Effect of Annealing Temperature on the Water Contact Angle of PVD Hard Coatings.

ABSTRACT: Various PVD (physical vapor deposition) hard coatings including nitrides and metal-doped diamond-like carbons (Me-DLC) were applied in plastic injection and die-casting molds to improve wear resistance and reduce sticking. In this study, nitrides hcp-AlN (hexagonal close-packed AlN), Cr₂N, (CrAl)₂N) and Me-DLC (Si-DLC and Cr-DLC) coatings were prepared using a closed field unbalanced magnetron reactive sputtering system. The coatings were annealed in air for 2 h at various temperatures, after which the anti-sticking properties were assessed using water contact angle (WCA) measurements. The as-deposited hcp-AlN, Cr₂N and (CrAl)₂N coatings exhibit hydrophobic behavior and exhibit respective WCAs of 119°, 106° and 101°. The as-deposited Si-DLC and Cr-DLC coatings exhibit hydrophilic behavior and exhibit respective WCAs of 74° and 88°. The annealed Cr₂N and (CrAl)₂N coatings exhibit hydrophobic behavior with higher WCAs, while the annealed hcp-AlN, Si-DLC and Cr-DLC coatings are hydrophilic. The increased WCA of the annealed Cr₂N and (CrAl)₂N coatings is related to their crystal structure and increased roughness. The decreased WCA of the annealed hcp-AlN, Si-DLC and Cr-DLC coatings is related to their crystal structures and has little correlation with roughness.

SUBMITTER: Yang YS

PROVIDER: S-EPMC5521310 | biostudies-other | 2013 Aug

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Temperature Dependence of Water Contact Angle on Teflon AF1600.

Project description:In this work, we investigate the change of contact angle (CA) of a water droplet during evaporation on a Teflon AF1600 surface in the temperature range between 20 and 80 °C under standard laboratory conditions. An almost constant initial CA and a significant increase of the stabilized CA have been observed. The results reveal a temperature-dependent CA change, mainly due to water adsorption on the solid surface. Soaking experiments indicate that besides adsorption, a temperature-independent friction-like force contributes to the pinning of triple-line and therefore to the CA change. We propose an adsorption coverage parameter and a friction-like force to describe the CA change. Furthermore, we describe a reproducible process to produce smooth and homogeneous Teflon AF1600 thin films, minimizing the influence of roughness and local heterogeneity on the CA.

| S-EPMC8812120 | biostudies-literature

Effects of Annealing Temperature and Ambient on Metal/PtSe2 Contact Alloy Formation.

Project description:Forming gas annealing is a common process step used to improve the performance of devices based on transition-metal dichalcogenides (TMDs). Here, the impact of forming gas anneal is investigated for PtSe2-based devices. A range of annealing temperatures (150, 250, and 350 °C) were used both in inert (0/100% H2/N2) and forming gas (5/95% H2/N2) environments to separate the contribution of temperature and ambient. The samples are electrically characterized by circular transfer length method structures, from which contact resistance and sheet resistance are analyzed. Ti and Ni are used as metal contacts. Ti does not react with PtSe2 at any given annealing step. In contrast to this, Ni reacts with PtSe2, resulting in a contact alloy formation. The results are supported by a combination of X-ray photoelectron spectroscopy, Raman spectroscopy, energy-dispersive X-ray spectroscopy, and cross-sectional transmission electron microscopy. The work sheds light on the impact of forming gas annealing on TMD-metal interfaces, and on the TMD film itself, which could be of great interest to improve the contact resistance of TMD-based devices.

| S-EPMC6812109 | biostudies-literature

Water and Carbon Dioxide Capillary Bridges in Nanoscale Slit Pores: Effects of Temperature, Pressure, and Salt Concentration on the Water Contact Angle.

Project description:We perform molecular dynamics (MD) simulations of a nanoscale water capillary bridge (WCB) surrounded by carbon dioxide over a wide range of temperatures and pressures (T = 280-400 K and carbon dioxide pressures PCO2 ≈ 0-80 MPa). The water-carbon dioxide system is confined by two parallel silica-based surfaces (hydroxylated β-cristobalite) separated by h = 5 nm. The aim of this work is to study the WCB contact angle (θc) as a function of T and PCO2. Our simulations indicate that θc varies weakly with temperature and pressure: Δθc ≈ 10-20° for PCO2 increasing from ≈0 to 80 MPa (T = 320 K); Δθc ≈ -10° for T increasing from 320 to 360 K (with a fixed amount of carbon dioxide). Interestingly, at all conditions studied, a thin film of water (1-2 water layers-thick) forms under the carbon dioxide volume. Our MD simulations suggest that this is due to the enhanced ability of water, relative to carbon dioxide, to form hydrogen-bonds with the walls. We also study the effects of adding salt (NaCl) to the WCB and corresponding θc. It is found that at the salt concentrations studied (mole fractions xNa = xCl = 3.50, 9.81%), the NaCl forms a large crystallite within the WCB with the ions avoiding the water-carbon dioxide interface and the walls surface. This results in θc being insensitive to the presence of NaCl.

| S-EPMC11375785 | biostudies-literature

Regulation of silk material structure by temperature-controlled water vapor annealing.

Project description:We present a simple and effective method to obtain refined control of the molecular structure of silk biomaterials through physical temperature-controlled water vapor annealing (TCWVA). The silk materials can be prepared with control of crystallinity, from a low content using conditions at 4 °C (? helix dominated silk I structure), to highest content of ?60% crystallinity at 100 °C (?-sheet dominated silk II structure). This new physical approach covers the range of structures previously reported to govern crystallization during the fabrication of silk materials, yet offers a simpler, green chemistry, approach with tight control of reproducibility. The transition kinetics, thermal, mechanical, and biodegradation properties of the silk films prepared at different temperatures were investigated and compared by Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), uniaxial tensile studies, and enzymatic degradation studies. The results revealed that this new physical processing method accurately controls structure, in turn providing control of mechanical properties, thermal stability, enzyme degradation rate, and human mesenchymal stem cell interactions. The mechanistic basis for the control is through the temperature-controlled regulation of water vapor to control crystallization. Control of silk structure via TCWVA represents a significant improvement in the fabrication of silk-based biomaterials, where control of structure-property relationships is key to regulating material properties. This new approach to control crystallization also provides an entirely new green approach, avoiding common methods that use organic solvents (methanol, ethanol) or organic acids. The method described here for silk proteins would also be universal for many other structural proteins (and likely other biopolymers), where water controls chain interactions related to material properties.

| S-EPMC3090511 | biostudies-literature

What Is the Value of Water Contact Angle on Silicon?

Project description:Silicon is a widely applied material and the wetting of silicon surface is an important phenomenon. However, contradictions in the literature appear considering the value of the water contact angle (WCA). The purpose of this study is to present a holistic experimental and theoretical approach to the WCA determination. To do this, we checked the chemical composition of the silicon (1,0,0) surface by using the X-ray photoelectron spectroscopy (XPS) method, and next this surface was purified using different cleaning methods. As it was proved that airborne hydrocarbons change a solid wetting properties the WCA values were measured in hydrocarbons atmosphere. Next, molecular dynamics (MD) simulations were performed to determine the mechanism of wetting in this atmosphere and to propose the force field parameters for silica wetting simulation. It is concluded that the best method of surface cleaning is the solvent-reinforced de Gennes method, and the WCA value of silicon covered by SiO2 layer is equal to 20.7° (at room temperature). MD simulation results show that the mechanism of pure silicon wetting is similar to that reported for graphene, and the mechanism of silicon covered by SiO2 layer wetting is similar to this observed recently for a MOF.

| S-EPMC7177545 | biostudies-literature

Thermal stability of Si/SiC/ta-C composite coatings and improvement of tribological properties through high-temperature annealing.

Project description:We report the structure, mechanical properties, thermal stability, and durability of Si/SiC/ta-C composite (Si-ta-C) coatings fabricated using simultaneous filtered cathodic vacuum arc deposition and direct current unbalanced magnetron sputtering. Si concentration of 1.25-6.04 at.% was achieved by increasing the unbalanced magnetron sputtering power from 25 to 175 W. Si addition provided functionality to the coating, such as heat resistance, while retaining the high hardness of ta-C coatings. The Si-ta-C coatings were stable up to 600 °C regardless of the Si content, while the coating containing 3.85 at.% Si was stable up to 700 °C. The friction behavior and mechanical properties were dependent on the coating film before and after annealing at 100-200 °C; however, annealing at 300-400 °C decreased disk wear and increased counterpart wear due to an increase in film hardness on account of an endothermic reaction that increased the number of Si-C bonds. This indicates that the basic hardness characteristics of the ta-C coating and the high-temperature structural change of the Si-ta-C coating are important for ensuring high-temperature durability. These characteristics were verified through the low coefficient of friction and wear rate of the 1.25 at.% Si-ta-C coating after annealing at 500 °C.

| S-EPMC8894414 | biostudies-literature

Effect of Annealing Temperature on ECD Grown Hexagonal-Plane Zinc Oxide.

Project description:Zinc oxide (ZnO) offers a great potential in several applications from sensors to Photovoltaic cells thanks to the material's dependency, to its optical and electrical properties and crystalline structure architypes. Typically, ZnO powder tends to be grown in the form of a wurtzite structure allowing versatility in the phase of material growths; albeit, whereas in this work we introduce an alternative in scalable yet relatively simple 2D hexagonal planed ZnO nanoflakes via the electrochemical deposition of commercially purchased Zn(NO?)? and KCl salts in an electrochemical process. The resulting grown materials were analyzed and characterized via a series of techniques prior to thermal annealing to increase the grain size and improve the crystal quality. Through observation via scanning electron microscope (SEM) images, we have analyzed the statistics of the grown flakes' hexagonal plane's size showing a non-monotonal strong dependency of the average flake's hexagonal flakes' on the annealing temperature, whereas at 300 °C annealing temperature, average flake size was found to be in the order of 300 ?m². The flakes were further analyzed via transmission electron microscopy (TEM) to confirm its hexagonal planes and spectroscopy techniques, such as Raman Spectroscopy and photo luminescence were applied to analyze and confirm the ZnO crystal signatures. The grown materials also underwent further characterization to gain insights on the material, electrical, and optical properties and, hence, verify the quality of the material for Photovoltaic cells' electron collection layer application. The role of KCl in aiding the growth of the less preferable (0001) ZnO is also investigated via various prospects discussed in our work. Our method offers a relatively simple and mass-producible method for synthesizing a high quality 2D form of ZnO that is, otherwise, technically difficult to grow or control.

| S-EPMC6120048 | biostudies-literature

The Nature of the Low-Temperature Crossover of Water in Hard Confinement.

Project description:The dynamics of water confined in mesoporous MIP (2-3 nm pores in size) with silica gel (secondary silica; further, the abbreviation SG will be used) and MAP (10-35 nm pores in size) without SG borosilicate glasses have been studied by broadband dielectric spectroscopy (BDS), nuclear magnetic resonance (NMR), and differential scanning calorimetry (DSC). MIP samples contain secondary silica inside the pores and provide a confinement size of about 2-3 nm, whereas MAP samples are free of secondary silica and provide a confinement size of about 10-35 nm. It is shown by BDS and NMR techniques that water exhibits a dynamic crossover of around 180 K when it is confined in MIP samples. By contrast, water confined in larger pores (MAP) does not exhibit any changes in its relaxation behavior. It is also shown that the crossover temperature depends on the hydration level (the higher the hydration level, the lower the crossover temperature). Below the crossover temperature, we find that water reorientation is isotropic (NMR) and that the temperature-dependent dielectric relaxation strength (BDS) follows the tendency expected for a solid-like material. In contrast, water reorientation is related to long-range diffusion above the crossover temperature, and the dielectric relaxation strength follows the tendency expected for a liquid-like material. Furthermore, the calorimetric results are compatible with crossing a glass transition near 180 K. Finally, the results are discussed within the Gibbs-Thomson model. In this framework, the crossover could be related to ice crystals melting.

| S-EPMC10258804 | biostudies-literature

Thermal Annealing Effect on Optical Properties of Binary TiO₂-SiO₂ Sol-Gel Coatings.

Project description:TiO₂-SiO₂ binary coatings were deposited by a sol-gel dip-coating method using tetrabutyl titanate and tetraethyl orthosilicate as precursors. The structure and chemical composition of the coatings annealed at different temperatures were analyzed by Raman spectroscopy and Fourier Transform Infrared (FTIR) spectroscopy. The refractive indices of the coatings were calculated from the measured transmittance and reflectance spectra. An increase in refractive index with the high temperature thermal annealing process was observed. The Raman and FTIR results indicate that the refractive index variation is due to changes in the removal of the organic component, phase separation and the crystal structure of the binary coatings.

| S-EPMC5452115 | biostudies-other

The effect of low-temperature annealing on discordance of U-Pb zircon ages.

Project description:Discordant U-Pb data of zircon are commonly attributed to Pb loss from domains with variable degree of radiation damage that resulted from α-decay of U and Th, which often complicates the correct age interpretation of the sample. Here we present U-Pb zircon data from 23 samples of ca. 1.7-1.9 Ga granitoid rocks in and around the Siljan impact structure in central Sweden. Our results show that zircon from rocks within the structure that form an uplifted central plateau lost significantly less radiogenic Pb compared to zircon grains in rocks outside the plateau. We hypothesize that zircon in rocks within the central plateau remained crystalline through continuous annealing of crystal structure damages induced from decay of U and Th until uplifted to the surface by the impact event ca. 380 Ma ago. In contrast, zircon grains distal to the impact have accumulated radiation damage at shallow and cool conditions since at least 1.26 Ga, making them vulnerable to fluid-induced Pb-loss. Our data are consistent with studies on alpha recoil and fission tracks, showing that annealing in zircon occurs at temperatures as low as 200-250 °C. Zircon grains from these samples are texturally simple, i.e., neither xenocrysts nor metamorphic overgrowths have been observed. Therefore, the lower intercepts obtained from regression of variably discordant zircon data are more likely recording the age of fluid-assisted Pb-loss from radiation-damaged zircon at shallow levels rather than linked to regional magmatic or tectonic events.

| S-EPMC8007740 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data