Damage Evolution in Complex-Phase and Dual-Phase Steels during Edge Stretching.

ABSTRACT: The role of microstructural damage in controlling the edge stretchability of Complex-Phase (CP) and Dual-Phase (DP) steels was evaluated using hole tension experiments. The experiments considered a tensile specimen with a hole at the center of specimen that is either sheared (sheared edge condition) or drilled and then reamed (reamed edge condition). The damage mechanism and accumulation in the CP and DP steels were systematically characterized by interrupting the hole tension tests at different strain levels using scanning electron microscope (SEM) analysis and optical microscopy. Martensite cracking and decohesion of ferrite-martensite interfaces are the dominant nucleation mechanisms in the DP780. The primary source of void nucleation in the CP800 is nucleation at TiN particles, with secondary void formation at martensite/bainite interfaces near the failure strain. The rate of damage evolution is considerably higher for the sheared edge in contrast with the reamed edge since the shearing process alters the microstructure in the shear affected zone (SAZ) by introducing work-hardening and initial damage behind the sheared edge. The CP microstructures were shown to be less prone to shear-induced damage than the DP materials resulting in much higher sheared edge formability. Microstructural damage in the CP and DP steels was characterized to understand the interaction between microstructure, damage evolution and edge formability during edge stretching. An analytical model for void evolution and coalescence was developed and applied to predict the damage rate in these rather diverse microstructures.

SUBMITTER: Pathak N

PROVIDER: S-EPMC5506944 | biostudies-other | 2017 Mar

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

An RVE-Based Study of the Effect of Martensite Banding on Damage Evolution in Dual Phase Steels.

Project description:The intent of this work is to numerically investigate the effect of second phase morphology on damage evolution characteristics of dual-phase (DP) steels. A strain gradient enhanced crystal plasticity framework is used in order to capture the deformation heterogeneity caused by lattice orientations and microstructural size effects. The investigation is focused on two different martensite distributions (banded and random) that are relevant for industrial applications. The effects of martensite morphology are compared by artificially generated 2D plane strain microstructures with initial void content. The Representative volume elements (RVEs) are subjected to tensile deformation imposed by periodic boundary conditions. Evolution of voids are analyzed individually as well as a whole and characterized with respect to average axial strain. It is found that during stretching voids exhibit varying evolution characteristics due to generation of inhomogeneous strain fields within the structure. The behavior of individual voids shows that the stress-state surrounding the void is different from the imposed far field macroscopic stress-state. The voids at the ferrite martensite interface and in ferrite grains of the randomly distributed martensite grow more than in the banded structure. On the other hand, voids formed by martensite cracking growth shows an opposite trend.

| S-EPMC7179025 | biostudies-literature

Ultrastrong lightweight compositionally complex steels via dual-nanoprecipitation.

Project description:High-performance lightweight materials are urgently needed, given the pressing quest for weight reduction and the associated energy savings and emission reduction. Here, by incorporating the multi-principal element feature of compositionally complex alloys, we develop the concept of lightweight steels further and propose a new class of compositionally complex steels (CCSs). This approach allows us to use the high solid solution strengthening and shift the alloys' compositions into previously unattainable phase regions where both nanosized shearable κ-carbides and non-shearable B2 particles are simultaneously formed. The achievement of dual-nanoprecipitation in our CCSs leads to materials with ultrahigh specific tensile strength (up to 260 MPa·cm3 g-1) and excellent tensile elongation (13 to 38%), a combination outperforming all other high-strength high-entropy alloys and advanced lightweight steels. Our concept of CCSs is thus useful for guiding the design of ultrastrong lightweight metallic materials.

| S-EPMC7673736 | biostudies-literature

Structure Evolution and Deformation Behavior of Polyethylene Film during Biaxial Stretching.

Project description:The structure evolution and deformation behavior of tenter-frame biaxially oriented polyethylene (TF-BOPE) films were investigated in this study. For sequential biaxial stretching, the original spherulites were broken into small pieces, and the fibrillar structure simultaneously formed during the machine direction (MD) stretching. Subsequently, the single fibrils were pulled away, and some fine fibrils developed via partial melting-recrystallization or lamellar rearrangement during the transverse direction (TD) stretching, which leads to the formation of the vein structure and nanosized fiber-like network. For simultaneous biaxial stretching, the fractured lamellae and the newly formed crystals were evenly distributed in the MD-TD plane like an isotropous fibrillar network. Moreover, compared with the unstretched sample, both films could achieve up to about 2 times the tensile modulus and 4.5 times the tensile strength and also exhibited the superior optical property.

| S-EPMC6964308 | biostudies-literature

Two-phase stretching of molecular chains.

Project description:Although stretching of most polymer chains leads to rather featureless force-extension diagrams, some, notably DNA, exhibit nontrivial behavior with a distinct plateau region. Here, we propose a unified theory that connects force-extension characteristics of the polymer chain with the convexity properties of the extension energy profile of its individual monomer subunits. Namely, if the effective monomer deformation energy as a function of its extension has a nonconvex (concave up) region, the stretched polymer chain separates into two phases: the weakly and strongly stretched monomers. Simplified planar and 3D polymer models are used to illustrate the basic principles of the proposed model. Specifically, we show rigorously that, when the secondary structure of a polymer is mostly caused by weak noncovalent interactions, the stretching is two phase, and the force-stretching diagram has the characteristic plateau. We then use realistic coarse-grained models to confirm the main findings and make direct connection to the microscopic structure of the monomers. We show in detail how the two-phase scenario is realized in the α-helix and DNA double helix. The predicted plateau parameters are consistent with single-molecules experiments. Detailed analysis of DNA stretching shows that breaking of Watson-Crick bonds is not necessary for the existence of the plateau, although some of the bonds do break as the double helix extends at room temperature. The main strengths of the proposed theory are its generality and direct microscopic connection.

| S-EPMC3581873 | biostudies-literature

Hydraulic fracture during epithelial stretching.

Project description:The origin of fracture in epithelial cell sheets subject to stretch is commonly attributed to excess tension in the cells' cytoskeleton, in the plasma membrane, or in cell-cell contacts. Here, we demonstrate that for a variety of synthetic and physiological hydrogel substrates the formation of epithelial cracks is caused by tissue stretching independently of epithelial tension. We show that the origin of the cracks is hydraulic; they result from a transient pressure build-up in the substrate during stretch and compression manoeuvres. After pressure equilibration, cracks heal readily through actomyosin-dependent mechanisms. The observed phenomenology is captured by the theory of poroelasticity, which predicts the size and healing dynamics of epithelial cracks as a function of the stiffness, geometry and composition of the hydrogel substrate. Our findings demonstrate that epithelial integrity is determined in a tension-independent manner by the coupling between tissue stretching and matrix hydraulics.

| S-EPMC4374166 | biostudies-literature

Cyclic stretching-induced epithelial cell reorientation is driven by microtubule-modulated transverse extension during the relaxation phase.

Project description:Many types of adherent cells are known to reorient upon uniaxial cyclic stretching perpendicularly to the direction of stretching to facilitate such important events as wound healing, angiogenesis, and morphogenesis. While this phenomenon has been documented for decades, the underlying mechanism remains poorly understood. Using an on-stage stretching device that allowed programmable stretching with synchronized imaging, we found that the reorientation of NRK epithelial cells took place primarily during the relaxation phase when cells underwent rapid global retraction followed by extension transverse to the direction of stretching. Inhibition of myosin II caused cells to orient along the direction of stretching, whereas disassembly of microtubules enhanced transverse reorientation. Our results indicate distinct roles of stretching and relaxation in cell reorientation and implicate a role of myosin II-dependent contraction via a microtubule-modulated mechanism. The importance of relaxation phase also explains the difference between the responses to cyclic and static stretching.

| S-EPMC8292395 | biostudies-literature

A new nanoscale metastable iron phase in carbon steels.

Project description:Metastable ω phase is common in body-centred cubic (bcc) metals and alloys, including high-alloying steels. Recent theoretical calculations also suggest that the ω structure may act as an intermediate phase for face-centred cubic (fcc)-to-bcc transformation. Thus far, the role of the ω phase played in fcc-bcc martensitic transformation in carbon steels has not been reported. In previous investigations on martensitic carbon steels, extra electron diffraction spots were frequently observed by transmission electron microscopy (TEM), and these spots were historically ascribed to the diffraction arising from either internal twins or carbides. In this paper, an intensive TEM investigation revealed that the extra spots are in fact attributed to the metastable ω phase in particle-like morphology with an overall size of several or dozens of nanometres. The strict orientation relationships between the ω phase and the ferrite matrix are in good agreement with those of the hexagonal (P6/mmm) ω phase in other bcc metals and alloys. The identification of the ω phase as well as the extra diffraction spots might provide a clue to help understand the physical mechanism of martensitic transformation in steels.

| S-EPMC4621516 | biostudies-other

Dual phase patterning during a congruent grain boundary phase transition in elemental copper.

Project description:The phase behavior of grain boundaries can have a strong influence on interfacial properties. Little is known about the emergence of grain boundary phases in elemental metal systems and how they transform. Here, we observe the nanoscale patterning of a grain boundary by two alternating grain boundary phases with distinct atomic structures in elemental copper by atomic resolution imaging. The same grain boundary phases are found by computational grain boundary structure search indicating a first-order transformation. Finite temperature atomistic simulations reveal a congruent, diffusionless transition between these phases under ambient pressure. The patterning of the grain boundary at room temperature is dominated by the grain boundary phase junctions separating the phase segments. Our analysis suggests that the reduced mobility of the phase junctions at low temperatures kinetically limits the transformation, but repulsive elastic interactions between them and disconnections could additionally stabilize the pattern formation.

| S-EPMC9184537 | biostudies-literature

Microstructure Evolution of HSLA Pipeline Steels after Hot Uniaxial Compression.

Project description:The mechanical properties of the high-strength low-alloy pipeline steels were mainly controlled by the subsequent phase transformations after rolling. The influence of hot uniaxial compression on the phase transformation of acicular ferrite was explored by viewing of the deformation degree, the deformation temperature, and the strain rate. The results show that the increase of deformation amounts raises the transformation starting and finishing temperature during the subsequent cooling and also promotes the polygonal ferrite transformation, which leads to the decrease of Vickers hardness accordingly. With the increasing of the deformation temperature, the achieved microstructure becomes coarsened and thus decreases the hardness. As the strain rate increases, the microstructure is refined and thus the hardness increases gradually; increasing the strain rate appropriately is beneficial to the refinement of the microstructure.

| S-EPMC5457077 | biostudies-other

Phase Transformation and Morphology Evolution of Ti50Cu25Ni20Sn? during Mechanical Milling.

Project description:Nanocrystalline/amorphous powder was produced by ball milling of Ti50Cu25Ni20Sn? (at.%) master alloy. Both laser diffraction particle size analyzer and scanning electron microscope (SEM) were used to monitor the changes in the particle size as well as in the shape of particles as a function of milling time. During ball milling, the average particle size decreased with milling time from >320 µm to ~38 µm after 180 min of milling. The deformation-induced hardening and phase transformation caused the hardness value to increase from 506 to 779 HV. X-ray diffraction (XRD) analysis was used to observe the changes in the phases/amorphous content as a function of milling time. The amount of amorphous fraction increased continuously until 120 min milling (36 wt % amorphous content). The interval of crystallite size was between 1 and 10 nm after 180 min of milling with 25 wt % amorphous fractions. Cubic Cu(Ni,Cu)Ti? structure was transformed into the orthorhombic structure owing to the shear/stress, dislocations, and Cu substitution during the milling process.

| S-EPMC6163940 | biostudies-other

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data