the behavior of a composite PUF panel with different compositions, and guide future formulations to attain more effective results in respect to temperature buffering and temperature peak delay.

| S-EPMC6212961 | biostudies-literature

Synthesis and Thermophysical Characterization of Fatty Amides for Thermal Energy Storage.

Project description:Nine monoamides were synthesized from carboxylic acids (C8-C18) and crude glycerol. The final monoamides were the result of a rearrangement of the acyl chain during the final hydrogenation process. The purity of the final compounds was determined by spectroscopic and mass spectrometry (MS) techniques. The thermophysical properties of solid monoamides were investigated to determine their capability to act as phase change materials (PCM) in thermal energy storage. Thermophysical properties were determined with a differential scanning calorimeter (DSC). The melting temperatures of the analyzed material ranged from 62.2 °C to 116.4 °C. The analyzed enthalpy of these monoamides ranged from 25.8 kJ/kg to 149.7 kJ/kg. Enthalpy values are analyzed considering the carbon chain and the formation of hydrogen bonds.

| S-EPMC6832967 | biostudies-literature

Data for the physical and mechanical properties of staple fibers cement paste composites.

Project description:The data presented herein are compiled of the research summary of "Staple-wire-reinforced high-volume fly-ash cement paste composites" (Aydin, in preparation) [1]. This data article provides general information about the novel high volume fly ash cement paste composites composed of various volume of staple wires. The dataset here also helps the readers to understand the mechanisms of staple wires on physical and mechanical properties of pure cement paste composites.

| S-EPMC5544468 | biostudies-literature

Light-Responsive Solid–Solid Phase Change Materials for Photon and Thermal Energy Storage

Project description:We report a series of adamantane-functionalized azobenzenes

| S-EPMC9838185 | biostudies-literature

Long-Term Autonomic Thermoregulating Fabrics Based on Microencapsulated Phase Change Materials.

Project description:Microcapsules loaded with n-docosane as phase change material (mPCMs) for thermal energy storage with a phase change transition temperature in the range of 36-45 °C have been employed to impregnate cotton fabrics. Fabrics impregnated with 8 wt % of mPCMs provided 11 °C of temperature buffering effect during heating. On the cooling step, impregnated fabrics demonstrated 6 °C temperature increase for over 100 cycles of switching on/off of the heating source. Similar thermoregulating performance was observed for impregnated fabrics stored for 4 years (1500 days) at room temperature. Temperature buffering effect increased to 14 °C during heating cycle and temperature increase effect reached 9 °C during cooling cycle in the aged fabric composites. Both effects remained stable in aged fabrics for more than 100 heating/cooling cycles. Our study demonstrates high potential use of the microencapsulated n-docosane for thermal management applications, including high-technical textiles, footwear materials, and building thermoregulating covers and paints with high potential for commercial applications.

| S-EPMC8806139 | biostudies-literature

Optically-controlled long-term storage and release of thermal energy in phase-change materials.

Project description:Thermal energy storage offers enormous potential for a wide range of energy technologies. Phase-change materials offer state-of-the-art thermal storage due to high latent heat. However, spontaneous heat loss from thermally charged phase-change materials to cooler surroundings occurs due to the absence of a significant energy barrier for the liquid-solid transition. This prevents control over the thermal storage, and developing effective methods to address this problem has remained an elusive goal. Herein, we report a combination of photo-switching dopants and organic phase-change materials as a way to introduce an activation energy barrier for phase-change materials solidification and to conserve thermal energy in the materials, allowing them to be triggered optically to release their stored latent heat. This approach enables the retention of thermal energy (about 200?J?g-1) in the materials for at least 10?h at temperatures lower than the original crystallization point, unlocking opportunities for portable thermal energy storage systems.

| S-EPMC5684416 | biostudies-literature

Organic Phase Change Materials for Thermal Energy Storage: Influence of Molecular Structure on Properties.

Project description:Materials that change phase (e.g., via melting) can store thermal energy with energy densities comparable to batteries. Phase change materials will play an increasing role in reduction of greenhouse gas emissions, by scavenging thermal energy for later use. Therefore, it is useful to have summaries of phase change properties over a wide range of materials. In the present work, we review the relationship between molecular structure and trends in relevant phase change properties (melting temperature, and gravimetric enthalpy of fusion) for about 200 organic compounds from several chemical families, namely alkanes (paraffins), fatty acids, fatty alcohols, esters, diamines, dinitriles, diols, dioic acids, and diamides. We also review availability and cost, chemical compatibility, and thermal and chemical stabilities, to provide practical information for PCM selection. Compounds with even chain alkyl lengths generally give higher melting temperatures, store more thermal energy per unit mass due to more efficient packing, and are of lower cost than the comparable compounds with odd alkyl chains.

| S-EPMC8588044 | biostudies-literature

Data for the physical and mechanical properties of high volume fly ash cement paste composites.

Project description:The data presented herein are compiled of the research summary of "Characterization of High-Volume Fly-Ash Cement Paste for Sustainable Construction Application" (Aydin and Arel, 2017) [1]. This data article provides general information about the ASTM Class C and Class F fly ash cement paste composites composed of silica fume, lime, water reducing admixtures in three different level of workability (0 mm, 100 mm and 200 mm). The dataset here also helps the readers to understand the links with the basic properties of the ingredients, for example, how can porosity be predicted based on the mixture design? how can the strength of the material be linked with the basic strengths of the constituent ingredients?.

| S-EPMC5711659 | biostudies-literature

Multiscale poromechanics of wet cement paste.

Project description:Capillary effects, such as imbibition drying cycles, impact the mechanics of granular systems over time. A multiscale poromechanics framework was applied to cement paste, which is the most common building material, experiencing broad humidity variations over the lifetime of infrastructure. First, the liquid density distribution at intermediate to high relative humidity is obtained using a lattice gas density functional method together with a realistic nanogranular model of cement hydrates. The calculated adsorption/desorption isotherms and pore size distributions are discussed and compare well with nitrogen and water experiments. The standard method for pore size distribution determination from desorption data is evaluated. Second, the integration of the Korteweg liquid stress field around each cement hydrate particle provided the capillary forces at the nanoscale. The cement mesoscale structure was relaxed under the action of the capillary forces. Local irreversible deformations of the cement nanograins assembly were identified due to liquid-solid interactions. The spatial correlations of the nonaffine displacements extend to a few tens of nanometers. Third, the Love-Weber method provided the homogenized liquid stress at the micrometer scale. The homogenization length coincided with the spatial correlation length of nonaffine displacements. Our results on the solid response to capillary stress field suggest that the micrometer-scale texture is not affected by mild drying, while nanoscale irreversible deformations still occur. These results pave the way for understanding capillary phenomena-induced stresses in heterogeneous porous media ranging from construction materials to hydrogels and living systems.

| S-EPMC6561161 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data