Acoustic Emission of Deformation Twinning in Magnesium.

ABSTRACT: The Acoustic Emission of deformation twinning in Magnesium is investigated in this article. Single crystal testing with combined full field deformation measurements, as well as polycrystalline testing inside the scanning electron microscope with simultaneous monitoring of texture evolution and twin nucleation were compared to testing at the laboratory scale with respect to recordings of Acoustic Emission activity. Single crystal testing revealed the formation of layered twin boundaries in areas of strain localization which was accompanied by distinct changes in the acoustic data. Testing inside the microscope directly showed twin nucleation, proliferation and growth as well as associated crystallographic reorientations. A post processing approach of the Acoustic Emission activity revealed the existence of a class of signals that appears in a strain range in which twinning is profuse, as validated by the in situ and ex situ microscopy observations. Features extracted from such activity were cross-correlated both with the available mechanical and microscopy data, as well as with the Acoustic Emission activity recorded at the laboratory scale for similarly prepared specimens. The overall approach demonstrates that the method of Acoustic Emission could provide real time volumetric information related to the activation of deformation twinning in Magnesium alloys, in spite of the complexity of the propagation phenomena, the possible activation of several deformation modes and the challenges posed by the sensing approach itself when applied in this type of materials evaluation approach.

SUBMITTER: Mo C

PROVIDER: S-EPMC5509273 | biostudies-other | 2016 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Deformation twinning and grain partitioning in a hexagonal close-packed magnesium alloy.

Project description:Pervasive deformation twinning in magnesium greatly affects its strength and formability. The local stress fields associated with twinning play a key role on deformation behavior and fracture but are extremely difficult to characterize experimentally. In this study, we perform synchrotron experiments with differential-aperture X-ray microscopy to measure the 3D stress fields in the vicinity of a twin with a spatial resolution of 0.5 micrometer. The measured local stress field aids to identify the sequence of events involved with twinning. We find that the selected grain deforms elastically before twinning, and the twin formation splits the grain into two non-interacting domains. Under further straining one domain of the grain continued to deform elastically, whereas the other domain deforms plastically by prismatic slip. This heterogeneous deformation behavior may be mediated by the surrounding medium and it is likely to lead to asymmetric twin growth.

| S-EPMC6232174 | biostudies-literature

Datasets for multi-scale diffraction analysis (synchrotron XRD and EBSD) of twinning-detwinning during tensile-compressive deformation of AZ31B magnesium alloy samples.

Project description:Diffraction data were collected using synchrotron X-ray scattering (sXRD) and electron back-scattered diffraction (EBSD) during in situ tensile-compressive deformation of Mg alloy AZ31B dogbone samples. The onset and evolution of twinning and detwinning were monitored based on intensity changes in sXRD 2D scattering patterns (which also provided average elastic strain values through the calculation of orientation-specific lattice spacing changes), and EBSD, that revealed the micro-scale grain morphology changes. The observations were interpreted and analysed with the help of crystal plasticity finite element modelling (CP-FEM), as reported in the published article (https://doi.org/10.1016/j.ijplas.2019.02.018).

| S-EPMC6744277 | biostudies-literature

Prediction of Mechanical Twinning in Magnesium Silicate Post-Perovskite.

Project description:The plastic properties of MgSiO3 post-perovskite are considered to be one of the key issues necessary for understanding the seismic anisotropy at the bottom of the mantle in the so-called D" layer. Although plastic slip in MgSiO3 post-perovskite has attracted considerable attention, the twinning mechanism has not been addressed, despite some experimental evidence from low-pressure analogues. On the basis of a numerical mechanical model, we present a twin nucleation model for post-perovskite involving the emission of 1/6 <110> partial dislocations. Relying on first-principles calculations with no adjustable parameters, we show that {110} twin wall formation resulting from the interaction of multiple twin dislocations occurs at a twinning stress comparable in magnitude to the most readily occurring slip system in post-perovskite. Because dislocation activities and twinning are competitive strain-producing mechanisms, twinning should be considered in future models of crystallographic preferred orientations in post-perovskite to better interpret seismic anisotropy in the lowermost lower mantle.

| S-EPMC5732224 | biostudies-literature

Size-induced twinning in InSb semiconductor during room temperature deformation.

Project description:Room-temperature deformation mechanism of InSb micro-pillars has been investigated via a multi-scale experimental approach, where micro-pillars of 2 µm and 5 µm in diameter were first fabricated by focused ion beam (FIB) milling and in situ deformed in the FIB-SEM by micro-compression using a nano-indenter equipped with a flat tip. Strain rate jumps have been performed to determine the strain rate sensitivity coefficient and the related activation volume. The activation volume is found to be of the order of 3-5 b3, considering that plasticity is mediated by Shockley partial dislocations. Transmission electron microscopy (TEM) thin foils were extracted from deformed micro-pillars via the FIB lift-out technique: TEM analysis reveals the presence of nano-twins as major mechanism of plastic deformation, involving Shockley partial dislocations. The presence of twins was never reported in previous studies on the plasticity of bulk InSb: this deformation mechanism is discussed in the context of the plasticity of small-scale samples.

| S-EPMC8486849 | biostudies-literature

Deformation-induced grain growth and twinning in nanocrystalline palladium thin films.

Project description:The microstructure and mechanical properties of nanocrystalline Pd films prepared by magnetron sputtering have been investigated as a function of strain. The films were deposited onto polyimide substrates and tested in tensile mode. In order to follow the deformation processes in the material, several samples were strained to defined straining states, up to a maximum engineering strain of 10%, and prepared for post-mortem analysis. The nanocrystalline structure was investigated by quantitative automated crystal orientation mapping (ACOM) in a transmission electron microscope (TEM), identifying grain growth and twinning/detwinning resulting from dislocation activity as two of the mechanisms contributing to the macroscopic deformation. Depending on the initial twin density, the samples behaved differently. For low initial twin densities, an increasing twin density was found during straining. On the other hand, starting from a higher twin density, the twins were depleted with increasing strain. The findings from ACOM-TEM were confirmed by results from molecular dynamics (MD) simulations and from conventional and in-situ synchrotron X-ray diffraction (CXRD, SXRD) experiments.

| S-EPMC3817795 | biostudies-literature

Strength and ductility with {1011} - {1012} double twinning in a magnesium alloy.

Project description:Based on their high specific strength and stiffness, magnesium alloys are attractive for lightweight applications in aerospace and transportation, where weight saving is crucial for the reduction of carbon dioxide emissions. Unfortunately, the ductility of magnesium alloys is usually limited. It is thought that one reason for the lack of ductility is that the development of - double twins (DTW) cause premature failure of magnesium alloys. Here we show with a magnesium alloy containing 4 wt% lithium, that the same impressively large compression failure strains can be achieved with DTWs as without. The DTWs form stably across the microstructure and continuously throughout straining, forming three-dimensional intra-granular networks, a potential strengthening mechanism. We rationalize that relatively easier <c+a> slip characteristic of this alloy plastically relaxed the localized stress concentrations that DTWs can generate. This result may provide key insight and an alternative perspective towards designing formable and strong magnesium alloys.

| S-EPMC5482718 | biostudies-literature

Deformation Induced Hierarchical Twinning Coupled with Omega Transformation in a Metastable ?-Ti Alloy.

Project description:Hierarchical twinning, at multiple length scales, was noted in a metastable body-centered cubic (bcc) ?-titanium alloy on tensile deformation. Site-specific characterization within the deformation bands, carried out using EBSD and TEM, revealed {332} <113> type primary bcc twins, containing different variants of secondary and tertiary twins, as well as the formation of stress-induced martensite (?"). Within the primary {332} <113> type twin, "destruction" of the prior quenched-in athermal ? phase was observed, while a stress-induced ? phase reforms within the tertiary twins, revealing the intricate nature of coupling between deformation twinning and displacive ? transformation.

| S-EPMC6362253 | biostudies-literature

Deformation Twinning in Polycrystalline Mg Microstructures at High Strain Rates at the Atomic Scales.

Project description:Large scale molecular dynamics (MD) simulations are carried out to investigate the twinning behavior as well as the atomic scale micromechanisms of growth of tension and compression twins in polycrystalline Mg microstructures at high strain rates. A new defect characterization algorithm (extended-common neighbor analysis (E-CNA)) is developed that allows for an efficient identification of various types of twins in HCP microstructures. Unlike other local orientation analysis methods, the E-CNA method allows for atomic scale characterization of the structure of different types of twin boundaries in HCP microstructures. The MD simulations suggest that the local orientation of individual grains with the loading axis plays a critical role in determining the ability of grains to nucleate either compression twins or tension twins. The twinning behavior is observed through nucleation of a pair of planar faults and lateral growth of the twins occurs through nucleation of steps along the planar faults. The kinetics of migration of steps that determine the rate of growth of twins are investigated at the atomic scales. The twin tip velocity computed at high strain rates compares well with the experimentally reported values in the literature.

| S-EPMC6400955 | biostudies-literature

Three-dimensional character of the deformation twin in magnesium.

Project description:Deformation twins are three-dimensional domains, traditionally viewed as ellipsoids because of their two-dimensional lenticular sections. In this work, we performed statistical analysis of twin shapes viewing along three orthogonal directions: the 'dark side' (DS) view along the twin shear direction (η1), the twinning plane normal (TPN) view (k1) and the 'bright side' (BS) view along the direction λ(=k1 × η1). Our electron back-scatter diffraction results show that twins in the DS and BS views normally exhibit a lenticular shape, whereas they show an irregular shape in the TPN view. Moreover, the findings in the TPN view revealed that twins grow faster along λ the lateral direction than along η1 the forward propagation direction at the initial stages of twin growth. These twin sections are irregular, indicating that growth is locally controlled and the overall shape is not perfectly ellipsoidal. We explain these findings using atomistic models, and ascribe them to differences in the mobility of the edge and screw components of the twinning dislocations.

| S-EPMC6658514 | biostudies-literature

Atomic-scale observation of nucleation- and growth-controlled deformation twinning in body-centered cubic nanocrystals.

Project description:Twinning is an essential mode of plastic deformation for achieving superior strength and ductility in metallic nanostructures. It has been generally believed that twinning-induced plasticity in body-centered cubic (BCC) metals is controlled by twin nucleation, but facilitated by rapid twin growth once the nucleation energy barrier is overcome. By performing in situ atomic-scale transmission electron microscopy straining experiments and atomistic simulations, we find that deformation twinning in BCC Ta nanocrystals larger than 15 nm in diameter proceeds by reluctant twin growth, resulting from slow advancement of twinning partials along the boundaries of finite-sized twin structures. In contrast, reluctant twin growth can be obviated by reducing the nanocrystal diameter to below 15 nm. As a result, the nucleated twin structure penetrates quickly through the cross section of nanocrystals, enabling fast twin growth via facile migration of twin boundaries leading to large uniform plastic deformation. The present work reveals a size-dependent transition in the nucleation- and growth-controlled twinning mechanism in BCC metals, and provides insights for exploiting twinning-induced plasticity and breaking strength-ductility limits in nanostructured BCC metals.

| S-EPMC10791697 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data