Hydrothermal-Assisted Sintering Strategy Towards Porous- and Hollow-Structured LiNb3O8 Anode Material.

ABSTRACT: Porous- and hollow-structured LiNb3O8 anode material was prepared by a hydrothermal-assisted sintering strategy for the first time. The phase evolution was studied, and the formation mechanism of the porous and hollow structure was proposed. The formation of the unique structure can be attributed to the local existence of liquid phase because of the volatilization of Li element. As the anode material, the initial discharge capacity is 285.1 mAhg-1 at 0.1 C, the largest discharge capacity reported so far for LiNb3O8. Even after 50 cycles, the reversible capacity can still maintain 77.6 mAhg-1 at 0.1 C, about 2.5 times of that of LiNb3O8 samples prepared by traditional solid-state methods. The significant improvement of Li storage capacity can be attributed to the special porous and hollow structure, which provides a high density of active sites and short parallel channels for fast intercalation of Li+ ions through the surface.

SUBMITTER: Zhai H

PROVIDER: S-EPMC5526831 | biostudies-other | 2017 Dec

REPOSITORIES: biostudies-other

ACCESS DATA

Json Xml

Similar Datasets

Preparation of Porous Stainless Steel Hollow-Fibers through Multi-Modal Particle Size Sintering towards Pore Engineering.

Project description:The sintering of metal powders is an efficient and versatile technique to fabricate porous metal elements such as filters, diffusers, and membranes. Neck formation between particles is, however, critical to tune the porosity and optimize mass transfer in order to minimize the densification process. In this work, macro-porous stainless steel (SS) hollow-fibers (HFs) were fabricated by the extrusion and sintering of a dope comprised, for the first time, of a bimodal mixture of SS powders. The SS particles of different sizes and shapes were mixed to increase the neck formation between the particles and control the densification process of the structure during sintering. The sintered HFs from particles of two different sizes were shown to be more mechanically stable at lower sintering temperature due to the increased neck area of the small particles sintered to the large ones. In addition, the sintered HFs made from particles of 10 and 44 μm showed a smaller average pore size (<1 μm) as compared to the micron-size pores of sintered HFs made from particles of 10 μm only and those of 10 and 20 μm. The novel HFs could be used in a range of applications, from filtration modules to electrochemical membrane reactors.

| S-EPMC5618125 | biostudies-literature

Electrochemically anodized porous silicon: Towards simple and affordable anode material for Li-ion batteries.

Project description:Silicon is being increasingly studied as the next-generation anode material for Li-ion batteries because of its ten times higher gravimetric capacity compared with the widely-used graphite. While nanoparticles and other nanostructured silicon materials often exhibit good cyclability, their volumetric capacity tends to be worse or similar than that of graphite. Furthermore, these materials are commonly complicated and expensive to produce. An effortless way to produce nanostructured silicon is electrochemical anodization. However, there is no systematic study how various material properties affect its performance in LIBs. In the present study, the effects of particle size, surface passivation and boron doping degree were evaluated for the mesoporous silicon with relatively low porosity of 50%. This porosity value was estimated to be the lowest value for the silicon material that still can accommodate the substantial volume change during the charge/discharge cycling. The optimal particle size was between 10-20?µm, the carbide layer enhanced the rate capability by improving the lithiation kinetics, and higher levels of boron doping were beneficial for obtaining higher specific capacity at lower rates. Comparison of pristine and cycled electrodes revealed the loss of electrical contact and electrolyte decay to be the major contributors to the capacity decay.

| S-EPMC5554169 | biostudies-literature

Facile Construction of Porous ZnMn2O4 Hollow Micro-Rods as Advanced Anode Material for Lithium Ion Batteries.

Project description:Spinel ZnMn2O4 is considered a promising anode material for high-capacity Li-ion batteries due to their higher theoretical capacity than commercial graphite anode. However, the insufficient cycling and rate properties seriously limit its practical application. In this work, porous ZnMn2O4 hollow micro-rods (ZMO HMRs) are synthesized by a facile co-precipitation method coupled with annealing treatment. On the basis of electrochemical analyses, the as-obtained samples are first characterized by X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, and scanning electron microscopy techniques. The influences of different polyethylene glycol 400 (PEG 400) additions on the formation of the hollow rod structure are also discussed. The abundant multi-level pore structure and hollow feature of ZMO HMRs effectively alleviate the volume expansion issue, rendering abundant electroactive sites and thereby guaranteeing convenient Li+ diffusion. Thanks to these striking merits, the ZMO HMRs anode exhibits excellent electrochemical lithium storage performance with a reversible specific capacity of 761 mAh g-1 at a current density of 0.1 A g-1, and a long-cycle specific capacity of 529 mAh g-1 after 1000 cycles at 2.0 A g-1 and keep a remarkable rate capability. In addition, the assembled ZMO HMRs-based full cells deliver an excellent rate capacity, and when the current density returns to 0.05 A g-1, the specific capacity can still reach 105 mAh g-1 and remains at 101 mAh g-1 after 70 cycles, maintaining a material-level energy density of approximately 273 Wh kg-1. More significantly, such striking electrochemical performance highlights that porous ZMO HMRs could be a promising anode candidate material for LIBs.

| S-EPMC9920744 | biostudies-literature

Hollow Hemispherical Lithium Iron Silicate Synthesized by an Ascorbic Acid-Assisted Hydrothermal Method as a Cathode Material for Li Ion Batteries.

Project description:High-capacity and high-voltage cathode materials are required to meet the increasing demand for energy density in Li ion batteries. Lithium iron silicate (Li2FeSiO4) is a cathode material with a high theoretical capacity of 331 mAh·g-1. However, its poor conductivity and low Li ion diffusion coefficient result in poor capability, hindering practical applications. Morphology has an important influence on the properties of materials, and nanomaterials with hollow structures are widely used in electrochemical devices. Herein, we report a novel hollow hemispherical Li2FeSiO4 synthesized by a template-free hydrothermal method with the addition of ascorbic acid. The hollow hemispherical Li2FeSiO4 consisted of finer particles with a shell thickness of about 80 nm. After carbon coating, the composite was applied as the cathode in Li ion batteries. As a result, the hollow hemispherical Li2FeSiO4/C exhibited a discharge capacity as high as 192 mAh·g-1 at 0.2 C, and the average capacities were 134.5, 115.5 and 93.4 mAh·g-1 at 0.5, 1 and 2 C, respectively. In addition, the capacity increased in the first few cycles and then decayed with further cycling, showing a warm-up like behavior, and after 160 cycles the capacities maintained 114.2, 101.6 and 79.3 mAh·g-1 at 0.5, 1 and 2 C, respectively. Such a method of adding ascorbic acid in the hydrothermal reaction can effectively synthesize hollow hemispherical Li2FeSiO4 with the enhanced electrochemical performance.

| S-EPMC9143007 | biostudies-literature

A Selective Oxidation Strategy towards the Yolk-Shell Structured ZnS@C Material for Ultra-Stable Li-Ion Storage.

Project description:Metal chalcogenides are attractive anode materials for lithium-ion batteries (LIBs) due to their high theoretical capacities. With the advantages of low cost and abundance reserves, ZnS is regarded as the prime candidate anode material for future generations, but its practical application is hindered by the large volume expansion during repeated cycling processes and inherent poor conductivity. Rational design of the microstructure with large pore volume and high specific surface area is of great significance to solve these problems. Here, a carbon-coated ZnS yolk-shell structure (YS-ZnS@C) has been prepared by selective partial oxidation of a core-shell structured ZnS@C precursor in air and subsequent acid etching. Studies show that the carbon wrapping and proper etching to bring cavities can not only improve the material's electrical conductivity, but can also effectively alleviate the volume expansion problem of ZnS during its cycles. As a LIB anode material, the YS-ZnS@C exhibits an obvious superiority in capacity and cycle life compared to ZnS@C. The YS-ZnS@C composite shows a discharge capacity of 910 mA h g-1 at the current density of 100 mA g-1 after 65 cycles, compared to only 604 mA h g-1 for ZnS@C after 65 cycles. Notably, at a large current density of 3000 mA g-1, a capacity of 206 mA h g-1 can still be maintained after 1000 cycles (over three times of the capacity for ZnS@C). It is expected that the synthetic strategy developed here is applicable to designing various high-performance metal chalcogenide-based anode materials for LIBs.

| S-EPMC10004707 | biostudies-literature

Unique Urchin-like Ca2Ge7O16 Hierarchical Hollow Microspheres as Anode Material for the Lithium Ion Battery.

Project description:Germanium is an outstanding anode material in terms of electrochemical performance, especially rate capability, but its developments are hindered by its high price because it is rare in the crust of earth, and its huge volume variation during the lithium insertion and extraction. Introducing other cheaper elements into the germanium-based material is an efficient way to dilute the high price, but normally sacrifice its electrochemical performance. By the combination of nanostructure design and cheap element (calcium) introduction, urchin-like Ca2Ge7O16 hierarchical hollow microspheres have been successfully developed in order to reduce the price and maintain the good electrochemical properties of germanium-based material. The electrochemical test results in different electrolytes show that ethylene carbonate/dimethyl carbonate/diethyl carbonate (3/4/3 by volume) with 5 wt% fluoroethylene carbonate additive is the most suitable solvent for the electrolyte. From the electrochemical evaluation, the as-synthesized Ca2Ge7O16 hollow microspheres exhibit high reversible specific capacity of up to 804.6 mA h g(-1) at a current density of 100 mA g(-1) after 100 cycles and remarkable rate capability of 341.3 mA h g(-1) at a current density of 4 A g(-1). The growth mechanism is proposed based on our experimental results on the growth process.

| S-EPMC4462153 | biostudies-literature

Hollow porous SiO2 nanocubes towards high-performance anodes for lithium-ion batteries.

Project description:The high theoretical capacity and low discharge potential of silicon have attracted much attention on Si-based anodes. Herein, hollow porous SiO2 nanocubes have been prepared via a two-step hard-template process and evaluated as electrode materials for lithium-ion batteries. The hollow porous SiO2 nanocubes exhibited a reversible capacity of 919 mAhg(-1) over 30 cycles. The reasonable property could be attributed to the unique hollow nanostructure with large volume interior and numerous crevices in the shell, which could accommodate the volume change and alleviate the structural strain during Li ions' insertion and extraction, as well as allow rapid access of Li ions during charge/discharge cycling. It is found that the formation of irreversible or reversible lithium silicates in the anodes determines the capacity of a deep-cycle battery, fast transportation of Li ions in hollow porous SiO2 nanocubes is beneficial to the formation of Li2O and Si, contributing to the high reversible capacity.

| S-EPMC3610094 | biostudies-literature

Biomass-Derived Porous Carbon from Agar as an Anode Material for Lithium-Ion Batteries.

Project description:New porous activated carbons with a high surface area as an anode material for lithium-ion batteries (LIBs) were synthesized by a one-step, sustainable, and environmentally friendly method. Four chemical activators-H2SO4, H3PO4, KOH, and ZnCl2-have been investigated as facilitators of the formation of the porous structure of activated carbon (AC) from an agar precursor. The study of the materials by Brunauer-Emmett-Teller (BET) and scanning electron microscopy (SEM) methods revealed its highly porous meso- and macro-structure. Among the used chemical activators, the AC prepared with the addition of KOH demonstrated the best electrochemical performance upon its reaction with lithium metal. The initial discharge capacity reached 931 mAh g-1 and a reversible capacity of 320 mAh g-1 was maintained over 100 cycles at 0.1 C. High rate cycling tests up to 10 C demonstrated stable cycling performance of the AC from agar.

| S-EPMC8746817 | biostudies-literature

Urea-assisted hydrothermal synthesis of a hollow hierarchical LiNi0.5Mn1.5O4 cathode material with tunable morphology characteristics.

Project description:A hollow hierarchical LiNi0.5Mn1.5O4 cathode material has been synthesized via a urea-assisted hydrothermal method followed by a high-temperature calcination process. The effect of reactant concentration on the structure, morphology and electrochemical properties of the carbonate precursor and corresponding LiNi0.5Mn1.5O4 product has been intensively investigated. The as-prepared samples were characterized by XRD, FT-IR, SEM, CV, EIS, GITT and constant-current charge/discharge tests. The results show that all samples belong to a cubic spinel structure with mainly Fd3m space group, and the Mn3+ content and impurity content initially decrease and then increase slightly with the reactant concentration increasing. SEM observation shows that the particle morphology and size of carbonate precursor can be tailored by changing reactant concentration. The LiNi0.5Mn1.5O4 sample obtained from the carbonate precursor hydrothermally synthesized at a reactant concentration of 0.3 mol L-1 exhibits the optimal overall electrochemical properties, with capacity retention rate of 96.8% after 100 cycles at 1C rate and 10C discharge capacity of 124.9 mA h g-1, accounting for 99.9% of that at 0.2C rate. The excellent electrochemical performance can be mainly attributed to morphological characteristics, that is, smaller particle size with homogeneous distribution, in spite of lower Mn3+ content.

| S-EPMC9085430 | biostudies-literature

Novel Hybrid Nanoparticles of Vanadium Nitride/Porous Carbon as an Anode Material for Symmetrical Supercapacitor.

Project description:AbstractHybrid materials of vanadium nitride and porous carbon nanoparticles (VN/PCNPs) were fabricated by a facile pyrolysis process of vanadium pentoxide (V2O5) xerogel and melamine at relatively low temperature of 800 °C for supercapacitor application. The effects of the feed ratio of V2O5 to melamine (r), and nitrogen flow rate on the microstructure and electrochemical performance were also investigated. It was found that the size of the as-synthesized nanoparticles is about 20 nm. Both r value and N2 flow rate have enormous impacts on morphology and microstructure of the nanoparticle, which correspondingly determined the electrochemical performance of the material. The VN/C hybrid nanoparticles exhibited high capacitive properties, and a maximum specific capacitance of 255.0 F g-1 was achieved at a current density of 1.0 A g-1 in 2 M KOH aqueous electrolyte and the potential range from 0 to -1.15 V. In addition, symmetrical supercapacitor fabricated with the as-synthesized VN/PCNPs presents a high specific capacitance of 43.5 F g-1 at 0.5 A g-1 based on the entire cell, and an energy density of 8.0 Wh kg-1 when the power density was 575 W kg-1. Even when the power density increased to 2831.5 W kg-1, the energy density still remained 6.1 Wh kg-1.Graphical abstract

| S-EPMC6223780 | biostudies-literature

OmicsDI is part of the ELIXIR infrastructure

OmicsDI is an Elixir interoperability service. Learn more ›

Tweets

OmicsDI Databases

PRIDE
PeptideAtlas
MassIVE
JPOST Repository
Physiome Model Repository

EGA
EVA
ENA
LINCS
PAXDB
Cell Collective

MetaboLights
Metabolomics Workbench
MetabolomeExpress
GNPS
BioModels
FAIRDOMHub

ArrayExpress
dbGaP
ExpressionAtlas
GEO
NODE

Information

Databases
Help
API
Contact us
Code on GitHub
Terms of use
Submit Data